CN102416745A - Plastic base material film for food packaging and processing technology thereof - Google Patents
Plastic base material film for food packaging and processing technology thereof Download PDFInfo
- Publication number
- CN102416745A CN102416745A CN2011102228589A CN201110222858A CN102416745A CN 102416745 A CN102416745 A CN 102416745A CN 2011102228589 A CN2011102228589 A CN 2011102228589A CN 201110222858 A CN201110222858 A CN 201110222858A CN 102416745 A CN102416745 A CN 102416745A
- Authority
- CN
- China
- Prior art keywords
- lldpe
- ldpe
- material film
- 10min
- packaging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a plastic base material film for food packaging, prepared by carrying out co-extrusion blow molding on an inner layer, an interface layer and an external layer, wherein, the raw materials of the inner layer comprise low density polyethylene, linear low density polyethylene and metallocene linear low density polyethylene, the raw materials of the interface layer and the external layer comprise low density polyethylene and linear low density polyethylene. The plastic base material film for food packaging has good barrier property, good air tightness, good antifouling property, good pressure resistance, good impact resistance, high heat-sealing intensity, and good heat-sealing performance, and meets all the requirements and criteria of national food safety authentication. The processing technology has the advantages of reasonable design, and simple flow, and is easy to realize.
Description
Technical field
The present invention relates to the packaging material of food, specifically is a kind of plastic basis material film and processing technology thereof of packaging for foodstuff.
Background technology
Present packaging for foodstuff industry says that the packing base material film quantity that needs is big, kind is many, adopts the very difficult packing instructions that adapt to Special food of film of single raw material production.Trace it to its cause, though mainly be that respectively to produce producer's production technology of plastic raw materials each has something to recommend him, every kind of raw material all has its weak point, so the film of producing is difficult to satisfy the demand of various situation.Adopt different material to mix the way of using though some companies also have, owing to lack the necessary testing equipment and the testing program of checkout equipment and system, its effect is unsatisfactory.
Packaging for foodstuff plastic basis material film is produced with blow moiding method with the polyethylene raw material usually.But it is competent to want to reach above-mentioned these performance requirements and be not single polyethylene blown film technology institute, has therefore developed the polyethylene raw material of multiple performance.Yet; The polyethylene film of individual layer is poor to the barrier of gases such as oxygen; Pack fried time-like, be prone to cause sealing part to pollute, general flexible package punch polyethylene film is poor to the sealing property (claiming the field trash sealing property again) of this type of packing; Can not satisfy the requirement of its technology of the package and connection with wrapping of piece storage period, therefore must adopt barrier property and be mingled with sealing property all good multilaminar polyethylene modified film or laminated film.
Summary of the invention
In order to overcome above-mentioned defective, the invention provides and a kind ofly possess that high barrier, high-air-tightness, resistance tocrocking, heat seal strength are high, heat sealability is good, the plastic basis material film and the processing technology thereof of the packaging for foodstuff of certain resistance to pressure and resistance to impact arranged.
Technical scheme of the present invention is achieved in that a kind of plastic basis material film of packaging for foodstuff; Form by internal layer, intermediate layer and outer three-layer co-extruded blowing; Said internal layer raw material comprises LDPE low density polyethylene (LDPE), LLDPE LLDPE and mLLDPE metallocene linear-low density polyethylene, and said intermediate layer and outer raw material are LDPE low density polyethylene (LDPE) and LLDPE LLDPE.
The mass ratio of LDPE, LLDPE and mLLDPE is 25-35:35-45:15-35 in the said internal layer, and wherein the melt index of LDPE is 1.8-2.2g/10min, and density is 0.923-0.926g/cm
2The melt index of LLDPE is 1.9-2.2g/10min, and density is 0.918-0.922g/cm
2The melt index of mLLDPE is 1.9-2.4g/10min, and density is 0.910-0.915g/cm
2
LDPE, LLDPE mass ratio are 35-45:55-65 in the said intermediate layer, and wherein the melt index of LDPE is 1.8-2.2g/10min, and density is 0.923-0.926g/cm
2The melt index of LLDPE is 1.9-2.2g/10min, and density is 0.918-0.922g/cm
2
The mass ratio of LDPE and LLDPE is 30-40:65-75 in the said skin, and wherein the melt index of LDPE is 0.8-2.1g/10min, and density is 0.923-0.926g/cm
2The melt index of LLDPE is 1.9-2.2g/10min, and density is 0.918-0.922g/cm
2
Mass ratio between said internal layer, intermediate layer and the skin is 1:1:1.
The processing technology of the plastic basis material film of packaging for foodstuff is: said raw material is mixed in proportion, stir; Send into extrusion machine fused mass and extrude, melt temperature is 175-195 ℃; Carry out the typing of die head blown film, die head temperature is to raise gradually from bottom to top, and its scope is controlled at 165-205 ℃; Traction cutting then; Last rolling.
