CN102477639A - Antistatic warm keeping fabric - Google Patents
Antistatic warm keeping fabric Download PDFInfo
- Publication number
- CN102477639A CN102477639A CN2010105580861A CN201010558086A CN102477639A CN 102477639 A CN102477639 A CN 102477639A CN 2010105580861 A CN2010105580861 A CN 2010105580861A CN 201010558086 A CN201010558086 A CN 201010558086A CN 102477639 A CN102477639 A CN 102477639A
- Authority
- CN
- China
- Prior art keywords
- fiber
- antistatic
- conductive fiber
- cotton
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an antistatic warm keeping fabric, which comprises the following fibers in percentage by weight: 3%-15% of conductive fiber, 50%-70% of polyester fiber, 10%-30% of spandex fiber and 30%-50% of cotton or other fibers. The antistatic warm keeping fabric disclosed by the invention eliminates electrostatic hazards and simultaneously ensures the warm keeping effect, and the fabric is soft and elastic, is made of natural and environment-friendly raw materials, and can be widely used as the fabric of underwear, cotton-padded clothes and sports clothes.
Description
Technical field
The present invention relates to a kind of novel fabric, especially a kind of lining that has anti-static function and take into account good warming effect belongs to the technical field of fabric panel.
Background technology
Along with the raising day by day of living standard, the modern more and more pays attention to healthy, when selecting underclothes, except considering its color and style, also will consider the security of clothing, the feature of environmental protection and functional.On clothing basic function basis of invariable, the Clothes lining is is constantly researched and developed in the security of the emphasis clothing that People more and more is many, utilizes new technology to reduce the clothing dress and possibly give people's trouble caused, reduces potential safety hazard, improves the functional of clothing lining.
Static is that the human friction of understanding the earliest plays the electric charge that electrical phenomena produces, and it is static with respect to the power electricity of frequent use, and characteristic is that electric current is little, does not form the loop.Be characterized in motion, had friction will produce the static reaction, just may produce electric discharge phenomena when current potential is high.General electrostatic shock can make people produce pain and tremble, and the comfort that people wear dress ornament can reduce greatly, can make people produce mental handicape, and people's life is exerted an influence.For this reason, people begin to be placed on notice on the antistatic clothing lining of research and development, through the improvement to lining composition or production technology, make common lining have anti-static function.
Common on the market processing modification method has following several kinds:
1) surfactant addition type fiber: adopt and to add surfactant to carry out co-blended spinning in the spinning solution method, utilize surfactant continuous diffusion mobility from inside to outside, make fiber surface contain surfactant, but its result of use relatively a little less than;
2) blend, combined polymerization and graft modification type antistatic fibre, processing technology is had relatively high expectations, and cost is high;
3) metallic conduction fiber (with the general fibre blending), proportioning components and processing method are bigger to the antistatic effect influence;
4) carbon element conductive fiber (doping, coating, charing), technology falls behind.
Summary of the invention
To the demand, the invention provides a kind of antistatic thermal fabric, through rational material mixture ratio, suitable processing technology makes lining under the prerequisite that guarantees than high degree of comfort, has antistatic effect, and warming respond well.
The present invention is a kind of antistatic thermal fabric, and the fibrous and quality percentage composition of this lining is: conductive fiber 3%-15%, polyster fibre 50%-70%, spandex fibre 10%-30%, cotton or other fiber 30%-50%.
In the present invention's one preferred embodiment, described fabric quality percentage composition is: conductive fiber 4%-8%, polyster fibre 55%-65%, spandex fibre 15%-25%, cotton or other fiber 30%-40%.
In the present invention's one preferred embodiment, described conductive fiber can be that metallic compound type conductive fiber, metal are a kind of in conductive fiber, the conducting polymer fiber type.
In the present invention's one preferred embodiment, the silk footpath of described conductive fiber is 0.04-0.12mm.
In the present invention's one preferred embodiment, described other fiber comprises one or more in man-made cellulose fibers, natural silk, the cashmere.
The present invention has disclosed a kind of antistatic thermal fabric, and this lining has guaranteed the warming effect of lining when eliminating electrostatic hazard, and sense of touch is soft, with elasticity, the raw material natural environmental-protective can be widely used as the lining of various underwears, cotton dress and sportswear.
?
The specific embodiment
In order to make those skilled in the art person understand technical scheme of the present invention better, and make above-mentioned purpose of the present invention, feature and advantage can be more obviously understandable, below in conjunction with embodiment the present invention done further detailed explanation.
