CN102167927B - Ink composition with high-weather-resistance black dye for ink-jet printing - Google Patents
Ink composition with high-weather-resistance black dye for ink-jet printing Download PDFInfo
- Publication number
- CN102167927B CN102167927B CN 201110103188 CN201110103188A CN102167927B CN 102167927 B CN102167927 B CN 102167927B CN 201110103188 CN201110103188 CN 201110103188 CN 201110103188 A CN201110103188 A CN 201110103188A CN 102167927 B CN102167927 B CN 102167927B
- Authority
- CN
- China
- Prior art keywords
- ink
- black
- degree
- mill base
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses an ink composition with a high-weather-resistance black dye for ink-jet printing. The composition is prepared by mixing following components in percentage by weight: 6-12 percent of polyhydroxy alcohol, 13-30 percent of solvents, 0.1-3 percent of surfactants, 0-0.5 percent of pH regulators, 0.1-0.3 percent of bactericides, 20-40 percent of mordant black dye paste and the balance of deionized water. The invention also provides a method for purifying the mordant black dye paste, which comprises the following steps of: mixing mordant black dye raw powder and deionized water based on a weight ratio of 1:9, heating, filtering, and performing desalination treatment to obtain the mordant black dye paste. The ink composition with the high-weather-resistance black dye for ink-jet printing, disclosed by the invention, has extremely high light fastness and ozone resistance, the printing quality is good, the optical density is high, the quality guarantee period is long, and a nozzle is not blocked.
Description
[technical field]
The present invention relates to the water-soluble dye composition for ink that spray ink Printing is used, particularly relate to a kind of ink composition for ink-jet printing with high-weatherability black dyes.
[background technology]
The dye ink that is used for ink-jet printer is the ink of molecular level CL, is composite solution completely.Be easy to by absorbed after the dye ink air brushing, it is printed on the smooth slick paper, and excellent to the radiation performance of light, color restoration capability is stronger, therefore obtains extensively with using.But because there is the protection of one layer of polymeric on dye ink surface unlike paint ink; the look material of dye ink is that individual molecule independently exists; under gaseous corrosions such as the irradiation of UV-light and ozone; molecule decomposes easily and destroys; cause color to change; cause and fade, make the application cycle of outdoor use shorten.
[summary of the invention]
The present invention is intended to solve the sun-resistant and anti-ozone problem of aqueous dye ink, and provide a kind of by to the purifying of media black dyes improving the light fastness and the ozone resistance of aqueous black dye ink, and do not stop up the ink composition for ink-jet printing with high-weatherability black dyes of shower nozzle.
The present invention also aims to provide a kind of purification process of media black dye paste.
For achieving the above object, the invention provides a kind of ink composition for ink-jet printing with high-weatherability black dyes, this composition for ink is mixed by following component by weight percentage:
Optimum ratio with ink composition for ink-jet printing of high-weatherability black dyes of the present invention is:
Polyhydroxy-alcohol is selected from glycerine, glycol ether, ethylene glycol, 1, one or more in 2-hexylene glycol, polyoxyethylene glycol, polypropylene glycol, the propylene glycol;
Solvent is selected from one or more in nitrogenous hydrophilic organic solvent, pure ether solvent, the high volatilization hydrophilic solvent, and the weight percent content of solvent in composition for ink is:
Nitrogenous hydrophilic organic solvent 5~12
Alcohol ether solvent 8~12
High volatilization hydrophilic solvent 0~6;
Nitrogenous hydrophilic organic solvent is selected from N-N-methyl-2-2-pyrrolidone N-, 1, one or more in 3-dimethyl-imidazolinone, 2-Pyrrolidone, the N,N-dimethylacetamide; The alcohol ether solvent is selected from a kind of in diethylene glycol monobutyl ether, triglycol monobutyl ether, the butyl glycol ether; High volatilization hydrophilic solvent is selected from a kind of in Virahol, the ethylene glycol ethyl ether;
Tensio-active agent is selected from worried 104, the worried TG that disappears of disappearing, it is worried 440 to disappear, it is worried 465 to disappear, a kind of in worried 485 disappears;
The pH regulator agent is selected from a kind of in diethanolamine, trolamine, the trihydroxy-aminomethane;
Sterilant is selected from a kind of in the shield GXL of government office in feudal China, bright Sheng D7, P 91 anticorrosion and bactericidal agents;
The Mordant Black dye paste is selected from a kind of in Mordant Black PV, medium black P 2 B, Mordant Black T or the acid black 172;
Surplus is a deionized water.
