CN102277527A - 一种蠕墨铸铁及其制备方法和应用 - Google Patents
一种蠕墨铸铁及其制备方法和应用 Download PDFInfo
- Publication number
- CN102277527A CN102277527A CN2011102422038A CN201110242203A CN102277527A CN 102277527 A CN102277527 A CN 102277527A CN 2011102422038 A CN2011102422038 A CN 2011102422038A CN 201110242203 A CN201110242203 A CN 201110242203A CN 102277527 A CN102277527 A CN 102277527A
- Authority
- CN
- China
- Prior art keywords
- cast iron
- vermicular cast
- iron
- mould
- steel scrap
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种蠕墨铸铁及其制备方法和应用，它由以下重量份数的原料制成：废钢100、SiC2-3、增碳剂0.5-1、Re-Mg-Ti-Ca蠕化剂0.6-0.8、硅铁孕育剂1-1.2。本发明制备的蠕墨铸铁的基体组织为珠光体+铁素体，力学性能为：抗拉强度≥340Mpa；延伸率≥1%，布氏硬度为170-230HB，蠕化率≥80%，满足性能要求。
Description
技术领域
本发明属于蠕墨铸铁的生产领域，特别涉及用废钢和废碳化硅为原料，生产蠕墨铸铁的方法和应用。
背景技术
蠕墨铸铁作为一种新型铸铁材料在20世纪60年代，由于蠕墨铸铁兼有球墨铸铁和灰铸铁的性能，以及良好的热疲劳性，使在汽车发动机缸体、缸盖、排气管、制动盘、制动鼓等方面的应用取得了良好的效果。传统的工艺使用铸造生铁、废钢、回炉料作为原料来配制，在成本上较高。其中也有用废钢和增碳剂来配制原铁液的。但是如果加入增碳剂的量过多，对产品的组织及性能都有一定的影响。
发明内容
本发明用废钢和废碳化硅为主要原料配制原铁液，对于碳含量不足适当加入增碳剂，这样制备出的蠕墨铸铁具有优异的性能，在蠕化以及后期的工艺上能保持性能的稳定性。由于采用废钢和废碳化硅，节约了成本，社会效益显著。
本发明的技术方案是：一种蠕墨铸铁，它由以下重量份数的原料制成：废钢100、SiC 2-3、增碳剂0.5-1、Re-Mg-Ti-Ca蠕化剂0.6-0.8、硅铁孕育剂1-1.2。
所述的蠕墨铸铁的制备方法，它的步骤如下：
（1）用中频炉熔炼废钢，温度达到1480-1530℃时，将SiC和增碳剂加入；
（2）将Re-Mg-Ti-Ca蠕化剂放入包底，采用冲入法进行蠕化处理，铁液出铁温度为1480-1520℃；
（3）用硅铁孕育剂进行孕育处理；
（4）将孕育后的铁液进行浇注，采用顶注法、潮模砂造型，浇注温度为1330-1390℃，浇注时间为10-12分钟。
所述的蠕墨铸铁可应用在制造制动盘、制动鼓或模具。
本发明的显著优点：本发明使用废钢和废碳化硅为主要原料配制铁液，由于废钢和废碳化硅来源很多，原料采购方便，变废为宝，并节省成本，增加企业效益；本发明改善了直接用废钢和增碳剂和硅铁配制原铁液，用废钢加废碳化硅来配比，进而改善了产品性能，制备的蠕墨铸铁性能优异，金相以及蠕化率同时达到要求指标，稳定性好。
本发明制备的蠕墨铸铁的基体组织为珠光体+铁素体，力学性能为：抗拉强度≥340Mpa；延伸率≥1%，布氏硬度为170-230HB，蠕化率≥80%，满足性能要求。
具体实施方式
实施例1
蠕墨铸铁，它由以下重量份数的原料制成：废钢100 kg、SiC 3 kg、增碳剂0.5 kg、Re-Mg-Ti-Ca蠕化剂0.6 kg、硅铁孕育剂1.2 kg。
所述的蠕墨铸铁的制备方法，它的步骤如下：
（1）用中频炉熔炼废钢，温度达到1480℃时，将SiC和增碳剂加入；
（2）将Re-Mg-Ti-Ca蠕化剂放入包底，采用冲入法进行蠕化处理，铁液出铁温度为1480℃；
（3）用硅铁孕育剂进行孕育处理；
（4）将孕育后的铁液进行浇注，采用顶注法、潮模砂造型，浇注温度为1330℃，浇注时间为12分钟。
