CN102079939A - Water-based environment-friendly insulating paint and preparation method thereof - Google Patents
Water-based environment-friendly insulating paint and preparation method thereof Download PDFInfo
- Publication number
- CN102079939A CN102079939A CN 201010503223 CN201010503223A CN102079939A CN 102079939 A CN102079939 A CN 102079939A CN 201010503223 CN201010503223 CN 201010503223 CN 201010503223 A CN201010503223 A CN 201010503223A CN 102079939 A CN102079939 A CN 102079939A
- Authority
- CN
- China
- Prior art keywords
- aqueous
- base material
- water
- wetting agent
- material wetting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a water-based environment-friendly insulating paint, which consists of 30 to 70 percent of waterborne alkyd resin, 1 to 2 percent of base material wetting agent, 8 to 10 percent of aqueous dispersing agent, and 20 to 25 percent of water-based crosslinking agent. A preparation method comprises the following steps of: mixing the waterborne alkyd resin with the aqueous dispersing agent, and reducing the temperature to 60+/-5DEG C; adding the water-based crosslinking agent, the base material wetting agent and water in turn; and quickly stirring until a uniform state is achieved. The raw materials are low in price, environment-friendly, wide in application range and harmless to a human body in the preparing and using processes; and in the preparing process, the process is easy to control, the process time is short, energy is saved, and the produced finished product has excellent performance, and can be regulated according to actual requirements of customers to meet the requirements of the customers.
Description
Technical field
The present invention relates to a kind of insullac, especially a kind of aqueous, environmental protective insullac and preparation method thereof.
Background technology
Traditional insullac is generally solvent-free or solvent paint, the cost height, in the use, mostly adopt and contain a large amount of toluene, dimethylbenzene, vinylbenzene, solvent wet goods and make solvent and thinner, these volatile organic matters (VOC) all have toxicity and inflammable and explosive property usually, in construction, drying process, directly enter atmosphere, not only cause environmental pollution, also HUMAN HEALTH is produced very big harm.
Summary of the invention
At the weak point that exists in the problems referred to above, the invention provides that a kind of prices of raw and semifnished materials are cheap, environmental protection, produce with use in can not produce injury, aqueous, environmental protective insullac that use range is wider and preparation method thereof to human body.
For achieving the above object, the invention provides a kind of aqueous, environmental protective insullac, be made up of aqueous alkide resin, base material wetting agent, aqueous dispersant, water cross-linking agent and water, the ratio range of above-mentioned raw materials is as follows: aqueous alkide resin 30～70%, base material wetting agent 1～2%, aqueous dispersant 8～10%, water cross-linking agent 20～25%.
Described aqueous alkide resin is formed after being prepared by linolenic acid 40g, TriMethylolPropane(TMP) 40g, Tetra hydro Phthalic anhydride 30g, neopentyl glycol 3g, TMA 12g and butyl carbitol 40g.
The model of described aqueous dispersant is AMP95; The model of described water cross-linking agent is 303LF; The model of described base material wetting agent is AR420.
The present invention also provides a kind of preparation method of aqueous, environmental protective insullac simultaneously, earlier aqueous alkide resin is mixed with aqueous dispersant, be cooled to 60 ℃ ± 5 ℃, add water cross-linking agent, base material wetting agent and water more successively after inciting somebody to action, stir until the homogeneous state fast then.
Between described water cross-linking agent and described base material wetting agent, can also add melamine resin.
Compared with prior art, the present invention has the following advantages:
The invention provides a kind of aqueous, environmental protective insullac, form by aqueous alkide resin, base material wetting agent, aqueous dispersant, water cross-linking agent and water, wherein, aqueous alkide resin is 30～70%, the base material wetting agent is 1～2%, aqueous dispersant is 8～10%, water cross-linking agent is 20～25%.Its preparation method is earlier aqueous alkide resin to be mixed with aqueous dispersant, is cooled to 60 ℃ ± 5 ℃, will after add water cross-linking agent, base material wetting agent and water more successively, quick then stirring is until the homogeneous state.Cheap, the environmental protection of the prices of raw and semifnished materials used among the present invention, use range is wider, in preparation and use human body is not all had injury; In preparation process, technology is more easy to control, and the process time is shorter, and energy efficient, but the end properties excellence of producing can be adjusted product according to client's actual needs, thereby reach requirement of client.
