CN102337431A - 铝锰钙合金 - Google Patents
铝锰钙合金 Download PDFInfo
- Publication number
- CN102337431A CN102337431A CN2011102723425A CN201110272342A CN102337431A CN 102337431 A CN102337431 A CN 102337431A CN 2011102723425 A CN2011102723425 A CN 2011102723425A CN 201110272342 A CN201110272342 A CN 201110272342A CN 102337431 A CN102337431 A CN 102337431A
- Authority
- CN
- China
- Prior art keywords
- manganese
- alloy
- aluminum
- calcium
- calcium alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铝锰钙合金,它包含如下重量百分比的成分:Al 55-59%;Mn10-15%;Ca 2~5%;Ti 0~0.05%;C 0~0.5%;P 0~0.04%;S 0~0.04%;Si 0~0.2%;余量为Fe;所述铝锰钙合金粒度为10-50mm 95~100%。本发明的合金脱氧效果好,可改善钢中夹杂,同时能降低脱氧产物熔点,使其在浇铸时不易凝结,并附带有脱硫效果的炼钢用铝锰钙合金。
Description
技术领域
本发明涉及一种用于炼钢终脱氧的铝锰钙铁合金。
背景技术
炼钢中用铝锰脱氧效果好,合金比重大,易在钢水中下沉,脱氧的同时可实现锰的合金化等优点,主要是其脱氧产物AL2O3在钢中形成的夹杂成条状,其不可塑性导致钢的冲击韧性和延伸率降低。同时,由于AL2O3熔点高,其在钢水浇铸时易凝结,堵塞水口,对连铸尤为不利。
技术方案
本发明的目的是在保持上述铝锰合金脱氧剂优点的情况下,提供一种还具有可改善钢中夹杂,同时能降低脱氧产物熔点,使其在浇铸时不易凝结,并附带有脱硫效果的炼钢用铝锰钙合金。
本发明合金在现有的铝锰合金中加了金属钙。因为钙和氧的亲和力很强,故加入钙后合金的脱氧效果不仅不会降低,反而原有铝锰合金的优点保持不变,钙作为变性剂加入后,使钢中夹杂物球化,夹杂物形态改善,从而使成品钢的冲击韧性和延伸率得以提高。另外,加入改后,使脱氧产物形成钙铝酸盐,它的熔点较低,在钢水中易上浮除去,不仅在浇铸时不易凝结堵塞水口,而且还使钢水中的夹杂物含量降低。由于钙与硫的亲和力也很强,因此本合金在确保良好脱氧能力的同时,还附带有脱硫效果。
本发明采用的技术方案如下:
本发明的铝锰钙合金包含如下重量百分比的成分:
Al 55-59%;
Mn 10-15%;
Ca 2~5%;
Ti 0~0.05%;
C 0~0.5%;
P 0~0.04%;
S 0~0.04%;
Si 0~0.2%;
余量为Fe;
上述合金粒度为10-50mm 95~100%
有益效果:本发明的合金脱氧效果好,可改善钢中夹杂,同时能降低脱氧产物熔点,使其在浇铸时不易凝结,并附带有脱硫效果的炼钢用铝锰钙合金。
具体实施方式
根据下述实施例,可以更好地理解本发明。然而,本领域的技术人员容易理解,实施例所描述的内容仅用于说明本发明,而不应当也不会限制权利要求书中所详细描述的本发明。
实施例1:
以0.5t中频电炉且每批总投量为200kg为例。
1、本发明的制备先按以下重量配料备用:
1、铝 114kg
2、钙 60kg
3、电解锰 22kg
4、铁 4kg
2、本发明的制备工艺步骤如下:
1、加入废钢升温熔化;
2、加入电解锰熔化;
3、加入钙块熔化;
4、加入铝块待其完全熔化后搅拌除渣;
5、出炉铸块;
6、破碎装袋(粒径10~50mm)。
3、按上述配料经上述工艺制备得到的铝锰钙合金的检验,要求如下:
(1)铝锰钙合金的质量检查和验收应符合GB/T3650的规定;
(2)铝含量按GB-T 6987.5-2001硅铝合金化学分析方法EDTA滴定法测定;
(3)按GB/T 1506-2002化学分析方法,电位滴定法测定锰的含量;
(4)按硅钙合金化学分析方法EDTA滴定测定钙量;
(5)其它元素按GB5686进行。
经检验,最终成品化学成分(重量百分含量)如下:
Al 57%;
Mn 11%;
Ca 3%;
Ti 0.03%;
C 0.1%;
P 0.03%;
S 0.01%;
Si 0.1%;
Fe 28.73%。
上述合金粒度为10-50mm 95~100%。
试验例:上述合金作为炼钢终脱氧剂,在钢水中的脱氧,脱硫及改善夹杂物含量均由于常规铝锰合金。
Claims (1)
1.一种铝锰钙合金,其特征在于它包含如下重量百分比的成分:
Al 55-59%;
Mn 10-15%;
Ca 2~5%;
Ti 0~0.05%;
C 0~0.5%;
P 0~0.04%;
S 0~0.04%;
Si 0~0.2%;
余量为Fe;
所述铝锰钙合金粒度为10-50mm 95~100%。