CN102416964A - Bathroom floor and manufacturing method thereof - Google Patents
Bathroom floor and manufacturing method thereof Download PDFInfo
- Publication number
- CN102416964A CN102416964A CN201110310744XA CN201110310744A CN102416964A CN 102416964 A CN102416964 A CN 102416964A CN 201110310744X A CN201110310744X A CN 201110310744XA CN 201110310744 A CN201110310744 A CN 201110310744A CN 102416964 A CN102416964 A CN 102416964A
- Authority
- CN
- China
- Prior art keywords
- floor
- carpet veneer
- plank layer
- short
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of vehicle bathrooms, in particular to a bathroom floor and a manufacturing method thereof. The bathroom floor comprises wood board layers and chopped strand mat layers coated on the outer sides of the wood board layers, wherein wood boards have light weight and are easy to form and convenient to process and install; and after chopped strand mats are coated on the outer sides of the wood boards, the wood boards can be water-proof, flame-retardant, sound-proof and wear-resistant and meet the using requirement of the floor, and the floor has long service life and is attractive. The manufacturing method for the bathroom floor comprises the following steps of: a, pasting a chopped strand mat layer on the surface of a mold by using resin; b, paving a wood board layer on the chopped strand mat layer before the resin is completely cured; c, pasting a chopped strand mat layer on the wood board layer; d, paving a wood board layer on the chopped strand mat layer before the resin is completely cured; and e, pasting a chopped strand mat layer on the wood board layer, and stripping after the chopped strand mat layer is cured. Due to the technical scheme, the chopped strand mat layers and the wood board layers are firmly bonded to form a whole by the resin, so that the quality of the floor is ensured; and the process is simple and is easy to operate.
Description
Technical field
The present invention relates to field, vehicle sanitary accomodation, particularly floor, sanitary accomodation and preparation method thereof.
Background technology
Along with developing rapidly of modern high ferro, at a high speed, comfortable motor-car more and more receives people's favor, also wants technological improvement as the base plate of vehicle sanitary accomodation, could satisfy the demand of market development.Traditional vehicle sanitary accomodation base plate is to record moulding with cement, and extremely inconvenience is installed, and relatively heavier, is not easy to cleaning.
Summary of the invention
The purpose of this invention is to provide a kind of light weight, the floor of being convenient to process, sanitary accomodation.
Be to realize above-mentioned purpose, the present invention has adopted following technical scheme: floor, a kind of sanitary accomodation comprises that plank layer and the weak point that is wrapped in the plank layer outside cut carpet veneer.
Because adopt above technical scheme, the lighter weight of plank is easy to moulding; Be convenient to processing and install, the outside of plank superscribes short cut behind the felt can waterproof, fire-retardant, sound insulation, wear-resisting; Satisfy the operating needs on floor, and the service life on this floor is longer, comparatively attractive in appearance.
Another object of the present invention provides the preparation method on floor, the simple sanitary accomodation of a kind of operation.
For realizing above-mentioned purpose, the present invention has adopted following technical scheme: the preparation method on floor, a kind of sanitary accomodation may further comprise the steps:
A, on the surface of mould, paste the short carpet veneer of cutting with resin;
B, treat to lay the plank layer on the carpet veneer short cutting before the resin complete curing;
C, on the plank layer, paste the short carpet veneer of cutting;
D, treat to lay the plank layer on the carpet veneer short cutting before the resin complete curing;
E, on the plank layer, paste and short cut carpet veneer, wait to solidify the back molding.
Owing to adopt above technical scheme, through using resin weak point is cut carpet veneer and firm being bonded as one of plank layer, guarantee the quality on floor, and this operation is comparatively simple, easily operation.
Description of drawings
Fig. 1 is a structural representation of the present invention.
The specific embodiment
Like Fig. 1, floor, a kind of sanitary accomodation comprises that plank layer 10 and the weak point that is wrapped in plank layer 10 outside cut carpet veneer 20; Plank is more a lot of than the light weight of cement, and moulding easily, processes arbitrarily according to the shape and size that the sanitary accomodation is required; Short characteristics of cutting felt are heat insulation, wear-resisting, fire-retardant, moistureproof and anticorrosive, after the outer wrap weak point of plank layer 10 is cut carpet veneer 20, make the floor of this structure have higher intensity and can bear the moist environment in sanitary accomodation; Weak point is cut the safety that wear-resisting, the fire-retardant characteristic of felt has also improved the floor, sanitary accomodation; Prolonged service life, this structure is also comparatively attractive in appearance, is convenient to cleaning.
As shown in Figure 1, described plank layer 11 and the short carpet veneer 20 stratiform arranged alternate of cutting, wherein plank layer 10 is provided with two-layerly altogether, shortly cuts carpet veneer 20 and is provided with three layers altogether, in other words is exactly that plank layer 11 and short is cut between the carpet veneer 20 each other alternately stack and constituted the floor.
