CN102373624A - Method for manufacturing high-strength typhoon prevention cloth - Google Patents
Method for manufacturing high-strength typhoon prevention cloth Download PDFInfo
- Publication number
- CN102373624A CN102373624A CN2010102634732A CN201010263473A CN102373624A CN 102373624 A CN102373624 A CN 102373624A CN 2010102634732 A CN2010102634732 A CN 2010102634732A CN 201010263473 A CN201010263473 A CN 201010263473A CN 102373624 A CN102373624 A CN 102373624A
- Authority
- CN
- China
- Prior art keywords
- tablecloth
- high strength
- manufacturing approach
- finished product
- strength according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a method for manufacturing high-strength typhoon prevention cloth, which comprises the following steps of: sufficiently mixing 100 parts by weight of polymer resin, 5 to 8 parts by weight of bridging agent and 10 to 100 parts by weight of solvent; uniformly coating the mixture on the surface of a foundation; carrying out drying treatment on the foundation to form a semifinished product, so that the semifinished product has functions of fire resistance, solarization resistance, waterproofness, antibacterial and antifungal performance and the like; and carrying out hole rolling treatment on the semifinished product by selecting a pin wheel device with suitable pin diameter and pitch to form a plurality of breathable micropores on the semifinished product, so that the manufacturing of the typhoon prevention cloth with air permeability can be completed.
Description
Technical field
The present invention relates to a kind of manufacturing approach of the anti-tablecloth, particularly a kind of manufacturing approach that the high-tenacity characteristic is arranged and have the anti-tablecloth of high strength of stable air permeability.
Background technology
Typhoon is a classification of tropical cyclone.On meteorology, can be because of the different titles of provincialism also difference to some extent, be that title, the hurricane (HURRICANE) of Eastern Pacific is the title of the North Atlantic Ocean and Western Pacific, the title that cyclone (CYCLONE) is the Indian Ocean etc. like typhoon (TYPHOON).Building is not destroyed by typhoon (or being called hurricane, cyclone) for protection, and except material selection of building own and structural strength height, gate and window also possibly cause the harm of main structure.In order to make the weakness of avoiding gate and window to become building; Building after 2005 all can be built according to back new building rules; But building is attacked for the protection typhoon before 2005, has proposed various anti-platform equipment at present, is used to protect architectural openings; Like window, door or sliding glass door, with opposing storm and the effect relevant with typhoon or similar incidents.
Wherein anti-platform equipment for example uses the glued board thin slice, and it is fixed on the building as the covering of window and door, and the user need be cut to suitable opening size and with its installation with the glued board thin slice.Yet, use the bulky of glued board thin slice and have weight, and when dismounting, can be when installing employed fixture, like nail etc., and cause the damage of building structure.
Another anti-platform equipment uses the warp coating fabric that is made by plastic cement coated polyester material, is thick usually substantially through the coating fabric, in order to necessity protection of opposing typhoon damage.Wherein fabric possesses along its peripheral grommet, and usually uses the screw that is attached on the building and wing nut fastener and be fixed on the building.Yet fabric is heavy and be difficult to installation, and huge relatively as far as storage, and fabric has high relatively deflection, easy its shape of loss and tightness under low velocity.
In view of this, the present invention satisfies the deficiency to above-mentioned prior art, proposes the manufacturing approach of the anti-tablecloth of a kind of high strength, effectively to overcome these above-mentioned problems.
Summary of the invention
Main purpose of the present invention is in the manufacturing approach that the anti-tablecloth of a kind of high strength is provided; It has the anti-tablecloth of high strength, security and reliability; Can be applicable to desire in the building structure of reinforcement, come from the protection effect of the impact of big wind-induced destruction and typhoon or similar incidents generation in order to opposing.
Another object of the present invention is in the manufacturing approach that the anti-tablecloth of a kind of high strength is provided, and it can make the anti-tablecloth have anti-combustion effect, is transporting and preserving the misgivings that do not have on the safety.
A purpose more of the present invention is in the manufacturing approach that the anti-tablecloth of a kind of high strength is provided, and it has water-fast, sun-resistant characteristic, can use for a long time.
Another purpose of the present invention is in the manufacturing approach that the anti-tablecloth of a kind of high strength is provided, and it has the characteristic of antibacterial and mouldproof, is therefore using and preserving the higher convenience of tool.
