CN102152577A - Easy-removing cover film with high-temperature resistant polypropylene cup material function and preparation method thereof - Google Patents
Easy-removing cover film with high-temperature resistant polypropylene cup material function and preparation method thereof Download PDFInfo
- Publication number
- CN102152577A CN102152577A CN 201010594075 CN201010594075A CN102152577A CN 102152577 A CN102152577 A CN 102152577A CN 201010594075 CN201010594075 CN 201010594075 CN 201010594075 A CN201010594075 A CN 201010594075A CN 102152577 A CN102152577 A CN 102152577A
- Authority
- CN
- China
- Prior art keywords
- layer
- epiphragma
- film
- hot sealing
- sealing layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the field of food package, and relates to an easy-removing cover film with the high-temperature resistant polypropylene cup material function, which comprises a printing layer polyethylene terephthalate film printed with an oil ink printing pattern; the printing layer polyethylene terephthalate after printed with the oil ink printing pattern is sequentially stuck with a blocked layer nylon film or silicon-plated polyester film and a heat sealing layer casting polypropylene film to form the easy-removing cover film, wherein the casting polypropylene film is produced by adopting a three-layer coextrusion technique, and a peeling way belongs to cohesion peeling. The easy-removing cover film can bear the sterilization under the high temperature of 131 DEG C for 45min, does not have phenomena like delamination, peeling and damage after the sterilization, and has plump and flat package as well as excellent effects; has proper heat sealing strength and firm sealing opening, is smooth without a pause feeling when being removed; and has good blocking performances and anti-pollution performance as well as longer product guarantee period. The easy-removing cover film can be combined with the polypropylene cup material to replace traditional glass bottles and tinplate tank high-temperature sterilization package products, reduces the package cost, and has broad market prospect.
Description
Technical field
The invention belongs to the packaging for foodstuff field, be specifically related to a kind of have a fire resistant polypropylene cup material function easily take off epiphragma and preparation method thereof.
Background technology
At present, packings such as various tinned fruits, canned meat, canned fish, congee class have begun to attempt using easily takes off mode that epiphragma combines with the polypropylene cup and replaces that the packing energy consumption is big, carrying cost is high, and big glass bottle and jar and can take up room.Handle half an hour to one hour because packings such as tinned fruit, canned meat, canned fish, congee class need to stand 110 ℃～121 ℃ high-temperature sterilizations in process of production, the conventional composite flexible package is easily taken off packing technique that epiphragma combines with the polypropylene cup and is mainly used in the packaging fields of processing food such as normal temperature or low temperature jelly, sour milk, pudding.The combination of this kind epiphragma and polypropylene cup can not bear high-temperature heating treatment, occurs problems such as sealing property is poor, barrier resistance tocrocking difference after the high-temperature heating treatment easily.Therefore, research and development have fire resistant polypropylene cup material function easily to take off epiphragma significant for the development that promotes packaging for foodstuff fields such as can, congee class.
From the technology that epiphragma and cup are peeled off, the lift-off technology of realizing easily taking off function is mainly based on following three kinds of methods:
(1) delamination: delamination is meant epiphragma when cup is opened, and the hot sealing layer of epiphragma and other composite bed generation layerings and producing peeled off.The compound fastness of the hot sealing layer of epiphragma is less than sealing-strength, and hot sealing layer is thinner, is easy to break to form layering, and peeling force size (being heat seal strength) is wayward, when opening epiphragma, phenomenons such as wire drawing, band burr is arranged easily.
(2) interface peel: interface peel is called totally again to be peeled off, and when epiphragma was opened from cup, the hot sealing layer of epiphragma can strip down from cup fully.After epiphragma was peeled off, epiphragma and cup did not have obvious color, the transparency to change, and the stripper surface of cup is clean, neat, attractive in appearance.This mode of peeling off is the mode of peeling off that at present a lot of jelly, sour milk, pudding etc. are easily taken off epiphragma, condition effect was bigger when but the size of its peeling force was subjected to sealing, heat-sealing window relative narrower, stand the high-temperature sterilization process after, epiphragma promptly can come off automatically, peel off.
