CN102503326A - Environmentally-friendly concrete interface treating agent - Google Patents
Environmentally-friendly concrete interface treating agent Download PDFInfo
- Publication number
- CN102503326A CN102503326A CN2011103172256A CN201110317225A CN102503326A CN 102503326 A CN102503326 A CN 102503326A CN 2011103172256 A CN2011103172256 A CN 2011103172256A CN 201110317225 A CN201110317225 A CN 201110317225A CN 102503326 A CN102503326 A CN 102503326A
- Authority
- CN
- China
- Prior art keywords
- agent
- powder
- treating agent
- interface treating
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a concrete interface agent which uses modified S95 grade slag powder as a raw material, and belongs to the technical field of solid waste comprehensive utilization and chemical building material. The raw material proportion in the agent of the invention is as follows: 35-50% of modified S95 grade slag powder, 15-30% of cement, 30-45% of sand, 2.0-5.0% of emulsion powder, 0.1-0.5% of water-retaining agent and 0.1-0.3% of anti-cracking agent. According to proportion, materials are weighed and orderly placed into a blender and mixed adequately to obtain the interface treating agent. The interface agent is packaged in form of powder and is convenient to convey. The interface treating agent can be used on the spot by adding water and agitating uniformly. The environmentally-friendly concrete interface treating agent has excellent water-retaining performance, strong construction performance and bonding force and the like.
Description
Technical field
The present invention relates to a kind of is the feedstock production concrete interface treating agent with the modified S 95-grade slag powder, belongs to solid waste comprehensive utilization and chemical building material technical field.
Background technology
Concrete interface treating agent has superpower bonding force, good water tolerance, stability to aging.Improve motar and can effectively avoid the coat of plaster hollowing, come off problems such as shrinkage cracking the cohesive strength of basic unit.Be used to handle surfaces such as concrete, gas concrete, Dinas brickes and flyash brick, solve, cause the coat of plaster hollowing, ftracture, peel off etc. because these water absorbent surface property are strong or smooth to cause that the interface is difficult for bonding.Can strengthen between the new-old concrete greatly and the cohesive force of concrete and motar.The cutter hair operation that can replace the conventional concrete surface; Improve gas concrete surface plastering technology; Also has very strong perviousness; Can fully soak into nearly layer material surface, improve the adsorptive power of newly smearing putty and base material and increase viscosifying power, be the indispensable supplementary material of modern architecture and decoration construction.
In order to solve problems such as ubiquitous hollowing ftractures between body of wall basic unit and the float coat, flake, come off, and reduce the dependence of interfacial agents, press for and seek a kind of environmentally friendly material cement.
Summary of the invention
The purpose of this invention is to provide a kind of modified S 95-grade slag powder that utilizes and be the feedstock production concrete interface treating agent.
Interfacial agents of the present invention is characterised in that the composition and the mass percent of this interfacial agents are following:
Modified S 95 slag powders: 35-50%
Cement: 15-30%
Sand: 30-45%
Latex powder: 2.0-5.0%
Water-holding agent: 0.1-0.5%
Anti-fissuring agent: 0.1-0.3%
Described modified S 95-grade slag powder is with superfine steel slag micropowder (specific surface area>=600 m
2/ kg; Superfine steel slag less than 30 μ m particle diameters accounts for more than 90% of total mass, metal Ferrum content≤0.5%) and be properties-correcting agent by the beta-type semi-hydrated gypsum that the coal-fired plant flue gas desulphurization gypsum calcination forms, the S95 grade slag powder is carried out modification; S95 grade slag powder after the modification has the early strength height; Its 3 days activity index>=80%, 7 day activity index>=90%, 28 day activity index>=100%.
Described cement is 42.5 grades or 52.5 grades of ordinary Portland cements.
Described anti-fissuring agent is a polypropylene fibre, and diameter is 30-50 μ m, and length is 5-10mm.
Described sand, particle diameter are 0.05-0.5mm.
Described latex powder is any or two kinds in styrene-propene yogurt rubber powder, propenoate latex powder, the vinyl acetate-ethylene latex powder.
