CN102501447A - 双银 low-e玻璃 - Google Patents
双银 low-e玻璃 Download PDFInfo
- Publication number
- CN102501447A CN102501447A CN2011103489177A CN201110348917A CN102501447A CN 102501447 A CN102501447 A CN 102501447A CN 2011103489177 A CN2011103489177 A CN 2011103489177A CN 201110348917 A CN201110348917 A CN 201110348917A CN 102501447 A CN102501447 A CN 102501447A
- Authority
- CN
- China
- Prior art keywords
- layer
- glass
- silver
- nicro
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种双银LOW-E玻璃,包括有玻璃基片,在玻璃基片的复合面上由内到外依次相邻地复合有十一个膜层,其特征在于:其中第一膜层即最内层为Si3N4层,第二层为TiO2层,第三层为NiCrO2层,第四层为TiO2层,第五层为Ag层,第六层为NiCrO层,第七层为TiO2层,第八层为NiCrO层,第九层为Ag层,第十层为NiCrO层最外层为Si3N4层。本发明目的是克服了现有技术的不足,提供一种透过率高,提高膜层硬度及避免不良原子深入破坏银层的双银LOW-E玻璃。
Description
【技术领域】
本发明涉及一种镀膜玻璃,更具体地说是一种双银LOW-E玻璃。
【背景技术】
玻璃是在当代的生产和生活中扮演着重要角色,建筑物的门窗汽车车窗和挡风玻璃等等许多地方都用到玻璃,给生产和生活带来了很多的方便。但是普通玻璃阳光透过率低,钢化后透过率和漂移量大,颜色偏差大。
【发明内容】
本发明目的是克服了现有技术的不足,提供一种透过率高,提高膜层硬度及避免不良原子深入破坏银层的双银LOW-E玻璃。
本发明是通过以下技术方案实现的:
一种双银LOW-E玻璃,包括有玻璃基片1,在玻璃基片的复合面上由内到外依次相邻地复合有十一个膜层,其特征在于:其中第一膜层即最内层为Si3N4层21,第二层为TiO2层22,第三层为NiCrO2层23,第四层为TiO2层24,第五层为Ag层25,第六层为NiCrO层26,第七层为TiO2层27,第八层为NiCrO层28,第九层为Ag层29,第十层为NiCrO层20最外层为Si3N4层211。
如上所述的双银LOW-E玻璃,其特征在于所述第一膜层的Si3N4层21的厚度为15~20nm。
如上所述的双银LOW-E玻璃,其特征在于所述第二膜层的TiO2层22的厚度为25~35nm。
如上所述的双银LOW-E玻璃,其特征在于所述第三膜层的NiCrO2层23的厚度为2~5nm。
如上所述的双银LOW-E玻璃,其特征在于所述第四层TiO2层24的厚度为5~10nm。
如上所述的双银LOW-E玻璃,其特征在于所述第五层Ag层25的厚度为8nm。
如上所述的双银LOW-E玻璃,其特征在于所述第六层NiCrO层26的厚度为2~5nm。
如上所述的双银LOW-E玻璃,其特征在于所述第七层TiO2层27的厚度为25~35nm。
如上所述的双银LOW-E玻璃,其特征在于所述第八层NiCrO层26的厚度为2~5nm。
如上所述的双银LOW-E玻璃,其特征在于所述第九层Ag层25的厚度为10nm,所述第十层NiCrO层20的厚度为2~5nm,所述最外层Si3N4层211的厚度为25~35nm。
与现有技术相比,本发明有如下优点:
1、本玻璃利用TiO2可降低银层的面电阻,减少银的消耗,又可以减少LOW-E热处理后产生光散射,Si3N4作顶膜及底膜,提高膜层硬度及避免不良原子深入破坏银层镀膜层,使整个膜层在高温下耐热性更好,机械性更好,具有对可见光高透过及对中远红外线高反射的特 性。
2、本玻璃透光率T(透过透明或半透明体的光通量与其入射光通量的百分率)≥78%;本玻璃辐射率≤0.04,辐射率是某物体的单位面积辐射的热量同单位面积黑体在相同温度、相同条件下辐射热量之比。辐射率定义是某物体吸收或反射热量的能力。玻璃的辐射率越接近于零,其绝热性能就越好。反射率RG=7%~15%,遮阳系数SC=0.5~0.65。
3、本玻璃可以用作中空玻璃使用,在两片中空玻璃合片之前可以长期储存,异地合片加工方便。
4、本玻璃钢化后透过率偏差小,漂移小,颜色偏差小a*=-2~-4,b*=-4~-7。
【附图说明】
图1是本发明结构示意图。
【具体实施方式】
一种双银LOW-E玻璃,包括有玻璃基片1,在玻璃基片的复合面上由内到外依次相邻地复合有十一个膜层,其中第一膜层即最内层为Si3N4层21,第二层为TiO2层22,第三层为NiCrO2层23,第四层为TiO2层24,第五层为Ag层25,第六层为NiCrO层26,第七层为TiO2层27,第八层为NiCrO层28,第九层为Ag层29,第十层为NiCrO层20最外层为Si3N4层211。
