CN102329409A - 超低密度聚氨酯鞋底原液合成工艺 - Google Patents
超低密度聚氨酯鞋底原液合成工艺 Download PDFInfo
- Publication number
- CN102329409A CN102329409A CN 201110242647 CN201110242647A CN102329409A CN 102329409 A CN102329409 A CN 102329409A CN 201110242647 CN201110242647 CN 201110242647 CN 201110242647 A CN201110242647 A CN 201110242647A CN 102329409 A CN102329409 A CN 102329409A
- Authority
- CN
- China
- Prior art keywords
- density polyurethane
- polyurethane sole
- polyester polyol
- composite catalyst
- stoste
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种超低密度聚氨酯鞋底原液合成工艺,聚酯化反应,将二元羧酸和多元醇进行在复合催化剂作用下进行聚酯化反应,获得聚酯多元醇,所述的复合催化剂包括有醋酸盐、三乙烯二胺、辛酸亚锡/硅催化剂;获得聚酯多元醇与匀泡剂、接枝聚酯、硅油混合获得A组分;将获得聚酯多元醇与异氰酸酯及聚醚多元醇预聚得到B组分。本发明节能减排效果显著,且原料利用率高。本发明具有更质轻和耐磨、耐折、耐油、耐化学品等优点。传统低密度聚氨酯鞋底原液在鞋底成型密度在0.32-0.38,本发明将成型密度降到了0.26-0.30,大大的降低了成本,提高了经济效益。
Description
技术领域
本发明涉及一种化工产品合成工艺,具体是指超低密度聚氨酯鞋底原液合成工艺。
背景技术
随着人们生活水平的提高,人们对鞋类产品技术指标要求也越来越高, 由于低密度聚氨酯鞋底具有质轻、耐磨、耐折、耐油、耐化学品等优点,人们对低密度聚氨酯鞋底原液需求量日益提高。但是,现有的低密度聚氨酯鞋底原液生产大多是采用高密度工艺,其流程是二元羧酸与多元醇聚酯化反应获得聚酯多元醇,但是这种工艺具有以下缺点
(1)生产周期长,反应周期为20小时以上;
(2)能源消耗大,生产一吨产品消耗电能在150元以上;
(3)原料利用率低,聚氨酯合成中的酯化反应率为82%以下;
(4)生产过程中水的回收率低,一吨产品消耗水在0.5吨以上。
发明内容
本发明的目的是为了克服现有技术存在的缺点和不足,而提供一种原料循环利用,具有更质轻和耐磨、耐折、耐油、耐化学,且节能减排效果显著的超低密度聚氨酯鞋底原液合成工艺。
为实现上述目的,本发明的技术方案是包括以下步骤
(1)聚酯化反应,将二元羧酸和多元醇进行在复合催化剂作用下进行聚酯化反应,获得聚已二酸对苯二甲酸乙二醇二乙二醇酯(以下简称聚酯多元醇),所述的复合催化剂包括有醋酸盐、三乙烯二胺、辛酸亚锡/硅催化剂,该复合催化剂催化剂的量相对于二元羧酸和多元醇的总质量的比例为1:155-165;
(2)将步骤(1)获得聚酯多元醇与辅料硅油混合获得A料;将步骤(1)获得聚酯多元醇与异氰酸酯及聚醚多元醇预聚得到B料。
进一步设置是所述的匀泡剂、接枝聚酯和硅油的质量分数比为:0.5:6:0.4。
进一步设置是所述的辅料为匀泡剂硅油,该匀泡剂包括有以下组分,按质量份数计,八甲基环四硅氧烷:聚醚硅氧烷=1:3-5。
进一步设置是所述的二元羧酸为:所述的二元羧酸为已二酸与对苯二甲酸,且已二酸与对苯二甲酸质量比=1:1-3,所述的多元醇为乙二醇与二乙二醇的混合物,且乙二醇与二乙二醇质量比=1:1-5。
进一步设置是所述的复合催化剂的各组分配比为,以质量分数计:
醋酸盐 醋酸钾1-3份,醋酸锌1-8份
三乙烯二胺 30-50份
辛酸亚锡/硅催化剂 30-50份。
本发明的优点在于:在新的工艺中采用复合催化剂, 以醋酸盐、三乙烯二胺、辛酸亚锡/硅催化剂相互复配的基础上形成新型的复合催化剂体系,在新的复合催化剂下,实现了合成工艺周期为16小时,大大降低能耗,减少成本。具体对比如下:
传统聚酯化工艺:
二元羧酸+多元醇---聚酯多元醇(聚酯多元醇的聚合反应周期为20个小时, 聚酯多元醇的聚合反应速率75%,耗水1.2吨/吨,耗电150元/吨)
本发明聚酯化工艺:
二元羧酸+多元醇+复合催化剂---聚酯多元醇(聚酯多元醇的聚合反应周期为16个小时聚酯多元醇的聚合反应速率85%,耗水0.5吨/吨,耗电120元/吨)。
(2)采用了全水发泡,在合成中间体没有油性,减少了污染,大大降低排放。提高了水的回收率,新的工艺中一吨产品水的消耗量为0.5吨.
