CN102336980A - Processing modifier for polyvinyl chloride cable material - Google Patents
Processing modifier for polyvinyl chloride cable material Download PDFInfo
- Publication number
- CN102336980A CN102336980A CN2011101410404A CN201110141040A CN102336980A CN 102336980 A CN102336980 A CN 102336980A CN 2011101410404 A CN2011101410404 A CN 2011101410404A CN 201110141040 A CN201110141040 A CN 201110141040A CN 102336980 A CN102336980 A CN 102336980A
- Authority
- CN
- China
- Prior art keywords
- modifier
- cable material
- polyvinyl chloride
- chloride cable
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing modifier for a polyvinyl chloride cable material. The processing modifier comprises the following components in part by weight: 4 to 5 parts of chlorinated paraffin, 1 to 2 parts of calcium stearate, 2 to 3 parts of rubber and plastic modifier, 0.5 to 1.0 part of lead stearate, 3 to 4 parts of lead sulfate tribasic, 0.25 part of bisphenol A and 0.5 to 1 part of titanium white. A processing method comprises the following steps of: preparing various components; mixing; stirring; heating; cooling; and discharging and packaging. The processing modifier has the advantages of novel concept, standard process, simple operation, low price, no pollution, capacity of improving toughness and strength of the product and reducing the cost of the product when used for processing the cable material, suitability for batch production and the like, and can be widely applied to the fields such as polyvinyl chloride cable material processing and the like.
Description
Technical field
The present invention relates to a kind of processing of plastic properties-correcting agent that is used for, particularly relate to a kind of modifier that is used for polyvinyl chloride cable material.
Background technology
Up to now, the auxiliary materials such as clorafin that the existing modifier that is used for polyvinyl chloride cable material adds are many, therefore; The polyvinyl chloride cable material fragility of producing is bigger, and toughness and intensity are relatively poor, and cost is than higher; The demand that can not adapt to market; Its application receives very big restriction, how to change this situation, and this is the problem that the present invention will solve.
Summary of the invention
The objective of the invention is to cover the shortage, and a kind of modifier that is used for polyvinyl chloride cable material is provided in order to overcome the defective of above-mentioned background technology.
To achieve these goals, the technical scheme that is used for the modifier of polyvinyl chloride cable material of the present invention is such:
Modifier of the present invention comprises following component and weight part:
Clorafin 4～5; Calcium stearate 0.5～2; Rubber and plastic properties-correcting agent 2～5; Lead stearate 0.5～1.0; Lead sulfate tribasic 3～4; Dihydroxyphenyl propane 0.2～0.5; White titanium pigment 0.5～1.
Described modifier comprises following component and weight part:
Clorafin 4.2～4.9; Calcium stearate 0.6～1.8; Rubber and plastic properties-correcting agent 2.1～4.8; Lead stearate 0.52～0.65; Lead sulfate tribasic 3.1～3.8; Dihydroxyphenyl propane 0.3～0.4; White titanium pigment 0.6～0.9.
Described modifier comprises following component and weight part:
Clorafin 4.5; Calcium stearate 1.5; Rubber and plastic properties-correcting agent 3.5; Lead stearate 0.55; Lead sulfate tribasic 3.4; Dihydroxyphenyl propane 0.3; White titanium pigment 0.8.
Described rubber and plastic properties-correcting agent is to be composited by ethylene vinyl acetate and aluminic acid lipoprotein coupling agent, and its proportioning is: ethylene vinyl acetate: aluminic acid lipoprotein coupling agent=1.5～2.5: 0.05～0.1.
The proportioning of described rubber and plastic properties-correcting agent is: ethylene vinyl acetate: aluminic acid lipoprotein coupling agent=1.8: 0.08.
The modifier that is used for polyvinyl chloride cable material of the present invention has following beneficial effect: reasonable idea, technological specification, simple to operate, cheap, pollution-free; Be used for toughness and intensity that the polyvinyl chloride cable material processing can improve product, promote the quality of product, reduce production cost of products.The present invention can form industrialized mass production as early as possible, can be widely used in the polyvinyl chloride cable material manufacture field.
Embodiment
Below in conjunction with embodiment the present invention is made further detailed description, but this embodiment should not be construed as limitation of the present invention.
Embodiment 1
Modifier of the present invention is joined by following processing sequence system:
One, produces the preparation of each component of said modifier and weight part
1, the preparation of rubber and plastic properties-correcting agent:
Get ethylene vinyl acetate 1.5 by described rubber and plastic properties-correcting agent proportioning, aluminic acid lipoprotein coupling agent 0.05 is inserted in the whisking appliance together, under normal temperature condition, stirs, and gets final product discharging, subsequent use after stirring.
2, the preparation of described each component and weight part:
Clorafin 4; Calcium stearate 1; Rubber and plastic properties-correcting agent 2; Lead stearate 0.5; Lead sulfate tribasic 3; Dihydroxyphenyl propane 0.3; White titanium pigment 0.5, subsequent use.
Two. the preparation of described modifier:
1, batch mixing: above-mentioned each ingredients weight parts for preparing is mixed, drop into mixing and stirring in the kneader together, heating to 135 ℃～140 ℃ can stop to heat, subsequent use;
2, discharging is packed: can discharging packing, i.e. finished product---described modifier packing after the above-mentioned batch mixing that processes is cooled to normal temperature.