Described plank layer 11 is provided with lightening hole 11, and its surface is provided with shallow slot 12, lightening hole 11 is set under the prerequisite that does not influence floor intensity can further alleviates the quality on floor.
Like Fig. 1, a kind of, the preparation method on floor, sanitary accomodation may further comprise the steps:
A, on the surface of mould 30, paste the short carpet veneer 20a that cuts with resin;
B, treat to lay plank layer 10a on the carpet veneer 20a short cutting before the resin complete curing;
C, on plank layer 10a, paste the short carpet veneer 20b that cuts;
D, treat to lay plank layer 10b on the carpet veneer 20b short cutting before the resin complete curing;
E, on plank layer 10b, paste and short cut carpet veneer 20c, wait to solidify the back molding.
Through using resin that weak point is cut carpet veneer 20 and 10 firm being bonded as one of plank layer, guarantee the quality on floor, and this operation is comparatively simple, easily operation.
The cure time of resin is 15-20 minute among described step b, the d.
The thickness that described weak point is cut carpet veneer 20 is 2-3mm.
The thickness of described plank layer 10 is 10-20mm.
The thickness on general floor is about 30mm, but the equal out of reach requirement of thickness of the plank that uses on the market at present so the present invention adopts hierachical structure, uses two-layer plank to be formed by stacking, and reduces production costs greatly.Connect two-layer plank layer 10 failure-free as a whole through using resin to paste the short carpet veneer 20 of cutting; Because the sanitary accomodation is comparatively moist, the big easy abrasion of flow of the people, operating needs has been satisfied not on simple plank surface; Establish in the external packets of plank layer 10 and short cut carpet veneer 20 and can protect plank layer 10; Thereby improve the in-use performance on floor, increase the service life, enlarge range of use.
Among described step b, the d with the surface finish of plank layer 10 coarse and offer shallow slot 12 above that after be laid on short cutting on the carpet veneer 20; That is to say that the plank layer 10 short contact surface of cutting carpet veneer 20 are not a plane; Wherein shallow slot 12 is equivalent to the effect of stop-return slot, can effectively prevent to link to each other the relative changing of the relative positions to take place between two-layer, and the rough surface of plank layer 10 can strengthen adherence force; Shallow slot 12 has increased stickup face; Thereby make plank layer 10 and short stickup of cutting between the carpet veneer 20 more reliable, improve floor quality, increase the service life.
Lay the artificial stone floor on the carpet veneer 20c short cutting among the described step e, artificial stone is comparatively smooth attractive in appearance, only needs direct mount during use, need not the polishing finishing, reduces work capacity, increases work efficiency.
Claims (9)
1. floor, a sanitary accomodation is characterized in that: the weak point that comprises plank layer (10) and be wrapped in plank layer (10) outside is cut carpet veneer (20).
2. floor, sanitary accomodation according to claim 1 is characterized in that: described plank layer (11) and short carpet veneer (20) the stratiform arranged alternate of cutting, wherein plank layer (10) is provided with two-layerly altogether, shortly cuts carpet veneer (20) and is provided with three layers altogether.
3. floor, sanitary accomodation according to claim 1 is characterized in that: described plank layer (11) is provided with lightening hole (11), and its surface is provided with shallow slot (12).
4. preparation method who is used to prepare floor, the described sanitary accomodation of claim 1 is characterized in that: may further comprise the steps:
A, on the surface of mould (30), paste the short carpet veneer (20a) of cutting with resin;
B, treat before the resin complete curing to go up and lay plank layer (10a) at the short carpet veneer (20a) of cutting;
C, on plank layer (10a), paste the short carpet veneer (20b) of cutting;
D, treat before the resin complete curing to go up and lay plank layer (10b) at the short carpet veneer (20b) of cutting;
E, on plank layer (10b), paste and short cut carpet veneer (20c), wait to solidify the back molding.
5. the preparation method on floor, sanitary accomodation according to claim 4 is characterized in that: the cure time of resin is 15-20 minute among described step b, the d.
6. the preparation method on floor, sanitary accomodation according to claim 4 is characterized in that: the thickness that described weak point is cut carpet veneer (20) is 2-3mm.
7. the preparation method on floor, sanitary accomodation according to claim 4 is characterized in that: the thickness of described plank layer (10) is 10-20mm.
8. the preparation method on floor, sanitary accomodation according to claim 4 is characterized in that: among described step b, the d with the surface finish of plank layer (10) coarse and offer shallow slot (12) above that after be laid on short cutting on the carpet veneer (20).
9. the preparation method on floor, sanitary accomodation according to claim 4 is characterized in that: go up laying artificial stone floor at the short carpet veneer (20c) of cutting among the described step e.