CN102190506B - 双组分界面剂 - Google Patents

双组分界面剂 Download PDF

Info

Publication number
CN102190506B
CN102190506B CN 201010118751 CN201010118751A CN102190506B CN 102190506 B CN102190506 B CN 102190506B CN 201010118751 CN201010118751 CN 201010118751 CN 201010118751 A CN201010118751 A CN 201010118751A CN 102190506 B CN102190506 B CN 102190506B
Authority
CN
China
Prior art keywords
component
agent
group
parts
dual
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 201010118751
Other languages
English (en)
Other versions
CN102190506A (zh
Inventor
窦钦锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI NATURE BUILDING MATERIAL CO Ltd
Original Assignee
SHANGHAI NATURE BUILDING MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI NATURE BUILDING MATERIAL CO Ltd filed Critical SHANGHAI NATURE BUILDING MATERIAL CO Ltd
Priority to CN 201010118751 priority Critical patent/CN102190506B/zh
Publication of CN102190506A publication Critical patent/CN102190506A/zh
Application granted granted Critical
Publication of CN102190506B publication Critical patent/CN102190506B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种双组分界面剂，属混凝土界面处理领域。以重量份数计，所述双组分界面剂包括以下组分：1)A组分：改性环氧树脂100份，稀释剂20-50份，附着力促进剂3-8份，气相二氧化硅2-10份；2)B组份：固化剂10-20份，助剂1-5份；所述A、B组分的质量比为1∶2.5。本发明的双组分界面剂具有良好的粘结性和防水性，能够浸封底层孔隙和加大附着力，广泛使用在自流平、瓷砖胶粘剂、腻子和修补砂浆施工前的底涂，在混凝土、水泥砂浆、石膏板及水泥纤维板上等都可使用。

