CN102120845A - 光缆用聚乙烯护套料 - Google Patents
光缆用聚乙烯护套料 Download PDFInfo
- Publication number
- CN102120845A CN102120845A CN 201010504834 CN201010504834A CN102120845A CN 102120845 A CN102120845 A CN 102120845A CN 201010504834 CN201010504834 CN 201010504834 CN 201010504834 A CN201010504834 A CN 201010504834A CN 102120845 A CN102120845 A CN 102120845A
- Authority
- CN
- China
- Prior art keywords
- density polyethylene
- polyethylene resin
- sheath material
- optical cable
- medium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种聚乙烯护套料,尤其涉及一种光缆用聚乙烯护套料。它由高密度聚乙烯树脂、中密度聚乙烯树脂、线型低密度聚乙烯树脂、抗氧化剂加工助剂组成,经称量、混合、挤出、切粒、干燥、包装而成。
Description
技术领域
本发明涉及一种聚乙烯护套料,尤其涉及一种光缆用聚乙烯护套料。
背景技术
目前,随着我国经济建设的发展,通讯事业也日新月异的发生着变化,用于通讯光缆护套材料的质量要求越来越高,人们希望其有优良的耐候性、韧性、耐磨性和耐环境应力开裂性外,人们还希望同时能有良好的加工艺性及柔软性,生长出的光缆表面光滑平整,而现有生产的光缆用护套大都是高密度聚乙烯护套材料,其加工温度比较高,这就对生产光缆的设备提出了较高的要求,加工难度比较大,且生产的光缆硬度高,对于光缆的成盘比较困难。总之,现有的护套材料生产出的光缆产品不够理想,故现有的护套材料及其制备工艺有待于进一步的改进。
发明内容
为了解决上述弊端,本发明提供一种光缆用聚乙烯护套材料,它由高密度聚乙烯树脂、中密度聚乙烯树脂、低密度聚乙烯树脂、线型低密度聚乙烯树脂、抗氧化剂加工助剂组成,经称量、混合、挤出、切粒、干燥、包装而成,其特征在于它是由下述重量(kg)配比的原材料制备的光缆用护套材料:
高密度聚乙烯树脂 35-55 抗氧化剂 0.1-0.5
中密度聚乙烯树脂 5-15 加工助剂 0.05--0.2
线型低密度聚乙烯树脂 35-50 碳黑母粒 4.8-5.6。
其中,所述的聚乙烯护套材料,其特征还在于:它是优选下述重量(kg)配比的原材料制备的护套材料:
高密度聚乙烯树脂 42.5 抗氧化剂 0.2
中密度聚乙烯树脂 9 加工助剂 0.1
线型低密度聚乙烯树脂 43 碳黑母粒 5.2。
具体实施方式
以下结合实掩例进一步说明本发明
实施例
①商购并称量下述重量(1c9)配比的原材料
高密度聚乙烯树脂 42.5 抗氧化剂0.2
中密度聚乙烯树脂 9 加工助剂0.1
线型低密度聚乙烯树脂 43 碳黑母粒5.2。
②将上述原材料混合均匀,备用@用双螺杆挤出机挤出备用混合材料,其螺杆转速为240-280转/分
③切粒,其颗粒大小切成巾3mm的圆粒,
④用干燥机干燥,即得100K9本发明的光缆用聚乙烯护套材料。又名为光缆
用中密度聚乙烯护套材料。
本发明的光缆用聚乙烯护套材料,经对试制的护套材料进行性能测试,其各项性能均能符合Q/HFT001-1997标准的要求。
在光缆厂光纤光缆护套线上对该护套材料进行了工艺试验,主要情况如下:
①加工温度机筒温度:150-250″C机头温度:200-230℃滤网:so-120目
②护套材材料塑化均匀,挤出加工性能较好
③挤出的护套表面光滑、圜整,无杂志及其它缺陷,护套表面质量符合工艺要求,
④护套火花检验无击穿点。
本发明不限于上述实施例,在本发明的构思范围内,根据上述说明书的描述,本领域的普通技术人员还可作出一些显而易见的改变,但这些改变均应落入本发明权利要求的保护范围之内。
Claims (2)
1.一种光缆用聚乙烯护套料,它由高密度聚乙烯树脂、中密度聚乙烯树脂、低密度聚乙烯树脂、线型低密度聚乙烯树脂、抗氧化剂加工助剂组成,经称量、混合、挤出、切粒、干燥、包装而成,其特征在于它是由下述重量(kg)配比的原材料制备的光缆用护套材料:
高密度聚乙烯树脂 35-55
抗氧化剂 0.1-0.5
中密度聚乙烯树脂 5-15
加工助剂 0.05--0.2
线型低密度聚乙烯树脂 35-50
碳黑母粒 4.8-5.6。
2.如权利要求1所述的聚乙烯护套料,其特征还在于:它是优选下述重量(kg)配比的原材料制备的护套材料:
高密度聚乙烯树脂 42.5
抗氧化剂 0.2
中密度聚乙烯树脂 9
加工助剂 0.1
线型低密度聚乙烯树脂 43
碳黑母粒 5.2。