CN102176333A - 一种增加放射性废树脂水泥固化体辐照稳定性的方法 - Google Patents

一种增加放射性废树脂水泥固化体辐照稳定性的方法 Download PDF

Info

Publication number
CN102176333A
CN102176333A CN2011100484720A CN201110048472A CN102176333A CN 102176333 A CN102176333 A CN 102176333A CN 2011100484720 A CN2011100484720 A CN 2011100484720A CN 201110048472 A CN201110048472 A CN 201110048472A CN 102176333 A CN102176333 A CN 102176333A
Authority
CN
China
Prior art keywords
cement
resin
mass ratio
hair
solidified body
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011100484720A
Other languages
English (en)
Inventor
李俊峰
王建龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tsinghua University
Original Assignee
Tsinghua University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tsinghua University filed Critical Tsinghua University
Priority to CN2011100484720A priority Critical patent/CN102176333A/zh
Publication of CN102176333A publication Critical patent/CN102176333A/zh
Pending legal-status Critical Current

Abstract

本发明公开了属于放射性废物处理技术领域的一种增加放射性废树脂水泥固化体辐照稳定性的方法。该方法如下：通过在树脂水泥固化配方中添加头发来增加固化体的辐照稳定性。头发的添加量优选如下比例：头发与水泥的质量比为(0.005～0.01)∶1。所添加的头发长度可在1.5～2cm之间。优选的树脂水泥固化配方如下：沸石粉、脱水的放射性废树脂、水和水泥的质量比为(0.05～0.1)∶0.45∶0.3∶1。本发明通过采用在树脂水泥固化配方中添加头发的方法，可以防止树脂辐照分解导致的固化体开裂，从而提高固化体的辐照稳定性。

Description

一种增加放射性废树脂水泥固化体辐照稳定性的方法
技术领域
本发明属于放射性废物处理技术领域，特别涉及一种增加放射性废树脂水泥固化体辐照稳定性的方法。
背景技术
在核电站和核设施的运行和退役过程中会产生大量的放射性废树脂，放射性废树脂的高效处理是长期困扰我国核事业发展的难题之一。水泥固化是国内放射性废树脂处置普遍采用的方法。当放射性废树脂经过水泥固化后需要储存300-500年使其与环境隔离。长时间的辐照会导致水泥固化体中的树脂分解，从而影响固化体的稳定性。
本发明通过在树脂水泥固化体中投加耐辐照的头发作为纤维物质从而避免因为树脂辐照分解导致的固化体结构破坏。
发明内容
本发明的目的在于提供一种增加放射性废树脂水泥固化体辐照稳定性的方法，其特征在于：通过在树脂水泥固化配方中添加头发来增加固化体的辐照稳定性。
本发明还给出了头发的添加量，头发的添加量优选如下比例：头发与水泥的质量比为(0.005～0.01)∶1。
所添加的头发长度可在1.5～2cm之间。
本发明还给出了优选的树脂水泥固化配方，在该配方中添加头发能够较好的增加固化体的辐照稳定性。优选的树脂水泥固化配方如下：沸石粉、脱水的放射性废树脂、水和水泥的质量比为(0.05～0.1)∶0.45∶0.3∶1。
在树脂水泥固化过程中将水泥、沸石粉、头发、脱水的放射性废树脂和水按如下质量比1∶(0.05～0.10)∶(0.005～0.01)∶0.45∶0.3混合均匀，即可达到增加固化体的辐照稳定性的目标。
本发明所使用的水泥为可以为普通硅酸盐水泥或者矿渣水泥，优选标号为42.5Mpa的普通硅酸盐水泥。
本发明的有益效果：本发明通过采用在树脂水泥固化配方中添加头发的方法，可以防止树脂辐照分解导致的固化体开裂，从而提高固化体的辐照稳定性。
具体实施方式
下面的实施例可以使本专业技术人员更全面的理解本发明，但不以任何方式限制本发明。
以下实施例中所说的脱水树脂是指脱水的放射性废树脂。所添加的头发长度在1.5～2cm之间。
实施例1
将42.5MPa普通硅酸盐水泥、沸石粉、头发、脱水树脂和水按如下质量比1∶0.05∶0.005∶0.45∶0.3混合均匀，固化体养护28天后，经过1×106Gy的辐射照射，固化体抗压强度损失小于20％，固化体不出现裂纹。
实施例2
将42.5MPa普通硅酸盐水泥、沸石粉、头发、脱水树脂和水按如下质量比1∶0.10∶0.005∶0.45∶0.3混合均匀，固化体养护28天后，经过1×106Gy的辐射照射，固化体抗压强度损失小于20％，固化体不出现裂纹。
实施例3
将42.5MPa普通硅酸盐水泥、沸石粉、头发、脱水树脂和水按如下质量比1∶0.05∶0.010∶0.45∶0.3混合均匀，固化体养护28天后，经过1×106Gy的辐射照射，固化体抗压强度损失小于20％，固化体不出现裂纹。
实施例4
将42.5MPa普通硅酸盐水泥、沸石粉、头发、脱水树脂和水按如下质量比1∶0.10∶0.010∶0.45∶0.3混合均匀，固化体养护28天后，经过1×106Gy的辐射照射，固化体抗压强度损失小于20％，固化体不出现裂纹。
实施例5
将42.5MPa普通硅酸盐水泥、沸石粉、头发、脱水树脂和水按如下质量比1∶0.07∶0.007∶0.45∶0.3混合均匀，固化体养护28天后，经过1×106Gy的辐射照射，固化体抗压强度损失小于20％，固化体不出现裂纹。
实施例6
将42.5MPa普通硅酸盐水泥、沸石粉、头发、脱水树脂和水按如下质量比1∶0.08∶0.006∶0.45∶0.3混合均匀，固化体养护28天后，经过1×106Gy的辐射照射，固化体抗压强度损失小于20％，固化体不出现裂纹。
实施例7
将42.5MPa普通硅酸盐水泥、沸石粉、头发、脱水树脂和水按如下质量比1∶0.06∶0.009∶0.45∶0.3混合均匀，固化体养护28天后，经过1×106Gy的辐射照射，固化体抗压强度损失小于20％，固化体不出现裂纹。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，可轻易想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求的保护范围为准。

Claims (7)

1.一种增加放射性废树脂水泥固化体辐照稳定性的方法，其特征在于：通过在树脂水泥固化配方中添加头发来增加固化体的辐照稳定性。
2.根据权利要求1所述的方法，其特征在于：头发的添加量如下：头发与水泥的质量比为(0.005～0.01)∶1。
3.根据权利要求1所述的方法，其特征在于：所添加的头发长度在1.5～2cm之间。
4.根据权利要求1所述的方法，其特征在于：所述树脂水泥固化配方如下：沸石粉、脱水的放射性废树脂、水和水泥的质量比为(0.05～0.10)∶0.45∶0.3∶1。
5.根据权利要求1所述的方法，其特征在于：在树脂水泥固化过程中将水泥、沸石粉、头发、脱水的放射性废树脂和水按如下质量比1∶(0.05～0.10)∶(0.005～0.01)∶0.45∶0.3混合均匀。
6.根据权利要求1所述的方法，其特征在于：所使用的水泥为普通硅酸盐水泥或者矿渣水泥。
7.根据权利要求6所述的方法，其特征在于：所述水泥为标号为42.5Mpa的普通硅酸盐水泥。
CN2011100484720A 2011-02-28 2011-02-28 一种增加放射性废树脂水泥固化体辐照稳定性的方法 Pending CN102176333A (zh)