Description

双组分界面剂
技术领域
本发明属混凝土界面处理领域，具体涉及一种用于水泥基自流平施工中的双组份界面剂。
背景技术
在水泥基自流平的施工中，界面剂的刷涂是非常重要的一个环节。刷涂界面剂的目的主要有以下四点：一是对基层封闭，避免基层过多过快吸水，防止水泥基自流平砂浆过早丧失水分；二是增强基层与水泥基自流平砂浆层的粘结强度；三是防止气泡的产生；四是改善水泥自流平砂浆的流动性。但是，在一些起砂的基层上，普通的界面剂难以浸封基层。造成自流平与基层起壳，无法进行自流平的施工。特别是在一些防水性较差的地面，水气的上升容易导致粘结力的下降。
发明内容
本发明针对现有工业地坪的应用中所遇到诸多复杂问题，例如在一些起砂的地坪上做地坪面层，地面的防水性较差或者地面有很高的湿气来源等，提供一种双组分界面剂，它具有增强界面粘结性和防水性等功能，以解决上述问题。
本发明提供的双组分界面剂，以重量份数计，包括以下组分：
1)A组分：
改性环氧树脂                100份
稀释剂                      20-50份
附着力促进剂                3-8份
气相二氧化硅(＜100nm)       2-10份；
2)B组份：
固化剂                      10-20份
助剂                        1-5份。
所述改性环氧树脂为含有叔丁基苯酚或壬基苯酚嵌段的改性环氧树脂。
所述稀释剂为环氧丙烷丙烯醚、丁基缩水甘油醚、甘油环氧树脂、环氧氯丙烷中的一种或多种。
所述附着力促进剂为含有酸性基团的环氧丙烯酸树脂。
所述固化剂为聚醚胺类固化剂。
所述助剂包括消泡剂、流平剂、润湿剂。所述消泡剂为聚醚类消泡剂(例如BYK-606N)，所述流平剂、润湿剂均为以多元共聚物为基础的改性硅聚合物(例如流平剂K-729，润湿剂H-140)。所述消泡剂、流平剂、润湿剂的质量比为1-3∶1-3∶1。
上述配方，A组份的制备：先加入改性环氧树脂、稀释剂、附着力促进剂，待充分分散后，再加入气相二氧化硅。
B组份将固化剂与助剂充分混合。
将上述分别制备好的A、B组分按照质量比1∶2.5混合，即得到本发明的双组份界面剂，然后使用。
本发明的双组分界面剂具有良好的粘结性和防水性，能够浸封底层孔隙和加大附着力，广泛使用在自流平、瓷砖胶粘剂、腻子和修补砂浆施工前的底涂，在混凝土、水泥砂浆、石膏板及水泥纤维板上等都可使用。
具体实施方式
下面结合具体实例对本发明作进一步的描述，应理解，下面的实施例仅用来使本专业技术人员更全面的理解本发明，但不以任何方式限制本发明。
其中，环氧丙烷丙烯醚为山东海科新源化工有限公司生产，工业纯；丁基缩水甘油醚为山东海科新源化工有限公司生产，工业纯；甘油环氧树脂为山东海科新源化工有限公司生产，工业纯；聚醚类消泡剂为BYK公司BYK-606N消泡剂，分析纯；流平剂为广东标美氟硅精细化工的K-729，分析纯；润湿剂为深圳海川化工的H-140润湿剂，分析纯；其余产品均为本行业市售分析纯。
实施例1
配方(单位：Kg)：
1)A组份：
含有叔丁基苯酚的改性环氧树脂      100
环氧丙烷丙烯醚                    50
环氧丙烯酸树脂                 5
气相二氧化硅(＜100nm)          5
2)B组份：
聚醚胺类固化剂                 20
聚醚类消泡剂BYK-606N           1
流平剂K-729                    3
润湿剂H-140                    1
按照上述配方，先加入改性环氧树脂、稀释剂、附着力促进剂，待充分分散后，再加入气相二氧化硅，即得A组分。将固化剂与助剂充分混合即得B组分。
A、B组份分别高速分散后，按照1∶2.5质量比混合，即得本发明的双组份界面剂。经性能检测，本发明的双组分界面剂具有良好的粘结性和防水性，能够浸封底层孔隙和加大附着力。
实施例2
配方(单位：Kg)：
1)A组份：
含有叔丁基苯酚的改性环氧树脂       100
丁基缩水甘油醚                     20
环氧丙烯酸树脂                     8
气相二氧化硅(＜100nm)
2)B组份：
聚醚胺类固化剂                     10
聚醚类消泡剂BYK-606N               2
流平剂K-729                        2
润湿剂H-140                        1
按照上述配方，先加入改性环氧树脂、稀释剂、附着力促进剂，待充分分散后，再加入气相二氧化硅，即得A组分。将固化剂与助剂充分混合即得B组分。
A、B组份分别高速分散后，按照1∶2.5质量比混合，即得到本发明的双组份的界面剂。经性能检测，本发明的双组分界面剂具有良好的粘结性和防水性，能够浸封底层孔隙和加大附着力。
实施例3
配方(单位：Kg)：
1)A组份：
含有壬基苯酚嵌段的改性环氧树脂     100
甘油环氧树脂                       25
环氧丙烯酸树脂                     8
气相二氧化硅(＜100nm)              10
2)B组份为：
聚醚胺类固化剂                     20
聚醚类消泡剂BYK-606N               3
流平剂K-729                        1
润湿剂H-140                        1
按照上述配方，先加入改性环氧树脂、稀释剂、附着力促进剂，待充分分散后，再加入气相二氧化硅，即得A组分。将固化剂与助剂充分混合即得B组分。
A、B组份分别高速分散后，按照1∶2.5质量比混合，即得到本发明的双组份的界面剂。经性能检测，本发明的双组分界面剂具有良好的粘结性和防水性，能够浸封底层孔隙和加大附着力。

Claims (1)

1.一种双组分界面剂，其特征在于，以重量份数计，包括以下组分：
1)A组分：
Figure FSB00000922898500011
2)B组分：
固化剂                       10-20份
助剂                         1-5份；
所述A、B组分的质量比为1∶2.5；
所述改性环氧树脂为含有叔丁基苯酚或壬基苯酚嵌段的改性环氧树脂；
所述稀释剂为环氧丙烷丙烯醚、丁基缩水甘油醚、甘油环氧树脂、环氧氯丙烷中的一种或多种；
所述附着力促进剂为含有酸性基团的环氧丙烯酸树脂；
所述固化剂为聚醚胺类固化剂；
所述助剂包括消泡剂、流平剂和润湿剂；
所述消泡剂为聚醚类消泡剂，所述流平剂、润湿剂均为以多元共聚物为基础的改性硅聚合物；
所述消泡剂、流平剂、润湿剂的质量比为1-3∶1-3∶1。 
CN 201010118751 2010-03-05 2010-03-05 双组分界面剂 Active CN102190506B (zh)