CN102363709B - 一种喷涂用聚氨酯弹性手感漆涂料及用途 - Google Patents
一种喷涂用聚氨酯弹性手感漆涂料及用途 Download PDFInfo
- Publication number
- CN102363709B CN102363709B CN201110183769.8A CN201110183769A CN102363709B CN 102363709 B CN102363709 B CN 102363709B CN 201110183769 A CN201110183769 A CN 201110183769A CN 102363709 B CN102363709 B CN 102363709B
- Authority
- CN
- China
- Prior art keywords
- hydroxyl value
- saturated polyester
- polyester resin
- percent
- value saturated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种喷涂用聚氨酯弹性手感漆涂料及用途，该涂料的重量百分比组成为：高羟值饱和聚酯树脂18～30，低羟值饱和聚酯树脂10～20，再加入流平剂0.2～1.0，醋酸丁酯30～40，二甲苯10～30，哑粉6～8，哑粉高速分散至细度5微米以下，催干剂0.05～0.15，高羟值饱和聚酯树脂和低羟值饱和聚酯树脂的固体含量都等于或大于40%，流平剂为硅氧烷，哑粉为二氧化硅,溶剂为醋酸丁酯和二甲苯的混合物。本发明的涂料可用作电子和电器产品塑胶外壳的喷涂用涂料。其提供一种触摸手感好,有弹性的喷涂用聚氨酯弹性手感漆涂料。
Description
技术领域
本发明涉及有机涂料，特别是涉及一种用于电子和电器产品塑胶外壳的喷涂用聚氨酯弹性手感漆涂料。
背景技术
目前，各种电子或电器产品，如数码相机、笔记本电脑、手机等已广泛应用于人们的生活中。这类产品的外壳大多由塑料和塑胶材料制成，其外壳在加工成型后都需要在表面喷涂保护和装饰用的涂料。传统的机壳用涂料多选用面漆为聚氨酯涂料,无任何弹性手感。
随着大规模涂料喷涂生产的需求，很多终端用户越来越重视使用时用手触摸的手感要求，因此急需开发一种喷涂用聚氨酯弹性手感漆涂料。
发明内容
本发明旨在解决上述问题，提供一种触摸手感好,有弹性的喷涂用聚氨酯弹性手感漆涂料。
本发明的技术方案如下：
为实现上述目的，本发明提供一种喷涂用聚氨酯弹性手感漆涂料，其中，其重量百分比组成为：
高羟值饱和聚酯树脂 18～30
低羟值饱和聚酯树脂 10～20
醋酸丁酯 30～40
二甲苯 10～30
哑粉 6～8
流平剂 0.2～1
催干剂 0.05～0.15。
所述的喷涂用聚氨酯弹性手感漆涂料，其中一个优选方案，重量百分比组成为：
高羟值饱和聚酯树脂 27.5
低羟值饱和聚酯树脂 12.5
醋酸丁酯 32
二甲苯 20.9
哑粉 6.5
流平剂 0.5
催干剂 0.1。
所述的喷涂用聚氨酯弹性手感漆涂料，其中一个优选方案，重量百分比组成为：
高羟值饱和聚酯树脂 20.5
低羟值饱和聚酯树脂 19.5
醋酸丁酯 32
二甲苯 20.9
哑粉 6.5
流平剂 0.5
催干剂 0.1。
