CN102146224B - Coating containing magnesium and rare earth for ocean climate resistance preservative treatment - Google Patents
Coating containing magnesium and rare earth for ocean climate resistance preservative treatment Download PDFInfo
- Publication number
- CN102146224B CN102146224B CN 201010623727 CN201010623727A CN102146224B CN 102146224 B CN102146224 B CN 102146224B CN 201010623727 CN201010623727 CN 201010623727 CN 201010623727 A CN201010623727 A CN 201010623727A CN 102146224 B CN102146224 B CN 102146224B
- Authority
- CN
- China
- Prior art keywords
- coating
- alloy powder
- silicon alloy
- zinc silicon
- aluminium zinc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to coating for preservative treatment of ocean climate resistance engineering parts. The coating comprises the following components: 30.0 to 50.0 grams of aluminum-zinc-silicon alloy powder, 10.0 to 25.0mL of organic solvent, 1.0 to 4.0 grams of nano oxide particle reinforcing agent, 15.0 to 30.0mL of deionized water, 2.0 to 5.0 grams of binder, 1.0 to 3.0 grams of corrosion inhibitor, 0.1 to 2.0mL of dispersing agent and 0.1 to 2.0 grams of thickener, wherein the aluminum-zinc-silicon alloy powder consists of Al, Zn, Si, Mg and RE.
Description
Technical field
The present invention relates to water-soluble aluminum zinc silicon coating that a kind of marine climate resistant engineering component rotproofing uses and preparation method thereof.
Background technology
Engineer equipment in coastal waters and ocean ambient atmosphere of living in is rainy, high temperature, many salt fogs and high wind stream, its service condition press ISO9225 environmental evaluation standard generally>the C5 level, belong to extreme environment.Exposed part will receive intensive atomospheric corrosion, galvanic corrosion and the comprehensive action of airflow scouring erosive, and the work-ing life of various steelwork is far below general landlocked outdoor environment.Like the wind power plant of under the oceanic climate condition, being on active service since the external member of unit such as cabin, hood, pylon, root of blade flange gasket, joint bolt, connection spring etc. directly be exposed in the extreme corrosion atmosphere; Adopt conventional safeguard procedures; Often only several months just produce serious corrosion; Therefore, the wind-powered electricity generation external member surface treatment novel material and the novel process of weather resistance>15 year is provided, become the active demand of wind-powered electricity generation industry development.
In addition, the corrosion prevention of boats and ships steel member also is a long-standing difficult problem, and except housing, deck, the corrosion prevention maintenance cost of various masts, antenna is very surprising.Along with the speed-raising of country to infrastructure development project, many bridge spanning the seas go into operation in succession or set up the project, like port-Australia-pearl bridge etc.In the design and construction of bridge, the importance that the corrosion prevention of the steel member of different types of rridges is handled is more and more protruded.As in the construction of Hangzhou Gulf Great Bridge, surfacecti proteon is handled with regard to more than one hundred million units.
Therefore, pressing for the engineering component rotproofing problem that solves marine climate resistant, is to solve marine climate resistant corrosive effective way in engineering component surface hot dip Al-Zn-Si series alloy coating in the prior art, has obtained a large amount of practical applications.The application number that formerly proposes like the applicant is 2009102627168, and denomination of invention adopts cast aluminium alloy to do rotproofing in " a kind of marine climate resistant engineering component carries out antiseptic method " patented claim, and can arrive 20 years work-ing life.Yet there is technological temperature high (greater than 800 ℃) in the hot dip alloy coat in this invention, is prone to cause part deformation; Wear resistance is not enough, and the anti-impact erosion is indifferent; Therefore defectives such as technology, equipment are complicated, and processing of big area workpiece and field work are restricted are used still to exist greatly and are limited.
