CN102225762A - Preparation method of hafnium carbide powder - Google Patents
Preparation method of hafnium carbide powder Download PDFInfo
- Publication number
- CN102225762A CN102225762A CN2011101359959A CN201110135995A CN102225762A CN 102225762 A CN102225762 A CN 102225762A CN 2011101359959 A CN2011101359959 A CN 2011101359959A CN 201110135995 A CN201110135995 A CN 201110135995A CN 102225762 A CN102225762 A CN 102225762A
- Authority
- CN
- China
- Prior art keywords
- powder
- hafnium carbide
- temperature
- hafnium
- resol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a preparation method of hafnium carbide powder, which comprises the following steps of material preparation, mixing, curing, pulverization, compression molding, sintering, decarburization and pulverization, and is characterized in that: phenolic resin is mixed with hafnium dioxide powder with a particle size of 0.1-3 microns to form sludge; the sludge is cured at 40 DEG C-100 DEGC, and is pulverized and compressed to become a block; the block is sintered at 1300 DEG C-1800 DEG C in inert gas or reducing gas atmosphere for 6-8 hours to prepare a hafnium carbide block; and the hafnium carbide powder is obtained by decarburization and pulverization. The invention has the characteristics of simple process, high purity of the hafnium carbide powder, and low cost.
Description
Technical field
The present invention relates to a kind of preparation method of hafnium carbide powder, belong to the ceramic powder preparing technical field.
Background technology
At present, the hafnium carbide powder is mainly made by the hafnium oxide carbothermic method, and its reaction equation is:
HfO
2+3C＝HfC+2CO↑
Above-mentioned reaction process belongs to the solid-solid reaction type, and reaction process is by the material diffusion control.The shortcoming of this method be hafnium oxide powder and carbon black or graphite powder mix inhomogeneous and carbon black or graphite powder active lower, make the hafnium oxide reduction not exclusively, become the impurity of product.In addition, the carbon black or the graphite powder active that remain in the hafnium carbide powder are low, need comparatively high tempss (greater than 600 ℃) just can make C generate carbon monoxide in oxidizing atmosphere during decarburization or carbonic acid gas excludes, the oxygen level in the high more powder of temperature is high more, causes the decline of hafnium carbide powder quality.
Summary of the invention
The objective of the invention is to overcome the defective that exists in the prior art, the reaction synthesis process of the hafnium carbide powder that a kind of cost is low, sintering activity is good is provided.Its technical scheme is:
The preparation method of hafnium carbide powder of the present invention is that the high-activity carbon that adopts resol to form is a carbon source reduction hafnium oxide powder preparing hafnium carbide powder, may further comprise the steps:
1. feedstock production:
The first step: is that 5: 0.5～1 ratio mixes in mixing pan with the hafnium oxide powder of 0.1～3 μ m and resol with weight ratio, under 80～100 ℃ temperature, solidify, in powder-making machine, pulverize then and make the raw material powder 1 that median size is 10～20 μ m.
Second step: is that 5: 1～2 ratio mixes in mixing pan with above-mentioned raw materials powder 1 and resol with weight ratio, solidifies under 50～100 ℃ temperature, and pulverizing in powder-making machine then and making median size is 20～50 μ m raw material powder 2.
The 3rd step: is that 5: 2～3 ratio mixes in mixing pan with above-mentioned raw materials powder 2 and resol with weight ratio, solidifies under 40～80 ℃ temperature, and pulverizing in powder-making machine then and making median size is 50～100 μ m raw material powder 3.
2. the hafnium carbide powder is synthetic:
With the pressure lower lock block of above-mentioned raw materials powder 3 at 0.5～3Mpa, inertia or reducing atmosphere atmosphere are fired and were made the hafnium carbide block in 6-8 hour under 1300 ℃～2000 ℃ temperature then.
3. carbonization treatment
With the oxidizing atmosphere insulation decarburization in 6～12 hours under 350～550 ℃ temperature of above-mentioned hafnium carbide block, the cooling back is pulverized and is made the hafnium carbide powder.
The preparation method of described hafnium carbide powder, hafnium oxide powder and resol mixing proceed step by step.
The present invention compared with prior art has the following advantages:
1, the present invention adopts resol that the hafnium oxide powder is wrapped up and forms isolated micron-sized hafnium oxide particle, the resol carbonization forms active very high porous high-activity carbon when temperature raises, make that the beginning temperature of hafnium oxide and carbon reaction is descended significantly, the micro channel of the porous high-activity carbon that obtains can successfully be discharged the carbon monoxide of hafnium oxide and carbon reaction generation, simultaneously, can suitably reduce the resol consumption or reduce step according to required high-activity carbon amount;
2, the high reactivity porous high-activity carbon that forms after the resol carbonization has wrapped up the hafnium oxide particle, has suppressed the growth of hafnium carbide crystal grain when reaction forms hafnium carbide, can obtain the hafnium carbide powder of grain-size homogeneous.
3, this technical matters is simple, stable, and production cost is low, and the powder application performance is good.
Embodiment
Embodiment 1
1, feedstock production:
The first step: is that 5: 0.5 ratio mixes in mixing pan with the hafnium oxide powder of 0.1 μ m and resol with weight ratio, solidifies under 80 ℃ temperature, pulverizes in powder-making machine then and makes the raw material powder 1 that median size is 10 μ m.
