CN102277583A - 制备生物转化膜金属板的前处理方法 - Google Patents
制备生物转化膜金属板的前处理方法 Download PDFInfo
- Publication number
- CN102277583A CN102277583A CN 201110240803 CN201110240803A CN102277583A CN 102277583 A CN102277583 A CN 102277583A CN 201110240803 CN201110240803 CN 201110240803 CN 201110240803 A CN201110240803 A CN 201110240803A CN 102277583 A CN102277583 A CN 102277583A
- Authority
- CN
- China
- Prior art keywords
- metal sheet
- time
- rinsing
- metal plate
- clean
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种制备生物转化膜金属板的前处理方法，取金属板；在常温条件下，将金属板放入清洗剂中浸泡3-10min，所述清洗剂由生物有机酸、维生素、食用碳酸氢钠、缓蚀剂、表面活性剂、水组成；将金属板从清洗剂中取出，用自来水进行第一次漂洗，第一次漂洗的时间为3-5min，自来水的温度≥45℃；第一次漂洗之后，再在常温状态下用自来水对金属板进行第二次漂洗，第二次漂洗时间为1-3min。本发明具有生产工艺简单、清洗效果好、安全环保的优点。
Description
技术领域
本发明涉及一种制备生物转化膜金属板的前处理方法。
背景技术
目前，金属板清洗的过程是将原金属板表面进行除油、除锈，清洗的过程是将金属板浸入盐酸或硫酸等清洗介质中，其目的是为了去除粘附在金属板基质表面的油垢、污垢，一般的表面处理工艺为：脱脂；两次水洗；除锈；再次水洗；表面调整；又一次水洗；磷化处理；最后一次水洗；晾干；这一整套处理工艺不仅清洗过程慢，而且存在很严重的排放问题，同时清洗时使用的盐酸或硫酸等清洗介质对人体有危害，对环境也会造成很大的污染。
发明内容
本发明的目的是为了克服以上的不足，提供一种生产工艺简单、清洗效果好、安全环保的制备生物转化膜金属板的前处理方法。
本发明是通过以下技术方案来实现：一种制备生物转化膜金属板的前处理方法，包括以下步骤：
A、取金属板；
B、在常温条件下，将金属板放入清洗剂中浸泡3-10min，所述清洗剂由生物有机酸、维生素、食用碳酸氢钠、缓蚀剂、表面活性剂、水组成；
C、将金属板从清洗剂中取出，用自来水进行第一次漂洗，第一次漂洗的时间为3-5min，自来水的温度≥45℃；
D、第一次漂洗之后，再在常温状态下用自来水对金属板进行第二次漂洗，第二次漂洗时间为1-3min。
本发明的进一步改进在于：清洗剂由生物有机酸、维生素、食用碳酸氢钠、缓蚀剂、表面活性剂、水组成。
本发明与现有技术相比具有以下优点：本发明对金属板表面进行清理处理，即将金属板放入含有有机物质的清洗剂中，将除油、除锈工艺合并在同一个工序内完成，清洗的过程是将粘附在金属板基质表面的油垢、污垢经清洗介质润湿渗透，并与金属板基质剥离分散，经中温水漂洗和常温水漂洗，使金属板基质表面被清洁干净，清洗步骤简单，清洗效果好，采用的清洗剂环保无危害。
具体实施方式：
为了加深对本发明的理解，下面将结合实施例对本发明作进一步详述，以下实施例仅用于解释本发明，并不构成对本发明保护范围的限定。
本发明一种制备生物转化膜金属板的前处理方法，取金属板；在常温条件下，将金属板放入清洗剂中浸泡3-10min，所述清洗剂由生物有机酸、维生素、食用碳酸氢钠、缓蚀剂、表面活性剂、水组成；将金属板从清洗剂中取出，用自来水进行第一次漂洗，第一次漂洗的时间为3-5min，自来水的温度≥45℃，最佳温度为45℃；第一次漂洗之后，再在常温状态下用自来水对金属板进行第二次漂洗，第二次漂洗时间为1-3min。
所述清洗剂按质量比包括以下成分：
生物有机酸：0.02-4%；
维生素：0.3～1%；
食用碳酸氢钠：3-5%；
缓蚀剂：2-10%；
表面活性剂：1.01-2.05%；
水：78-86%。
其中，生物有机酸为柠檬酸和乳酸的混合液，柠檬酸占清洗剂总质量的0.01-3%，所述乳酸占清洗剂总质量的0.01-1%，维生素为维生素B，缓蚀剂为酒石酸，表面活性剂为辛基酚聚氧乙烯醚和十二烷基磺酸钠的混合物，辛基酚聚氧乙烯醚占清洗剂总重量的0.01-0.05%，十二烷基磺酸钠占清洗剂总重量的1-2%。
金属板放入清洗剂中，清洗药剂对粘附在金属基质表面的油垢、污垢润湿渗透，清洗药剂中的生物介质及活性剂的游离使金属基质表面的油垢、污垢与金属基质脱离分散，同时可借助一定机械动力加强清洗效果，以防油垢、污垢再次沉积。
本发明对金属板表面进行清理处理，即将金属板放入含有有机物质的清洗剂中，将除油、除锈工艺合并在同一个工序内完成，清洗的过程是将粘附在金属板基质表面的油垢、污垢经清洗介质润湿渗透，并与金属板基质剥离分散，经中温水漂洗和常温水漂洗，使金属板基质表面被清洁干净，清洗步骤简单，清洗效果好，采用的清洗剂环保无危害。
Claims (2)
1.一种制备生物转化膜金属板的前处理方法，其特征在于：
A、取金属板；
B、在常温条件下，将金属板放入清洗剂中浸泡3-10min，所述清洗剂由生物有机酸、维生素、食用碳酸氢钠、缓蚀剂、表面活性剂、水组成；
C、将金属板从清洗剂中取出，用自来水进行第一次漂洗，第一次漂洗的时间为3-5min，自来水的温度≥45℃；
D、第一次漂洗之后，再在常温状态下用自来水对金属板进行第二次漂洗，第二次漂洗时间为1-3min。
2.根据权利要求1所述生物转化膜金属板的制造方法，其特征在于：所述清洗剂由生物有机酸、维生素、食用碳酸氢钠、缓蚀剂、表面活性剂、水组成。