CN102108169A - Automatic temperature controlling cable resin composition and preparation method thereof - Google Patents

Automatic temperature controlling cable resin composition and preparation method thereof Download PDF

Info

Publication number
CN102108169A
CN102108169A CN 201110033091 CN201110033091A CN102108169A CN 102108169 A CN102108169 A CN 102108169A CN 201110033091 CN201110033091 CN 201110033091 CN 201110033091 A CN201110033091 A CN 201110033091A CN 102108169 A CN102108169 A CN 102108169A
Authority
CN
China
Prior art keywords
percent
resin composition
automatic temperature
temperature control
control cable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201110033091
Other languages
Chinese (zh)
Other versions
CN102108169B (en
Inventor
周洪良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGYIN SOUTHERN GRANULATION FACTORY CO Ltd
Original Assignee
JIANGYIN SOUTHERN GRANULATION FACTORY CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGYIN SOUTHERN GRANULATION FACTORY CO Ltd filed Critical JIANGYIN SOUTHERN GRANULATION FACTORY CO Ltd
Priority to CN201110033091A priority Critical patent/CN102108169B/en
Publication of CN102108169A publication Critical patent/CN102108169A/en
Application granted granted Critical
Publication of CN102108169B publication Critical patent/CN102108169B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to an automatic temperature controlling cable resin composition. The composition comprises the following main components in percentage by weight: 85 to 90 percent of modified polyvinyl chloride (PVC), 5 to 10 percent of PVC stabilizer, 3 to 8 percent of filler, 0.2 to 0.5 percent of BaTiO3, 0.1 to 0.2 percent of SrTiO3, 0.1 to 0.3 percent of Y2O3, 0.1 to 0.3 percent of Nb2O5, 0.2 to 0.4 percent of SiO2, 0.1 to 0.2 percent of MnO2, 0.1 to 0.3 percent of Yb2O3 and 0.2 to 0.4 percent of Tu2O3. The invention also relates to a preparation method of the automatic temperature controlling cable resin composition. The automatic temperature controlling cable resin composition has the advantages of high positive temperature coefficient (PTC) strength, high temperature control performance, energy conservation, environmental friendliness, low fluctuation of self limit temperature and the like and is convenient to use.