Contribution of the present invention is that it efficiently solves the sun-resistant and anti-ozone problem of dye ink.Owing to contain through the Mordant Black dye paste in the composition for ink of the present invention, this Mordant Black dye paste has good dyeing behavior, the dyeing circulation ratio is splendid, the tinctorial strength height, equalization is good, and high light fastness and ozone resistance are arranged, good with the image quality that composition for ink of the present invention is printed, the optical density (OD) height, long quality-guarantee period, and nonchoking nozzle.
[embodiment]
The following example is to further explanation of the present invention and explanation, and the present invention is not constituted any limitation.
Embodiment 1
1, the purifying of Mordant Black dye paste
Get 30 kilograms in the former powder of Mordant Black PV, join in the electrically heated stirring tank of the deionized water that fills 270 kilograms, heating while stirring, treat that temperature reaches 80 degree back restir 1 hour, after the whole dissolvings of the dyestuff powder that guarantees to add, carry out coarse filtration with 5 microns PP filter core again, carry out filtration treatment with ultra-filtration membrane and the nanofiltration membrane assembled filter that can remove sodium-chlor when temperature is lower than 60 again when spending, to remove the by product and the sodium-chlor of molecular weight at 30,000 above materials.Replenish deionized water in the process of purifying, guaranteeing the penetrating amount of film, and detect the specific conductivity of the liquid that leaches, specific conductivity stops to add deionized water when 20ms/cm is following, continues nanofiltration and the volume of mill base is controlled at about 200 liters, promptly reaches requirement; Stop purifying, barrelling.
Get 100 kilograms of Mordant Black PV mill bases behind the above-mentioned purifying, join volume and be in 200 liters the electrically heated stirring tank, heating while stirring, after treating that temperature reaches 80 degree, add 10.1 kilograms of potassium bichromate, heating while stirring, after being heated to 96 degree, add 0.345 mole Glacial acetic acid or tartrate, insulation reaction is after 3 hours under the condition of 96 to 99 degree, cool to 50 degree, with the sodium hydroxide adjust pH is about 7 to 9, and the concentration of carrying out desalination and controlling mill base with nanofiltration equipment gets high-weatherability black PV mill base 13~18% again, can stop purifying and barrelling, ink to be prepared this moment.
2, the ink composition for ink-jet printing with high-weatherability black dyes is prepared by following proportioning, referring to table 1.
Table 1
Proportioning | Weight (WT%) |
Triglycol | 6 |
The N-N-methyl-2-2-pyrrolidone N- | 8 |
The triglycol monobutyl ether | 8 |
Virahol | 3 |
Disappear worried 104 | 0.2 |
High-weatherability ink-jet black PV mill base | 30 |
The trihydroxy-aminomethane | 0.1 |
The bright Sheng of sterilant D7 | 0.1 |
Deionized water | 44.6 |
Add up to | 100 |
3, testing method:
Press the composition for ink that example 1 proportioning becomes, even, static through high-speed stirring, use 1un, 0.45un after the filter membrane of 0.2un filters step by step, obtains having the ink composition for ink-jet printing of high-weatherability black dyes.It is printed on above ink composition on the printing paper of selling on the market with Epson stylus Photo T50 model ink-jet printer.
