CN102337114A - 一种无机硼交联剂及其制备方法 - Google Patents

一种无机硼交联剂及其制备方法 Download PDF

Info

Publication number
CN102337114A
CN102337114A CN 201110221072 CN201110221072A CN102337114A CN 102337114 A CN102337114 A CN 102337114A CN 201110221072 CN201110221072 CN 201110221072 CN 201110221072 A CN201110221072 A CN 201110221072A CN 102337114 A CN102337114 A CN 102337114A
Authority
CN
China
Prior art keywords
parts
crosslinking agent
fracturing fluid
sodium hydroxide
boric acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201110221072
Other languages
English (en)
Inventor
杜彪
杨海燕
陆红军
万华
赵燕红
吕俊华
薛小佳
吴江
李建山
叶智
邓卫珍
窦淼
王伟波
程晓亮
吕明洁
程芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XI'AN CHANGQING CHEMICAL INDUSTRY GROUP Co Ltd
Original Assignee
XI'AN CHANGQING CHEMICAL INDUSTRY GROUP Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XI'AN CHANGQING CHEMICAL INDUSTRY GROUP Co Ltd filed Critical XI'AN CHANGQING CHEMICAL INDUSTRY GROUP Co Ltd
Priority to CN 201110221072 priority Critical patent/CN102337114A/zh
Publication of CN102337114A publication Critical patent/CN102337114A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种无机硼交联剂及其制备方法。目前国内外储层改造普遍使用水基压裂液，以硼砂为交联剂的压裂液体系耐温差，只能用于较浅的储层改造；采用有机硼交联剂的压裂液耐温能力得到增强，但是导致压裂液破胶剂用量大及破胶困难，对储层及支撑裂缝的渗透率伤害较大。本发明由水200～350份，硼酸100～200份，木糖醇300～400份，氢氧化钠150～200份组成，按上述的用量进行配比，将水加入到反应釜中，加入硼酸，直至完全溶解，在搅拌条件下，缓缓加入木糖醇，在40～50℃下反应60～90分钟，然后缓缓加入氢氧化钠，完全溶解后即得到无机硼交联剂。本发明通过提高交联剂的pH值提高压裂液的耐温性能，通过加入多元醇提高无机硼交联剂的延迟交联时间。

Description

一种无机硼交联剂及其制备方法
技术领域
本发明涉及一种用于油气储层压裂改造的增产工艺中所使用的无机硼交联剂及其制备方法。
背景技术
目前国内外储层改造普遍使用水基压裂液，以硼的无机物或有机物为交联剂，稠化剂大都采用瓜尔胶及其衍生物，但是存在以下不足：以硼砂为交联剂的压裂液体系耐温差，只能用于较浅的储层改造；采用有机硼交联剂的压裂液耐温能力得到增强，但是导致压裂液破胶剂用量大及破胶困难，对储层及支撑裂缝的渗透率伤害较大，上述因素在一定程度上影响了改造效果。
发明内容
本发明所解决的技术问题是提供一种无机硼交联剂及其制备方法，能够提高交联剂的pH值提高压裂液的耐温性能并通过加入多元醇提高无机硼交联剂的延迟交联时间。
为解决上述的技术问题，本发明采取的技术方案：
一种无机硼交联剂，其特殊之处在于：由以下物质按照重量份组成：
水                                  200～350份
硼酸                                100～200份
木糖醇                              300～400份
氢氧化钠                            150～200份。
一种无机硼交联剂的制备方法，其特殊之处在于：所述的制备方法为按上述的用量进行配比，将水加入到反应釜中，加入硼酸，直至完全溶解，在搅拌条件下，缓缓加入木糖醇，在40～50℃下反应60～90分钟，然后缓缓加入氢氧化钠，完全溶解后即得到无机硼交联剂。
与现有技术相比，本发明的有益效果：
1、本发明通过提高交联剂的pH值提高压裂液的耐温性能。
2、本发明通过加入多元醇提高无机硼交联剂的延迟交联时间。
具体实施方式
下面结合具体实施方式对本发明进行详细说明。
本发明由以下物质按照重量份组成：
水                                  200～350份
硼酸                                100～200份
木糖醇                              300～400份
氢氧化钠                            150～200份
所述的制备方法为按上述的用量进行配比，将水加入到反应釜中，加入硼酸，直至完全溶解，在搅拌条件下，缓缓加入木糖醇，在40～50℃下反应60～90分钟，然后缓缓加入氢氧化钠，完全溶解后即得到无机硼交联剂。
实施例1：本发明由以下物质按照重量份组成：
水                                  200份
硼酸                                100份
木糖醇                              300份
氢氧化钠                            150份
所述的制备方法为按上述的用量进行配比，将水加入到反应釜中，加入硼酸，直至完全溶解，在搅拌条件下，缓缓加入木糖醇，在40℃下反应60分钟，然后缓缓加入氢氧化钠，完全溶解后即得到无机硼交联剂。
实施例2：
本发明由以下物质按照重量份组成：
水                               350份
硼酸                             150份
木糖醇                           400份
氢氧化钠                         200份
所述的制备方法为按上述的用量进行配比，将水加入到反应釜中，加入硼酸，直至完全溶解，在搅拌条件下，缓缓加入木糖醇，在50℃下反应90分钟，然后缓缓加入氢氧化钠，完全溶解后即得到无机硼交联剂。
实施例3：
本发明由以下物质按照重量份组成：
水                                  275份
硼酸                                200份
木糖醇                              350份
氢氧化钠                            175份
所述的制备方法为按上述的用量进行配比，将水加入到反应釜中，加入硼酸，直至完全溶解，在搅拌条件下，缓缓加入木糖醇，在45℃下反应75分钟，然后缓缓加入氢氧化钠，完全溶解后即得到无机硼交联剂。
采用实施例2制得的交联剂按照标准SY-T6216-1996压裂用交联剂性能规定的技术要求，进行检测,检验报告如下：
序号 检验项目 单位 检验结果
1 外 观 /  无色均匀液体
2 密 度 （30℃） g/cm3 1.11
3 pH 值 / 14.0
4 水溶性 / 与水互溶
5 交联性能 / 能形成可用玻璃棒挑挂的冻胶
6 延时时间   1~10min可调
该无机硼交联剂能与瓜胶交联，形成冻胶；其0.3%的瓜胶浓度形成的压裂液耐温能达到100℃以上，现在市面上销售的有机硼交联剂、无机硼交联剂能与同等浓度的瓜胶形成冻胶，但是该交联剂与无机硼交联剂相比，其交联后破胶彻底，消耗破胶剂较少。该交联剂与其他无机硼交联剂比，其他无机硼交联0.3%瓜胶浓度耐温基本低于60℃，故其比其他无机硼交联剂耐温性能好。

Claims (2)

1.一种无机硼交联剂，其特征在于：由以下物质按照重量份组成：
水                                  200～350份
硼酸                                100～200份
木糖醇                              300～400份
氢氧化钠                            150～200份。
2.根据权利要求1所述的一种无机硼交联剂的制备方法，其特征在于：所述的制备方法为按上述的用量进行配比，将水加入到反应釜中，加入硼酸，直至完全溶解，在搅拌条件下，缓缓加入木糖醇，在40～50℃下反应60～90分钟，然后缓缓加入氢氧化钠，完全溶解后即得到无机硼交联剂。
CN 201110221072 2011-08-03 2011-08-03 一种无机硼交联剂及其制备方法 Pending CN102337114A (zh)