CN102465243A - Method for preventing double-zero aluminum foil from rebounding after tapping off - Google Patents
Method for preventing double-zero aluminum foil from rebounding after tapping off Download PDFInfo
- Publication number
- CN102465243A CN102465243A CN2010105429208A CN201010542920A CN102465243A CN 102465243 A CN102465243 A CN 102465243A CN 2010105429208 A CN2010105429208 A CN 2010105429208A CN 201010542920 A CN201010542920 A CN 201010542920A CN 102465243 A CN102465243 A CN 102465243A
- Authority
- CN
- China
- Prior art keywords
- temperature
- aluminum foil
- stay
- stove
- insulating cover
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for preventing a double-zero aluminum foil from rebounding after tapping off, which comprises the following steps of: placing a high-temperature tapped aluminum coil on the ground; covering the aluminum coil with a thermal-insulating cover; and slowly cooling the aluminum coil to the required temperature. In winter with lower outdoor temperature, a thickened thermal-insulating cover is covered for keeping warm. At other seasons, a single-layer thermal-insulating cover is adopted. The single-layer thermal-insulating cover is made of a piece of single-layer high-temperature resisting cotton canvas. The thickened thermal-insulating cover is made of a cotton canvas cover filled with an asbestos material. According to the method, the phenomena of the uneven cooling caused by an ultrahigh cooling speed under the condition of exposing the high-temperature tapped aluminum coil in air, the aluminum coil rebounding caused by concentration of internal stress and the internal wrinkling are reduced. The problem of low use efficiency of a furnace, caused by a process of slowly cooling the double-zero aluminum foil in the furnace, is solved. The method is simple and practical.
Description
Technical field
The invention belongs to the nonferrous metallurgy processing technique field, relate to specifically a kind of outside the aluminium foil stove of high temperature annealing low temperature slowly cool off the method for having prevented thick stick.
Background technology
It is the aluminium foil below the 0.009mm that double-zero aluminum foil refers generally to thickness; Because of it has shading, performance such as fresh-keeping, anticorrosion; Be widely used as the inner lining material of industries such as cigarette, food, medicine, electronics, all be combined with each other to strengthen the intensity of wrapping material during use with other wrapping material such as base materials such as plastics, paper.Require aluminium foil to have good formability and bright even curface in the recombination process.Traditional aluminium foil production process is: roll → close volume → finish rolling (pairing is rolling) → cut → anneal → pack in the blank → thick.Through the aluminium foil after rolling, because work hardening, plasticity is relatively poor, and the surface is surperficial unholiness all with one deck oil film as thin as a wafer, does not meet the food product pack requirement, so aluminium foil all is with the supply of material of annealing soft state usually.
In the annealing process, generally all to pass through intensification, four processes that are incubated, cool off, come out of the stove, owing to heat conducting reason, aluminium volume different piece has the temperature difference, in the aluminium volume heating and cooling period, it is big that the temperature difference can become.According to principle of expanding with heat and contracting with cold, the aluminium of this moment is rolled up the corresponding increase of internal stress, has surpassed the ys of corresponding position aluminium foil when internal stress; Aluminium foil generation viscous deformation forms macroscopic the thick stick in aluminium volume surface, plays the outer ring that thick stick usually occurs in aluminium volume external diameter 0~3cm; And the wrinkling aluminium volume that is created in usually is inner; Naked eyes cannot see, and can only in use find, and the degree of a thick stick have the increase with aluminium volume width and volume footpath to increase the weight of trend.In recombination process, there has been the aluminium volume of thick stick smoothly to launch, have after compound and significantly play the thick stick vestige, influence the external quality of wrapped product, so generally can only take off the processing of giving up.And the cost of composite base material is bigger than the aluminium foil cost of same length, and be lost in about 1.0% because of the improper lumber recovery that causes of thick stick technology preventive measures of having annealed general every year.
