CN102070924A - Multifunctional facing coating of wood fireproof door - Google Patents
Multifunctional facing coating of wood fireproof door Download PDFInfo
- Publication number
- CN102070924A CN102070924A CN 201010594299 CN201010594299A CN102070924A CN 102070924 A CN102070924 A CN 102070924A CN 201010594299 CN201010594299 CN 201010594299 CN 201010594299 A CN201010594299 A CN 201010594299A CN 102070924 A CN102070924 A CN 102070924A
- Authority
- CN
- China
- Prior art keywords
- coating
- facing coating
- white
- multifunctional
- cornstarch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a multifunctional facing coating of a wood fireproof door, comprising the following components in percentage by weight: 25.5-37wt% of white latex, 45-60wt% of cornstarch, 12-15wt% of gray soil material and 2.5-3wt% of white cement, wherein the solid content of white latex is 45+/-2%, the lowest film forming temperature is more than or equal to 5 DEG C, the viscosity is 3000-50000 mpa, and a is less than or equal to 25 DEG C; the granularity of the cornstarch is 450-800 meshes/inch; the granularity of the gray soil powder is 450-800 meshes/inch; and the mark of the white cement is 325-425. In the multifunctional facing coating, paste mixed by a large dose of white latex and superfine ingredients is fine and moist, has strong adhesive force after being coated, has a strong facing coating and has small possibility of cracking after being knocked, thus the facing coating is fireproof, waterproof, antisepticise and anti-cracking. The multifunctional facing coating can be applied both in border hard materials, but also in board coating.
Description
Technical field
The present invention relates to a kind of fire-proof wooden door facing coating, specifically, the present invention relates to the coating that a kind of fire-proof wooden door facing has fire prevention, waterproof, anticorrosion, anti-cracking function.
Background technology
Fire door is the safety equipment of modern building indispensability, its fire resistance depends primarily on fire resisting construction and material, its measures for the prevention of fire be built-in fire-retardant material the door core, be coated with sanitas, and the F R Oil enamelled coating of external fireproof panel and brushing, this structure and used material all have stronger fire retardancy and antiseptic property, satisfy the Building Fire Protection code requirement.But the coating structure density of prior art is poor, and sticking power is not strong, and it is easy to crack to be clashed into the back, and particularly coating is made moist behind bump and produced and peel off.The fire prevention facing coating damage of fire-proof wooden door must reduce fire resistance, loses due anti-fire action, constitutes potential safety hazard.
Summary of the invention
The present invention is primarily aimed at the deficiencies in the prior art, propose that a kind of component is simple, material is easily purchased, application easily, the fire-proof wooden door multifunctional veneer coating of dense structure, strong adhesion, except that keeping good fire prevention, antiseptic property, also have waterproof, anti crack performance preferably behind this paint coating.
The present invention is achieved through the following technical solutions technical object.
Fire-proof wooden door multifunctional veneer coating, its improvements are to comprise the following component of amount by weight percentage: white glue with vinyl 25.5%～37%, Cornstarch 45%～60%, grey calcium powder 12%～15%, white cement 2.5%～3%; Described white glue with vinyl solid content 45 ± 2%, minimum film-forming temperature 〉=5 ℃, viscosity is 3000～50000mpa.a≤25 ℃; Described Cornstarch granularity is 450 order/inches～800 order/inches; Described grey calcium powder granularity is 450 order/inches～800 order/inches; Described white cement is 325～425 labels.
The present invention compared with prior art has following positively effect:
1, the lotion exquisiteness that becomes with ultra-fine batch mixes of heavy dose of white glue with vinyl, moisten, application postadhesion power is strong, the facing coating is solid;
2, coating structure densification, good flame retardation effect;
3, coat-thickness is thin, and application is even, and impact resistant capability is strong, and coating is clashed into not easy to crack so water resistance is good;
4, component raw material is inorganic materials, does not contain formaldehyde, benzene class material, non-environmental-pollution.
Embodiment
Further specify the present invention below by the embodiment that on fire door frame material, makes the facing coating.Embodiment makes the application simultaneous test with three groups of different proportionings, and concrete component sees the following form 1:
The heavy 5kg of the every example of the foregoing description reconciles into paste respectively after weighing by component, then paste material is injected hopper and makes frame material machine and be coated with, and is coated with three layers altogether, and every layer of coat-thickness is 0.10mm～0.15mm, and coating added after the drying through 3～5 hours again and is coated with down one deck.Detect by GB/T8625-2005 " the difficult combustion of material of construction test method " after the coating drying, specimen size is 1000mm * 120mm * 80mm, and test item is a flame retardancy, and detected result sees the following form:
As can be known from the above table, the coating of application of the present invention and the coating of prior art all improve a lot on performance, and particularly coating is incrust, and flameproof effect is good.In addition, coating of the present invention is thin, and power consumption is few, and cost is low.
Claims (1)
1. a fire-proof wooden door multifunctional veneer coating is characterized in that comprising the following component of amount by weight percentage: white glue with vinyl 25.5%～37%, Cornstarch 45%～60%, grey calcium powder 12%～15%, white cement 2.5%～3%; Described white glue with vinyl solid content 45 ± 2%, minimum film-forming temperature 〉=5 ℃, viscosity is 3000～50000mpa.a≤25 ℃; Described Cornstarch granularity is 450 order/inches～800 order/inches; Described grey calcium powder granularity is 450 order/inches～800 order/inches; Described white cement is 325～425 labels.