所述的喷涂用聚氨酯弹性手感漆涂料，其中，所述含高羟值饱和聚酯树脂和低羟值饱和聚酯树脂的固体含量都等于或大于40%。
高羟值饱和聚酯树脂和低羟值饱和聚酯树脂都与固化剂异氰酸酯反应, 低羟值饱和聚酯树脂提供更好的手感, 高羟值饱和聚酯树脂提供更好的机械性能。
所述的喷涂用聚氨酯弹性手感漆涂料，其中，所述流平剂为硅氧烷，用于增加漆膜表面流平和手感，哑粉为二氧化硅,溶剂为醋酸丁酯和二甲苯。
所述的喷涂用聚氨酯弹性手感漆涂料，其中，高羟值饱和聚酯树脂羟值为130 ｍｇ ＫＯＨ／ｇ，低羟值饱和聚酯树脂羟值为50 ｍｇ ＫＯＨ／ｇ。
本发明也提供了一种喷涂用聚氨酯弹性手感漆涂料，用于电子和电器产品塑胶外壳的喷涂用涂料。
本发明的贡献在于，它提供一种触摸手感好,有弹性的喷涂用聚氨酯弹性手感漆涂料。因传统的机壳用聚氨酯涂料多采用羟基丙烯酸树脂制成，我们选用表现优良的饱和聚酯树脂，并经过大量试验与改进，制成综合性能优的聚氨酯弹性手感漆涂料。
具体实施方式
本发明提供了一种喷涂用聚氨酯弹性手感漆涂料及用途，为使本发明的目的、技术方案及效果更加清楚、明确，以下实施例对本发明进一步详细说明。应当理解，此处所描述的具体实施例仅用以解释本发明，并不用于限定本发明。
实施例1
取高羟值饱和聚酯树脂27.5份（重量），羟值为130 ｍｇ ＫＯＨ／ｇ，低羟值饱和聚酯树脂12.5份，羟值为50 ｍｇ ＫＯＨ／ｇ，再加入流平剂0.5份（重量），其中流平剂选用BYK-333型硅氧烷，所形成的混合物经低速分散均匀后，加入醋酸丁酯溶剂32份（重量），然后搅拌10份钟，加入二甲苯20.9份（重量），再加入6.5份（重量）哑粉OK520,高速分散至细度5微米以下,最后加入催干剂T-12二月桂酸二丁基锡0.1份（重量），分散均匀后用300目网纱过滤即得成品。
实施例2
取高羟值饱和聚酯树脂20.5份（重量），羟值为130 ｍｇ ＫＯＨ／ｇ，低羟值饱和聚酯树脂19.5份，羟值为50 ｍｇ ＫＯＨ／ｇ，再加入流平剂0.5份（重量），其中流平剂选用BYK-333型硅氧烷，所形成的混合物经低速分散均匀后，加入醋酸丁酯溶剂32份（重量），然后搅拌10份钟，加入二甲苯20.9份（重量），再加入6.5份哑粉OK520,高速分散至细度5微米以下,最后加入催干剂T-12二月桂酸二丁基锡0.1份（重量），分散均匀后用300目网纱过滤即得成品。
实施例3
取高羟值饱和聚酯树脂12.5份（重量），羟值为130 ｍｇ ＫＯＨ／ｇ，低羟值饱和聚酯树脂27.5份，羟值为50 ｍｇ ＫＯＨ／ｇ，再加入流平剂0.5份（重量），其中流平剂选用BYK-333型硅氧烷，所形成的混合物经低速分散均匀后，加入醋酸丁酯溶剂32份（重量），然后搅拌10份钟，加入二甲苯27.4份（重量），再加入6.5份哑粉OK520,高速分散至细度5微米以下,最后加入催干剂T-12二月桂酸二丁基锡0.1份（重量），分散均匀后用300目网纱过滤即得成品。
实施例4
取高羟值饱和聚酯树脂18份（重量），羟值为130 ｍｇ ＫＯＨ／ｇ，低羟值饱和聚酯树脂10份，羟值为50 ｍｇ ＫＯＨ／ｇ，再加入流平剂1份（重量），其中流平剂选用BYK-333型硅氧烷，所形成的混合物经低速分散均匀后，加入醋酸丁酯溶剂32.85份（重量），然后搅拌10份钟，加入二甲苯30份（重量），再加入8份哑粉OK520,高速分散至细度5微米以下,最后加入催干剂T-12二月桂酸二丁基锡0.15份（重量），分散均匀后用300目网纱过滤即得成品。