Embodiment 2:
1, the purifying of Mordant Black dye paste
Get 30 kilograms in the former powder of medium black P 2 B, join in the electrically heated stirring tank of the deionized water that fills 270 kilograms, heating while stirring, treat that temperature reaches 80 degree back restir 1 hour, after the whole dissolvings of the dyestuff powder that guarantees to add, carry out coarse filtration with 5 microns PP filter core again, carry out filtration treatment with ultra-filtration membrane and the nanofiltration membrane assembled filter that can remove sodium-chlor when temperature is lower than 60 again when spending, to remove the by product and the sodium-chlor of molecular weight at 30,000 above materials.Replenish deionized water in the process of purifying, guaranteeing the penetrating amount of film, and detect the specific conductivity of the liquid that leaches, specific conductivity stops to add deionized water when 20ms/cm is following, continues nanofiltration and the volume of mill base is controlled at about 200 liters, promptly reaches requirement; Stop purifying, barrelling.
Get 100 kilograms of medium black P 2 B mill bases behind the above-mentioned purifying, join volume and be in 200 liters the electrically heated stirring tank, heating while stirring, after treating that temperature reaches 80 degree, add 9.19 kilograms of potassium bichromate, heating while stirring, after being heated to 96 degree, add 0.314 mole Glacial acetic acid or tartrate, insulation reaction is after 3 hours under the condition of 96 to 99 degree, cool to 50 degree, with the sodium hydroxide adjust pH is about 7 to 9, and the concentration of carrying out desalination and controlling mill base with nanofiltration equipment gets high-weatherability ink-jet black P2B mill base 13~18% again, can stop purifying and barrelling, ink to be prepared this moment.
2, the ink composition for ink-jet printing with high-weatherability black dyes is prepared by following proportioning, referring to table 2.
Table 2
Proportioning | Weight (WT%) |
Propylene glycol | 8 |
1, the 3-dimethyl-imidazolinone | 8 |
Diethylene glycol monobutyl ether | 12 |
Ethylene glycol ethyl ether | 3 |
Disappear worried 465 | 1 |
High-weatherability ink-jet black P2B mill base | 20 |
Trolamine | 0.3 |
The bright Sheng of sterilant P91 | 0.3 |
Deionized water | 47.4 |
Add up to | 100 |
3, testing method:
Press the composition for ink that example 2 proportionings become, even, static through high-speed stirring, use 1un, 0.45un after the filter membrane of 0.2un filters step by step, obtains having the ink composition for ink-jet printing of high-weatherability black dyes.It is printed on above ink composition on the printing paper of selling on the market with Epson stylus Photo T50 model ink-jet printer.
Embodiment 3
1, the purifying of Mordant Black dye paste
Get 30 kilograms in the former powder of Mordant Black T, join in the electrically heated stirring tank of the deionized water that fills 270 kilograms, heating while stirring, treat that temperature reaches 80 degree back restir 1 hour, after the whole dissolvings of the dyestuff powder that guarantees to add, carry out coarse filtration with 5 microns PP filter core again, carry out filtration treatment with ultra-filtration membrane and the nanofiltration membrane assembled filter that can remove sodium-chlor when temperature is lower than 60 again when spending, to remove the by product and the sodium-chlor of molecular weight at 30,000 above materials.Replenish deionized water in the process of purifying, guaranteeing the penetrating amount of film, and detect the specific conductivity of the liquid that leaches, specific conductivity stops to add deionized water when 20ms/cm is following, continues nanofiltration and the volume of mill base is controlled at about 200 liters, promptly reaches requirement; Stop purifying, barrelling.
Get 100 kilograms of Mordant Black T mill bases behind the above-mentioned purifying, join volume and be in 200 liters the electrically heated stirring tank, heating while stirring, after treating that temperature reaches 80 degree, add 8.55 kilograms of potassium bichromate, heating while stirring, after being heated to 96 degree, add 0.292 mole Glacial acetic acid or tartrate, insulation reaction is after 3 hours under the condition of 96 to 99 degree, cool to 50 degree, with the sodium hydroxide adjust pH is about 7 to 9, and the concentration of carrying out desalination and controlling mill base with nanofiltration equipment gets the black T mill base of high-weatherability ink-jet black 13~18% again, can stop purifying and barrelling, ink to be prepared this moment.