所述的蠕墨铸铁可应用在制造制动盘、制动鼓或模具。
实施例2
蠕墨铸铁，它由以下重量份数的原料制成：废钢100 kg、SiC 3 kg、增碳剂1 kg、Re-Mg-Ti-Ca蠕化剂0.8 kg、硅铁孕育剂1.2 kg。
所述的蠕墨铸铁的制备方法，它的步骤如下：
（1）用中频炉熔炼废钢，温度达到1530℃时，将SiC和增碳剂加入；
（2）将Re-Mg-Ti-Ca蠕化剂放入包底，采用冲入法进行蠕化处理，铁液出铁温度为1480℃；
（3）用硅铁孕育剂进行孕育处理；
（4）将孕育后的铁液进行浇注，采用顶注法、潮模砂造型，浇注温度为1330℃，浇注时间为12分钟。
所述的蠕墨铸铁可应用在制造制动盘、制动鼓或模具。
实施例3
蠕墨铸铁，它由以下重量份数的原料制成：废钢100 kg、SiC 3 kg、增碳剂0.6 kg、Re-Mg-Ti-Ca蠕化剂0.7 kg、硅铁孕育剂1.2 kg。
所述的蠕墨铸铁的制备方法，它的步骤如下：
（1）用中频炉熔炼废钢，温度达到1520℃时，将SiC和增碳剂加入；
（2）将Re-Mg-Ti-Ca蠕化剂放入包底，采用冲入法进行蠕化处理，铁液出铁温度为1500℃；
（3）用硅铁孕育剂进行孕育处理；
（4）将孕育后的铁液进行浇注，采用顶注法、潮模砂造型，浇注温度为1380℃，浇注时间为12分钟。
所述的蠕墨铸铁可应用在制造制动盘、制动鼓或模具。
实施例4
蠕墨铸铁，它由以下重量份数的原料制成：废钢100 kg、SiC 3 kg、增碳剂0.6 kg、Re-Mg-Ti-Ca蠕化剂0.8 kg、硅铁孕育剂1.1 kg。
所述的蠕墨铸铁的制备方法，它的步骤如下：
（1）用中频炉熔炼废钢，温度达到1480℃时，将SiC和增碳剂加入；
（2）将Re-Mg-Ti-Ca蠕化剂放入包底，采用冲入法进行蠕化处理，铁液出铁温度为1520℃；
（3）用硅铁孕育剂进行孕育处理；
（4）将孕育后的铁液进行浇注，采用顶注法、潮模砂造型，浇注温度为1380℃，浇注时间为10分钟。
所述的蠕墨铸铁可应用在制造制动盘、制动鼓或模具。
实施例5
蠕墨铸铁，它由以下重量份数的原料制成：废钢100 kg、SiC 2.5 kg、增碳剂0.8 kg、Re-Mg-Ti-Ca蠕化剂0.7 kg、硅铁孕育剂1.2 kg。
所述的蠕墨铸铁的制备方法，它的步骤如下：
（1）用中频炉熔炼废钢，温度达到1510℃时，将SiC和增碳剂加入；
（2）将Re-Mg-Ti-Ca蠕化剂放入包底，采用冲入法进行蠕化处理，铁液出铁温度为1500℃；
（3）用硅铁孕育剂进行孕育处理；
（4）将孕育后的铁液进行浇注，采用顶注法、潮模砂造型，浇注温度为1380℃，浇注时间为12分钟。
所述的蠕墨铸铁可应用在制造制动盘、制动鼓或模具。
实施例6
蠕墨铸铁，它由以下重量份数的原料制成：废钢100 kg、SiC 2-3 kg、增碳剂1 kg、Re-Mg-Ti-Ca蠕化剂0.8 kg、硅铁孕育剂1.2 kg。
所述的蠕墨铸铁的制备方法，它的步骤如下：
（1）用中频炉熔炼废钢，温度达到1520℃时，将SiC和增碳剂加入；
（2）将Re-Mg-Ti-Ca蠕化剂放入包底，采用冲入法进行蠕化处理，铁液出铁温度为1520℃；
（3）用硅铁孕育剂进行孕育处理；
（4）将孕育后的铁液进行浇注，采用顶注法、潮模砂造型，浇注温度为1330℃，浇注时间为12分钟。
所述的蠕墨铸铁可应用在制造制动盘、制动鼓或模具。
本发明产品的成分为：C 3.4-3.6%，Si2.3-2.6%，Mn1.4-1.6%，P≤0.5% S≤0.2%。
Claims (3)
1.一种蠕墨铸铁，其特征在于：它由以下重量份数的原料制成：废钢100、SiC 2-3、增碳剂0.5-1、Re-Mg-Ti-Ca蠕化剂0.6-0.8、硅铁孕育剂1-1.2。
2.如权利要求1所述的蠕墨铸铁的制备方法，其特征在于：它的步骤如下：
（1）用中频炉熔炼废钢，温度达到1480-1530℃时，将SiC和增碳剂加入；
（2）将Re-Mg-Ti-Ca蠕化剂放入包底，采用冲入法进行蠕化处理，铁液出铁温度为1480-1520℃；
（3）用硅铁孕育剂进行孕育处理；
（4）将孕育后的铁液进行浇注，采用顶注法、潮模砂造型，浇注温度为1330-1390℃，浇注时间为10-12分钟。
3.如权利要求1所述的蠕墨铸铁可应用在制造制动盘、制动鼓或模具。