No shuttle glass fibre plain edge cloth fold method
Technical field
The invention belongs to the glass fabric textile technology field, what relate generally to is a kind of no shuttle glass fibre plain edge cloth fold method.
Background technology
At present, with its fabric width both sides of the woven glass fabric of shuttleless loom the burr greater than 0.5cm are arranged respectively, these burr bring certain operation easier (user who has even refusal use) not only can for user's use, but also can cause unnecessary waste.Therefore, the burr problem has restricted being widely used of no shuttle glass fabric.The burr problem that can the plain edge invagination method in the cotton spinning used for reference solve glass fabric is the direction that we study always; Because cotton fiber is flexible; The side shoring device of selvedge setting can not only play supporting role preferably, and can not produce temple mark to selvedge.Organize on the limit of existing cotton spinning cloth is to adopt plain weave basically, the fabric that utilizes the close and firm of getting in touch between the plain weave yarn to form is stiff satisfy tuck-in selvage through the limit yarn opening clear, the needs that latitude limit yarn folds into.Its plain edge folds into technology: distribute through yarn process: slitter edge yarn, invagination fabric tissue warp thread, fabric tissue footpath yarn.Weaving process: opening → wefting insertion, the invagination → beat up → warp let-off → batch.Warp thread is gaited, reed-in method: the slitter edge yarn, and each 18 on cloth width of cloth both sides, leno edge machine is worn in each two of front and back, middle 14 orders of gaiting: 1,2; Fold into the fabric tissue warp thread: 40 warp thread plain weaves, the order 1,2 of gaiting.Reed-in method: 2 warp thread of each dent; Fabric tissue footpath yarn: the order 3,4,5,6 of gaiting; Denting: 2 warp thread of every dent.The plain edge that uses the method to fold into is plain weave, and needs side shoring device and leno edge machine.
The plain edge that above-mentioned plain edge invagination technology is applied directly to glass fabric folds in the technology obviously to be infeasible, because glass fibre does not have elasticity, to wear no resistance that the employing side shoring device not only can produce temple mark, and the easy fluffing of warp thread fractures.In addition, tuck-in selvage partly is a plain weave, can not satisfy the requirement of glass fabric to its warp-wise power, broadwise power and thickness outward appearance, therefore can not solve the burr problem of glass fabric.
Summary of the invention
The objective of the invention is to propose a kind of no shuttle glass fabric plain edge fold method.Solve the burr problem on existing no shuttle glass fabric fabric width both sides, make the plain edge of invagination reach quality requirement, avoid waste, enhance productivity, widen the Application Areas of no shuttle glass fabric.
Realize that the technical scheme that above-mentioned purpose is taked is: the fell position at no shuttle glass fiber loom is provided with cloth supporting plate, and the both sides end of this cloth supporting plate all has the effect that picking-up and double cloth temple are played in acclivitous inclination angle; The flanging glass fiber yarn on glass fabric both sides partly adopts and changes brokentwlllweave fabric weaving technology.
The present invention is directed to the characteristic of glass fibre and the characteristics of glass fabric; Through improving the structure of cloth supporting plate, make it both play the effect of picking-up and double cloth temple at the fell place, stop temple mark; And the limit warp yarn friction is reduced; End breakage descends, and running rate improves, and output, quality all have raising.Need not leno edge machine, side shoring device makes apparatus structure simple, and the operating space is big when handling the limit yarn, and efficient improves.Maintenance of equipment is easy to maintenance, has practiced thrift maintenance time, has improved efficiency.Because the glass fiber yarn of flanging part adopts and changes brokentwlllweave fabric weaving technology; Fold into cloth surface evenness, thickness, the mellowness uniformity of whole cloth behind the 2cm weft yarn like this; Not having the edge tracking view picture is one; Woven glass fabric does not have burr, and the outward appearance of cloth cover has no fault (temple mark, weft bow limit bad etc.), reaches the processing quality requirement.Partly through the ingenious design of denting, without leno edge machine strand limit, weft tension can reach effective control to the slitter edge yarn, and weft yarn is effectively cut off to satisfy on time and folded into length and tension force requirement.
Description of drawings
Fig. 1 is a structural representation of the present invention.
Fig. 2 is the vertical view of Fig. 1.
Fig. 3 is 26 drafting plans of limit of the present invention yarn.
Fig. 4 is 4 drafting plans in the limit of the present invention.
Fig. 5 is a reed draft of the present invention.
Among the figure: 1, cloth supporting plate, 2, the inclination angle.
The specific embodiment
In conjunction with accompanying drawing, it is following to provide embodiments of the invention: but the present invention does not limit to following examples.
No shuttle glass fabric plain edge fold method of the present invention is at the fell position of existing no shuttle glass fiber loom cloth supporting plate 1 to be set; The both sides end of this cloth supporting plate 1 all has the effect that picking-up and double cloth temple are played in acclivitous inclination angle 2, inclination angle 10-30 degree (shown in Fig. 1-2).
The weaving of glass fabric still is traditional textile technology, and flanging (plain edge) part on glass fabric cloth width of cloth both sides adopts and changes brokentwlllweave fabric weaving technology.Said flanging (plain edge) glass fiber yarn respectively is 30.Confirm that because be less than 30 glass fiber yarns, burr can not fold into the cloth width of cloth for the selection of flanging glass fiber yarn quantity after through repetition test, can not reach and fold into the effect that burr are realized plain edge cloth.And can cause unnecessary waste more than 30 glass fiber yarns, and therefore, finally confirm as 30 glass fiber yarns, fold into cloth surface evenness, thickness, the mellowness uniformity of whole cloth behind the 2cm weft yarn like this, not having the edge tracking view picture is one.
Following conduplication side (plain edge) the part wherein technology (technology on both sides is just the same) of 30 glass fiber yarns on one side specifies as follows:
Distribute through yarn process: slitter edge yarn, fabric tissue warp-wise yarn
Weaving process: opening → wefting insertion, the invagination → beat up → warp let-off → batch
Fig. 3-4 is depicted as glass fabric cloth width of cloth both sides and folds into the gaiting of part, reed-in method: each 30 glass fiber yarn of glass fabric cloth width of cloth both sides are for folding into part; Wherein each 20 six roots of sensation limit yarn is the brokentwlllweave order of gaiting: 3,4,5,6, and each four orders of gaiting on limit are 1,2; Reed-in method: single, double warp thread circulation is worn.
Shown in Figure 5ly be the gaiting of glass fabric cloth width of cloth both sides slitter edge yarn, reed-in method: each 14 slitter edge yarn of both sides order 1,2 of gaiting; Denting: each dent penetrates warp thread radical 22020202022 successively.