2, the ink composition for ink-jet printing with high-weatherability black dyes is prepared by following proportioning, referring to table 3.
Proportioning | Weight (WT%) |
Polypropylene glycol | 6 |
2-Pyrrolidone | 5 |
In the butyl glycol ether | 8 |
Disappear worried 440 | 0.3 |
High-weatherability ink-jet black is deceived the T mill base | 40 |
Diethanolamine | 0.1 |
The shield GXL of sterilant government office in feudal China | 0.1 |
Deionized water | 40.5 |
Add up to | 100 |
3, testing method:
Press the composition for ink that example 3 proportionings become, even, static through high-speed stirring, use 1un, 0.45un after the filter membrane of 0.2un filters step by step, obtains having the ink composition for ink-jet printing of high-weatherability black dyes.It is printed on above ink composition on the printing paper of selling on the market with Epson stylus Photo T50 model ink-jet printer.
Embodiment 4
1, the purifying of Mordant Black dye paste
Get 30 kilograms in the former powder of acid black 172, join in the electrically heated stirring tank of the deionized water that fills 270 kilograms, heating while stirring, treat that temperature reaches 80 degree back restir 1 hour, after the whole dissolvings of the dyestuff powder that guarantees to add, carry out coarse filtration with 5 microns PP filter core again, carry out filtration treatment with ultra-filtration membrane and the nanofiltration membrane assembled filter that can remove sodium-chlor when temperature is lower than 60 again when spending, to remove the by product and the sodium-chlor of molecular weight at 30,000 above materials.In the process of purifying, replenish deionized water, guaranteeing the penetrating amount of film, and detect the specific conductivity of the liquid that leaches, specific conductivity is when 20ms/cm is following, stop to add deionized water, continue nanofiltration and the volume of mill base is controlled at about 200 liters, concentration is controlled at 13~18% and promptly reaches requirement; Get ink-jet black 172 mill bases, can stop purifying and barrelling, ink to be prepared this moment.
2, the ink composition for ink-jet printing with high-weatherability black dyes is prepared by following proportioning, referring to table 4.
Table 4
Proportioning | Weight (WT%) |
1, the 2-hexylene glycol | 12 |
N,N-dimethylacetamide | 5 |
Diethylene glycol monobutyl ether | 12 |
Ethylene glycol ethyl ether | 3 |
Worried TG disappears | 0.5 |
Purified back acid black 172 mill base | 22 |
Trolamine | 0.1 |
The bright Sheng of sterilant D7 | 0.3 |
Deionized water | 45.1 |
Add up to | 100 |
3, testing method:
Press the composition for ink that example 4 proportionings become, even, static through high-speed stirring, use 1un, 0.45un after the filter membrane of 0.2un filters step by step, obtains having the ink composition for ink-jet printing of high-weatherability black dyes.It is printed on above ink composition on the printing paper of selling on the market with Epson stylus Photo T50 model ink-jet printer.
Embodiment 5
1, the ink composition for ink-jet printing with high-weatherability black dyes is prepared by following proportioning, referring to table 5.
Table 5
Proportioning | Weight (WT%) |
Triglycol | 6 |
The N-N-methyl-2-2-pyrrolidone N- | 12 |
The triglycol monobutyl ether | 8 |
Ethylene glycol ethyl ether | 1 |
Disappear worried 485 | 1 |
Bright Sheng black SP mill base | 30 |
The trihydroxy-aminomethane | 0.3 |
The bright Sheng of sterilant P91 | 0.1 |
Deionized water | 41.6 |
Add up to | 100 |
2, testing method:
Press the composition for ink that example 5 proportionings become, even, static through high-speed stirring, use 1un, 0.45un after the filter membrane of 0.2un filters step by step, obtains having the ink composition for ink-jet printing of high-weatherability black dyes.It is printed on above ink composition on the printing paper of selling on the market with Epson stylus Photo T50 model ink-jet printer.
