CN102174307A - 高强度pvc真空吸塑胶 - Google Patents
高强度pvc真空吸塑胶 Download PDFInfo
- Publication number
- CN102174307A CN102174307A CN2011100084130A CN201110008413A CN102174307A CN 102174307 A CN102174307 A CN 102174307A CN 2011100084130 A CN2011100084130 A CN 2011100084130A CN 201110008413 A CN201110008413 A CN 201110008413A CN 102174307 A CN102174307 A CN 102174307A
- Authority
- CN
- China
- Prior art keywords
- percent
- acetone
- degree
- temperature
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高强度PVC真空吸塑胶,按质量百分比计量,其成分包括:聚己二酸,1,4-丁二醇酯17-25%,磺酸盐改性聚多元醇0.002-0.006%,丙酮45-50%,六亚甲基二异氰酸酯0.01-0.04%,异佛尔酮二异氰酸酯0.01-0.03%,扩链剂0.01-0.03%,去离子水30%-40%,粘结改良剂5%-10%;其制备方法为:将聚己二酸,1,4-丁二酯和磺酸盐改性聚多元醇按比例加入到双层玻璃反应釜里加热至140度左右溶解,降温至70-90度加入六亚甲基二异氰酸酯和异佛尔酮二异氰酸酯,在此温度里反应2小时,降温到55度加入去离子水、扩链剂反应1小时,再加入丙酮稀释溶解,逐步升温到60-70度抽真空约3小时回收丙酮,最后加入粘接改良剂搅拌0.5小时后过滤出料,即得WPU胶成品。
Description
技术领域
本发明涉及一种胶水,具体为一种高强度PVC真空吸塑胶,特别地,本发明还提供了该胶水的制备工艺。
背景技术
目前,国内外木工行业用WPU工业用真空吸塑胶,随着装饰装修行业的快速发展和成熟,近年来人们对吸塑胶应用上的要求也不断的细化,不论是价格还是操作都要求更便宜更精细。
现在国内市场上的WPU真空吸塑胶有很多生产企业都是用WPU和EVA乳液复配,按25-40%添加EVA的比例和一些助剂来降低成本,例如大多数客户都购买的拜耳公司的U54这一牌号的WPU,复配出的成品在操作过程中会出现胶水难喷涂、粘度高、出胶量小生产效率上不去,冬季时需将吸塑胶加温来将低产品粘度,加温后的产品会形成胶膜、需要过滤,吸塑薄的PVC(例如10-15丝米)材质会有麻点,影响成品板材的美观,耐热性差、机械性能低,需要通过加MDI来加强粘结强度,加了MDI后需要经过充分搅拌才能使用、工序繁琐。
且现国内市场上还有一些企业做的产品味道大,操作环境空气质量差,市场售价基本上在30-35元/KG左右。
发明内容
针对现有技术中存在的问题及不足,本发明选用丙酮法通过助剂改性,然后用亲水单体扩链,制备出一种粘结强度高,耐热性和耐水性优良、粘度低、易喷涂且成本低(售价25元/KG)的高强度PVC真空吸塑胶,主要应用与PVC和各种板材的吸塑。
一种高强度PVC真空吸塑胶,按质量百分比计量,其成分包括:聚己二酸,1,4-丁二醇酯17-25%,磺酸盐改性聚多元醇0.002-0.006%,丙酮45-50%,六亚甲基二异氰酸酯0.01-0.04%,异佛尔酮二异氰酸酯0.01-0.03%,扩链剂0.01-0.03%,去离子水30%-40%,粘结改良剂5%-10%。
一种高强度PVC真空吸塑胶,其制备方法为:将聚己二酸,1,4-丁二酯和磺酸盐改性聚多元醇按比例加入到双层玻璃反应釜里加热至140度左右溶解,降温至70-90度加入六亚甲基二异氰酸酯和异佛尔酮二异氰酸酯,在此温度里反应2小时。降温到55度加入去离子水、扩链剂反应1小时,再加入丙酮稀释溶解,逐步升温到60-70度抽真空约3小时回收丙酮,最后加入粘接改良剂搅拌0.5小时后过滤出料,即得WPU胶成品。
本发明通过LY/T1601-2002方法测试,产品质量稳定,粘结强度高,耐热性和耐水性优良、粘度低、易喷涂,且成本低。
附图说明
图1为本发明的配方比图。
具体实施方式
下面结合附图及实施例对本发明进一步进行说明
如图1所示,一种高强度PVC真空吸塑胶,按质量百分比计量,其成分包括:聚己二酸,1,4-丁二醇酯17-25%,磺酸盐改性聚多元醇0.002-0.006%,丙酮45-50%,六亚甲基二异氰酸酯0.01-0.04%,异佛尔酮二异氰酸酯0.01-0.03%,扩链剂0.01-0.03%,去离子水30%-40%,粘结改良剂5%-10%。
实施例1:一种高强度PVC真空吸塑胶的制备
将20%的聚己二酸,1,4-丁二酯和磺酸盐改性聚多元醇按比例加入到双层玻璃反应釜里加热至140度左右溶解,降温至70-90度加入六亚甲基二异氰酸酯和异佛尔酮二异氰酸酯,在此温度里反应2小时,降温到55度加入去离子水、扩链剂反应1小时,再加入丙酮稀释溶解,逐步升温到60-70度抽真空约3小时回收丙酮,最后加入粘接改良剂搅拌0.5小时后过滤出料,即得WPU胶成品。
对上述制备的高强度PVC真空吸塑胶进行PVC门板测试工艺如下:
1.材质;雕花密度板,含水率8-12%,长2米,宽1.2米,厚度0.02米,砂光后表面保持无尘。
2.工艺;将WPU胶倒进R-1003型1.5毫米口径的喷枪储罐里,均匀喷涂在砂光后的材质上,每平方米的上胶量约60-100克,晾至胶体表干后,放进真空吸塑机,敷上12丝米的PVC膜,180度抽真空吸塑120秒取出。
3、LY/T1601-2002方法测试;目测板面上平滑无麻点现象,30分钟后测常态木破率,用手剥离PVC,PVC粘合面上都均匀密布着密度板木屑;养生3天,锯1块30厘米正方型的板材试件放置在60±2℃的恒温干燥箱中连续干燥2小时,无任一胶层反弹开裂,取出晾至30分钟,用手剥离PVC,PVC粘合面上均匀密布着密度板木屑。
本发明产品质量稳定,粘结强度高,耐热性和耐水性优良、粘度低、易喷涂,且成本低。
Claims (2)
1.一种高强度PVC真空吸塑胶,其特征在于,按质量百分比计量,其成分包括:聚己二酸,1,4-丁二醇酯17-25%,磺酸盐改性聚多元醇0.002-0.006%,丙酮45-50%,六亚甲基二异氰酸酯0.01-0.04%,异佛尔酮二异氰酸酯0.01-0.03%,扩链剂0.01-0.03%,去离子水30%-40%,粘结改良剂5%-10%。
2.如权利要求1所述高强度PVC真空吸塑胶的制备方法,其特征在于,具体制备方法为:将聚己二酸,1,4-丁二酯和磺酸盐改性聚多元醇按比例加入到双层玻璃反应釜里加热至140度左右溶解,降温至70-90度加入六亚甲基二异氰酸酯和异佛尔酮二异氰酸酯,在此温度里反应2小时,降温到55度加入去离子水、扩链剂反应1小时,再加入丙酮稀释溶解,逐步升温到60-70度抽真空约3小时回收丙酮,最后加入粘接改良剂搅拌0.5小时后过滤出料,即得WPU胶成品。