CN102442139B - Production method for turquoise clear-mud inkstone - Google Patents
Production method for turquoise clear-mud inkstone Download PDFInfo
- Publication number
- CN102442139B CN102442139B CN201110303313.0A CN201110303313A CN102442139B CN 102442139 B CN102442139 B CN 102442139B CN 201110303313 A CN201110303313 A CN 201110303313A CN 102442139 B CN102442139 B CN 102442139B
- Authority
- CN
- China
- Prior art keywords
- mud
- inkstone
- clear
- production method
- turquoise
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a production method for turquoise clear-mud inkstone, which solves problems that a production method for clear-mud inkstone is lost for years and colors of the inkstone cannot be manually controlled. The production method for turquoise clear-mud inkstone includes that ancient silt taken from the Hutuo river within the border of the Wutai county of Shanxi province is sun-dried, the dried ancient silt is placed in a water vat to be soaked for two hours, the soaked ancient silt is stirred to form mud, the mud is filtered, cattle bone powder with the weight of 5% of that of the mud is added into filtered mud, the mud is stirred again and filled in a cloth bag, water content in the mud is filtered out, the mud without the water content is beaten to form a mud pie, the mud pie is placed in a mold to make into a blank, the blank is placed in a fire-resistant box prior to being placed in a kiln, the temperature of the kiln is controlled to be in a range of 980 DEG C and 1050 DEG C, the blank is fired for 72 hours, and turquoise clear-mud inkstone is obtained. The production method has the advantages that the ancient technology is inherited while the production method is innovative, the production process, which is lost for a long time, for clear-mud inkstone is restored, and the produced clear-mud inkstone is excellent in quality and has advantages in terms of both the shape and the color.
Description
Technical field
The present invention relates to a kind of production method of Chengni inkstone, be specially a kind of production method of turquoise clear-mud inkstone.
Background technology
Sedimentary clay inkstone is one of China's four major famous inkstones, it and Duanxi inkstone, inhales inkstone, the Taohe River inkstone and is called China's " four major famous inkstones ".Sedimentary clay inkstone is opened the meticulous beginning of China's inkstone circle.Its predecessor is the Tao Yan in ancient times.The enlightenment that ancients are produced by brick, eaves tile, manufactures meticulously in conjunction with Tao Yanzai, and step distillation is then sedimentary clay inkstone.This inkstone starts from the Tang Dynasty, and the Song dynasty is developed into peak, and after this progressively decline, finally lost.The feature of sedimentary clay inkstone is that matter is hard fine and smooth, hard and not dry, and carefully and not sliding, water storage does not dry up, and goes through cold not ice, sends out China ink benefit milli, deep or light suitable, gentle calmness, and, there is multiple different colours in the refined U.S. of color and luster.In < < study four spectrum > >, say: " after the Song dynasty, exploitation natural stone is chiseled inkstone, class sedimentary clay inkstone, also name ' sedimentary clay inkstone '.Its category has ' yellow eel is yellow ', ' crust green ', ' mineral granule ', ' rose violet ', ' bean cotyledon sand ' etc. "; Expert on historical relics points out: " because of the source of silt and the weather of manufacturing process, fire the color that the difference of the duration and degree of heating is had nothing in common with each other." it seems that ancients have a mind to fire shades of colour, but objective formation in sintering procedure, the formation of color is with contingency, non-artificial can control.
The sintering procedure that Chengni inkstone is concrete and technique, the Ze Zhi Qing Dynasty is just lost.The ancient sedimentary clay inkstone of finding today is very rare, and top grade difficulty is especially asked, and traces it to its cause, probably with regard to being that manufacture craft is complicated and output is very low.
Summary of the invention
The present invention is directed to the problem that the lost and inkstone color of Chengni inkstone production method cannot manual control, a kind of production method of turquoise clear-mud inkstone is provided.
The present invention realizes by following steps: a kind of production method of turquoise clear-mud inkstone, comprises the following steps: the heavy mud airing of Gu of taking from the domestic Hutuohe River in Wutai County, Shanxi Province is dry; The heavy mud of Gu after drying is put into water vat to be soaked two hours; The heavy mud of Gu after soaking is stirred into mud; Mud is filtered; In the mud after filtering, add the Os Bovis seu Bubali powder that accounts for quality of mud fluid 5%; To adding the mud of Os Bovis seu Bubali powder to stir, and pack Bag filter moisture wherein into; To filtering out the mud of moisture, carry out kneading beating, make it be shaped to walk; Walk is put into mould and make blank; Blank is put into fire-resistant box, fire-resistant box is put into kiln, kiln temperature is controlled at 980 ℃ ~ 1050 ℃, fires 72 hours, obtains turquoise clear-mud inkstone.