For reaching above-mentioned purpose, the present invention provides the manufacturing approach of the anti-tablecloth of a kind of high strength, and its step comprises: at first macromolecule resin 100 weight portions, bridging agent 5-8 weight portion and solvent 10-100 weight portion are mixed to form a mixture; Coating mixture is surperficial in a base cloth, and carries out dried to form semi-finished product; And the pinwheel that utilizes suitable aperture and appropriate well distance is installed on and rolls the hole on the semi-finished product and handle, and makes to form a plurality of ventilative micropores on the semi-finished product to accomplish an anti-tablecloth finished product.
In sum, it is lighter that the anti-tablecloth of the present invention has impact resistance and the weight better than existing fabric shielding, more convenient when taking in, and can effectively resist the protection effect that building comes from the impact of big wind-induced destruction and typhoon or similar incidents generation.Moreover the anti-tablecloth has anti-combustion effect, thus transporting and preserving the misgivings that do not have on the safety, and have water-fast, sun-resistant characteristic; Can use for a long time; Have economic benefit, and a characteristic, therefore have convenience using and preserve with antibacterial and mouldproof.
Under explain in detail through specific embodiment, when the effect that is easier to understand the object of the invention, technology contents, characteristics and is reached.
Description of drawings
Fig. 1 is a structural representation of the present invention;
Fig. 2 is a flow chart of steps of the present invention.
Description of reference numerals: 10-base cloth; The 12-mixture; The 14-semi-finished product; The 16-micropore of breathing freely; 18-prevents tablecloth finished product.
The specific embodiment
The anti-tablecloth of the present invention can be applicable to desire in the building structure of reinforcement, as for fear of the gate and window become the weakness of building, come from the protection effect of the impact that big wind-induced destruction and hurricane or similar incidents produces in order to opposing.See also Fig. 1; The anti-tablecloth comprises a base cloth 10 and mixture 12, and wherein base cloth 10 is mylar, nylon cloth, cotton, polyester/nylon blending gauze, blending Woven Fabrics, flat fabric, band, plaids, drillipg, orange red figured cloth, N/T interweave cloth, dyed yarn interweave cloth, Ta Futa, OXFORD, satin etc.Mixture 12 is formed by macromolecule resin 100 weight portions, bridging agent 5-8 weight portion and solvent 10-100 weight portion mixed preparing.Earlier mixture 12 is evenly coated on the surface of base cloth 10; All evenly be coated with mixture 12 like upper surface or lower surface or upper and lower surface; Is example at this to coat upper surface, and carries out dried, makes the base cloth 10 that is coated with mixture 12 form semi-finished product 14; Select the pinwheel device (not shown) of suitable aperture and appropriate well distance on semi-finished product 14, to roll the hole processing again, make to form a plurality of ventilative micropores 16 on the semi-finished product 14 to accomplish an anti-tablecloth finished product 18.
Please consult Fig. 2 simultaneously, below specify each step.At first in step S10; Utilize an agitating device that macromolecule resin 100 weight portions, bridging agent 5-8 weight portion and solvent 10-100 weight portion are controlled in 40 ℃-60 ℃ with speed of agitator 1000 rev/mins of (rpm/min), temperature and evenly mix, to form a mixture 12.Wherein, when bridging agent mixes with macromolecule resin, can increase crosslink density, adding solvent mainly is in order to adjustment degree of sticking together.Macromolecule resin can be acryl, Polyurethane, polyvinyl chloride, gathers ethyl acetate, siloxane polymer, polyether ester, Merlon etc., and above-mentioned macromolecule resin characteristic has all excellent specific properties such as antibiotic property, tearing toughness, high density, anti-contamination, anti-combustion, heat shock resistance, weatherability, chemicals-resistant, cleaning maintenance easily, UV resistant irradiation.Bridging agent can be melamine (melamine) or isocyanates (isocyanate) etc., and solvent is toluene or butanone.
Come in step S12 again, utilize the even coating mixture 12 of a paper device on the surface of a base cloth 10, about 1 minute time of process leaves standstill; And carry out dried to form semi-finished product 14; Again semi-finished product 14 being inserted a drying device, like baking oven, is 120-200 ℃ in heating-up temperature; And time of staying 30-180 carries out heat drying second to be handled; After treating intensive drying, the solvent in the mixture 12 is evenly brought into play, can be obtained having anti-combustion, dynamopathic semi-finished product 14 such as water-fast, sun-resistant, antibiotic, mildew-resistant, ventilative, high strength.