(3) poly-peeling off in: interior poly-peeling off is meant epiphragma when cup is opened, the hot sealing layer of epiphragma produces interfacial failure earlier and inside takes place peels off, self is destroyed, a hot sealing layer part is stayed on the epiphragma main body, another part has then been stayed cup surface, after epiphragma is peeled off, peels off that vestige is clear to be white in color, peel strength is lower usually, can realize that easily taking off of fire resistant polypropylene cup material epiphragma peel off.But because interior poly-stripping damage is the hot sealing layer of self, the preparation technology of its hot sealing layer film has relatively high expectations, and adopts the coated heat sealing adhesive process to be about to have the heat-seal adhesive of easily peeling off character usually and coats the epiphragma heat cover, makes it have easy fissility.At present only there is the large-scale trans-corporation's coated heat sealing adhesive process of external a few family to develop the fire resistant polypropylene cup and easily takes off epiphragma, as gondola B-Pack, Japan eastern beautiful etc., and domestic manufacturer unable production hot sealing layer film mainly depends on external import.
Summary of the invention
In view of this, first technical problem to be solved by this invention provide a kind of have a fire resistant polypropylene cup material function easily take off epiphragma.This fire resistant polypropylene cup material is easily taken off epiphragma and has been overcome the deficiencies in the prior art, not only can tolerate 131 ℃ high temperature sterilization, and epiphragma does not have layering, disrepair phenomenon after the sterilization, and feel does not smoothly have the pause and transition in rhythm or melody sense when opening, phenomenons such as no wire drawing, band burr.
Second technical problem to be solved by this invention provides the preparation method that this fire resistant polypropylene cup material is easily taken off epiphragma.
Technical problem to be solved by this invention is achieved through the following technical solutions:
A kind of have a fire resistant polypropylene cup material function easily take off epiphragma, comprise the printed layers polyethylene terephthalate thin film behind the ink printing pattern, the described bonding successively barrier layer nylon film of printed layers polyethylene terephthalate thin film behind the ink printing pattern or plating silicon polyester film and hot sealing layer cast polypropylene film gone up forms and easily takes off epiphragma.
Wherein the printed layers polyethylene terephthalate thin film is used for the pattern of ink printing client needs; Barrier layer nylon film or plating silicon polyester film have higher barrier property and antifouling property; The hot sealing layer cast polypropylene film also can be described as peel ply, is used to realize easily taking off peeling off of epiphragma and cup.
Described hot sealing layer cast polypropylene film is made up of hot sealing layer, supporting layer, corona layer.Wherein said hot sealing layer comprises high temperature resistant HOPP, polyethylene or ethylene-vinyl acetate copolymer, additive, described high temperature resistant HOPP is a base material, and described polyethylene or ethylene-vinyl acetate copolymer are evenly dispersed in the base material with the form of " isolated island "; Supporting layer uses high temperature resistant HOPP resin; The corona layer uses conventional HOPP resin.
The hot sealing layer cast polypropylene film that the present invention easily takes off epiphragma is a peel ply.Owing to there are two kinds of different phases in the material of peeling off, phase and phase is directly incompatible, the contact and the containment relationship that just have the physics aspect, contact-making surface in two-phase has just produced the interface like this, externally peel off at two alternate interfaces under the effect of pulling force, thereby realize the effect of peeling off easily take off, its principle is the interior poly-principle of peeling off; Supporting layer uses high temperature resistant HOPP resin, and good temperature resistance and deflection are provided, and is easy to the walk machine of co-extrusion film on client's packaging production line; The corona layer adopts conventional HOPP resin, is easy to beat sided corona treatment and improves the surface tension state, and the corona value reaches more than 38 dyne when walking machine.
The mass percentage content of each composition is in the described hot sealing layer: high temperature resistant HOPP 91～98.2%, incompatible phase polyethylene or ethylene-vinyl acetate copolymer 1～7%, surplus are additive.
Described additive is 0.5～1% slipping agent, 0.2～0.5% defoamer, 0.1～0.5% antistatic additive.
Described slipping agent can be selected one or both the mixing in oleamide or the erucyl amide, and described defoamer is the polyurethane defoamer, and described antistatic additive is a non-ionic antistatic agent.