Embodiment 1
The practical implementation step is following:
A) selection is got the raw materials ready, and the fibrous and quality percentage composition of this lining is: conductive fiber 6%, polyster fibre 50%, spandex fibre 10%, cotton or other fiber 34%;
B) preparation functional yarn; Lining adopts organizine and tram to weave and forms; Wherein organizine is processed into the low twist complex yarn after adopting conductive fiber, cotton fiber and cashmere through drafting, rove, spun yarn, winding process; Tram adopts polyster fibre, and spandex fibre and natural silk are processed into the low twist complex yarn after through drafting, rove, spun yarn, winding process;
C) weave cotton cloth, on the loom yarn behind the winder is being processed functional cloth;
D) singe, temperature is controlled at 900 ℃, and speed is 2m/s;
E) destarch washing was banked up cloth 40 minutes in the amylase of 0.8/L, temperature is controlled at 85 ℃;
F) dyeing, fixation adopt reducing dye vat blue HSM to cooperate levelling agent, diffusant and acetum to improve the printing and dyeing effect earlier, add active dye fixing agent KS then, with 2% vinegar acid for adjusting pH value 5～6, and fixation bath raio 1:20,60 ℃ of temperature, 25 minutes time;
G) washing uses the soda ash of 0.4 grams per liter and the neutral detergent of 0.3 grams per liter that cloth was washed 10 minutes at normal temperatures, and bath raio is 1:40, washs at normal temperatures 10 minutes with clear water then, and bath raio is 1:60;
H) bake and bank up with earth, bake and bank up with earth technological temperature and be no more than 100 ℃;
I) finished product typing, adopting Monforts setting machine temperature is 190 ℃, speed is 16m/min, overfeeding 30%.
Embodiment 2
The practical implementation step is following:
A) selection is got the raw materials ready, and the fibrous and quality percentage composition of this lining is: conductive fiber 4%, polyster fibre 45%, spandex fibre 15%, cotton or other fiber 36%;
B) preparation functional yarn; Lining adopts organizine and tram to weave and forms; Wherein organizine is processed into the low twist complex yarn after adopting conductive fiber, cotton fiber and cashmere through drafting, rove, spun yarn, winding process; Tram adopts polyster fibre, and spandex fibre and natural silk are processed into the low twist complex yarn after through drafting, rove, spun yarn, winding process;
C) weave cotton cloth, on the loom yarn behind the winder is being processed functional cloth;
D) singe, temperature is controlled at 900 ℃, and speed is 3m/s;
E) destarch washing was banked up cloth 45 minutes in the amylase of 1.2G/L, temperature is controlled at 90 ℃;
F) dyeing, fixation adopt reducing dye vat blue HSM to cooperate levelling agent, diffusant and acetum to improve the printing and dyeing effect earlier, add active dye fixing agent KS then, with 2% vinegar acid for adjusting pH value 5～6, and fixation bath raio 1:20,60 ℃ of temperature, 25 minutes time;
G) washing uses the soda ash of 0.4 grams per liter and the neutral detergent of 0.3 grams per liter that cloth was washed 10 minutes at normal temperatures, and bath raio is 1:40, washs at normal temperatures 10 minutes with clear water then, and bath raio is 1:60;
H) bake and bank up with earth, bake and bank up with earth technological temperature and be no more than 100 ℃;
I) finished product typing, adopting Monforts setting machine temperature is 200 ℃, speed is 16m/min, overfeeding 40%.
The present invention has disclosed a kind of antistatic thermal fabric; Be characterized in: this lining has guaranteed the warming effect of lining when eliminating electrostatic hazard; And sense of touch is soft, with elasticity, the raw material natural environmental-protective can be widely used as the lining of various underwears, cotton dress and sportswear.
Protection scope of the present invention is not limited thereto, and any technical staff who is familiar with the present technique field is in the technical scope that the present invention discloses, and the variation that can expect easily or replacement all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claim was defined.
Claims (5)
1. antistatic thermal fabric, the fibrous and quality percentage composition of this lining is: conductive fiber 3%-15%, polyster fibre 50%-70%, spandex fibre 10%-30%, cotton or other fiber 30%-50%.
2. antistatic thermal fabric according to claim 1 is characterized in that, described fabric quality percentage composition is: conductive fiber 4%-8%, polyster fibre 55%-65%, spandex fibre 15%-25%, cotton or other fiber 30%-40%.
3. antistatic thermal fabric according to claim 1 is characterized in that, described conductive fiber can be that metallic compound type conductive fiber, metal are a kind of in conductive fiber, the conducting polymer fiber type.
4. antistatic thermal fabric according to claim 3 is characterized in that, the silk footpath of described conductive fiber is 0.04-0.12mm.
5. antistatic thermal fabric according to claim 1 is characterized in that, described other fiber comprises one or more in man-made cellulose fibers, natural silk, the cashmere.