CN102352462B - Anchor rod rebar with high strength and high impact toughness and preparation method thereof - Google Patents
Anchor rod rebar with high strength and high impact toughness and preparation method thereof Download PDFInfo
- Publication number
- CN102352462B CN102352462B CN2011102942742A CN201110294274A CN102352462B CN 102352462 B CN102352462 B CN 102352462B CN 2011102942742 A CN2011102942742 A CN 2011102942742A CN 201110294274 A CN201110294274 A CN 201110294274A CN 102352462 B CN102352462 B CN 102352462B
- Authority
- CN
- China
- Prior art keywords
- tempering
- temperature
- preparation
- strength
- quenching
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
Claims (3)