Described water-holding agent is any or two kinds in Natvosol, hydroxyethylmethyl-cellulose, the Vltra tears.
According to the said ratio batching, put into mixing machine successively, even through thorough mixing, promptly get interface treating agent; Need add a certain amount of water in use, can use after stirring.
The dried powder boundary agent that the inventive method makes has following characteristics:
1. have good water-retentivity and workability.
2. the dried powder boundary agent is a powdery solid, is convenient to transportation; During use, adding water can fully stir.
3. preparation technology and equipment requirements are simple, help suitability for industrialized production and apply.
4. modified S 95-grade slag powder replaces a part of cement, and it is about about 10 not only to practice thrift cost, has also opened up a new approach of solid waste comprehensive utilization.
Embodiment
After specific embodiment of the present invention being described at present.
Be example with preparation 100g interfacial agents in the instance.
Embodiment 1
By regulation proportioning weigh batching, the consumption of each raw material is following:
Modified S 95 slag powders: 35.0g
Cement: 20.0g
Sand: 41.0g
Latex powder: 3.5g
Water-holding agent: 0.4g
Anti-fissuring agent: 0.1g
Above-mentioned various raw materials are put into mixing machine, after thorough mixing is even, promptly get interfacial agents.An amount of moisture content of adding stirs and can be used for the processing of body of wall basic unit during use.
Embodiment 2
By regulation proportioning weigh batching, the consumption of each raw material is following:
Modified S 95 slag powders: 39.0g
Cement: 27.5g
Sand: 30.0g
Latex powder: 3.0g
Water-holding agent: 0.4g
Anti-fissuring agent: 0.1g
Above-mentioned various raw materials are put into mixing machine, after thorough mixing is even, promptly get interfacial agents.An amount of moisture content of adding stirs and can be used for the processing of body of wall basic unit during use.
Embodiment 3
By regulation proportioning weigh batching, the consumption of each raw material is following:
Modified S 95 slag powders: 45.0g
Cement: 15.0g
Sand: 37.0g
Latex powder: 2.5g
Water-holding agent: 0.35g
Anti-fissuring agent: 0.15g
Above-mentioned various raw materials are put into mixing machine, after thorough mixing is even, promptly get interfacial agents.An amount of moisture content of adding stirs and can be used for the processing of body of wall basic unit during use.
Utilize modified S 95-grade slag powder all can reach the technical indicator of JG/T907-2002 " concrete interface treating agent " standard code for concrete interface agent each item performance of feedstock production.
Claims (1)
1. environment-friendly type concrete interface treating agent, it is characterized in that: the composition and the mass percent of this interface treating agent are following:
Modified S 95 slag powders: 35-50%
Cement: 15-30%
Sand: 30-45%
Latex powder: 2.0-5.0%
Water-holding agent: 0.1-0.5%
Anti-fissuring agent: 0.1-0.3%
Described modified S 95-grade slag powder is to be properties-correcting agent with superfine steel slag micropowder with by the beta-type semi-hydrated gypsum that the coal-fired plant flue gas desulphurization gypsum calcination forms, and the S95 grade slag powder is carried out modification; The specific surface area of superfine steel slag micropowder>=600 m
2/ kg accounts for more than 90% of total mass, metal Ferrum content≤0.5% less than the superfine steel slag micropowder of 30 μ m particle diameters; 3 days activity index>=80%, 7 day activity indexs>=90%, 28 day activity index>=100% of S95 grade slag powder after the modification;
Described cement is 42.5 grades or 52.5 grades of ordinary Portland cements;
Described anti-fissuring agent is a polypropylene fibre, and diameter is 30-50 μ m, and length is 5-10mm;
Described sand, particle diameter are 0.05-0.5mm;
Described latex powder is any or two kinds in styrene-propene yogurt rubber powder, propenoate latex powder, the vinyl acetate-ethylene latex powder;
Described water-holding agent is any or two kinds in Natvosol, hydroxyethylmethyl-cellulose, the Vltra tears.