General using temperature control system in the industry; Take the method for slow heating and cooling to control the inner temperature difference of aluminium volume in the annealing process; And then control the thick stick of having annealed: promptly in the annealed temperature rise period, full power of changing over or half power are heated to the method for temperature of processing requirement, and adopt the well heater converter technique; Reach the long-time method that slowly heats up, reduce the aluminium volume internal difference in temperature of temperature rise period.Colling stages changes annealing process end in the past, and aluminium is directly exposed to refrigerative method in the air after rolling out stove, and has adopted elder generation in stove, slowly to be cooled to just directly come out of the stove behind the assigned temperature.The speed of heating and cooling reduces greatly like this, and the inner temperature difference of aluminium volume reduces, rise the thick stick phenomenon be improved significantly.But the heating and cooling time lengthening, the whole annealing cycle has also increased about 20~30% than former technology.The utilization ratio of lehre greatly reduces, and annealing cost increases, and and cause a large amount of work in-process to overstock, annealing is produced pressure and is strengthened.
For solving this contradiction, the applicant has also invented the drying room that heat exchange is used (patent No. 200810234535) specially, needs slow refrigerative to go out furnace charge and the furnace charge that advances that needs preheating in order to processing.Even but like this, configuration can not be satisfied the needs to the thick stick prevention technology of having annealed fully.
Summary of the invention
For solving above-mentioned production problem; The purpose of this invention is to provide a kind of double-zero aluminum foil annealing back and realize the outer slowly refrigerative method of stove; It is too fast because of speed of cooling that the aluminium that can prevent to come out of the stove volume is directly exposed in the air, inhomogeneous cooling even and produce aluminium volume surface rise thick stick, inner maybe be wrinkling etc. defective.
Play the thick stick method after a kind of prevention double-zero aluminum foil is come out of the stove, the double-zero aluminum foil volume of coming out of the stove after the annealing is placed on the ground, cover with stay-warm case integral body then, after treating slowly to be cooled to the temperature of requirement, remove stay-warm case.
Play the method for thick stick after aforementioned prevention double-zero aluminum foil is come out of the stove,, adopt the covering of individual layer stay-warm case in other seasons in the lower stay-warm case insulation that covers thickening winter of external temperature.
Play the method for thick stick after aforementioned prevention double-zero aluminum foil is come out of the stove, described individual layer stay-warm case is the high temperature resistant cotton canvas of individual layer, and described thickening stay-warm case is the cotton canvas cover that fills the pinner cotton material.
Beneficial effect of the present invention is: the aluminium volume with width 1000mm is an example, and falling temperature method in the traditional burner drops to specified tapping temperature from holding-zone in stove, and with per hour 3 ℃ of calculating of temperature drop, arriving specified tapping temperature needs about 20 hours.The present invention is simple and practical, does not take equipment such as body of heater, whole annealing cycle decreased average 10%~15%; It is long to have overcome the descent of temperature method annealing cycle, and annealing efficiency is low, and energy consumption is big; The problem that production cost is high, adopt method of the present invention after, aluminium foil plays thick stick and is clearly better; Annealing cost descends more than 10%, and annual photoelectric charge just can be practiced thrift more than 2,000,000 yuan, and economic benefit is considerable; With aluminium foil is placed directly into outdoor exposure and in air, lowers the temperature relatively, play the thick stick ratio and reduce 70%, condemnation factor reduces 70%, the total quality of aluminium foil is highly improved.
Embodiment
Following form is in Various Seasonal (winter (embodiment 1), summer (embodiment 2)), and under room temperature (25 ℃) situation, aluminium adopts the effect of covered protection cover of the present invention to compare after rolling out stove.
Above-mentioned embodiment does not limit technical scheme of the present invention in any form, and the technical scheme that mode obtained that every employing is equal to replacement or equivalent transformation all drops on protection scope of the present invention.
Claims (3)
1. play the thick stick method after the prevention double-zero aluminum foil is come out of the stove, it is characterized in that the double-zero aluminum foil volume of coming out of the stove after the annealing is placed on the ground, cover with stay-warm case integral body then, after treating slowly to be cooled to the temperature of requirement, remove stay-warm case.
2. play the method for thick stick after prevention double-zero aluminum foil according to claim 1 is come out of the stove, it is characterized in that adopting the covering of individual layer stay-warm case in other seasons in the lower stay-warm case insulation that covers thickening winter of external temperature.
3. play the method for thick stick after prevention double-zero aluminum foil according to claim 2 is come out of the stove, it is characterized in that described individual layer stay-warm case is the high temperature resistant cotton canvas of individual layer, described thickening stay-warm case is the cotton canvas cover that fills the pinner cotton material.