Second step: is that 5: 1 ratio mixes in mixing pan with above-mentioned raw materials powder 1 and resol with weight ratio, solidifies under 50 ℃ temperature, and pulverizing in powder-making machine then and making median size is 20 μ m raw material powder 2.
The 3rd step: is that 5: 2 ratio mixes in mixing pan with above-mentioned raw materials powder 2 and resol with weight ratio, solidifies under 40 ℃ temperature, and pulverizing in powder-making machine then and making median size is 50 μ m raw material powder 3.
2, the hafnium carbide powder is synthetic:
With the pressure lower lock block of above-mentioned raw materials powder 3 at 0.5Mpa, inertia or reducing atmosphere atmosphere are fired and were made the hafnium carbide block in 6 hours under 1300 ℃ ℃ temperature then.
3, carbonization treatment
With the oxidizing atmosphere insulation decarburization in 6 hours under 350 ℃ temperature of above-mentioned hafnium carbide block, system hafnium carbide powder is pulverized in the cooling back.
It is 99.99% pure that raw materials used purity is.
Embodiment 2
1, feedstock production:
The first step: is that 5: 0.75 ratio mixes in mixing pan with the hafnium oxide powder of 1.5 μ m and resol with weight ratio, solidifies under 90 ℃ temperature, pulverizes in powder-making machine then and makes the raw material powder 1 that granularity is 15 μ m.
Second step: is that 5: 1.5 ratio mixes in mixing pan with above-mentioned raw materials powder 1 and resol with weight ratio, solidifies under 75 ℃ temperature, and pulverizing in powder-making machine then and making granularity is 35 μ m raw material powder 2.
The 3rd step: is that 5: 2.5 ratio mixes in mixing pan with above-mentioned raw materials powder 2 and resol with weight ratio, solidifies under 60 ℃ temperature, and pulverizing in powder-making machine then and making granularity is 75 μ m raw material powder 3.
2, the hafnium carbide powder is synthetic:
With the pressure lower lock block of above-mentioned raw materials powder 3 at 1.5Mpa, inertia or reducing atmosphere atmosphere are fired and were made the hafnium carbide block in 7 hours under 1650 ℃ ℃ temperature then.
3, carbonization treatment
With the oxidizing atmosphere insulation decarburization in 9 hours under 450 ℃ temperature of above-mentioned hafnium carbide block, the cooling back is pulverized and is made the hafnium carbide powder.
It is 99.99% pure that raw materials used purity is.
Embodiment 3
1, feedstock production:
The first step: is that 5: 1 ratio mixes in mixing pan with the hafnium oxide powder of 3 μ m and resol with weight ratio, solidifies under 100 ℃ temperature, pulverizes in powder-making machine then and makes the raw material powder 1 that granularity is 20 μ m.
Second step: is that 5: 2 ratio mixes in mixing pan with above-mentioned raw materials powder 1 and resol with weight ratio, solidifies under 100 ℃ temperature, and pulverizing in powder-making machine then and making granularity is 50 μ m raw material powder 2.
The 3rd step: is that 5: 3 ratio mixes in mixing pan with above-mentioned raw materials powder 2 and resol with weight ratio, solidifies under 80 ℃ temperature, and pulverizing in powder-making machine then and making granularity is 100 μ m raw material powder 3.
2, the hafnium carbide powder is synthetic:
With the pressure lower lock block of above-mentioned raw materials powder 3 at 3Mpa, inertia or reducing atmosphere atmosphere are fired and were made the hafnium carbide block in 8 hours under 2000 ℃ ℃ temperature then.
3, carbonization treatment
With the oxidizing atmosphere insulation decarburization in 12 hours under 550 ℃ temperature of above-mentioned hafnium carbide block, the cooling back is pulverized and is made the hafnium carbide powder.
It is 99.99% pure that raw materials used purity is.
Claims (1)
1. the preparation method of a hafnium carbide powder is characterized in that: the high-activity carbon that adopts the resol carbonization to form is a carbon source reduction hafnium oxide powder preparing hafnium carbide powder, may further comprise the steps:
1. feedstock production:
The first step: is that 5: 0.5～1 ratio mixes in mixing pan with the hafnium oxide powder of 0.1～3 μ m and resol with weight ratio, under 80～100 ℃ temperature, solidify, in powder-making machine, pulverize then and make the raw material powder 1 that median size is 10～20 μ m.
Second step: is that 5: 1～2 ratio mixes in mixing pan with above-mentioned raw materials powder 1 and resol with weight ratio, solidifies under 50～100 ℃ temperature, and pulverizing in powder-making machine then and making median size is 20～50 μ m raw material powder 2.
The 3rd step: is that 5: 2～3 ratio mixes in mixing pan with above-mentioned raw materials powder 2 and resol with weight ratio, solidifies under 40～80 ℃ temperature, and pulverizing in powder-making machine then and making median size is 50～100 μ m raw material powder 3.
2. the hafnium carbide powder is synthetic:
With the pressure lower lock block of above-mentioned raw materials powder 3 at 0.5～3Mpa, inertia or reducing atmosphere atmosphere are fired and were made the hafnium carbide block in 6-8 hour under 1300 ℃-1800 ℃ temperature then.
3. carbonization treatment
With the oxidizing atmosphere insulation decarburization in 6～12 hours under 350～550 ℃ temperature of above-mentioned hafnium carbide block, the cooling back is pulverized and is made the hafnium carbide powder.