CN102504725A - 书刊侧胶及其生产方法 - Google Patents

书刊侧胶及其生产方法 Download PDF

Info

Publication number
CN102504725A
CN102504725A CN2011103058053A CN201110305805A CN102504725A CN 102504725 A CN102504725 A CN 102504725A CN 2011103058053 A CN2011103058053 A CN 2011103058053A CN 201110305805 A CN201110305805 A CN 201110305805A CN 102504725 A CN102504725 A CN 102504725A
Authority
CN
China
Prior art keywords
eva
vinyl acetate
side glue
parts
content
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011103058053A
Other languages
English (en)
Other versions
CN102504725B (zh
Inventor
陈惠娟
邵宝有
李光鹏
汪小亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG GOOD ADHESIVE CO Ltd
Original Assignee
ZHEJIANG GOOD ADHESIVE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG GOOD ADHESIVE CO Ltd filed Critical ZHEJIANG GOOD ADHESIVE CO Ltd
Priority to CN201110305805.3A priority Critical patent/CN102504725B/zh
Publication of CN102504725A publication Critical patent/CN102504725A/zh
Application granted granted Critical
Publication of CN102504725B publication Critical patent/CN102504725B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明所设计的一种书刊侧胶，它包括石蜡10-20份，聚乙烯蜡0-10份，VA(醋酸乙烯)含量为28％，熔融指数为25的EVA(乙烯-醋酸乙烯共聚物)5-30份，VA(醋酸乙烯)含量为28％，熔融指数为400的EVA(乙烯-醋酸乙烯共聚物)5-30份，VA(醋酸乙烯)含量为33％，熔融指数为25的EVA(乙烯-醋酸乙烯共聚物)5-30份，抗氧剂0.1-1.5份，增塑剂0-5份，填料2-10份，聚烯烃5-20份，松香树脂5-30份，石油树脂5-30份，偶联剂0.1-1份。该书刊侧胶能对封面覆膜或特种油墨体系的书刊进行粘合，且粘合牢度高，不易发生脱胶等现象。另外，该书刊侧胶对特种材质也具有较高的粘结强度，使其粘合的适用范围更广。该书刊侧胶的固化时间为7-14秒，可调整配方使其满足不同型号设备、不同运行速度要求。