Embodiment 2
Present embodiment and embodiment 1 are basic identical, and its difference is:
One, produces the preparation of each component of said modifier and weight part
1, the preparation of rubber and plastic properties-correcting agent:
Get ethylene vinyl acetate 1.8 by described rubber and plastic properties-correcting agent proportioning, aluminic acid lipoprotein coupling agent 0.08 is inserted in the whisking appliance together, under normal temperature condition, stirs, and gets final product discharging, subsequent use after stirring.
2, the preparation of described each component and weight part:
Clorafin 4.2; Calcium stearate 1.1; Rubber and plastic properties-correcting agent 2.1; Lead stearate 0.52; Tribasic vitriol 3.1; Dihydroxyphenyl propane 0.32; White titanium pigment 0.6, subsequent use.
Embodiment 3
Present embodiment and embodiment 1 are basic identical, and its difference is:
One, produces the preparation of each component of said modifier and weight part
1, the preparation of rubber and plastic properties-correcting agent:
Get ethylene vinyl acetate 2.5 by described rubber and plastic properties-correcting agent proportioning, aluminic acid lipoprotein coupling agent 0.1 is inserted in the whisking appliance together, under normal temperature condition, stirs, and gets final product discharging, subsequent use after stirring.
2, the preparation of described each component and weight part:
Clorafin 4.5; Calcium stearate 1.5; Rubber and plastic properties-correcting agent 3.5; Lead stearate 0.55; Lead sulfate tribasic 3.4; Dihydroxyphenyl propane 0.4; White titanium pigment 0.7, subsequent use.
Embodiment 4
Present embodiment and embodiment 1 are basic identical, and its difference is:
One, produces the preparation of each component of said modifier and weight part
1, the preparation of rubber and plastic properties-correcting agent:
Get ethylene vinyl acetate 2.5 by described rubber and plastic properties-correcting agent proportioning, aluminic acid lipoprotein coupling agent 0.1 is inserted in the whisking appliance together, under normal temperature condition, stirs, and gets final product discharging, subsequent use after stirring.
2, the preparation of described each component and weight part:
Clorafin 4.9; Calcium stearate 1; Rubber and plastic properties-correcting agent 4; Lead stearate 0.58; Lead sulfate tribasic 3.8; Dihydroxyphenyl propane 0.45; White titanium pigment 0.9, subsequent use.
Embodiment 5
Present embodiment and embodiment 1 are basic identical, and its difference is:
One, produces the preparation of each component of said modifier and weight part
1, the preparation of rubber and plastic properties-correcting agent:
Get ethylene vinyl acetate 2.5 by described rubber and plastic properties-correcting agent proportioning, aluminic acid lipoprotein coupling agent 0.1 is inserted in the whisking appliance together, under normal temperature condition, stirs, and gets final product discharging, subsequent use after stirring.
2, the preparation of described each component and weight part:
Clorafin 5; Calcium stearate 2; Rubber and plastic properties-correcting agent 5; Lead stearate 0.6; Lead sulfate tribasic 4; Dihydroxyphenyl propane 0.5; White titanium pigment 1, subsequent use.
Obviously, those skilled in the art can carry out various changes and modification to the present invention and not break away from the spirit and scope of the present invention.Like this, belong within the scope of claim of the present invention and equivalent technologies thereof if of the present invention these are revised with modification, then the present invention also is intended to comprise these changes and modification interior.
The content of not doing in this specification sheets to describe in detail belongs to this area professional and technical personnel's known prior art.
Claims (5)
1. modifier that is used for polyvinyl chloride cable material, it is characterized in that: said modifier comprises following component and weight part:
Clorafin 4～5; Calcium stearate 0.5～2; Rubber and plastic properties-correcting agent 2～5; Lead stearate 0.5～1.0; Lead sulfate tribasic 3～4; Dihydroxyphenyl propane 0.2～0.5; White titanium pigment 0.5～1.
2. the modifier that is used for polyvinyl chloride cable material according to claim 1 is characterized in that: said modifier comprises following component and weight part:
Clorafin 4.2～4.9; Calcium stearate 0.6～1.8; Rubber and plastic properties-correcting agent 2.1～4.8; Lead stearate 0.52～0.65; Lead sulfate tribasic 3.1～3.8; Dihydroxyphenyl propane 0.3～0.4; White titanium pigment 0.6～0.9.
3. the modifier that is used for polyvinyl chloride cable material according to claim 1 is characterized in that: said modifier comprises following component and weight part:
Clorafin 4.5; Calcium stearate 1.5; Rubber and plastic properties-correcting agent 3.5; Lead stearate 0.55; Lead sulfate tribasic 3.4; Dihydroxyphenyl propane 0.3; White titanium pigment 0.8.
4. according to the described modifier that is used for polyvinyl chloride cable material of arbitrary claim in the claim 1 to 3; It is characterized in that: described rubber and plastic properties-correcting agent is to be composited by ethylene vinyl acetate and aluminic acid lipoprotein coupling agent, and its proportioning is: ethylene vinyl acetate: aluminic acid lipoprotein coupling agent=1.5～2.5: 0.05～0.1.
5. the modifier that is used for polyvinyl chloride cable material according to claim 4 is characterized in that: described proportioning is an ethylene vinyl acetate: aluminic acid lipoprotein coupling agent=1.8: 0.08.