CN102134459B - Processing process of weft polyester shrunk adhesive band - Google Patents
Processing process of weft polyester shrunk adhesive band Download PDFInfo
- Publication number
- CN102134459B CN102134459B CN201010608339.1A CN201010608339A CN102134459B CN 102134459 B CN102134459 B CN 102134459B CN 201010608339 A CN201010608339 A CN 201010608339A CN 102134459 B CN102134459 B CN 102134459B
- Authority
- CN
- China
- Prior art keywords
- polyester
- band
- adhesive band
- weft
- adopts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a processing process for a weft polyester shrunk adhesive band. In the method, warps are 150 to 200D polyester yarns, wefts are 30 to70D polyester yarns, the warps and the wefts are woven plainly into a band-shaped product, the plainly-woven band-shaped product is impregnated with glue and baked, the impregnating material comprises components including 35 to 45 percent of epoxy resin, 45 to 60 percent of diluent and 0.5 to 2 percent of curing agent, and the baking temperature is 50 to 80 DEG C. The processing process has the advantages that: the curing temperature of the weft polyester shrunk adhesive band processed by the process is low (120 DEG C), and the curing time is short (6 to 12 hours); and when the weft polyester shrunk adhesive band is used for binding wire coils, the operation is convenient, hand sticking is avoided, energy is saved, environment is protected, production cost is low, labor intensity of operators is lowered, and the insulating performance and sealing performance of the wire coils bond by the weft polyester shrunk adhesive band are both improved greatly.
Description
Technical field
The present invention relates to a kind of complete processing that has the latitude polyester to shrink adhesive tape.
Background technology
In mutual inductor, the existing Binding material of transformer winding, tie up easily loose, impregnation series products inconvenient operation, sticking hand easily produces rubbish and substandard products, temperature requirement when products solidifying higher (150 ℃), grow (8～20 hours) set time, wastes energy and cost.
Summary of the invention
Technical problem to be solved by this invention is: a kind of complete processing that has the latitude polyester to shrink adhesive tape is provided.
In order to solve the problems of the technologies described above, the technical solution used in the present invention is: have the latitude polyester to shrink the complete processing of adhesive tape, comprise: warp thread adopts: 150～200D polyester dacron silk, weft yarn adopts: 30～70D POLYESTER YARNS plain weave product that becomes band, the band-type product that plain weave becomes is carried out impregnation, cured processing, and described impregnation material comprises following component: Resins, epoxy 35%～45%, thinner 45%～60%, solidifying agent 0.5%～2%; Described stoving temperature is 50～80 ℃.
In order to solve the problems of the technologies described above better, the further technical scheme that the present invention adopts is: described warp thread adopts: 200D polyester dacron silk, weft yarn adopts: the 40D POLYESTER YARNS, and described impregnation material comprises following component: Resins, epoxy 40%, thinner 59%, solidifying agent 1%; Described stoving temperature is 60 ℃.
In order to solve the problems of the technologies described above better, the further technical scheme that the present invention adopts is: described warp thread adopts: 150D polyester dacron silk, weft yarn adopts: the 50D POLYESTER YARNS, and described impregnation material comprises following component: Resins, epoxy 45%, thinner 53%, solidifying agent 2%; Described stoving temperature is 70 ℃.
Advantage of the present invention is: shrink adhesive tape by the above-mentioned processes latitude polyester that has out, solidification value low (120 ℃), lack set time (6～12 hours), can produce certain thermal contraction when being heated makes by lashings naturally fastening in the vertical, not loose, when solidifying, do not produced in the horizontal contraction by lashings, assurance is by the coverage effect of lashings, there is the latitude polyester to shrink the adhesion belt binding coil with above-mentioned, easy to operate, tack-free, energy-conservation, environmental protection, production cost is lower, has reduced operative employee's labour intensity, utilizes above-mentioned coil insulation performance and the sealing property that has the latitude polyester to shrink adhesion belt binding all to improve a lot.
Embodiment
Describe particular content of the present invention in detail below by specific embodiment.
Embodiment 1:
There is the latitude polyester to shrink the complete processing of adhesive tape, comprise: warp thread adopts: 200D polyester dacron silk, weft yarn adopts: the 40D POLYESTER YARNS plain weave product that becomes band, the band-type product that plain weave becomes is carried out impregnation, cured processing, and described impregnation material comprises following component: Resins, epoxy 40%, thinner 59%, solidifying agent 1%; Described stoving temperature is 60 ℃.
Embodiment 2:
There is the latitude polyester to shrink the complete processing of adhesive tape, comprise: warp thread adopts: 150D polyester dacron silk, weft yarn adopts: the 50D POLYESTER YARNS plain weave product that becomes band, the band-type product that plain weave becomes is carried out impregnation, cured processing, and described impregnation material comprises following component: Resins, epoxy 45%, thinner 53%, solidifying agent 2%; Described stoving temperature is 70 ℃.
Above-described embodiment is only for explanation the present invention's; and be not to be limitation of the present invention; the those of ordinary skill in relevant technologies field; in the situation that does not break away from the present invention's spirit and protection domain; can also make various variations and modification, so all technical schemes that are equal to also should belong to protection category of the present invention.
Claims (3)
1. there is the latitude polyester to shrink the complete processing of adhesive tape, it is characterized in that: comprising: warp thread adopts: 150～200D polyester dacron silk, weft yarn adopts: 30～70D POLYESTER YARNS plain weave product that becomes band, the band-type product that plain weave becomes is carried out impregnation, cured processing, described impregnation material comprises following component: Resins, epoxy 35%～45%, thinner 45%～60%, solidifying agent 0.5%～2%, all components sum are 100%; Described stoving temperature is 50～80 ℃.
2. according to the complete processing that has the latitude polyester to shrink adhesive tape claimed in claim 1, it is characterized in that: described warp thread adopts: 200D polyester dacron silk, weft yarn adopts: the 40D POLYESTER YARNS, and described impregnation material comprises following component: Resins, epoxy 40%, thinner 59%, solidifying agent 1%; Described stoving temperature is 60 ℃.
3. according to the complete processing that has the latitude polyester to shrink adhesive tape claimed in claim 1, it is characterized in that: described warp thread adopts: 150D polyester dacron silk, weft yarn adopts: the 50D POLYESTER YARNS, and described impregnation material comprises following component: Resins, epoxy 45%, thinner 53%, solidifying agent 2%; Described stoving temperature is 70 ℃.