The hot sealing layer of described hot sealing layer cast polypropylene film, supporting layer, corona layer by layer between the thickness ratio be 0.5～1.5:2.5～3.5:0.5～1.5.
Described printing ink is no benzene polyurethane or acrylic acid modified resin printing ink.
Described adhesive is an adhesive for polyurethane, and consumption is 3.1 ~ 3.4g/m
2
The method of easily taking off epiphragma that preparation has fire resistant polypropylene cup material function is as follows:
(1) the hot sealing layer cast polypropylene film adopts the three-layer co-extruded explained hereafter that goes out, and concrete preparation method is:
A) batch mixing is with dry: the high temperature resistant HOPP raw material particle of hot sealing layer raw material-91～98.2%, 1～7% polyethylene or ethylene-vinyl acetate copolymer, 0.5～1% slipping agent, 0.2～0.5% defoamer, 0.1～0.5% antistatic additive are mixed, fully stir, it is mixed, carry out drying then and handle; And support layer material-high temperature resistant HOPP resin and corona layer material-conventional HOPP resin are carried out drying respectively handle;
B) fusion and film forming: the extruder of the raw material of each layer by separately is through heating and melting, the resin of fusion enters distributor and distributes in proportion, and more after filtering, the molten resin of elimination impurity is extruded from T pattern coextrusion head, and be attached to chilling roller surface rapidly, form cast polypropylene film;
C) thickness measuring, corona and rolling: after the online thickness measure of cast polypropylene film process that the cooling of chilling roller forms, carry out sided corona treatment, be wound into semi-finished product then at the corona layer;
D) Ageing Treatment with cut: the semi-finished product of above rolling are carried out Ageing Treatment so that stable performance, and then cut into the desired volume film of client, i.e. cast polypropylene film finished product as requested.
(2) by gravure printing technique needed pattern of ink printing client on the sided corona treatment face of printed layers polyethylene terephthalate thin film;
(3) by the plating silicon face of dry type complex method, then in 70%RH(relative humidity with adhesive composite nylon film treated side on the printing surface of polyethylene terephthalate thin film or plating silicon polyester film) * condition of 50 ℃ * 48h of temperature under slaking.(4) again by the sided corona treatment face of dry type complex method, and then in 70%RH(relative humidity with the compound hot sealing layer cast polypropylene film of adhesive on the non-plating silicon face of the non-treated side of the nylon film of step (3) gained material or plating silicon polyester film) * condition of 50 ℃ * 96h of temperature under slaking.
(5) with the laminated film after the above-mentioned slaking according to the customer requirement size cut, rolling, packing, make the high temperature resistant epiphragma finished product of easily taking off.
Compared with prior art, the present invention can reach following beneficial effect:
(1) to adopt the modified random copolymerization cast polypropylene film be hot sealing layer film (easily take off layer) in the present invention, easily take off in the layer by two kinds of incompatible being distributed in mutually, according to the interior poly-principle of peeling off, realize the effect of peeling off easily take off, heat seal strength is 15～30N/15mm, peeling force fluctuation≤3N/15mm, heat seal strength is moderate, not only seal firmly, and open easily, level and smooth no pause and transition in rhythm or melody sense when opening.
(2) the selected material of the present invention can tolerate 131 ℃ * 45 minutes high temperature sterilization, does not have layering after the sterilization, peels off, phenomenon such as breakage.
(3) barrier layer of the present invention is selected nylon or plating silicon polyester for use, make the present invention that higher barrier property and antifouling property be arranged, transmitance≤the 5cc/m2.23 of oxygen ℃ * 24h * 70%RH, the transmitance of steam≤2g/ m2.38 ℃ * 24h * 90%RH, shelf life of products is longer.
(4) the selected material of the present invention has good shrinkage, behind the high temperature sterilization, packs full, smooth, respond well.
(5) the present invention combines with polypropylene cup material and can replace traditional vial, can high temperature sterilization packaging product, has reduced packing cost, and market prospects are wide.
Description of drawings
Fig. 1 is that embodiment one fire resistant polypropylene cup material is easily taken off the epiphragma structural representation.