Description

书刊侧胶及其生产方法
技术领域
本发明涉及热熔胶的生产领域，尤其是一种书刊侧胶及其生产方法。
背景技术
热熔胶粘剂可应用于社会生活的各个方面，主要有：建筑及装修工业，电子电器行业，包装工业，木工业，纸加工与书本装订工业，制鞋工业，卫生材料及医用工业等等。例如包装工业中，饮料业、奶业、啤酒业等，自从应用热熔胶即告别了捆扎的历史，直接用涂胶机自动喷胶、包装，实现了高速、自动、平稳的可能。再比如书刊装订工业，使用无线胶粘装订的书刊装订质量好，加工速度快，适用范围广，近年来在我国迅速推广应用。无线胶粘装订已基本替代铁丝平订老工艺。
安全环保，适用高速自动化生产的热熔胶已成为发达国家主要的胶粘剂品种，在未来5年内，热熔胶仍将是全球增长最快的品种之一。其中书刊装订用热熔胶，尤其是书刊侧胶的要求越来越高，这主要是因为书刊所用纸张种类繁多、型号复杂，并且还有多种覆膜，另外书刊印刷经常使用到油墨，且油墨厚度各异、体系繁多，市场现有EVA单体系普通书刊侧胶已不能满足广泛使用要求。
普通的书刊侧胶对表面具有覆膜体系或表面为特种油墨体系的书刊的粘合牢度差，经常出现脱胶、露背现象，对特种纸张的粘结也不够牢固，影响书刊装订质量。
发明内容
本发明的目的是为了解决上述技术的不足而提供一种粘合适用性广，且对油墨、覆膜体系粘合牢度高的书刊侧胶及其生产方法。
为了达到上述目的，本发明所设计的书刊侧胶，它包括石蜡10-20份，聚乙烯蜡0-10份，VA(醋酸乙烯)含量为28％，熔融指数为25的EVA(乙烯-醋酸乙烯共聚物)5-30份，VA(醋酸乙烯)含量为28％，熔融指数为400的EVA(乙烯-醋酸乙烯共聚物)5-30份，VA(醋酸乙烯)含量为33％，熔融指数为25的EVA(乙烯-醋酸乙烯共聚物)5-30份，抗氧剂0.1-1.5份，增塑剂0-5份，填料2-10份，聚烯烃5-20份，松香树脂5-30份，石油树脂5-30份，偶联剂0.1-1份，以上均为质量份数。
上述抗氧剂为链转移剂或者为阻酚类；填料为滑石粉或粘土或碳酸钙。
所述的书刊侧胶的生产方法：首先，反应釜加热至150摄氏度并控温，加入石蜡和聚乙烯蜡，待完全溶解后，把三种EVA，包括：VA(醋酸乙烯)含量为28％，熔融指数为25的EVA(乙烯-醋酸乙烯共聚物)，VA(醋酸乙烯)含量为28％，熔融指数为400的EVA(乙烯-醋酸乙烯共聚物)和VA(醋酸乙烯)含量为33％，熔融指数为25的EVA(乙烯醋酸乙烯共聚物)，与抗氧剂、填料、增塑剂和偶联剂拌匀后一起逐步加入反应釜中，待全部溶解后降温至130摄氏度并控温，再依次逐步加入聚烯烃、松香树脂、石油树脂，待全部溶解后降温至120摄氏度并控温，压力控制：加料过程中保持常压，加料完成并降温至120摄氏度后抽真空10-15分钟，再调整为常压；搅拌时间：在加料过程中保持搅拌，加料完成后减速搅拌，搅拌总时间控制在2-3小时；最后出料，冷却，造粒后得到书刊侧胶成品。
本发明所得到的书刊侧胶及其生产方法，其得到的书刊侧胶能对封面覆膜或特种油墨体系的书刊进行粘合，且粘合牢度高，不易发生脱胶等现象。另外，该书刊侧胶对特种材质也具有较高的粘结强度，使其粘合的适用范围更广。该书刊侧胶的固化时间为7-14秒，可调整配方使其满足不同型号设备、不同运行速度要求。
具体实施方式
下面通过实施例对本发明作进一步的描述。
实施例1：
本实施例描述的书刊侧胶，它包括石蜡10-20份，聚乙烯蜡0-10份，VA(醋酸乙烯)含量为28％，熔融指数为25的EVA(乙烯-醋酸乙烯共聚物)5-30份，VA(醋酸乙烯)含量为28％，熔融指数为400的EVA(乙烯-醋酸乙烯共聚物)5-30份，VA(醋酸乙烯)含量为33％，熔融指数为25的EVA(乙烯-醋酸乙烯共聚物)5-30份，抗氧剂0.1-1.5份，增塑剂0-5份，填料2-10份，聚烯烃5-20份，松香树脂5-30份，石油树脂5-30份，偶联剂0.1-1份，以上均为质量份数。
上述抗氧剂为链转移剂或者为阻酚类；填料为滑石粉或粘土或碳酸钙。
所述的书刊侧胶的生产方法：首先，反应釜加热至150摄氏度并控温，加入石蜡和聚乙烯蜡，待完全溶解后，把三种EVA，包括：VA(醋酸乙烯)含量为28％，熔融指数为25的EVA(乙烯-醋酸乙烯共聚物)，VA(醋酸乙烯)含量为28％，熔融指数为400的EVA(乙烯-醋酸乙烯共聚物)和VA(醋酸乙烯)含量为33％，熔融指数为25的EVA(乙烯醋酸乙烯共聚物)，与抗氧剂、填料、增塑剂和偶联剂拌匀后一起逐步加入反应釜中，待全部溶解后降温至130摄氏度并控温，再依次逐步加入聚烯烃、松香树脂、石油树脂，待全部溶解后降温至120摄氏度并控温，压力控制：加料过程中保持常压，加料完成并降温至120摄氏度后抽真空10-15分钟，再调整为常压；搅拌时间：在加料过程中保持搅拌，加料完成后减速搅拌，搅拌总时间控制在2-3小时；最后出料，冷却，造粒即可得到书刊侧胶成品。

Claims (3)

1.一种书刊侧胶，其特征是它包括石蜡10-20份，聚乙烯蜡0-10份，VA(醋酸乙烯)含量为28％，熔融指数为25的EVA(乙烯-醋酸乙烯共聚物)5-30份，VA(醋酸乙烯)含量为28％，熔融指数为400的EVA(乙烯-醋酸乙烯共聚物)5-30份，VA(醋酸乙烯)含量为33％，熔融指数为25的EVA(乙烯-醋酸乙烯共聚物)5-30份，抗氧剂0.1-1.5份，增塑剂0-5份，填料2-10份，聚烯烃5-20份，松香树脂5-30份，石油树脂5-30份，偶联剂0.1-1份，以上均为质量份数。
2.根据权利要求1所述的书刊侧胶，其特征是所述的抗氧剂为链转移剂或者为阻酚类；填料为滑石粉或粘土或碳酸钙。
3.一种如权利要求1所述的书刊侧胶的生产方法，其特征是反应釜加热至150摄氏度并控温，加入石蜡和聚乙烯蜡，待完全溶解后，把三种EVA，包括：VA(醋酸乙烯)含量为28％，熔融指数为25的EVA(乙烯-醋酸乙烯共聚物)，VA(醋酸乙烯)含量为28％，熔融指数为400的EVA(乙烯-醋酸乙烯共聚物)和VA(醋酸乙烯)含量为33％，熔融指数为25的EVA(乙烯-醋酸乙烯共聚物)，与抗氧剂、填料、增塑剂和偶联剂拌匀后一起逐步加入反应釜中，待全部溶解后降温至130摄氏度并控温，再依次逐步加入聚烯烃、松香树脂、石油树脂，待全部溶解后降温至120摄氏度并控温，压力控制：加料过程中保持常压，加料完成并降温至120摄氏度后抽真空10-15分钟，再调整为常压；搅拌时间：在加料过程中保持搅拌，加料完成后减速搅拌，搅拌总时间控制在2-3小时；最后出料，冷却，造粒，即可得到书刊侧胶成品。
CN201110305805.3A 2011-10-11 2011-10-11 书刊侧胶及其生产方法 Expired - Fee Related CN102504725B (zh)