实施例5
取高羟值饱和聚酯树脂23.75份（重量），羟值为130 ｍｇ ＫＯＨ／ｇ，低羟值饱和聚酯树脂20份，羟值为50 ｍｇ ＫＯＨ／ｇ，再加入流平剂0.2份（重量），其中流平剂选用BYK-333型硅氧烷，所形成的混合物经低速分散均匀后，加入醋酸丁酯溶剂40份（重量），然后搅拌10份钟，加入二甲苯10份（重量），再加入6份哑粉OK520,高速分散至细度5微米以下,最后加入催干剂T-12二月桂酸二丁基锡0.05份（重量），分散均匀后用300目网纱过滤即得成品。
实施例6
取高羟值饱和聚酯树脂30份（重量），羟值为130 ｍｇ ＫＯＨ／ｇ，低羟值饱和聚酯树脂12.4份，羟值为50 ｍｇ ＫＯＨ／ｇ，再加入流平剂0.5份（重量），其中流平剂选用BYK-333型硅氧烷，所形成的混合物经低速分散均匀后，加入醋酸丁酯溶剂30份（重量），然后搅拌10份钟，加入二甲苯20份（重量），再加入7份哑粉OK520,高速分散至细度5微米以下,最后加入催干剂T-12二月桂酸二丁基锡0.1份（重量），分散均匀后用300目网纱过滤即得成品。
上述实施例所得喷涂用聚氨酯弹性手感涂料的理化指标见下表：
| 粘度（秒）NK-2#杯 | 手感 | 耐磨RCA | 耐MEK | |
| 实施例1 | 18 | 良 | 优 | 优 |
| 实施例2 | 20 | 良 | 一般 | 一般 |
| 实施例3 | 25 | 优 | 差 | 差 |
| 实施例4 | 30 | 良 | 一般 | 一般 |
| 实施例5 | 22 | 良 | 良 | 一般 |
| 实施例6 | 16 | 良 | 优 | 一般 |
本发明提供一种触摸手感好,有弹性的喷涂用聚氨酯弹性手感漆涂料，可广泛应用于电子和电器产品塑胶外壳的喷涂。
应当理解的是，对本领域普通技术人员来说，可以根据上述说明加以改进或变换，而所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (4)
1.一种喷涂用聚氨酯弹性手感漆涂料，其特征在于，其重量百分比组成为：
高羟值饱和聚酯树脂 18～30
低羟值饱和聚酯树脂 10～20
醋酸丁酯 30～40
二甲苯 10～30
哑粉 6～8
流平剂 0.2～1
催干剂 0.05～0.15；
高羟值饱和聚酯树脂和低羟值饱和聚酯树脂都与固化剂异氰酸酯反应；
所述高羟值饱和聚酯树脂和低羟值饱和聚酯树脂的固体含量都等于或大于40%；
所述流平剂为硅氧烷，哑粉为二氧化硅；
高羟值饱和聚酯树脂的羟值为130 ｍｇ ＫＯＨ／ｇ，低羟值饱和聚酯树脂羟值为50 ｍｇ ＫＯＨ／ｇ。
2.如权利要求1所述的喷涂用聚氨酯弹性手感漆涂料，其特征在于，其重量百分比组成为：
高羟值饱和聚酯树脂 27.5
低羟值饱和聚酯树脂 12.5
醋酸丁酯 32
二甲苯 20.9
哑粉 6.5
流平剂 0.5
催干剂 0.1。
3.如权利要求1所述的喷涂用聚氨酯弹性手感漆涂料，其特征在于，其重量百分比组成为：
高羟值饱和聚酯树脂 20.5
低羟值饱和聚酯树脂 19.5
醋酸丁酯 32
二甲苯 20.9
哑粉 6.5
流平剂 0.5
催干剂 0.1。
4.如权利要求1所述的喷涂用聚氨酯弹性手感漆涂料，用于电子和电器产品塑胶外壳的喷涂用涂料。