Fig. 2 is the structural representation that embodiment one fire resistant polypropylene cup material is easily taken off the hot sealing layer film of epiphragma.
Fig. 3 is that embodiment one fire resistant polypropylene cup material is easily taken off the poly-design sketch of peeling off in the epiphragma.
The specific embodiment
For the ease of it will be appreciated by those skilled in the art that the present invention is done detailed description below in conjunction with embodiment and accompanying drawing.Printing ink and adhesive used among the embodiment are not limitation of the present invention, in fact, may be used to the present invention printed patterns and bonding each layer film on printed layers as long as meet high temperature resistant printing ink and the adhesive of easily taking off the epiphragma requirement.
Embodiment one
What present embodiment had fire resistant polypropylene (PP) cup material function easily takes off epiphragma as shown in Figure 1, and its structure is followed successively by from outside to inside: 1-printed layers polyethylene terephthalate thin film (PET); 2-does not have benzene polyurethane ink layer (INK); 3 and 5-adhesive for polyurethane (AD); 4-barrier layer nylon film (NY); 6-hot sealing layer cast polypropylene film (CPP).
Wherein the hot sealing layer film CPP of innermost layer as shown in Figure 2, this layer adopts the three-layer co-extruded explained hereafter that goes out, layer thickness is than 1:3:1,61 be the corona layer, adopts conventional homopolymerization PP resin, walks the dynamo-electric value of swooning and reaches more than 38 dyne; 62 for having the clear support layer of enough deflections, and material adopts high temperature resistant homopolymerization PP resin; 63 is the hot sealing layer with " isolated island " effect, and employing can be a base material with the resistant to elevated temperatures random copolymerization PP resin particle of PP cup material heat-sealing, and its incompatible phase PE is evenly dispersed in the base material with the form of " isolated island ".
Of the present invention peeling off is created among the hot sealing layer film CPP6, and Fig. 3 easily takes off the interior poly-design sketch of peeling off of epiphragma for the present invention.7 is cup, and effect is peeled off in 8 inside of easily taking off epiphragma for the present invention.
The preparation method who easily takes off epiphragma that present embodiment has high temperature resistant PP cup material function is as follows:
(1) innermost layer CPP adopts the three-layer co-extruded explained hereafter that goes out, and concrete preparation method is:
A) batch mixing is with dry: the high temperature resistant HOPP raw material particle of hot sealing layer raw material-91～98.2%, 1～7% polyethylene or ethylene-vinyl acetate copolymer, 0.5～1% slipping agent, 0.2～0.5% defoamer, 0.1～0.5% antistatic additive are mixed, fully stir, it is mixed, carry out drying then and handle; And support layer material-high temperature resistant HOPP resin and corona layer material-conventional HOPP resin are carried out drying respectively handle;
B) fusion and film forming: the extruder of the raw material of each layer by separately is through heating and melting, the resin of fusion enters distributor and distributes in proportion, and more after filtering, the molten resin of elimination impurity is extruded from T pattern coextrusion head, and be attached to chilling roller surface rapidly, form cast polypropylene film;
C) thickness measuring, corona and rolling: after the online thickness measure of cast polypropylene film process that the cooling of chilling roller forms, carry out sided corona treatment, be wound into semi-finished product then at the corona layer;
D) Ageing Treatment with cut: the semi-finished product of above rolling are carried out Ageing Treatment so that stable performance, and then cut into the desired volume film of client, i.e. cast polypropylene film finished product as requested.
(2) print client needed pattern at the sided corona treatment face of PET with INK by gravure printing technique;
(3) by the dry type complex method with the treated side of the compound NY of AD on the printing surface of PET, then in 70%RH(relative humidity) * condition of 50 ℃ * 48h of temperature under slaking.
(4) again by the dry type complex method with the sided corona treatment face of the compound CPP of adhesive on the non-treated side of the NY of PET/INK/AD/NY, and then in 70%RH(relative humidity) * condition of 50 ℃ * 96h of temperature under slaking.
(5) with the laminated film PET/INK/AD/NY/AD/CPP after the above-mentioned slaking according to the customer requirement size cut, rolling, packing, make the high temperature resistant epiphragma finished product of easily taking off.