所述最内层Si3N4层21,即氮化硅层;Si3N4是一种非常坚硬的材料,提高膜层硬度及避免不良原子深入破坏银层镀膜层,使整个膜层在高温下耐热性更好,机械性更好,它确保了整个镀层具有 良好的机械耐久性。Si3N4层21的厚度为15~20nm,nm是纳米,1m=109nm。
所述的第二层TiO2层22,即钛的氧化物——二氧化钛。采用高折射率n=2.5的TiO2是为了提高玻璃的透光率,降低银层的面电阻,减少银的消耗,又可以减少LOW-E热处理后产生光散射,而且玻璃呈中性颜色,TiO2膜表面非常光滑,因而改善了银膜的导电率。TiO2层的厚度是25~35nm。
所述第三膜层的NiCrO2层23,即二氧化镍铬层,二氧化镍铬层为了进一步保护银膜,以避免银膜在反应溅射过程受到浸蚀,还要在薄的银膜一侧或两侧增加所谓的“阻挡层”,对于镀层具有非常良好的抗化学和机械性能。厚度为2~5nm。
所述第四层TiO2层24,即钛的氧化物——二氧化钛,厚度为5~10nm。
所述第五层Ag层25,即金属银层,金属银提供了较低的辐射率,起环保节能的作用;厚度为8nm。
所述第六层NiCrO层26,即氧化镍铬层,氧化镍铬层为了进一步保护银膜,以避免银膜在反应溅射过程受到浸蚀,还要在薄的银膜一侧或两侧增加所谓的“阻挡层”,对于镀层具有非常良好的抗化学和机械性能。厚度为2~5nm。
所述第七层TiO2层27,即钛的氧化物——二氧化钛,厚度为25~35nm。
所述第八层NiCrO层26,即氧化镍铬层,厚度为2~5nm。
所述第九层Ag层25,即金属银层,金属银提供了较低的辐射率,起环保节能的作用;厚度为10nm。
所述第十层NiCrO层20,即氧化镍铬层,厚度为2~5nm。
所述的最外层Si3N4层211,即氮化硅层;它确保了整个镀层具有良好的机械耐久性。Si3N4膜是非常坚硬,而且抗划伤,它的硬度是玻璃的三倍,是TiO2的二倍;Si3N4的折射率为2.05,吸收率几乎为零,所以它作为Low-e镀层的顶层是非常适合的。Si3N4层的厚度为25~35nm。
双银LOW-E玻璃在阳光性能上有很大提高,两层银膜可以使发射率降到很低值,即传热系数降到低值;而且它在降低太阳能的同时,仍然能保持很高的可见光透过率,所以双银LOW-E镀层在阳光性能方面具有良好的选择性。
LOW-E玻璃也叫做低辐射镀膜玻璃。
本玻璃利用TiO2可降低银层的面电阻,减少银的消耗,又可以减少LOW-E热处理后产生光散射,Si3N4作顶膜及底膜,提高膜层硬度及避免不良原子深入破坏银层镀膜层,使整个膜层在高温下耐热性更好,机械性更好,具有对可见光高透过及对中远红外线高反射的特性。
本玻璃透光率T(透过透明或半透明体的光通量与其入射光通量的百分率)≥78%;本玻璃辐射率≤0.04,辐射率是某物体的单位面积辐射的热量同单位面积黑体在相同温度、相同条件下辐射热量之比。辐射率定义是某物体吸收或反射热量的能力。玻璃的辐射率越接近于零,其绝热性能就越好。反射率RG=715,遮阳系数SC=0.5~0.65。
本玻璃可以用作中空玻璃使用,在两片中空玻璃合片之前可以长期储存,异地合片加工方便。
本玻璃钢化后透过率偏差小,漂移小,颜色偏差小a*=-2~-4,b*=-4~-7。
Claims (10)
1.双银LOW-E玻璃,包括有玻璃基片(1),在玻璃基片的复合面上由内到外依次相邻地复合有十一个膜层,其特征在于:其中第一膜层即最内层为Si3N4层(21),第二层为TiO2层(22),第三层为NiCrO2层(23),第四层为TiO2层(24),第五层为Ag层(25),第六层为NiCrO层(26),第七层为TiO2层(27),第八层为NiCrO层(28),第九层为Ag层(29),第十层为NiCrO层(20)最外层为Si3N4层(211)。
2.根据权利要求1所述的双银LOW-E玻璃,其特征在于所述第一膜层的Si3N4层(21)的厚度为15~20nm。
3.根据权利要求1所述的双银LOW-E玻璃,其特征在于所述第二膜层的TiO2层(22)的厚度为25~35nm。
4.根据权利要求1所述的双银LOW-E玻璃,其特征在于所述第三膜层的NiCrO2层(23)的厚度为2~5nm。
5.根据权利要求1所述的双银LOW-E玻璃,其特征在于所述第四层TiO2层(24)的厚度为5~10nm。
6.根据权利要求1所述的双银LOW-E玻璃,其特征在于所述第五层Ag层(25)的厚度为8nm。
7.根据权利要求1所述的双银LOW-E玻璃,其特征在于所述第六层NiCrO层(26)的厚度为2~5nm。
8.根据权利要求1所述的双银LOW-E玻璃,其特征在于所述第七层TiO2层(27)的厚度为25~35nm。
9.根据权利要求1所述的双银LOW-E玻璃,其特征在于所述第八层NiCrO层(26)的厚度为2~5nm。
10.根据权利要求1所述的双银LOW-E玻璃,其特征在于所述第九层Ag层(25)的厚度为10nm,所述第十层NiCrO层(20)的厚度为2~5nm,所述最外层Si3N4层(211)的厚度为25~35nm。