In addition, the metal surface anticorrosive treatment technology of the seventies exploitation in last century, the sheet zinc-base chromic salts protective coating as common also is used to the protective treatment of offshore engineering component corrosion.Yet this coating contains sexavalent chrome, and certain pollution is arranged.And because passivation, agglutinating need, generally all be added with the chromic anhydride of 5%-10%, and therefore Cr6+ strong toxicity and have carcinogenesis exists serious harm to environment and human body.In addition, this coating curing temperature is up to 300 ℃, and also reach about 30min set time, and energy consumption is big; Hardness is low, wears no resistance.Workpiece usually can receive scratch, scratch in transportation, assembling, use, influence the outward appearance and the solidity to corrosion of product.
Summary of the invention
To these problems in the prior art, the invention provides a kind of environmental protection, water-soluble low-temperature immobilized marine climate resistant corrosive aluminium zinc silicon coating and preparation method thereof.
The coating that marine climate resistant engineering component rotproofing provided by the invention is used; Wherein said coating comprises aluminium zinc silicon alloy powder, organic solvent, nano-oxide particles toughener, deionized water, sticker, corrosion inhibitor, dispersion agent and thickening material; Wherein said formulation for coating material is with following proportioning: aluminium zinc silicon alloy powder: organic solvent: nano-oxide particles toughener: deionized water: sticker: corrosion inhibitor: dispersion agent: thickening material=30.0-50.0g: 10.0-25.0mL: 1.0-4.0g: 15.0-30.0mL: 2.0-5.0g: 1.0-3.0g: 0.1-2.0mL: 0.1-2.0g, wherein said aluminium zinc silicon alloy powder is made up of Al, Zn, Si, Mg, RE.
The preferred terepthaloyl moietie of wherein said organic solvent.
Wherein said sticker preferred boric acid fat coupling agent.
Wherein said corrosion inhibitor preferred boric acid.
The preferred Natvosol of wherein said thickening material.
The preferred ZGK 5 dipropylene glycol monomethyl ether of wherein said dispersion agent.
Preferably, wherein said nano-oxide particles toughener is selected from Al
2O
3, SiO
2In one or both.
Preferred, wherein said Al
2O
3Median size be 15~60nm, said SiO
2Median size be 25~70nm.
Preferred, wherein the nano-oxide particles toughener is SiO
2And Al
2O
3, and SiO
2And Al
2O
3Mass ratio is 1: (1~3).
Preferably, wherein said each composition mass percent of aluminium zinc silicon alloy powder is: Zn:35~58%, and Si:0.3~4.0%, Mg:0.1~5.0%, RE:0.02~1.0%, surplus is Al and unavoidable impurities.
Preferably, the mean diameter of wherein said aluminium zinc silicon alloy powder is 10-200 μ m.
On the other hand, the present invention also provides a kind of method for preparing the coating that said marine climate resistant engineering component rotproofing uses, and wherein by above-mentioned prescription, takes by weighing quantitative corrosion inhibitor; Dissolve in the quantitative deionized water, add sticker then, dispersion agent; Organic solvent stirs and makes it dissolving, under whipped state, slowly adds aluminium zinc silicon alloy powder and nano-oxide particles toughener; Add thickening material then, the temperature of control oil bath is 20-30 ℃ in the whipping process, stirs 0.5-1h.
Coating provided by the invention through the optimization to composition etc., has been developed a kind of water-soluble chromium-free low-temp first and has been solidified marine climate resistant corrosion Al-Zn-Si alloy coating.This coating has characteristics such as environmental friendliness, condition is stable, the coating prepn energy consumption is low.
Water-soluble aluminum zinc silicon coating provided by the invention has been broken through the constraint that aluminum current zinc silicon coating mainly adopts hot-dipping method to prepare.Compare with technologies such as hot dips; The present invention is through adding sticker; Dispersion agent, organic solvents etc. are made metallic paint, can utilize methods such as spraying, brushing to form coating at workpiece surface; Preparation technology of coating temperature of the present invention low (200 ℃) has overcome technical barriers such as workpiece deformation that hot dip alloy coating technique temperature high (greater than 600 ℃) causes and mechanical property reduction; Can utilize methods such as spraying, brushing to form coating at workpiece surface, process method, equipment are simple, are suitable for large complicated part and handle, and have widened the range of application of coating.