This is high temperature resistant, and PP cup material easily takes off epiphragma and PP cup material heat seal strength is 15～30N/15mm, and heat seal strength is moderate; Peeling force fluctuation≤3N/15mm when opening, and feel does not smoothly have the pause and transition in rhythm or melody sense; Can tolerate 131 ℃ * 45 minutes high temperature sterilization, not have layering after the sterilization, peel off, phenomenon such as breakage, and pack full, smooth, respond well; Transmitance≤the 5cc/m2 of test oxygen under the condition of 70%, 23 ℃ * 24h of relative humidity, the transmitance≤2g/m2 of test water steam under the condition of 90%, 38 ℃ * 24h of relative humidity has higher barrier property.
Embodiment 2
The structure of easily taking off epiphragma that present embodiment has high temperature resistant PP cup material function is followed successively by from outside to inside: polyethylene terephthalate thin film (PET), acrylic acid modified resin ink lay (INK), adhesive phase (AD), plating silicon polyester film (SPET), adhesive phase (AD), cast polypropylene film (CPP).
Wherein the CPP employing can be a base material with the resistant to elevated temperatures atactic copolymerized polypropene resin particle of polypropylene cup material heat-sealing, and its incompatible phase EVA is evenly dispersed in the base material with the form of " isolated island ".
The preparation method who easily takes off epiphragma that present embodiment has fire resistant polypropylene cup material function is as follows:
(1) innermost layer CPP adopts the three-layer co-extruded explained hereafter that goes out, and concrete preparation method is:
A) batch mixing is with dry: the high temperature resistant HOPP raw material particle of hot sealing layer raw material-91～98.2%, 1～7% polyethylene or ethylene-vinyl acetate copolymer, 0.5～1% slipping agent, 0.2～0.5% defoamer, 0.1～0.5% antistatic additive are mixed, fully stir, it is mixed, carry out drying then and handle; And support layer material-high temperature resistant HOPP resin and corona layer material-conventional HOPP resin are carried out drying respectively handle;
B) fusion and film forming: the extruder of the raw material of each layer by separately is through heating and melting, the resin of fusion enters distributor and distributes in proportion, and more after filtering, the molten resin of elimination impurity is extruded from T pattern coextrusion head, and be attached to chilling roller surface rapidly, form cast polypropylene film;
C) thickness measuring, corona and rolling: after the online thickness measure of cast polypropylene film process that the cooling of chilling roller forms, carry out sided corona treatment, be wound into semi-finished product then at the corona layer;
D) Ageing Treatment with cut: the semi-finished product of above rolling are carried out Ageing Treatment so that stable performance, and then cut into the desired volume film of client, i.e. cast polypropylene film finished product as requested.
(2) by the sided corona treatment face printing client needed pattern of gravure printing technique at PET;
(3) by the dry type complex method with the plating silicon face of adhesive composite S PET on the printing surface of PET, then in 70%RH(relative humidity) * condition of 50 ℃ * 48h of temperature under slaking;
(4) again the non-plating silicon face of the SPET by the PET/INK/AD/SPET of dry type complex method after with slaking with the sided corona treatment face of the compound CPP of adhesive, and then in 70%RH(relative humidity) * condition of 50 ℃ * 5day of temperature under slaking;
(5) with the laminated film PET/INK/AD/SPET/AD/CPP after the above-mentioned slaking according to the customer requirement size cut, rolling, packing, make the high temperature resistant epiphragma finished product of easily taking off.
This is high temperature resistant, and PP cup material easily takes off epiphragma and PP cup material heat seal strength is 15～30N/15mm, and heat seal strength is moderate; Peeling force fluctuation≤3N/15mm when opening, and feel does not smoothly have the pause and transition in rhythm or melody sense; Can tolerate 131 ℃ * 45 minutes high temperature sterilization, not have layering after the sterilization, peel off, phenomenon such as breakage, and pack full, smooth, respond well; Transmitance≤the 5cc/m of test oxygen under the condition of 70%, 23 ℃ * 24h of relative humidity
2, the transmitance≤2g/m2 of test water steam under the condition of 90%, 38 ℃ * 24h of relative humidity has higher barrier property.