Example 1 is deposited through the high temperature freezing and 60 one weeks of degree in subzero 24 one weeks of degree to the ink of example 5, stable performance, the injection print cartridge can clean and be printed to China ink continuously to the greatest extent, can satisfy the requirement of ink-jet after the selected high-weatherability black dyes of confirmation the present invention is purified.
The weathering resistance test:
Cause that the weathering resistance reduction mainly is the ozone in daylight middle-ultraviolet lamp and the atmosphere, has proposed easy light fastness testing method and ozone proof testing method in view of the above.Progressively improve test process through repetition test.Utilize the principle of aberration that this method has been appended quantitative evaluation, set up contact between aberration and light fastness rank and the anti-ozone rank by analysis, can extrapolate the rank of light fastness, anti-ozone rank, simple and fast by rate of fall-off or value of chromatism Δ E.
With the colour density of optics scenograph Eye-one test case 1, example 2, example 3, example 4, example 5 printing color lumps, under the UV lamp, shone 3 hours then, in its colour density of test, calculate the colour density rate of fall-off of color lump before and after the UV light irradiation.The colour density rate of fall-off is big more, shows that light permanency is poor more.On the contrary, the colour density rate of fall-off is low more, and light permanency is good more.
Print the colour density of color lump with optics scenograph Eye-one test case 1, example 2, example 3, example 4, example 5, under ozone environment (ozone disinfection cabinet) 3 hours then, in its colour density of test, calculate the colour density rate of fall-off of color lump before and after ozone disinfection cabinet is deposited.The colour density rate of fall-off is big more, shows that anti-ozone is poor more.On the contrary, the colour density rate of fall-off is low more, and anti-ozone is good more.
The sun-proof detailed data is as follows:
Table 1
Anti-ozone detailed data is as follows:
Table 2
Find from above test result, by example 1, example 2, example 3 good light fastness and ozone resistance are arranged all, the rate of fall-off of example 5 is bigger, light fastness and ozone resistance are relatively poor, 5 the contrast from example 1 to example, explanation is fine through the ink sun-proof and the anti-ozone of the preparation of the dye paste behind the purifying, and ink (example 5) sun-proof and the anti-ozone of the bright Sheng black SP mill base preparation that sell the market are very poor.In the delta data of table 1 and table 2 optical density (OD), confirm that example 1 has reached the effect of black dyes ink weather resistance of the presently claimed invention to example 3.Test data from example 4, acid black 172 is because be metallized dye, so it is better on the sun-proof performance, but the common ink-jet dye with present usefulness on ozone resistance does not have too many lifting, has only as example 1 and is undertaken being configured to sun-proof and the anti-ozone problem that ink could solve the aqueous black ink again behind the purifying by selecting the media black dyes to example 3.
More than embodiments of the invention are had been described in detail, but described content only is preferred embodiment of the present invention, can not be considered to be used to limit practical range of the present invention.All equalizations of doing according to the present patent application scope change and (the metallized dye acid black 172 being used for ink for ink-jet print such as comprising) such as improvement, all should still belong within the patent covering scope of the present invention.