Adopt coating of the present invention to make antiseptic engineering component and have many excellent properties, as: excellent solidity to corrosion, good scour resistance, and high heat/corrosion resistance is fabulous, even coating places under the hot conditions for a long time, its outward appearance can not change yet.Coatings prepared of the present invention and basal body binding force are strong, corrosion resistant performance is excellent, wear resisting property is good, long service life.Coating not only has stronger sticking power with metallic matrix in addition; Simultaneously bonding force is preferably also arranged with other various additional coatings; Just do not have inferior light silver gray attractive in appearance, can also become shades of colour by additional coatings, remedied the lower deficiency of self hardness in the prior art simultaneously.
Further through aluminium zinc silicon alloy is processed micron-sized powder; Corrosion-resistant, wear resistance, the anti-impact erosion ability of coating are greatly improved than hot dip aluminum plating zinc silicon coating and Aluminum Coating; Be applicable to that atmosphere is rainy, marine corrosive severe environment such as high temperature, many salt fogs and high wind stream, the corrosion-resistant means of defence of excellent combination property is provided for important engineering parts such as wind-powered electricity generation, boats and ships.
In sum; Coating that the marine climate resistant engineering component rotproofing of the present invention's exploitation is used and preparation method thereof; Solve pressing for of engineering component marine corrosion problem, in the corrosion engineering of industrial equipments such as oceanographic engineering and coastal waters wind-powered electricity generation, had important application prospects.
Embodiment
The water-soluble aluminum zinc silicon coating that the present invention provides a kind of marine climate resistant engineering component rotproofing to use, wherein said coating comprise aluminium zinc silicon alloy powder, organic solvent, nano-oxide particles toughener, deionized water, sticker, corrosion inhibitor, dispersion agent and thickening material.
Below; Associative list 1 provides some preferred embodiments of formulation for coating material proportioning according to the invention; But the content of each composition of the present invention is not limited to listed numerical value in this table; For a person skilled in the art, fully can be in table rationally summarize and reasoning on the basis of listed numerical range.
Table 1 formulation for coating material proportioning
Wherein, said aluminium zinc silicon alloy powder is made up of Al, Zn, Si, Mg, RE, below; Associative list 2 provides some preferred embodiments of each composition mass percent of aluminium zinc silicon alloy powder of the present invention; But the content of each composition of aluminium zinc silicon alloy powder of the present invention is not limited to listed numerical value in this table, and need to specify be, although listed the mass percent numerical value of relevant composition in the table 2; But these are not to describe as essential features; All be as preferred condition, all be in order providing in more detail, and be not to be to describe as prerequisite of the present invention about technical intelligence of the present invention.
Table 2: the mass percentage content (%) of each composition of aluminium zinc silicon alloy powder
Wherein, preferred, said organic solvent is a terepthaloyl moietie.
Preferably, said sticker is a boric acid fat coupling agent.
Preferably, said corrosion inhibitor is a boric acid.
Preferably, said thickening material is a Natvosol.
Preferably, said dispersion agent is the ZGK 5 dipropylene glycol monomethyl ether.
Preferably, said nano-oxide particles toughener is selected from Al
2O
3, SiO
2In one or both.
Preferred, wherein said Al
2O
3Median size be 15~60nm.
Preferred, wherein said SiO
2Median size be 25~70nm.
Preferred, wherein the nano-oxide particles toughener is Al
2O
3And SiO
2, and SiO
2And Al
2O
3Mass ratio is 1: (1~3), preferred, SiO wherein
2And Al
2O
3Ratio is 1: 2.
