CN102166049A - Antibacterial and waterproof fabric - Google Patents
Antibacterial and waterproof fabric Download PDFInfo
- Publication number
- CN102166049A CN102166049A CN2010105579667A CN201010557966A CN102166049A CN 102166049 A CN102166049 A CN 102166049A CN 2010105579667 A CN2010105579667 A CN 2010105579667A CN 201010557966 A CN201010557966 A CN 201010557966A CN 102166049 A CN102166049 A CN 102166049A
- Authority
- CN
- China
- Prior art keywords
- layer
- antibiotic
- resin
- waterproof fabrics
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an antibacterial and waterproof fabric, which consists of an antibacterial layer 1, a waterproof layer 2, a bonding layer 3 and a fabric layer 4, wherein the antibacterial layer 1 is prepared from 6 percent of bamboo carbon fibers and resin with the viscosity of between 3,000 and 3,200; the waterproof layer 2 is prepared from waterproof resin slurry; the bonding layer 3 is a self-soluble bonding membrane; and the fabric layer 4 is a blended fabric layer of terylene and spandex. The invention discloses the antibacterial and waterproof fabric. Through a reasonable structural design, the fabric has the special performance of water prevention and antibacterium, and high warm keeping performance due to high sweat absorbing performance and air permeability, and is widely applied.
Description
Technical field
The present invention relates to a kind of lining, relate in particular to the lining of a kind of surface, belong to fabric class technical field by antibiotic waterproof material.
Background technology
Along with the raising day by day of living standard, the modern more and more pays attention to healthy, except considering its color and style, also will consider the security of clothing, the feature of environmental protection and functional when selecting underclothes.For example whether clothing has sterilizing and deodorizing function, whether can discharge anion and play the effect that improves the health, and whether function of infrared ray emission or the like is arranged.The special area that is attached to subtropical climate in south; often it is sunny to have the morning; the weather that afternoon is overcast and rainy continuous; people go out or short distance in seldom can carry rain gear; at this moment because there is bigger water imbibition in normal laundry, more or less can adsorb rainwater, reduce the comfort level that people wear clothing; the words of untimely processing also can cause symptoms such as flu, fever, have influenced people and have lived normally.People wish that the clothing of wearing can play waterproof action as raincoat, do not lose the comfort level of dress simultaneously again, and gas permeability and absorption of perspiration preferably can be arranged.
Summary of the invention:
At the demand, the invention provides a kind of antibiotic waterproof fabrics, by rational material mixture ratio, the processing method of science makes this lining have waterproof and antibiotic property, is fit to make various overcoats, gym suit.
The present invention is a kind of antibiotic waterproof fabrics, this lining is made up of antibiotic layer 1, watertight composition 2, adhesive layer 3 and tissue layer 4, described antibiotic layer 1 raw material is the bamboo-carbon fibre of content 6% and the resin of viscosity 3000-3200, described watertight composition 2 raw materials are the water proof type resin slurry, described adhesive layer 3 is from the dissolubility bonding film, and described tissue layer 4 is terylene and spandex blended fabric layer.
In a preferred embodiment of the present invention, the percentage composition ratio of bamboo-carbon fibre and resin is 3: 250 in the described antibiotic layer 1, adopts the heat fused established law to make.
In a preferred embodiment of the present invention, described resin is an acrylic resin.
In a preferred embodiment of the present invention, described water proof type resin slurry composition and percentage composition are: polyurethane resin 70%-90%, acetone diluted agent 10%-20%, DBP plasticizer 2%-8%, water-soluble silicon oil 1%-2%.
In a preferred embodiment of the present invention, described is to connect watertight composition 2 and tissue layer 4 from the effect of dissolubility bonding film.
In a preferred embodiment of the present invention, described reaching in temperature from the dissolubility bonding film dissolved when 90 ℃-120 ℃ or force value reach 5-8MPa voluntarily, plays cementation.
The present invention has disclosed a kind of antibiotic waterproof fabrics, by reasonable structural design, makes this lining have waterproof and antibiotic property, and excellent absorption of perspiration and gas permeability have guaranteed the thermal property that lining is good, and lining is used very extensive.
Description of drawings
The present invention is further detailed explanation below in conjunction with the drawings and specific embodiments:
Fig. 1 is the structural representation of a kind of antibiotic waterproof fabrics of the embodiment of the invention;
Among the figure, the 1st, antibiotic layer, the 2nd, watertight composition, the 3rd, adhesive layer, the 4th, tissue layer.
The specific embodiment
In order to make those skilled in the art person understand technical scheme of the present invention better, and above-mentioned purpose of the present invention, feature and advantage can be become apparent more, the present invention is further detailed explanation below in conjunction with embodiment and embodiment accompanying drawing.
As shown in Figure 1, structural representation for a kind of antibiotic waterproof fabrics of the embodiment of the invention, this lining is made up of antibiotic layer 1, watertight composition 2, adhesive layer 3 and tissue layer 4, described antibiotic layer 1 raw material is the bamboo-carbon fibre of content 6% and the resin of viscosity 3000-3200, described watertight composition 2 raw materials are the water proof type resin slurry, described adhesive layer 3 is from the dissolubility bonding film, and described tissue layer 4 is terylene and spandex blended fabric layer.
