CN102417579A - 耐黄变聚氨酯纺织涂层剂的制备方法 - Google Patents
耐黄变聚氨酯纺织涂层剂的制备方法 Download PDFInfo
- Publication number
- CN102417579A CN102417579A CN2011103378827A CN201110337882A CN102417579A CN 102417579 A CN102417579 A CN 102417579A CN 2011103378827 A CN2011103378827 A CN 2011103378827A CN 201110337882 A CN201110337882 A CN 201110337882A CN 102417579 A CN102417579 A CN 102417579A
- Authority
- CN
- China
- Prior art keywords
- preparation
- coating agent
- spinning coating
- yellowing
- reaction kettle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐黄变聚氨酯纺织涂层剂的制备方法,包括以下步骤:首先,在干燥、清洁的反应釜中加入有机溶剂N-甲基吡咯烷酮、MDI、HDI以及催化剂量的二月桂酸二丁基锡,加热溶解;然后将计量的单羟基聚环氧乙烷、1,4-丁二醇混溶,并缓慢滴加到上述的反应釜中,控温反应1~5h得到预聚产物;再在获得产物中加入3,5-二甲唑和二乙醇胺,保温反应1~5h,得到封端的聚氨酯乳液;最后,向反应液中加入乙醇酸中和剂,调节pH=7~9,降温,封装产品。本发明制得了一种性能优异的纺织涂层剂,能提高涂膜的爽滑性和耐水性,具有良好的耐黄变性能。
Description
技术领域:
本发明涉及一种耐黄变聚氨酯纺织涂层剂,特别涉及耐黄变聚氨酯纺织涂层剂的制备方法。
背景技术:
聚氨酯是由多异氰酸酯与多元醇反应生成的以氨基甲酸酯基为重复单元的高分子化合物。聚氨酯树脂具有软硬度可调、耐磨、耐溶剂、耐低温及与大多数材料有较强粘接性等特点,近年来发展迅速。目前聚氨酯已经成功地应用于纺织印染行业,它能赋予织物优良的柔软度、丰满感、耐洗、耐磨、回弹性好、滑爽、手感好、抗静电等,在纺织行业中的研究开发和应用得到了广泛而迅速的发展。常用的多异氰酸酯单体主要有2,4-二甲基二异氰酸酯(TDI)、4,4’-二苯甲烷二异氰酸酯(MDI)、异佛尔酮二异氰酸酯(IPDI)、六亚甲基二异氰酸酯(HDI)等,由于TDI、MDI含有刚性芳环,使得聚氨酯的内聚力比较大,具有较强的拉伸强度,芳环的存在会使胶膜容易发黄。IPDI由于含有脂环也使聚氨酯的强度较大,而HDI不含环状结构,强度较小,但是其结构比较规整,使得聚氨酯胶膜结晶。作为纺织涂层的原料, TDI、MDI不耐黄变, IPDI的强度较大、HDI的胶膜结晶,将影响纺织物外观,单独使用都不能取得令人满意的效果。
发明内容:
发明目的:针对现有技术存在的缺陷,本发明提供了一种耐黄变聚氨酯纺织涂层剂的制备方法。
技术方案:为实现上述发明目的,本发明采用以下技术方案:
一种耐黄变聚氨酯纺织涂层剂的制备方法,包括以下步骤:首先,在干燥、清洁的反应釜中加入有机溶剂N-甲基吡咯烷酮、4,4-二苯甲烷二异氰酸酯MDI、六亚甲基二异氰酸酯HDI以及催化剂量的二月桂酸二丁基锡,加热40~60℃溶解待用;接着,将计量的单羟基聚环氧乙烷与1,4-丁二醇按照1.2-1.5:1的质量比混溶后,缓慢滴加到反应釜中,在80~100℃下控温反应1~5h,得到预聚产物;然后,在获得的预聚产物中加入由3,5-二甲唑和二乙醇胺按照5-6:1的质量比配制的复合封端剂,在80~100℃下保温反应1~5h,得到封端的聚氨酯乳液;最后,向封端的聚氨酯乳液中加入乙醇酸中和剂,调节pH=7~9,降至室温即可。
所述MDI与HDI的质量比为1~5:1。
根据以上的技术方案,可以实现以下的有益效果:与现有技术相比,本发明具有以下优点:本发明制得了一种性能优异的纺织涂层剂,能提高涂膜的爽滑性和耐水性,具有合适的拉升强度和延展性,具有良好的耐黄变性能。
具体实施方式:
下面结合实施例对本发明做进一步地详细说明,但是本发明要求保护的范围并不局限于实施例表示的范围。
实施例1:
在干燥,清洁的反应釜中依次加入有机溶剂N-甲基吡咯烷酮(125kg)和4,4’-二苯甲烷二异氰酸酯(300kg),六亚甲基二异氰酸酯(100kg)催化剂二月桂酸二丁基锡(1.35kg),搅拌下加热至40~60℃溶解,待用;
称取单羟基聚环氧乙烷(155kg),1,4-丁二醇(215kg),混溶,缓慢滴加入上述反应溶液中,控制温度在80~100℃,反应1~5h,反应毕,向反应产物中加入3,5-二甲唑(152kg)二乙醇胺(27.5kg),反应1~5h, 降温至80℃,加入中和剂乙醇酸(19.5kg), 调节PH=7.1,降温至室温,封装得产品。
Claims (2)
1.一种耐黄变聚氨酯纺织涂层剂的制备方法,其特征在于,包括以下步骤:首先,在干燥、清洁的反应釜中加入有机溶剂N-甲基吡咯烷酮、4,4-二苯甲烷二异氰酸酯MDI、六亚甲基二异氰酸酯HDI以及催化剂量的二月桂酸二丁基锡,加热40~60℃溶解待用;接着,将计量的单羟基聚环氧乙烷与1,4-丁二醇按照1.2-1.5:1的质量比混溶后,缓慢滴加到反应釜中,在80~100℃下控温反应1~5h,得到预聚产物;然后,在获得的预聚产物中加入由3,5-二甲唑和二乙醇胺按照5-6:1的质量比配制的复合封端剂,在80~100℃下保温反应1~5h,得到封端的聚氨酯乳液;最后,向封端的聚氨酯乳液中加入乙醇酸中和剂,调节pH=7~9,降至室温即可。
2.根据权利要求1所述一种耐黄变聚氨酯纺织涂层剂的制备方法,其特征在于:所述MDI与HDI的质量比为1~5:1。