Preferably, the mean diameter of wherein said aluminium zinc silicon alloy powder is 10-200 μ m.
On the other hand, the present invention also provides a kind of technology for preparing the preparation of marine climate resistant engineering component rotproofing use feature of environmental protection water-soluble aluminum zinc silicon coating to be: by above-mentioned prescription, take by weighing quantitative corrosion inhibitor; Dissolve in the quantitative deionized water, add sticker then, dispersion agent; Organic solvent; Stirring makes it dissolving, under whipped state, slowly adds aluminium zinc silicon alloy powder and nano-oxide particles toughener, adds thickening material then; The temperature of control oil bath is 20-30 ℃ in the whipping process, stirs 0.5-1h.The experimental performance data:
Certain inshore wind power generating set vital part " joint bolt " (material 40CrNiMo), the former protective treatment of adopting routine only promptly produces significant corrosion after the several months.Adopt coating of the present invention to apply to form 20 μ m thick layers, the thick ZGK 5 of application 15 μ m again is illustrated in through the accelerated corrosion analog reslt that its main performance index that reaches is in the seawater splash(spray)zone environment:
Neutral salt spray corrosion life: greater than 1600 hours
300 ℃ of humidity resistances: 240 hours
Coating bonding force: 50N
The quick corrosion life of an ammonium nitrate: greater than 8 hours
Marine climate resistant corrosion life: greater than 20 years (short-time test)
Claims (9)
1. the coating used of marine climate resistant engineering component rotproofing; Wherein said coating comprises aluminium zinc silicon alloy powder, organic solvent, nano-oxide particles toughener, deionized water, sticker, corrosion inhibitor, dispersion agent and thickening material; Wherein said sticker is a boric acid fat coupling agent; Said corrosion inhibitor is a boric acid; Said dispersion agent is the ZGK 5 dipropylene glycol monomethyl ether; Wherein said formulation for coating material is with following proportioning: aluminium zinc silicon alloy powder: organic solvent: nano-oxide particles toughener: deionized water: sticker: corrosion inhibitor: dispersion agent: thickening material=30.0-50.0g: 10.0-25.0mL: 1.0-4.0g: 15.0-30.0mL: 2.0-5.0g: 1.0-3.0g: 0.1-2.0mL: 0.1-2.0g, wherein said aluminium zinc silicon alloy powder is made up of Al, Zn, Si, Mg, RE.
2. coating as claimed in claim 1, wherein said organic solvent are terepthaloyl moietie.
3. coating as claimed in claim 1, wherein said thickening material are Natvosol.
4. coating as claimed in claim 1, wherein said nano-oxide particles toughener is selected from Al
2O
3, SiO
2In one or both.
5. coating as claimed in claim 4, wherein said Al
2O
3Median size be 15~60nm, said SiO
2Median size be 25~70nm.
6. like claim 4 or 5 described coating, wherein the nano-oxide particles toughener is SiO
2And Al
2O
3, and SiO
2And Al
2O
3Mass ratio is 1: (1~3).
7. coating as claimed in claim 1, wherein said each composition mass percent of aluminium zinc silicon alloy powder is: Zn:35~58%, Si:0.3~4.0%, Mg:0.1~5.0%, RE:0.02~1.0%, surplus is Al and unavoidable impurities.
8. coating as claimed in claim 1, the mean diameter of wherein said aluminium zinc silicon alloy powder is 10-200 μ m.
9. a method for preparing the coating that the said marine climate resistant engineering component rotproofing of claim 1 uses wherein by above-mentioned prescription, takes by weighing quantitative corrosion inhibitor; Dissolve in the quantitative deionized water, add sticker then, dispersion agent; Organic solvent stirs and makes it dissolving, under whipped state, slowly adds aluminium zinc silicon alloy powder and nano-oxide particles toughener; Add thickening material then, the temperature of control oil bath is 20-30 ℃ in the whipping process, stirs 0.5-1h.