Embodiment
The invention provides a kind of aqueous, environmental protective insullac, be made up of aqueous alkide resin, base material wetting agent, aqueous dispersant, water cross-linking agent and an amount of water, the ratio range of above-mentioned raw materials is as follows: aqueous alkide resin 30～70%, base material wetting agent 1～2%, aqueous dispersant 8～10%, water cross-linking agent 20～25%.The model of aqueous dispersant is AMP95; The model of water cross-linking agent is 303LF; The model of base material wetting agent is AR420.
Aqueous alkide resin is formed after being prepared by linolenic acid 40g, TriMethylolPropane(TMP) 40g, Tetra hydro Phthalic anhydride 30g, neopentyl glycol 3g, TMA 12g and butyl carbitol 40g.Its preparation method is to add linolenic acid 40g, TriMethylolPropane(TMP) 40g, Tetra hydro Phthalic anhydride 30g, neopentyl glycol 3g, TMA 12g in the normal temperature input and under stirring, be warming up to 250 ℃ ± 5 ℃ then, recycling effluent, control viscosity increases, treat that water outlet reaches about 80% of theoretical value, cool to 240 ℃ ± 5 ℃, control viscosity increases; Add butyl carbitol 40g when temperature is reduced to 70 ℃ ± 5 ℃, stir 30min, just obtained needed aqueous alkide resin, this aqueous alkide resin is translucent light yellow thick liquid, and this moment, its yield was between 85-88%.
Preparation method of the present invention is that elder generation is mixed aqueous alkide resin with aqueous dispersant, be cooled to 60 ℃ ± 5 ℃, add water cross-linking agent, base material wetting agent and water more successively after inciting somebody to action, stir until the homogeneous state fast then, after half an hour, the mixing raw material after the stirring is vitreous state.
Embodiment one
The invention provides a kind of aqueous, environmental protective insullac, be made up of aqueous alkide resin, base material wetting agent, aqueous dispersant, water cross-linking agent and an amount of water, the proportioning numerical value of above-mentioned raw materials is: aqueous alkide resin 30%, base material wetting agent 1%, aqueous dispersant 8%, water cross-linking agent 20%.The model of aqueous dispersant is AMP95; The model of water cross-linking agent is 303LF; The model of base material wetting agent is AR420.
Preparation method of the present invention is that elder generation is mixed aqueous alkide resin with aqueous dispersant, be cooled to 60 ℃ ± 5 ℃, add water cross-linking agent, base material wetting agent and water more successively after inciting somebody to action, stir until the homogeneous state fast then, after half an hour, the mixing raw material after the stirring is vitreous state.
Embodiment two
The invention provides a kind of aqueous, environmental protective insullac, be made up of aqueous alkide resin, base material wetting agent, aqueous dispersant, water cross-linking agent and an amount of water, the ratio range of above-mentioned raw materials is: aqueous alkide resin 40～60%, base material wetting agent 1.3～1.6%, aqueous dispersant 8.5～9.5%, water cross-linking agent 22～24%.The model of aqueous dispersant is AMP95; The model of water cross-linking agent is 303LF; The model of base material wetting agent is AR420.
Preparation method of the present invention is identical with embodiment one, does not therefore generally repeat.
Embodiment three
The invention provides a kind of aqueous, environmental protective insullac, be made up of aqueous alkide resin, base material wetting agent, aqueous dispersant, water cross-linking agent and an amount of water, the proportioning value of above-mentioned raw materials is: aqueous alkide resin 50%, base material wetting agent 2%, aqueous dispersant 10%, water cross-linking agent 25%.The model of aqueous dispersant is AMP95; The model of water cross-linking agent is 303LF; The model of base material wetting agent is AR420.
Preparation method of the present invention is identical with embodiment one, does not therefore generally repeat.
Embodiment four
The invention provides a kind of aqueous, environmental protective insullac, be made up of aqueous alkide resin, base material wetting agent, aqueous dispersant, water cross-linking agent and an amount of water, the proportioning value of above-mentioned raw materials is: aqueous alkide resin 60%, base material wetting agent 1.5%, aqueous dispersant 9%, water cross-linking agent 22%.The model of aqueous dispersant is AMP95; The model of water cross-linking agent is 303LF; The model of base material wetting agent is AR420.
Preparation method of the present invention is identical with embodiment one, does not therefore generally repeat.
