CN102091348A - Porous beta-calcium phosphate biological scaffold material and preparation method thereof - Google Patents
Porous beta-calcium phosphate biological scaffold material and preparation method thereof Download PDFInfo
- Publication number
- CN102091348A CN102091348A CN201110030831XA CN201110030831A CN102091348A CN 102091348 A CN102091348 A CN 102091348A CN 201110030831X A CN201110030831X A CN 201110030831XA CN 201110030831 A CN201110030831 A CN 201110030831A CN 102091348 A CN102091348 A CN 102091348A
- Authority
- CN
- China
- Prior art keywords
- calcium phosphate
- beta
- preparation
- porous beta
- bracket material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a porous beta-calcium phosphate biological scaffold material and a preparation method thereof. The invention adopts a technical scheme that: uniformly mixing CaCO3 and NH3H2PO4 according to a molar ratio of (1.3-1.8):1, performing machine molding under a pressure of 50 to 200MPa, and drying the molded blank body at 100 to 120 DEG C for 16 to 48 hours; and performing heat preservation for 1 to 8 hours at 900 to 1,200 DEG C to obtain the porous beta-calcium phosphate biological scaffold material. In the invention, the process is simple, the porous structure is controllable, the pressure strength of the product is 2 to 15MPa, the porosity is 35 to 75 percent and the aperture size of the pores is 20 to 150 mu m; therefore, more open pores are available, the pressure strength is high, and the purity of the beta-calcium phosphate phase is high. These pores are favorable for cells, fiber tissues, blood vessel tissues and other organic tissues to grow in, and the material is easy to degrade and can be used as repair materials for defected hard tissues of human bodies and used as a scaffold material for bone tissue engineering, and can also be used as a dental repair material.
Description
Technical field
The invention belongs to the biologic bracket material technical field.Be specifically related to a kind of porous beta-calcium phosphate biologic bracket material and preparation method thereof.Be mainly used in the timbering material in bone defect repair and the organizational project, also can be used as the tooth dental repair material.
Background technology
Biologic bracket material is one of three key factors in the organizational project as the extracellular matrix of seed cell, the new organization framework that forms, and its character directly influences biological characteristicses such as the absorption, propagation, differentiation of seed cell, finally influences tissue construction.Ideal tissue engineering bracket material is answered form, structure, the function of simulated tissue, better biocompatibility is arranged, degradable, also should have certain intensity and loose structure, because suitable aperture, porosity and bigger area-volume ratio, help cell adhesion, propagation, differentiation, for the cell growth provides enough spaces.Beta-calcium phosphate has better biocompatibility, is degradable biomaterial, and good biomechanical property is also arranged, and is suitable for doing the biologic bracket material in the organizational project.
The preparation of traditional beta-calcium phosphate powder has wet method, dry method and hydro-thermal method.Wet method comprises two kinds: a kind of is acid, aqueous slkali direct reaction, promptly at ambient temperature certain density phosphoric acid is added dropwise to Ca (OH)
2In the suspension, staticly settle after-filtration, get the former powder of beta-calcium phosphate; Another kind is soluble calcium salt and phosphate reaction, generally is with certain density (NH under room temperature and stirring condition
4)
2HPO
4Aqueous solution is added drop-wise to Ca (NO by certain speed
3)
2In the solution, through ageing, filtration washing, drying, be sintered into the beta-calcium phosphate powder.Hydro-thermal method is used less, generally is under hydrothermal condition, and the control temperature and pressure is with CaHPO
4Or CaHPO
42H
2O is that raw material makes calcium phosphate powder; Dry method is under hot conditions (>900 ℃), with CaHPO
42H
2O and CaCO
3Or Ca (OH)
2Solid state reaction takes place prepare the higher beta-calcium phosphate powder of purity.
The beta-calcium phosphate experiment condition complexity of traditional wet method and Hydrothermal Preparation, troublesome poeration, and the just powder that obtains need be reconfigured, and loose structure should not be controlled, and intensity is not high yet; And to add some bonding agent and porogen during traditional dry process, and often there is dephasign to exist, the purity of beta-calcium phosphate image is not high.
Summary of the invention
The present invention is intended to overcome the prior art defective, and purpose provides the preparation method of the porous beta-calcium phosphate biologic bracket material that a kind of processing technology is simple, air hole structure is controlled; Porous beta-calcium phosphate biologic bracket material open pore purity many, that have certain intensity and beta-calcium phosphate image with this method preparation are higher.
For achieving the above object, the technical solution used in the present invention is: earlier with CaCO
3And NH
4H
2PO
4Be in molar ratio (1.3~1.8): 1 mix homogeneously, be mechanical pressing under 50~200MPa condition at pressure again, base substrate after the molding under 100~120 ℃ of conditions dry 16~48 hours, then under 900~1500 ℃ of conditions, be incubated 1~8 hour and burn till, promptly get the porous beta-calcium phosphate biologic bracket material.
In the technique scheme: CaCO
3Particle diameter be 40nm~25 μ m, CaCO
3Purity>99wt%; NH
4H
2PO
4Particle diameter be 88 μ m~200 μ m, NH
4H
2PO
4Purity>99wt%.
Owing to adopt technique scheme, the simple gas of processing technology of the present invention, Controlled Pore Structure (being that aperture size size and voidage can be controlled by granularity, briquetting pressure and the sintering temperature of raw material); Adopt the porous beta-calcium phosphate biologic bracket material open pore of method of the present invention preparation many, have certain intensity, main thing is beta-calcium phosphate mutually.After testing: the compressive resistance of this biologic bracket material is 2~15MPa, porosity is 35~75%, the air vent aperture size is between 20~150 μ m, these pores help growing into of cell, fibrous tissue, vascular tissue and other organic organization, be easy to degraded, can be used as the timbering material that damaged repair materials of human body hard tissue and bone tissue engineer are used, also can be used as the tooth dental repair material.
