CN102199030A - Jade ceramic - Google Patents
Jade ceramic Download PDFInfo
- Publication number
- CN102199030A CN102199030A CN2011100470836A CN201110047083A CN102199030A CN 102199030 A CN102199030 A CN 102199030A CN 2011100470836 A CN2011100470836 A CN 2011100470836A CN 201110047083 A CN201110047083 A CN 201110047083A CN 102199030 A CN102199030 A CN 102199030A
- Authority
- CN
- China
- Prior art keywords
- pottery
- mud
- beautiful
- jade
- blank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a jade ceramic the blank of which is composed of the following components in percentage by weight: 80-85% of purplish red mud and 15-20% of round hill mud. The jade ceramic has the advantages of high plasticity, high strength of green compact, low drying shrinkage rate, high process performance and no need for insecure processes such as wax dipping or polishing, and can be processed into various earthenware, preferably tea sets.
Description
Technical field
The present invention relates to the ceramic technology field, relate in particular to a kind of beautiful making pottery.
Background technology
In the prior art, the blank of preparation mud emerging pottery generally is to adopt the purplish red mud and the white clay that originate in Qiezhou, Guangxi to be mixed and made into, and raw ore is red-purple and white, is clay matter structure, bulk, burn till present bronze-colored.The drying shrinkage of the pottery artwork that the blank of the emerging pottery of Qiezhou mud is produced is big, and the intensity of green compact is not high; And need waxdip, technique for grinding moulding, potential safety hazard is arranged for the consumption pottery.
Summary of the invention
Technical problem to be solved by this invention provides the jade pottery that a kind of blank of being made up of purplish red mud and group's mountain mud is fired, and improves plasticity-and green strength, has cancelled waxdip, technique for grinding simultaneously, helps the security of consumption pottery.
For solving above technical problem, the invention provides the emerging pottery of a kind of new mud, the emerging pottery of this mud is called beautiful making pottery, and the component of its blank and content are: purplish red mud (80%～85%), group's mountain mud (15%～20%), all per-cents are weight percentage.
Preferably, the weight percent of purplish red mud is 85%, and the weight percent of group's mountain mud is 15%.
Preferably, this jade pottery is fired through kiln by above-mentioned blank and is formed, and wherein, the furnace temperature of firing is 1160 ℃～1170 ℃.
Beautiful blank of making pottery of the present invention is made up of purplish red mud and group's mountain mud, and its plasticity-is good, and green strength is good, and drying shrinkage is little, and the favorable manufacturability energy is arranged, and need not waxdip, the non-safe technology of polishing, and can process all kinds of potteries, and it is better particularly to be processed as tea set.
Other features and advantages of the present invention will be set forth in the following description, and, partly from specification sheets, become apparent, perhaps understand by implementing the present invention.Purpose of the present invention and other advantages can realize and obtain by specifically noted structure in the specification sheets of being write, claims.
Embodiment
Embodiment 1
In the present embodiment, the blind proportion by subtraction of weight that this jade is made pottery is: the weight percent of purplish red mud is 85%, and the weight percent of group's mountain mud is 15%.
After pressing mentioned component and content batching, airing, fragmentation, sieve, after the pugging, moulding, fire through kiln and to form.For example, after described blank airing, the fragmentation, system sieve 60 orders add water 17%, deposit then 3 days; At the ripe mud of vacuum deairing machine pugging, manual assembly is fired finished product in kiln, and kiln temperature is 1160 ℃.
Embodiment 2
In the present embodiment, the weight percent that this jade is made pottery is: the weight percent of purplish red mud is 80%, and the weight percent of group's mountain mud is 20%.
After pressing mentioned component and content batching, add water for ball milling, sieve, after the slip casting, moulding, fire through kiln and to form.For example, after the described blank fragmentation, 55 jin of materials, water are gone into the wet-type ball mill ball milling after 32 hours for 45 jin, cross 250 mesh sieve pulpings, and injection forming is fired finished product in kiln, and kiln temperature is 1170 ℃.
Embodiment 3
In the present embodiment, the weight percent that this jade is made pottery is: the weight percent of purple pottery mud is 82%, and the weight percent of group's mountain mud is 18%.
After pressing mentioned component and content batching, natural drying, fragmentation, sieve, after the pugging, moulding, fire through kiln and to form.For example, after the described blank fragmentation, cross 40～60 mesh sieves, add water 20%, deposited then 5 days, vacuum pugging is made ripe mud, adopts roll forming or coldmoulding, fires finished product in kiln, and kiln temperature is 1165 ℃.
The jade pottery outward appearance that produces in the embodiment of the invention is chocolate, implicit cream-coloured Jinsha.It is fine and smooth as beautiful, gentle soft to stroke feel, therefore, is called beautiful making pottery according to the pottery mud of the embodiment of the invention.
After testing, the jade of the embodiment of the invention is made pottery, and in its chemical ingredients, it is overall 91%～94.6 that O (oxygen), Al (aluminium) and Si (silicon) account for, and also comprises other trace elements in addition, for example, potassium, titanium, iron, magnesium and calcium, total amount probably accounts for overall 9%.
In embodiments of the present invention, can adopt distinctive mountain mud of the distinctive purplish red mud in Qiezhou and Yixing, form by certain formula rate mixed sintering.Thereby make that beautiful plasticity-of making pottery is good, green strength is good, and drying shrinkage is little, and the favorable manufacturability energy is arranged, and can process all kinds of potteries, is particularly suitable for making tea set.
The jade pottery material uniqueness of the embodiment of the invention, feel such as jade, ventilative water-tight, nontoxicity, acid and alkali-resistance, emergency heat and cooling property resistance is cold, the perfume that overflows of making tea, anti-corrosive fresh-keeping is rich in the trace element to the human body beneficial.
The above is the preferred embodiments of the present invention only, is not limited to the present invention, and for a person skilled in the art, the present invention can have various changes and variation.Within the spirit and principles in the present invention all, any modification of being done, be equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. beautiful making pottery is characterized in that, the component and the content of the blank that described jade is made pottery are: purplish red mud (80%～85%), group's mountain mud (20%～15%), all per-cents are weight percentage.
2. beautiful making pottery according to claim 1 is characterized in that the weight percent of described purplish red mud is 85%, and the weight percent of described mountain mud is 15%.
3. beautiful making pottery according to claim 1 and 2 is characterized in that, described beautiful pottery is fired through kiln by described blank and formed, and wherein, the furnace temperature of firing is 1160 ℃～1170 ℃.