In step S14, utilize the pinwheel device with a plurality of needle bodies at last, on semi-finished product 14, roll the hole like circular wheel and handle, wherein the pin of needle body is 5-100mm for 0.02-0.5mm, needle gage directly.Because the decomposition temperature of semi-finished product 14 is 220 ℃; Therefore roll the decomposition temperature that the heating-up temperature of handling in the hole need be lower than semi-finished product 14; Be preferably 60-200 ℃ in this heating-up temperature; And time of staying 0.5-5 second, make a plurality of ventilative micropore 16 that forms suitable aperture and appropriate well distance on the semi-finished product 14 after, can accomplish an anti-tablecloth finished product 18 with highly-breathable.
In sum, it is lighter that the anti-tablecloth of the present invention has impact resistance and the weight better than existing fabric shielding, more convenient when taking in, and can effectively resist the protection effect that building comes from the impact of big wind-induced destruction and typhoon or similar incidents generation.Moreover the anti-tablecloth has anti-combustion effect, thus transporting and preserving the misgivings that do not have on the safety, and have water-fast, sun-resistant characteristic; Can use for a long time; Have economic benefit, and a characteristic, therefore have convenience using and preserve with antibacterial and mouldproof.
Only the above is merely preferred embodiment of the present invention, is not to be used for limiting the scope that the present invention implements.So be that all equalizations of doing according to described characteristic of application range of the present invention and spirit change or modification, all should be included in the claim of the present invention.
Claims (10)
1. the manufacturing approach of the anti-tablecloth of a high strength is characterized in that described step of manufacturing comprises:
A) macromolecule resin 100 weight portions, bridging agent 5-8 weight portion and solvent 10-100 weight portion are mixed to form a mixture;
B) this mixture is coated the surface of a base cloth, and carried out dried to form semi-finished product; And
C) utilize a pinwheel to be installed on and roll the hole processing on these semi-finished product, make to form a plurality of ventilative micropores on these semi-finished product to accomplish an anti-tablecloth finished product.
2. the manufacturing approach of the anti-tablecloth of high strength according to claim 1 is characterized in that, this macromolecule resin is acryl, Polyurethane, polyvinyl chloride, gather ethyl acetate, siloxane polymer, polyether ester or Merlon.
3. the manufacturing approach of the anti-tablecloth of high strength according to claim 1 is characterized in that this bridging agent is melamine or isocyanates.
4. the manufacturing approach of the anti-tablecloth of high strength according to claim 1 is characterized in that this solvent is toluene or butanone.
5. the manufacturing approach of the anti-tablecloth of high strength according to claim 1 is characterized in that, this step b) utilizes a paper device that this mixture is coated on this base cloth surface.
6. the manufacturing approach of the anti-tablecloth of high strength according to claim 1; It is characterized in that; This step b) to form this semi-finished product, utilizes the mode of a baking oven for heating to carry out dried after first time of repose is about 1 minute behind this this mixture of base cloth surface coated again.
7. the manufacturing approach of the anti-tablecloth of high strength according to claim 6 is characterized in that the heating-up temperature of this baking oven is 120-200 ℃, and time of staying 30-180 second.
8. the manufacturing approach of the anti-tablecloth of high strength according to claim 1 is characterized in that this pinwheel device has a plurality of needle bodies, and the pin of these a plurality of needle bodies directly is 0.02-0.5mm, and needle gage is 5-100mm.
9. the manufacturing approach of the anti-tablecloth of high strength according to claim 1 is characterized in that, this step c), and on these semi-finished product, rolling the heating-up temperature of handling in the hole is 60-200 ℃, and time of staying 0.5-5 second.
10. the manufacturing approach of the anti-tablecloth of high strength according to claim 1; It is characterized in that this base cloth is mylar, nylon cloth, cotton, polyester/nylon blending gauze, blending Woven Fabrics, flat fabric, band, plaids, drillipg, orange red figured cloth, N/T interweave cloth, dyed yarn interweave cloth, Ta Futa, OXFORD or satin.