The present invention holds Gu and innovates, and has recovered the production technology of lost Chengni inkstone for a long time, and the Chengni inkstone quality of producing is fine and smooth, solid thick Gu, shape system is various, and has realized on this basis the object of manual control Chengni inkstone appearance luster, and the Chengni inkstone shape and color of producing has both.Described production method possesses operability, for those skilled in the art are easy, realizes.The present invention follows the example of folk traditional craft, through a large amount of experiments and Process Exploration for many years, successfully realized the suitability for industrialized production of Chengni inkstone, the Chengni inkstone of producing has the multiple good characteristic of recording in ancient books, and obtained on this basis breakthrough, realized the control to Chengni inkstone appearance colour.The Chengni inkstone burning out can combine color and shape system, makes it have more artistic effect.The present invention, for carrying forward folk traditional craft, protects precious cultural heritage among the people also significant.
The specific embodiment
A production method for turquoise clear-mud inkstone, comprises the following steps: (a) that the heavy mud airing of Gu of taking from the domestic Hutuohe River in Wutai County, Shanxi Province is dry; (b) the heavy mud of the Gu after drying being put into water vat soaks two hours; (c) the heavy mud of the Gu after soaking is stirred into mud; (d) mud is filtered; (e) in the mud after filtering, add the Os Bovis seu Bubali powder that accounts for quality of mud fluid 5%; (f) will add the mud of Os Bovis seu Bubali powder to stir, and pack Bag filter moisture wherein into; (g) to filtering out the mud of moisture, carry out kneading beating, make it be shaped to walk; (h) walk is put into mould and make blank; (i) blank is put into fire-resistant box, fire-resistant box is put into kiln, kiln temperature is controlled at 980 ℃ ~ 1050 ℃, fires 72 hours, obtains turquoise clear-mud inkstone.The described filtration of step (d) is to adopt 10000-hole sieve to filter.
Take from the heavy mud of Gu in the domestic Hutuohe River in Wutai County, Shanxi Province, fine and glossy and have flexibility, in mud, contain ten several mineral materials; The very careful mud staying after 10000-hole sieve filters is exactly clear mud; Os Bovis seu Bubali is wanted grinds, adds Cheng Nizhong, and to adding the clear mud of Os Bovis seu Bubali powder to stir; After stirring, pack clear mud into cloth bag and sling, to filter out moisture wherein; The mud that taking-up afterwards filters out moisture carries out kneading beating, makes it be shaped to walk; Put into again mould and make inkstone blank, now can require to carry out Carving Machining according to art, make it possess various shape systems; While firing, temperature in kiln is controlled between 980 ℃ ~ 1050 ℃ (can select 980 ℃, 990 ℃, 1000 ℃, 1050 ℃), keep this temperature range that the fire-resistant box that blank is housed is fired 72 hours, the quality that just can obtain having dark green color and luster is fine and smooth, Fa Mo and do not damage the Chengni inkstone of milli.
Claims (2)
1. a production method for turquoise clear-mud inkstone, is characterized in that, comprises the following steps:
(a) the heavy mud airing of Gu of taking from the domestic Hutuohe River in Wutai County, Shanxi Province is dry;
(b) the heavy mud of the Gu after drying being put into water vat soaks two hours;
(c) the heavy mud of the Gu after soaking is stirred into mud;
(d) mud is filtered;
(e) in the mud after filtering, add the Os Bovis seu Bubali powder that accounts for quality of mud fluid 5%;
(f) to adding the mud of Os Bovis seu Bubali powder to stir, after stirring, pack Bag filter moisture wherein into;
(g) to filtering out the mud of moisture, carry out kneading beating, make it be shaped to walk;
(h) walk is put into mould and make blank;
(i) blank is put into fire-resistant box, fire-resistant box is put into kiln, kiln temperature is controlled at 980 ℃ ~ 1050 ℃, fires 72 hours, obtains turquoise clear-mud inkstone.
2. the production method of turquoise clear-mud inkstone as claimed in claim 1, is characterized in that described step (d) adopts 10000-hole sieve to filter.