Description

A kind of automatic temperature control cable material resin composition and preparation method thereof
Technical field
The present invention relates to a kind of cable material resin composition, relate in particular to a kind of automatic temperature control cable material resin composition and preparation method thereof with ptc characteristics.
Background technology
So-called PTC (Positive temperature coefficient) characteristic, i.e. positive temperature coefficient of resistance characteristic, along with temperature rises, heating element resistance increases, thus the outward current size is regulated in restriction or cut off electric current automatically, and temperature is kept constant.The heating cables of being made by the resin with this specific character is referred to as temperature automatically controlled type heating cables.
Present automatic temperature control cable resin combination is a matrix with crystalline macromolecular compound generally, conducting particless such as a large amount of blending carbon blacks, graphite and metal powder, the temperature automatically controlled type heating cables of making by this resin combination, in successive energising or power on/off circulation, because resistance raises, surface temperature descends very big.This is that the difference of polarity and thermal expansion between macromolecule matrix and conduction current carrier causes carbon black particle displacement and reunion on the one hand, has produced to be separated and to cause; Be that the adaptation difference causes between heating element and electrode on the other hand.It is low that carbon black, the graphite of while in the automatic temperature control cable resin combination has PTC intensity, the shortcoming of temperature-control performance difference; Chinese patent CN101608044 discloses a kind of automatic temperature control cable material resin composition and preparation method thereof, and its main ingredient and weight percent are: modified PVC 85~90, PVC stablizer 5~10, filler 1~5, BaTiO 30.1~0.3, SrTiO 30.1~0.2, Y 2O 30.1~0.3, Nb 2O 50.1~0.3, SiO 50.1~0.2, MnO 20.1~0.2; Certainly the fluctuation of limitting temperature of the temperature automatically controlled type heating cables that the automatic temperature control cable material resin composition of this patent is made is ± 10 ℃.
Summary of the invention
At above-mentioned shortcoming, the object of the present invention is to provide a kind of PTC intensity height, good temperature-control performance, limit the little automatic temperature control cable material resin composition of fluctuation of temperature certainly.
Technology contents of the present invention is, a kind of automatic temperature control cable material resin composition, and its main ingredient and weight percent are as follows:
Modified PVC 85~90
PVC stablizer 5~10
Filler 3~8
BaTiO 3 0.2~0.5
SrTiO 3 0.1~0.2
Y 2O 3 0.1~0.3
Nb 2O 5 0.1~0.3
SiO 2 0.2~0.4
MnO 2 0.1~0.2
Yb 2O 3 0.1~0.3
Tu 2O 3 0.2~0.4。
BaTiO in above-mentioned automatic temperature control cable material resin composition 3, SrTiO 3, Y 2O 3, Nb 2O 5, SiO 2, MnO 2, Yb 2O 3And Tu 2O 3Fineness be 1500~2000 orders.
Filler is this area pearl filler commonly used in above-mentioned automatic temperature control cable material resin composition, and the PVC stablizer is this area barium zinc stabilizer commonly used.
Another object of the present invention is to provide the preparation method of above-mentioned automatic temperature control cable material resin composition.
A kind of preparation method of automatic temperature control cable material resin composition, its step is as follows:
(1), each material is put into high-speed mixer as following weight percent:
Modified PVC 85~90, PVC stablizer 5~10, filler 3~8, BaTiO 30.2~0.5, SrTiO 30.1~0.2, Y 2O 30.1~0.3, Nb 2O 50.1~0.3, SiO 20.2~0.4, MnO 20.1~0.2, Yb 2O 30.1~0.3,
Tu 2O 3 0.2~0.4;
(2), above-mentioned material heated in high-speed mixer mixed 20~40 minutes, Heating temperature is 90~110 ℃;
(3), mixed material in the step (2) is promptly got automatic temperature control cable material resin composition by the tablets press extruding pelletization.
The advantage that the present invention compared with prior art has is: do not contain carbon black or graphite in the automatic temperature control cable material resin composition of the present invention, its PTC intensity height, good temperature-control performance and easy to use, energy-conserving and environment-protective thus, the fluctuation of limitting temperature certainly of the temperature automatically controlled type heating cables of making is ± 4 ℃.
Embodiment
In following routine embodiment, modified PVC is the WS1300 modified PVC that ShanghaiChlorine and Alkali Chemical Co Ltd produces, the PVC stablizer is the GZ-589BZ barium zinc stabilizer of Xiamen City with Allianz auspicious chemical industry company limited, and pearl filler is 1500 purpose water-ground limestones for the fineness that Omya company limited produces.
Example 1, with 88Kg modified PVC, 7Kg PVC stablizer, 3Kg pearl filler, 0.4Kg BaTiO 3, 0.15Kg SrTiO 3, 0.2Kg Y 2O 3, 0.3Kg Nb 2O 5, 0.3Kg SiO 2, 0.15Kg MnO 2, 0.2Kg Yb 2O 3, 0.3Kg Tu 2O 3Put into the high-speed mixer heating and mixed 30 minutes, Heating temperature is 105 ℃; BaTiO 3, SrTiO 3, Y 2O 3, Nb 2O 5, SiO 2, MnO 2, Yb 2O 3, and Tu 2O 3Fineness be 2000 orders; Mixed material promptly gets automatic temperature control cable material resin composition by the tablets press extruding pelletization.Automatic temperature control cable material resin composition is used for heating cables production, makes temperature automatically controlled type heating cables, the temperature of limit certainly of this heating cables is 86 ± 4 ℃.
Example 2, with 88Kg modified PVC, 6Kg PVC stablizer, 4Kg pearl filler, 0.5Kg BaTiO 3, 0.2Kg SrTiO 3, 0.2Kg Y 2O 3, 0.2Kg Nb 2O 5, 0.3Kg SiO 2, 0.1Kg MnO 2, 0.3Kg Yb 2O 3, 0.2Kg Tu 2O 3Put into the high-speed mixer heating and mixed 30 minutes, Heating temperature is 105 ℃; BaTiO 3, SrTiO 3, Y 2O 3, Nb 2O 5, SiO 2, MnO 2, Yb 2O 3, and Tu 2O 3Fineness be 2000 orders; Mixed material promptly gets automatic temperature control cable material resin composition by the tablets press extruding pelletization.Automatic temperature control cable material resin composition is used for heating cables production, makes temperature automatically controlled type heating cables, the temperature of limit certainly of this heating cables is 65 ± 4 ℃.

Claims (3)

1. automatic temperature control cable material resin composition, its main ingredient and weight percent are as follows:
Modified PVC 85~90
PVC stablizer 5~10
Filler 3~8
BaTiO 3 0.2~0.5
SrTiO 3 0.1~0.2
Y 2O 3 0.1~0.3
Nb 2O 5 0.1~0.3
SiO 2 0.2~0.4
MnO 2 0.1~0.2
Yb 2O 3 0.1~0.3
Tu 2O 3 0.2~0.4。
2. automatic temperature control cable material resin composition according to claim 1 is characterized in that BaTiO 3, SrTiO 3, Y 2O 3, Nb 2O 5, SiO 2, MnO 2, Yb 2O 3And Tu 2O 3Fineness be 1500~2000 orders.
3. the preparation method of automatic temperature control cable material resin composition according to claim 1, its step is as follows:
(1), each material is put into high-speed mixer as following weight percent:
Modified PVC 85~90, PVC stablizer 5~10, filler 3~8, BaTiO 30.2~0.5, SrTiO 30.1~0.2, Y 2O 30.1~0.3, Nb 2O 50.1~0.3, SiO 20.2~0.4, MnO 20.1~0.2, Yb 2O 30.1~0.3,
Tu 2O 3 0.2~0.4;
(2), above-mentioned material heated in high-speed mixer mixed 20~40 minutes, Heating temperature is 90~110 ℃;
(3), mixed material in the step (2) is promptly got automatic temperature control cable material resin composition by the tablets press extruding pelletization.
CN201110033091A 2011-01-31 2011-01-31 Automatic temperature controlling cable resin composition and preparation method thereof Expired - Fee Related CN102108169B (en)