The time of said stirring is 15-20min.
The rotating speed of said extruder is controlled at 80-120r/min.
The invention has the beneficial effects as follows: (1) packaging for foodstuff plastic basis material of the present invention thin-film barrier property and air-tightness are good; Have good resistance tocrocking, resistance to pressure and resistance to impact; Have heat seal strength height, characteristics that heat sealability is good simultaneously, meet the state food safety certification.(2) packaging for foodstuff plastic basis material film production process of the present invention, reasonable in design, flow process is simple, is easy to realize.(3) packaging for foodstuff plastic basis material film production process of the present invention has improved the inherent quality of product, has improved appearance, has reduced labour intensity simultaneously, has improved production efficiency.
The specific embodiment
Below in conjunction with specific embodiment the present invention is further explained.The manufacturing equipment of packaging for foodstuff plastic basis material film all adopts in following examples: three-layer co-extruded traction rotation blown film unit, drawn subsidiary engine, winder etc. and formed by three extruders, a die head, typing cage, a cover; Checkout equipment all adopts: GBL-L electronic tension tester and MXD-01 friction coefficient instrument.
With the ratio of raw material in internal layer low density polyethylene 30%, LLDPE LLDPE40%, metallocene linear polyethylene mLLDPE30%; The intermediate layer is in the ratio of low density polyethylene 40%, LLDPE LLDPE60%; Outer ratio in low density polyethylene 33%, LLDPE LLDPE67%; Mass ratio between internal layer, intermediate layer and the skin is 1:1:1 preparation raw materials for production; Stir 15-20min; Send into extrusion machine fused mass and extrude, melt temperature is 175-195 ℃, and the rotating speed of extruder is controlled at 80r/min; Carry out the typing of die head blown film, die head temperature is to raise gradually from bottom to top, and its scope is controlled at 165-195 ℃; Traction cutting then; Last rolling.The performance of products parameter of producing is: hot strength: 22.34Mpa; Elongation at break: 718.5%; Heat seal strength: 9.8; Coefficient of friction: 0.213.
The above; Be merely the preferable specific embodiment of the present invention; But protection scope of the present invention is not limited thereto; Any technical staff who is familiar with the present technique field is equal to replacement or change according to technical scheme of the present invention and inventive concept thereof in the technical scope that the present invention discloses, all should be encompassed within protection scope of the present invention.
Claims (6)
1. the plastic basis material film of a packaging for foodstuff; It is characterized in that; Form by internal layer, intermediate layer and outer three-layer co-extruded blowing; Said internal layer raw material comprises LDPE low density polyethylene (LDPE), LLDPE LLDPE and mLLDPE metallocene linear-low density polyethylene, and said intermediate layer and outer raw material are LDPE low density polyethylene (LDPE) and LLDPE LLDPE.
2. the plastic basis material film of packaging for foodstuff according to claim 1 is characterized in that,
The mass ratio of LDPE, LLDPE and mLLDPE is 25-35:35-45:15-35 in the said internal layer, and wherein the melt index of LDPE is 1.8-2.2g/10min, and density is 0.923-0.926g/cm
2The melt index of LLDPE is 1.9-2.2g/10min, and density is 0.918-0.922g/cm
2The melt index of mLLDPE is 1.9-2.4g/10min, and density is 0.910-0.915g/cm
2
LDPE, LLDPE mass ratio are 35-45:55-65 in the said intermediate layer, and wherein the melt index of LDPE is 1.8-2.2g/10min, and density is 0.923-0.926g/cm
2The melt index of LLDPE is 1.9-2.2g/10min, and density is 0.918-0.922g/cm
2
The mass ratio of LDPE and LLDPE is 30-40:65-75 in the said skin, and wherein the melt index of LDPE is 0.8-2.1g/10min, and density is 0.923-0.926g/cm
2The melt index of LLDPE is 1.9-2.2g/10min, and density is 0.918-0.922g/cm
2
3. the plastic basis material film of packaging for foodstuff according to claim 1 and 2 is characterized in that, the mass ratio between said internal layer, intermediate layer and the skin is 1:1:1.
4. like the processing technology of the plastic basis material film of each described packaging for foodstuff of claim 1-3, it is characterized in that processing step is: said raw material is mixed in proportion, stir; Send into extrusion machine fused mass and extrude, melt temperature is 175-195 ℃; Carry out the typing of die head blown film, die head temperature is to raise gradually from bottom to top, and its scope is controlled at 165-205 ℃; Traction cutting then; Last rolling.
5. the processing technology of the plastic basis material film of packaging for foodstuff according to claim 4 is characterized in that, the time of said stirring is 15-20min.
6. the processing technology of the plastic basis material film of packaging for foodstuff according to claim 4 is characterized in that, the rotating speed of said extruder is controlled at 80-120r/min.