Claims (5)
1. the ink composition for ink-jet printing with high-weatherability black dyes is characterized in that, this composition for ink is mixed by following component by weight percentage:
Surplus is a deionized water;
Described Mordant Black dye paste is selected from a kind of in Mordant Black PV, medium black P 2 B, Mordant Black T or the acid black 172 dye paste, wherein:
The purification process of described Mordant Black PV dye paste is as follows:
A, get former powder of Mordant Black PV and the deionized water that part by weight is l:9 and join in the electrically heated stirring tank, heated and stirred, temperature reach 80~90 degree backs and stir l~2 hour, carry out lowering the temperature after the coarse filtration, cool to 50~70 and carry out filtration treatment when spending, Mordant Black PV mill base;
B, get Mordant Black PV mill base, join in the electrically heated stirring tank, heated and stirred, temperature reaches 80~90 degree, adds potassium bichromate again, is heated to 96~99 degree, add Glacial acetic acid or tartrate then, and cooling to 40~60 degree after being incubated 3~4 hours, desalination is handled and the concentration of control mill base with carrying out behind the sodium hydroxide adjust pH, obtains high-weatherability ink-jet black PV mill base;
The purification process of described medium black P 2 B dyestuff mill base is as follows:
A, get former powder of medium black P 2 B and the deionized water that part by weight is l:9 and join in the electrically heated stirring tank, heated and stirred, temperature reach 80~90 degree backs and stir l~2 hour, carry out lowering the temperature after the coarse filtration, cool to 50~70 and carry out filtration treatment when spending, the medium black P 2 B mill base;
B, get the medium black P 2 B mill base, join in the electrically heated stirring tank, heated and stirred, temperature reaches 80~90 degree, adds potassium bichromate again, is heated to 96~99 degree, add Glacial acetic acid or tartrate then, and cooling to 40~60 degree after being incubated 3~4 hours, desalination is handled and the concentration of control mill base with carrying out behind the sodium hydroxide adjust pH, obtains high-weatherability ink-jet black P2B mill base;
The purification process of described Mordant Black T dye paste is as follows:
A, get former powder of Mordant Black T and the deionized water that part by weight is l:9 and join in the electrically heated stirring tank, heated and stirred, temperature reach 80~90 degree backs and stir l~2 hour, carry out lowering the temperature after the coarse filtration, cool to 50~70 and carry out filtration treatment when spending, Mordant Black T mill base;
B, get Mordant Black T mill base, join in the electrically heated stirring tank, heated and stirred, temperature reaches 80~90 degree, adds potassium bichromate again, is heated to 96~99 degree, add Glacial acetic acid or tartrate then, and cooling to 40~60 degree after being incubated 3~4 hours, desalination is handled and the concentration of control mill base with carrying out behind the sodium hydroxide adjust pH, obtains the black T mill base of high-weatherability ink-jet black;
The purification process of described acid black 172 dye paste is as follows:
Former powder of acid black 172 and the deionized water of getting part by weight and be l:9 join in the electrically heated stirring tank, heated and stirred, temperature reaches 80~90 degree backs and stirs l~2 hour, carry out lowering the temperature after the coarse filtration, cool to 50~70 and carry out filtration treatment when spending, concentration is controlled at 13~18%, gets the acid black 172 dye paste.
3. as composition for ink as described in claim l or 2, it is characterized in that described polyhydroxy-alcohol is selected from glycerine, glycol ether, ethylene glycol, l, one or more in 2-hexylene glycol, polyoxyethylene glycol, polypropylene glycol, the propylene glycol; Described tensio-active agent is selected from one or several in the worry 104 that disappears, the worried TG that disappears, the worry 440 that disappears, the worry 465 that disappears, the worry 485 that disappears; It is in diethanolamine, trolamine, the trihydroxy-aminomethane one or several that described pH regulator agent is selected from; It is in the shield GXL of government office in feudal China, bright Sheng D7, the P9l sterilant one or several that described sterilant is selected from.
4. as composition for ink as described in claim l or 2, it is characterized in that described solvent is selected from nitrogenous hydrophilic organic solvent, pure ether solvent, high volatilization hydrophilic solvent, the weight percent content of described solvent in composition for ink is:
Nitrogenous hydrophilic organic solvent 5~12
Alcohol ether solvent 8~12
High volatilization hydrophilic solvent 0~6.
5. as composition for ink as described in the claim 4, it is characterized in that described nitrogenous hydrophilic organic solvent is selected from N-N-methyl-2-2-pyrrolidone N-, l, one or more in 3-dimethyl-imidazolinone, 2-Pyrrolidone, the N,N-dimethylacetamide; Described pure ether solvent is selected from a kind of in diethylene glycol monobutyl ether, triglycol monobutyl ether, the butyl glycol ether; Described high volatilization hydrophilic solvent is selected from a kind of in Virahol, the ethylene glycol ethyl ether.