Embodiment five
The invention provides a kind of aqueous, environmental protective insullac, form by aqueous alkide resin, base material wetting agent, aqueous dispersant, water cross-linking agent and an amount of water, the gravimetric value of above-mentioned raw materials is: aqueous alkide resin 165g, base material wetting agent 3g, aqueous dispersant 20g, water cross-linking agent 30g, melamine resin 18g, water 600g.The model of aqueous dispersant is AMP95; The model of water cross-linking agent is 303LF; The model of base material wetting agent is AR420.
Its preparation method is, adds aqueous dispersant 20g in the aqueous alkide resin of 165g again, is cooled to 60 ℃ ± 5 ℃ and adds water cross-linking agent 30g, melamine resin 18g, base material wetting agent 3g again; Add entry 600g, be stirred to the homogeneous state fast, half an hour is above transparent.
The present invention has high thermotolerance and good insulation performance, and sticking power is good, and cementability is outstanding, dry and curing speed express train, and water tolerance and solvent resistance are good, excellent advantages such as anti-moisture regain ability.This product uses water as dispersion agent, really reaches the discharging of zero VOC, and is harmless, nontoxic, and safety is not fired not quick-friedly, is the green product of the friendly type of a kind of novel environmental.Be mainly used in the electrical equipment and electrical coil that dipping is worked for a long time in hot environment; be applicable to the impregnation or the application of transformer, motor, motor, generator, circuit card, wiring board, coil, resistance, armature, electric capacity, spindle, rotor, enameled wire, effects such as protection against the tide, heat radiation, insulation, fixing, protection circuit plate are arranged.Also can be used as transistor protective layer, impregnated glass envelope curve and woven fiber glass.
Technical feature of the present invention is as follows:
Only the above person only is preferred embodiment of the present invention, is familiar with the professional person of this skill such as. after understanding technique means of the present invention, natural energy is changed under instruction of the present invention according to the needs of reality.Therefore all equal variation and modifications of being done according to the present patent application claim once should still belong in the scope that patent of the present invention contains.
Claims (9)
1. an aqueous, environmental protective insullac is made up of aqueous alkide resin, base material wetting agent, aqueous dispersant, water cross-linking agent and water, it is characterized in that the ratio range of above-mentioned raw materials is as follows:
Aqueous alkide resin 30～70%, base material wetting agent 1～2%, aqueous dispersant 8～10%, water cross-linking agent 20～25%.
2. a kind of aqueous, environmental protective insullac as claimed in claim 1 is characterized in that the weight proportion of above-mentioned raw materials is: aqueous alkide resin 30%, base material wetting agent 1%, aqueous dispersant 8%, water cross-linking agent 20%.
3. a kind of aqueous, environmental protective insullac as claimed in claim 1, it is characterized in that the weight proportion scope of above-mentioned raw materials is: aqueous alkide resin 40～60%, base material wetting agent 1.3～1.6%, aqueous dispersant 8.5～9.5%, water cross-linking agent 22～24%.
4. a kind of aqueous, environmental protective insullac as claimed in claim 1 is characterized in that the weight proportion of above-mentioned raw materials is: aqueous alkide resin 50%, base material wetting agent 2%, aqueous dispersant 10%, water cross-linking agent 25%.
5. a kind of aqueous, environmental protective insullac as claimed in claim 1 is characterized in that the weight proportion of above-mentioned raw materials is: aqueous alkide resin 60%, base material wetting agent 1.5%, aqueous dispersant 9%, water cross-linking agent 22%.
6. as any described a kind of aqueous, environmental protective insullac in the claim 1 to 5, it is characterized in that described aqueous alkide resin is formed after being prepared by linolenic acid 40g, TriMethylolPropane(TMP) 40g, Tetra hydro Phthalic anhydride 30g, neopentyl glycol 3g, TMA 12g and butyl carbitol 40g.
7. as any described a kind of aqueous, environmental protective insullac in the claim 1 to 5, it is characterized in that the model of described aqueous dispersant is AMP95; The model of described water cross-linking agent is 303LF; The model of described base material wetting agent is AR420.
8. the preparation method of a kind of aqueous, environmental protective insullac as claimed in claim 1, it is characterized in that, earlier aqueous alkide resin is mixed with aqueous dispersant, be cooled to 60 ℃ ± 5 ℃, add water cross-linking agent, base material wetting agent and water more successively after inciting somebody to action, stir until the homogeneous state fast then.
9. the preparation method of a kind of aqueous, environmental protective insullac as claimed in claim 8 is characterized in that, can also add melamine resin between described water cross-linking agent and described base material wetting agent.