CN102206066B - Tile glue - Google Patents
Tile glue Download PDFInfo
- Publication number
- CN102206066B CN102206066B CN 201110087334 CN201110087334A CN102206066B CN 102206066 B CN102206066 B CN 102206066B CN 201110087334 CN201110087334 CN 201110087334 CN 201110087334 A CN201110087334 A CN 201110087334A CN 102206066 B CN102206066 B CN 102206066B
- Authority
- CN
- China
- Prior art keywords
- tile
- glue
- quartz sand
- portland cement
- ordinary portland
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a tile glue, comprising ordinary portland cement, quartz sand, re-dispersible emulsion powder, heavy calcium carbonate, water reducer, cellulose ether and efflorescence inhibitor. By utilizing the technical scheme, since the efflorescence inhibitor is added, there is no yellowing and efforescence phenomenon after construction; and the portion of the re-dispersible emulsion powder is increased, so that the technical effect of pasting glass onto glass directly can be achieved.
Description
Technical field
The present invention relates to a kind of glue for tile, belong to the construction material field.
Background technology
At present, glue for tile has obtained using comparatively widely and promoting at construction field.
A kind of disclosed dry powder color ceramic tile adhesive comprises following component (weight part): white cement 35%~65%; Quartz sand 20%~30%; Filler 10%~35%; Latex powder 2.0%~3.0%; Water-holding agent 0.1%~0.4%; Lignocellulose 0.5%~1.0%; High-alumina cement 0.5%~0.8%; Plaster stone 0.3%~0.5%; Water reducer 0.2%~1.0%; Tinting material 0~0.6%.
Taked the later glue for tile of such scheme, cheap, degree of safety is high, and, can the accumulation of salt in the surface soil tell white, directly operation on the basal plane of humidity.
But its cementability is not strong, thickness is too thick, the construction complicated.
And, can't be on old ceramic tile tiling, and ceramic tile must soak, basic unit also must be moistening.
Summary of the invention
The present invention is directed to the shortcoming of currently available products, a kind of novel glue for tile is provided, described glue for tile has that bonding strength is high, the accumulation of salt in the surface soil is not told white, old ceramic tile need not to beat, approximately 3-10mm gets final product direct bonding ceramic tile, mosaic and little shape lithotome need not to soak, basic unit need not be moistening, thin layer construction is directly bonding, and the space is saved in weight reduction, reduce artificial, can reach 2-5mm thick on glass the direct effect of sticking glass, this product is water-fast, freeze-thawing resistant, ageing-resistant, is a kind of ideal adhesive material.
It is as described below that the present invention solves the problems of the technologies described above the technical scheme that adopts:
A kind of glue for tile comprises following component: ordinary Portland cement, quartz sand, redispersable latex powder, water-ground limestone, water reducer and ether of cellulose, and, also be added with accumulation of salt in the surface soil inhibitor.
Further, described each composition (weight part):
Wherein, described ordinary Portland cement is white or grey, and described quartz sand is 50-80 purpose quartz sand.
The present invention owing to having increased accumulation of salt in the surface soil inhibitor, therefore, after construction, can not occur turning to be yellow and tell white phenomenon with the accumulation of salt in the surface soil after having taked technique scheme; And, due to the ratio that has strengthened the redispersion latex powder, therefore, can reach the directly technique effect of direct sticking glass on glass.(thickness only needs approximately 2-5mm)
Embodiment
Below in conjunction with specific embodiment, the present invention is carried out a detailed description.
Such as described in the present invention, the present invention is directed to glue for tile and improve, namely outside the composition of ordinary Portland cement, quartz sand, redispersable latex powder, water-ground limestone, water reducer and ether of cellulose, also be added with a certain amount of accumulation of salt in the surface soil inhibitor.
Owing to having increased accumulation of salt in the surface soil inhibitor, therefore, after construction, can not occur turning to be yellow and tell white phenomenon with the accumulation of salt in the surface soil, have the rear former coloured technique effect of appearance preservation of construction.Protection product (being the marble ceramic tile)
In addition, among general common glue for tile, the ratio of latex powder is all 2.0%~3.0%, therefore, its when in use, the ceramic tile water that also will wet, basic unit is also moistening, could construct.
And glue for tile of the present invention, we strengthen the ratio of redispersable latex powder, and therefore, in construction, ceramic tile does not need to soak, and it is moistening that basic unit does not need, and can directly paste; And, when in use, can directly take technique and the method for the sticking glass of glass.Reduce manually, the space is saved in weight reduction, saves cost.
Preferably, described each composition (weight part):
Wherein, described ordinary Portland cement is white or grey, and described quartz sand is 50-80 purpose quartz sand.
The below carries out simple a description to the construction process of above-mentioned glue for tile:
1, remove dust, hollowing, the foreign matter of substrate surface, keep surfacing, cleaning.
2, with adhesive material with the profile of tooth scraper plate be put on equably will sticking brick basic unit.
3, provide the complete graceful cutter glue for tile of breach to comb and scrape adhesive material, (being the profile of tooth scraper plate)
4, ceramic tile is pasted gently from the bottom up and is got final product.(going back adjustable position in 1 hour)
5, the adhesive material that stays with the wet clean ceramic tile surface of cloth sassafras.
6, glue for tile was pasted after 2-3 days, can carry out filleting.
The below compares description for the performance of this glue for tile:
The contrast of glue for tile performance data:
Performance | Usual production | Patented product |
Shearing resistance | MPa≥1.00 | MPa≥2.2 |
Water tolerance | MPa≥0.7 | MPa≥2.0 |
Freeze-thaw resistance | MPa≥0.7 | MPa≥1.25 |
Temperature tolerance | MPa≥0.7 | MPa≥1.7 |
Linear shrinkage | <0.5 | <0.1 |
Can find from form, the effect of this patent product is very good.Can be in the building field large-scale popularization.
It should be noted that above-mentioned specific embodiment is exemplary, under above-mentioned instruction of the present invention, those skilled in the art can carry out various improvement and distortion on the basis of above-described embodiment, and these improvement or distortion drop in protection scope of the present invention.
It will be understood by those skilled in the art that top specific descriptions just in order to explain purpose of the present invention, is not for restriction the present invention.Protection scope of the present invention is limited by claim and equivalent thereof.
Claims (1)
1. glue for tile comprises following component:
Ordinary Portland cement, quartz sand, redispersable latex powder, water-ground limestone, water reducer and ether of cellulose is characterized in that, also are added with accumulation of salt in the surface soil inhibitor; Described each composition (weight part):
Wherein, described ordinary Portland cement is white or grey, and described quartz sand is 50-80 purpose quartz sand.