Therefore, preparation technology of the present invention is simple, and air hole structure is controlled; Prepared porous beta-calcium phosphate biologic bracket material open pore is many, compressive resistance is higher and the purity of beta-calcium phosphate image is higher.Can be used as the timbering material that damaged repair materials of human body hard tissue and bone tissue engineer are used, also can be used as the tooth dental repair material.
The specific embodiment
The present invention will be further described below in conjunction with the specific embodiment, is not the restriction to its protection domain.
In this specific embodiment: CaCO
3Purity>99wt%; NH
4H
2PO
4Purity>99wt%.Repeat no more in following examples.
Embodiment 1
A kind of porous beta-calcium phosphate biologic bracket material and preparation method thereof: be the CaCO of 1 μ m~25 μ m with particle diameter earlier
3NH with 200 μ m~160 μ m
4H
2PO
4Be in molar ratio (1.3~1.5): 1 mix homogeneously, be mechanical pressing under 50~100MPa condition at pressure again, base substrate after the molding under 100~110 ℃ of conditions dry 16~24 hours, then under 900~1100 ℃ of conditions, be incubated 1~3 hour and burn till, promptly get the porous beta-calcium phosphate biologic bracket material.
Adopt said method, can obtain thing is that 20~90 μ m, porosity are 55~75% and to burn the back compressive resistance be the porous beta-calcium phosphate biologic bracket material of 2~5Mpa for beta-calcium phosphate, aperture size mutually.
Embodiment 2
A kind of porous beta-calcium phosphate biologic bracket material and preparation method thereof: be the CaCO of 500nm~1 μ m with particle diameter earlier
3NH with 120 μ m~160 μ m
4H
2PO
4(1.5~1.6) in molar ratio: 1 mix homogeneously, be mechanical pressing under 100~150MPa condition at pressure again, base substrate after the molding under 110~115 ℃ of conditions dry 24~36 hours, then under 1100~1300 ℃ of conditions, be incubated 3~5 hours and burn till, promptly get the porous beta-calcium phosphate biologic bracket material.
Adopt said method, can obtain thing is that 30~120 μ m, porosity are 45~70% and to burn the back compressive resistance be the porous beta-calcium phosphate biologic bracket material of 3~8Mpa for beta-calcium phosphate, aperture size mutually.
Embodiment 3
A kind of porous beta-calcium phosphate biologic bracket material and preparation method thereof: be the CaCO of 40nm~500nm with particle diameter earlier
3NH with 88 μ m~120 μ m
4H
2PO
4Be in molar ratio (1.6~1.8): 1 mix homogeneously, mechanical pressing under the 150~200MPa condition of pressure position again, base substrate after the molding under 115~120 ℃ of conditions dry 36~48 hours, then under 1300~1500 ℃ of conditions, be incubated 5~8 hours and burn till, promptly get the porous beta-calcium phosphate biologic bracket material.
Adopt said method, can obtain thing is that 50~150 μ m, porosity are 35~60% and to burn the back compressive resistance be the porous beta-calcium phosphate biologic bracket material of 5~15Mpa for beta-calcium phosphate, aperture size mutually.
The technology of this specific embodiment is simple, air hole structure is controlled (being that aperture size size and voidage can be controlled by granularity, briquetting pressure and the sintering temperature of raw material); Prepared porous beta-calcium phosphate biologic bracket material open pore is many, have certain intensity, main thing is beta-calcium phosphate mutually.After testing: the compressive resistance of this biologic bracket material is 2~15MPa, porosity is 35~75%, the air vent aperture size is between 20~150 μ m, these pores help growing into of cell, fibrous tissue, vascular tissue and other organic organization, be easy to degraded, can be used as the timbering material that damaged repair materials of human body hard tissue and bone tissue engineer are used, also can be used as the tooth dental repair material.
Therefore, this specific embodiment technology is simple, and air hole structure is controlled; Prepared porous beta-calcium phosphate biologic bracket material open pore is many, compressive resistance is higher and the purity of beta-calcium phosphate image is higher.Can be used as the timbering material that damaged repair materials of human body hard tissue and bone tissue engineer are used, also can be used as the tooth dental repair material.
Claims (4)
1. the preparation method of a porous beta-calcium phosphate biologic bracket material is characterized in that earlier CaCO
3And NH
4H
2PO
4Be in molar ratio (1.3~1.8): 1 mix homogeneously, be mechanical pressing under 50~200MPa condition at pressure again, base substrate after the molding under 100~120 ℃ of conditions dry 16~48 hours, then under 900~1500 ℃ of conditions, be incubated 1~8 hour and burn till, promptly get the porous beta-calcium phosphate biologic bracket material.
2. the preparation method of porous beta-calcium phosphate biologic bracket material according to claim 1 is characterized in that described CaCO
3Particle diameter be 40nm~25 μ m, CaCO
3Purity>99wt%.
3. the preparation method of porous beta-calcium phosphate biologic bracket material according to claim 1 is characterized in that described NH
4H
2PO
4Particle diameter be 88 μ m~200 μ m, NH
4H
2PO
4Purity>99wt%.
4. according to the prepared porous beta-calcium phosphate biologic bracket material of preparation method of each described porous beta-calcium phosphate biologic bracket material in the claim 1~3.