(3)在新的工艺下,采用新的配方,在聚酯多元醇中加入了异氰酸酯和聚醚多元醇及接枝聚酯,降低制品成型密度提高了原料的利用率。新工艺的二元羧酸和二元醇的利用率为85%以上。
下面结合具体实施方式对本发明做进一步介绍。
具体实施方式
下面通过实施例对本发明进行具体的描述,只用于对本发明进行进一步说明,不能理解为对本发明保护范围的限定,该领域的技术工程师可根据上述发明的内容对本发明作出一些非本质的改进和调整。
实施例1
包括以下步骤
(1)聚酯化反应,将二元羧酸和多元醇进行在复合催化剂作用下进行聚酯化反应,获得聚酯多元醇,所述的复合催化剂包括有醋酸盐、三乙烯二胺、辛酸亚锡/硅催化剂;该复合催化剂催化剂的量相对于二元羧酸和多元醇的总质量的比例为1:155,本工艺采用常规聚酯化反应条件即可,所述的二元羧酸为已二酸与对苯二甲酸,所述的多元醇为乙二醇与二乙二醇的混合物,且已二酸与对苯二甲酸质量比=1:1,乙二醇与二乙二醇质量比=1:1,所述的复合催化剂的各组分配比为,以质量分数计:
醋酸盐 醋酸钾1份,醋酸锌1份
三乙烯二胺 30份
辛酸亚锡/硅催化剂 30份。
(2)将步骤(1)获得聚酯多元醇与辅料混合获得A料,所述的辅料为匀泡剂及接枝聚酯,该匀泡剂包括有以下组分,按质量份数计,八甲基环四硅氧烷:聚醚硅氧烷=1:3。;
(3)将步骤(1)获得聚酯多元醇与异氰酸酯及聚醚多元醇预聚得到B料。
实施例2
包括以下步骤
(1)聚酯化反应,将二元羧酸和多元醇进行在复合催化剂作用下进行聚酯化反应,获得聚酯多元醇,所述的复合催化剂包括有醋酸盐、三乙烯二胺、辛酸亚锡/硅催化剂,该复合催化剂催化剂的量相对于二元羧酸和多元醇的总质量的比例为1:160,本工艺采用常规聚酯化反应条件即可,所述的二元羧酸为已二酸和对苯二甲酸,所述的多元醇为乙二醇与二乙二醇的混合物,且已二酸与对苯二甲酸质量比=1:1-2,乙二醇与二乙二醇质量比=1:2.5,所述的复合催化剂的各组分配比为,以质量分数计:
醋酸盐 醋酸钾2.5份,醋酸锌5份
三乙烯二胺 40份
辛酸亚锡/硅催化剂 40份。
(2)将步骤(1)获得聚酯多元醇与辅料混合获得A料,所述的辅料为匀泡剂及接枝聚酯组成,该匀泡剂包括有以下组分,按质量份数计,八甲基环四硅氧烷:聚醚硅氧烷=1:4。;
(3)将步骤(1)获得聚酯多元醇与异氰酸酯及聚醚多元醇预聚得到B料。
实施例3
包括以下步骤
(1)聚酯化反应,将二元羧酸和多元醇进行在复合催化剂作用下进行聚酯化反应,获得聚酯多元醇,所述的复合催化剂包括有醋酸盐、三乙烯二胺、辛酸亚锡/硅催化剂,该复合催化剂催化剂的量相对于二元羧酸和多元醇的总质量的比例为1:165,本工艺采用常规聚酯化反应条件即可,所述的二元羧酸为乙二酸与对苯二甲酸,所述的多元醇为乙二醇与二乙二醇的混合物,且已二酸与对苯二甲酸质量比=1: 3,乙二醇与二乙二醇质量比=1:5,所述的复合催化剂的各组分配比为,以质量分数计:
醋酸盐 醋酸钾3份,醋酸锌8份
三乙烯二胺 50份
辛酸亚锡/硅催化剂 50份。
(2)将步骤(1)获得聚酯多元醇与辅料混合获得A组分,所述的辅料为匀泡剂该匀泡剂包括有以下组分,按质量份数计,八甲基环四硅氧烷:聚醚硅氧烷=1:5。;
(3)将步骤(1)获得聚酯多元醇与异氰酸酯及聚醚多元醇预聚得到B组分。
Claims (5)
1.一种超低密度聚氨酯鞋底原液合成工艺,其特征在于包括以下步骤:
聚酯化反应,将二元羧酸和多元醇进行在复合催化剂作用下进行聚酯化反应,获得聚酯多元醇,所述的复合催化剂包括有醋酸盐、三乙烯二胺、辛酸亚锡/硅催化剂,该复合催化剂催化剂的量相对于二元羧酸和多元醇的总质量的比例为1:155-165;
将步骤(1)获得聚酯多元醇与辅料混合,获得A组分,该辅料包括有匀泡剂、接枝聚酯和硅油;
将步骤(1)获得聚酯多元醇与异氰酸酯及聚醚多元醇预聚得到B组分,其中异氰酸酯的质量占B组分的各原料的总和的22-22.2%。
2.根据权利要求1所述的一种超低密度聚氨酯鞋底原液合成工艺,其特征在于:所述的匀泡剂、接枝聚酯和硅油的质量分数比为:0.5:6:0.4。
3.根据权利要求1所述的一种超低密度聚氨酯鞋底原液合成工艺,其特征在于:所述的匀泡剂包括有以下组分,按质量份数计:
八甲基环四硅氧烷:聚醚硅氧烷 1:3-5。
4.根据权利要求1或2所述的一种超低密度聚氨酯鞋底原液合成工艺,其特征在于:所述的二元羧酸为已二酸与对苯二甲酸,且已二酸与对苯二甲酸质量比=1:1-3,所述的多元醇为乙二醇与二乙二醇的混合物,且乙二醇与二乙二醇质量比=1:1-5。
5.根据权利要求3所述的一种超低密度聚氨酯鞋底原液合成工艺,其特征在于:所述的复合催化剂的各组分配比为,以质量分数计:
醋酸盐 醋酸钾1-3份,醋酸锌1-8份
三乙烯二胺 30-50份
辛酸亚锡/硅催化剂 30-50份。