Embodiment 1
The concrete preparation process of lining is as follows:
A) coating of watertight composition is applied to waterproof layer material on the tack coat, and distance is controlled between the 0.1mm between the used scraper edge of a knife and the coated layer, coated with after be positioned over drying in oven, temperature is controlled at 135 ℃, the time is 20 minutes;
Wherein the preparation process of waterproof layer material is as follows:
1) at first, selecting waterproof layer material is the water proof type resin slurry, and its composition and percentage composition are: polyurethane resin 83%, acetone diluted agent 12%, DBP plasticizer 4%, water-soluble silicon oil 1%;
2) then, the raw material that configures is positioned in the reaction vessel, adds thermal agitation and fully mix, temperature is controlled at 30 ℃, and mixing time is 40 minutes;
3) last, it is standby to be cooled to room temperature.
B) coating of antibiotic layer is coated to antibiotic layer on the watertight composition for preparing, and distance is controlled between the 0.12mm between the used scraper edge of a knife and the coated layer, coated with after be positioned over drying in oven, temperature is controlled at 115 ℃, the time is 20 minutes;
Wherein the preparation process of antibiotic layer material is: at first, be that the acrylic resin of 6% bamboo-carbon fibre and viscosity 3000 carries out proportioning according to 3: 250 percentage composition with content; Then, be heated to 210 ℃, during add 8% butanone diluent resin, it is standby fully to mix the back.
C) thermoset forming, heating or exert pressure between tack coat for preparing (comprising watertight composition and antibiotic layer on it) and tissue layer makes two parts be fused into one, and heating and temperature control or applies the pressure of 6MPa about 100 ℃; Wherein bonding layer material is from the dissolubility bonding film, reaches in temperature and dissolves voluntarily when 90 ℃-120 ℃ or force value reach 5-12MPa, plays cementation.
The performance of the lining that makes by this technology is as follows: thickness 0.3mm, water pressure resistance 3.5KPa.
The concrete preparation process of lining is as follows:
A) coating of watertight composition is applied to waterproof layer material on the tack coat, and distance is controlled between the 0.12mm between the used scraper edge of a knife and the coated layer, coated with after be positioned over drying in oven, temperature is controlled at 140 ℃, the time is 30 minutes;
Wherein the preparation process of waterproof layer material is as follows:
1) at first, selecting waterproof layer material is the water proof type resin slurry, and its composition and percentage composition are: polyurethane resin 86%, acetone diluted agent 10%, DBP plasticizer 3%, water-soluble silicon oil 1%;
2) then, the raw material that configures is positioned in the reaction vessel, adds thermal agitation and fully mix, temperature is controlled at 45 ℃, and mixing time is 40 minutes;
3) last, it is standby to be cooled to room temperature.
B) coating of antibiotic layer is coated to antibiotic layer on the watertight composition for preparing, and distance is controlled between the 0.14mm between the used scraper edge of a knife and the coated layer, coated with after be positioned over drying in oven, temperature is controlled at 120 ℃, the time is 25 minutes;
Wherein the preparation process of antibiotic layer material is: at first, be that the acrylic resin of 6% bamboo-carbon fibre and viscosity 3000 carries out proportioning according to 3: 250 percentage composition with content; Then, be heated to 240 ℃, during add 8% butanone diluent resin, it is standby fully to mix the back.
C) thermoset forming, heating or exert pressure between tack coat for preparing (comprising watertight composition and antibiotic layer on it) and tissue layer makes two parts be fused into one, and heating and temperature control or applies the pressure of 6MPa about 100 ℃; Wherein bonding layer material is from the dissolubility bonding film, reaches in temperature and dissolves voluntarily when 90 ℃-120 ℃ or force value reach 5-12MPa, plays cementation.
The performance of the lining that makes by this technology is as follows: thickness 0.4mm, water pressure resistance 4KPa.
The present invention has disclosed a kind of antibiotic waterproof fabrics, is characterized in: by reasonable structural design, make this lining have waterproof and antibiotic property, excellent absorption of perspiration and gas permeability have guaranteed the thermal property that lining is good, and lining is used very extensive.
Protection scope of the present invention is not limited thereto, and anyly is familiar with those skilled in the art in the technical scope that the present invention discloses, and the variation that can expect easily or replacement all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claim was defined.
Claims (6)
1. antibiotic waterproof fabrics, this lining is made up of antibiotic layer (1), watertight composition (2), adhesive layer (3) and tissue layer (4), described antibiotic layer (1) raw material is the bamboo-carbon fibre of content 6% and the resin of viscosity 3000-3200, described watertight composition (2) raw material is the water proof type resin slurry, described adhesive layer (3) is from the dissolubility bonding film, and described tissue layer (4) is terylene and spandex blended fabric layer.
2. antibiotic waterproof fabrics according to claim 1 is characterized in that, the percentage composition ratio of bamboo-carbon fibre and resin is 3: 250 in the described antibiotic layer (1), adopts the heat fused established law to make.
3. antibiotic waterproof fabrics according to claim 2 is characterized in that, described resin is an acrylic resin.
4. antibiotic waterproof fabrics according to claim 1, it is characterized in that described water proof type resin slurry composition and percentage composition are: polyurethane resin 70%-90%, acetone diluted agent 10%-20%, DBP plasticizer 2%-8%, water-soluble silicon oil 1%-2%.
5. antibiotic waterproof fabrics according to claim 1 is characterized in that, described is to connect watertight composition (2) and tissue layer (4) from the effect of dissolubility bonding film.
6. antibiotic waterproof fabrics according to claim 5 is characterized in that, described reaching in temperature from the dissolubility bonding film dissolved when 90 ℃-120 ℃ or force value reach 5-8MPa voluntarily, plays cementation.