The foregoing description only is a preferred embodiments of the present invention; should not be construed as limiting the invention; under the situation that does not break away from the technical solution of the present invention scope; any technology contents of above-mentioned announcement that utilizes is made the equivalent variations scheme that part is changed or modified, and all should fall within protection scope of the present invention.
Claims (9)
- One kind have a fire resistant polypropylene cup material function easily take off epiphragma, it is characterized in that: comprise the printed layers polyethylene terephthalate thin film behind the ink printing pattern, the described bonding successively barrier layer nylon film of printed layers polyethylene terephthalate thin film behind the ink printing pattern or plating silicon polyester film and hot sealing layer cast polypropylene film gone up forms and easily takes off epiphragma.
- 2. according to claim 1 a kind of have a fire resistant polypropylene cup material function easily take off epiphragma, it is characterized in that: described hot sealing layer cast polypropylene film is produced with coextrusion process by hot sealing layer, supporting layer, corona layer, described hot sealing layer comprises high temperature resistant HOPP, polyethylene or ethylene-vinyl acetate copolymer, additive, described high temperature resistant HOPP is a base material, and described polyethylene or ethylene-vinyl acetate copolymer are evenly dispersed in the base material with the form of " isolated island "; Supporting layer uses high temperature resistant HOPP resin; The corona layer uses conventional HOPP resin.
- 3. according to claim 2 a kind of have a fire resistant polypropylene cup material function easily take off epiphragma, it is characterized in that: the mass percentage content of each composition is in the described hot sealing layer: high temperature resistant HOPP 91～98.2%, incompatible phase polyethylene or ethylene-vinyl acetate copolymer 1～7%, surplus are additive.
- 4. according to claim 3 a kind of have a fire resistant polypropylene cup material function easily take off epiphragma, it is characterized in that: described additive is 0.5～1% slipping agent, 0.2～0.5% defoamer, 0.1～0.5% antistatic additive.
- 5. according to claim 4 a kind of have a fire resistant polypropylene cup material function easily take off epiphragma, it is characterized in that: described slipping agent can be selected one or both the mixing in oleamide or the erucyl amide, described defoamer is the polyurethane defoamer, and described antistatic additive is a non-ionic antistatic agent.
- 6. according to claim 2 a kind of have a fire resistant polypropylene cup material function easily take off epiphragma, it is characterized in that: the hot sealing layer of described hot sealing layer cast polypropylene film, supporting layer, corona layer by layer between the thickness ratio be 0.5～1.5:2.5～3.5:0.5～1.5.
- According to claim 1～6 any one described a kind of have a fire resistant polypropylene cup material function easily take off epiphragma, it is characterized in that: described printing ink is no benzene polyurethane or acrylic acid modified resin printing ink.
- According to claim 7 any one described a kind of have a fire resistant polypropylene cup material function easily take off epiphragma, it is characterized in that: described adhesive is the agent of polyurethane gluing, and consumption is 3.1 ~ 3.4g/m 2
- 9. described preparation method who easily takes off epiphragma with fire resistant polypropylene cup material function of claim 1 is characterized in that preparation process is:(1) the thin cast polypropylene film of hot sealing layer adopts the three-layer co-extruded explained hereafter that goes out, and skin is a hot sealing layer, and the centre is a supporting layer, and internal layer is the corona layer, and its layer thickness ratio is 0.5～1.5:2.5～3.5:0.5～1.5;(2) by the treated side printing client needed pattern of printing ink on the gravure printing technique at the printed layers film;(3) by the dry type complex method with compound barrier layer nylon film of adhesive on the material of step (2) preparation or plating silicon polyester film, under temperature, humidity and time are respectively 45～55 ℃, 60～80%, 45～55h condition, carry out maturation process then;(4) again by the dry type complex method with the hot sealing layer cast polypropylene film of adhesive composite steps (1) gained on step (3) the gained material, and then be respectively maturation process under 45～55 ℃, 60～80%, 3～6 days the condition in temperature, humidity and time;(5) with step (4) gained high temperature resistant easily take off epiphragma according to the customer requirement size cut, rolling, packing, make the high temperature resistant epiphragma finished product of easily taking off.