CN102372950A - Production technology of slurry for water-based paint - Google Patents
Production technology of slurry for water-based paint Download PDFInfo
- Publication number
- CN102372950A CN102372950A CN2010102618439A CN201010261843A CN102372950A CN 102372950 A CN102372950 A CN 102372950A CN 2010102618439 A CN2010102618439 A CN 2010102618439A CN 201010261843 A CN201010261843 A CN 201010261843A CN 102372950 A CN102372950 A CN 102372950A
- Authority
- CN
- China
- Prior art keywords
- slurry
- water
- transferpump
- production
- transfer pump
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Relating to the technical field of chemical production, the invention provides a production technology of a slurry for water-based paint. The technology comprises the following production processes of: adding water and auxiliary agents into a mixing tank (1) and starting stirring, after stirring uniformly, adding pigments and filler slowly under stirring, after material adding, continuing stirring until mixed uniformly, then conveying the mixture to a grinding machine (3A) with a transfer pump (2A), letting the slurry generated by the grinding machine flowing into a middle receiving trough (4), then pumping the slurry into a grinding machine (3B) for grinding with a transfer pump (2B), controlling the fineness of the obtained slurry that flows into a receiving trough (5), then pumping the slurry into a slurry storage trough (6) with a transfer pump (2C), adding auxiliary agents, and adjusting the slurry to a qualified product, which is pumped into a filter (7) by a transfer pump (2D) for filtering and packaging. With excellent performance, convenient application and innovated concept, the technology of the invention can improve the quality of a paint product, reduce cost, and mitigate labor intensity, improve production environment, as well as save treatment cost of ''three wastes''.
Description
Technical field:
The invention belongs to chemical production technical field, be specifically related to the production technique of a kind of water-borne coatings with slurry.
Background technology:
So far, the most of medium and small coating material production of our province enterprise adopts slurrying---and lacquer man plants and produces latex coating.This is a very proven technique route, and its gordian technique is the technology of oar of making paints, and the quality of pigment oar has determined the quality of coating products; But the medium and small coating material production of the above-mentioned technology of nearly all employing enterprise does not all have well to solve high-quality pigment oar problem; Thereby product quality level is lower, in addition, and the production environment of factory; Labor strength and disposal of three wastes problem are more outstanding, the existence of serious threat enterprise.
Summary of the invention:
The purpose of this invention is to provide the production technique of a kind of water-borne coatings with slurry, its excellent performance, easy to use, theory is innovated, and can improve the quality of coating products, reduces cost, and can also reduce labor intensity, and improves production environment, saves disposal of three wastes expense.
In order to solve the existing problem of background technology, the present invention adopts following technical scheme: its production craft step is: input water and auxiliary agent start stirring in mixing filling 1, after stirring, under agitation slowly drop into pigment; Feed intake finish after, continue to stir, evenly after; Deliver to milling drum 3A with transferpump 2A, groove 4 in the middle of the slurry behind the milling drum flows into is delivered to milling drum 3B grinding with transferpump 2B again; Control slurry fineness, slurry flows into groove 5, and transferpump 2C is to slurry storage tank 6 then; Add auxiliary agent, and be adjusted to qualified products, product filters and packages to strainer 7 through transferpump 2D.
Described auxiliary agent is F102, Ucar 35, F111, ED15, PT-3.
Described pigment is titanium white, lime carbonate, talcum powder.
Excellent performance of the present invention, easy to use, theory is innovated, and can improve the quality of coating products, reduces cost, and can also reduce labor intensity, and improves production environment, saves disposal of three wastes expense.
Description of drawings:
Fig. 1 is a production technique formula table of the present invention;
Fig. 2 is technological process of production figure of the present invention.
Embodiment:
With reference to Fig. 1-2, this embodiment adopts following technical scheme: its production craft step is: input water and auxiliary agent start stirring in mixing filling 1, after stirring, under agitation slowly drop into pigment and filler; Feed intake finish after, continue to stir, evenly after; Deliver to milling drum 3A with transferpump 2A, groove 4 in the middle of the slurry behind the milling drum flows into is delivered to milling drum 3B grinding with transferpump 2B again; Control slurry fineness, slurry flows into groove 5, and transferpump 2C is to slurry storage tank 6 then; Add auxiliary agent, and be adjusted to qualified products, product filters and packages to strainer 7 through transferpump 2D.
In this embodiment, milling drum 3A, milling drum 3B belongs to the segmentation grinding steps; Pigment is in process of lapping; Receive bump and the fragmentation of spherical medium, the size of its final grain warp and the stroke speed of spherical medium in the unit time, collision frequency and quality are directly proportional.The bump number of times depends on the quantity of medium and the rotating speed of machine, and quality is then relevant with the material proportion of the diameter of ball and ball.
Because the quality of ball is relevant with spherical diameter, diameter is bigger, and the quality of ball is bigger; Simultaneously, the diameter of ball is relevant with the fineness of product (pigment slurry) again, and diameter is bigger, and fineness is bigger, and therefore, the paint grinder mill that desire is bigger with particle diameter becomes the particle diameter smaller particles, should take to grind stage by stage.
This embodiment excellent performance, easy to use, theory is innovated, and can improve the quality of coating products, reduces cost, and can also reduce labor intensity, and improves production environment, saves disposal of three wastes expense.
Claims (3)
1. a water-borne coatings is with the production technique of starching, and its production craft step is: input water and auxiliary agent start stirring in mixing filling (1), after stirring, under agitation slowly drop into pigment and filler; Feed intake finish after, continue to stir, evenly after; Deliver to milling drum (3A) with transferpump (2A), groove (4) in the middle of the slurry behind the milling drum flows into uses transferpump (2B) to deliver to milling drum (3B) grinding again; Control slurry fineness, slurry flows into groove (5), and transferpump (2C) is to slurry storage tank (6) then; Add auxiliary agent, and be adjusted to qualified products, product filters and packages through transferpump (2D) to strainer (7).
2. a kind of water-borne coatings according to claim 1 is characterized in that with the production technique of slurry described auxiliary agent is F102, Ucar 35, F111, ED15, PT-3.
3. a kind of water-borne coatings according to claim 1 is characterized in that with the production technique of slurry described pigment is titanium white, lime carbonate, talcum powder.