CN102040783A - 高抗冲高透明环保阻燃聚氯乙烯粒料 - Google Patents

高抗冲高透明环保阻燃聚氯乙烯粒料 Download PDF

Info

Publication number
CN102040783A
CN102040783A CN2009100707473A CN200910070747A CN102040783A CN 102040783 A CN102040783 A CN 102040783A CN 2009100707473 A CN2009100707473 A CN 2009100707473A CN 200910070747 A CN200910070747 A CN 200910070747A CN 102040783 A CN102040783 A CN 102040783A
Authority
CN
China
Prior art keywords
polyvinyl chloride
transparency
transparent
impact
friendly flame
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2009100707473A
Other languages
English (en)
Inventor
揣成智
王燕
陈昊
王获
王福强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN
Original Assignee
DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN filed Critical DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN
Priority to CN2009100707473A priority Critical patent/CN102040783A/zh
Publication of CN102040783A publication Critical patent/CN102040783A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种高抗冲高透明环保阻燃聚氯乙烯粒料。其特征在于：采用先进的生产技术，将聚甲基丙烯酸甲酯-聚丁二烯-聚苯乙烯共聚物，即MBS；氯化聚乙烯，即CPE；环保阻燃剂；透明增强剂和各种助剂组合在一起。环保透明阻燃剂赋予材料环保阻燃性，同时透明增强剂还降低材料中晶粒的尺寸，使得材料在获得较大抗冲击性和环保阻燃性的同时，不失高透明性。

Description

高抗冲高透明环保阻燃聚氯乙烯粒料
技术领域 本发明涉及一种高抗冲高透明环保阻燃聚氯乙烯粒料。
背景技术 通过聚氯乙烯、聚甲基丙烯酸甲酯-聚丁二烯-聚苯乙烯共聚物、氯化聚乙烯、环保阻燃剂FR7080、透明增强剂TMZQ210、稳定剂、加工改性剂、增塑剂、润滑剂等合理混配，生产出多种用途的高抗冲高透明聚氯乙烯粒料。
PVC树脂的年产量居合成树脂第二位，已经被广泛地应用于日常生活的各个领域。透明制品是其一项重要的应用领域，虽然近年来由于其它透明材料的应用，PVC透明制品在市场中的份额在减少。但因聚氯乙烯来源广泛，加工工艺简单，设备投资少，价格便宜；同时，可以针对不同的用途及性能要求方便地调整配方以达到用户的要求和最佳的性能价格比。因此，采用聚氯乙烯树脂制作的透明制品仍被广泛的使用。
传统的PVC透明材料大多是PVC/MBS合金材料，但是随着MBS添加量的增加，合金材料原有的阻燃性也随之下降，限制了其应用。为了使材料具有高透明高抗冲的性能，并同时兼具良好的环保阻燃性能，以及较高拉伸强度、弯曲强度、热稳定性，制备PVC/CPE/MBS合金材料并用环保阻燃剂对其进行阻燃改性是十分必要的。
发明内容 本发明提供一种高抗冲高透明环保阻燃PVC粒料，它是由聚氯乙烯、透明性增强剂、环保透明阻燃剂、稳定剂、加工改性剂、聚甲基丙烯酸甲酯-聚丁二烯-聚苯乙烯共聚物、氯化聚乙烯、增塑剂、润滑剂等组成，首先将计量好的PVC、MBS、CPE、透明性增强剂、环保透明阻燃剂、稳定剂、加工改性剂、增塑剂、润滑剂，于高速混合机中高速混合均匀后出料备用；再经双螺杆挤出机挤出造粒，制得高抗冲高透明环保阻燃PVC粒料。该粒料组分中不仅有较大份数MBS、CPE对PVC树脂进行增韧改性，同时还加入环保透明阻燃剂对材料进行阻燃改性；透明性增强剂的加入使得材料的透明性大幅度提高。
具体实施方式
以下通过实施例进一步说明本发明：
实施例1：
高抗冲高透明环保阻燃聚氯乙烯粒料配方：(Kg)
  PVC   100
  MBS   15
  CPE   10
  透明性增强剂TMZQ210   1
  稳定剂(市售有机锡稳定剂)   3
  加工改性剂(市售ACR401)   2
  增塑剂(聚邻苯二甲酸二辛酯)   2
  润滑剂   1
  环保透明阻燃剂FR7080   1
将PVC、MBS、透明性增强剂、环保透明阻燃剂、稳定剂、增塑剂放入高混机中混合搅拌，温度达到90℃时开始抽湿，抽湿的同时将润滑剂放入高混机中并继续混合，当温度升至135℃时，将高混机中的混合料放进冷混机中进行冷却，冷却到80℃以下时加入加工改性剂，继续冷却到50℃后出料备用，然后经双螺杆挤出机挤出造粒制得高抗冲高透明环保阻燃PVC/CPE/MBS三相合金粒料。
其挤出成型工艺(温度℃)参数：
  1段   2段   3段   4段   5段   6段   模头
  温度，℃   160   160   170   170   180   190   200
实施例2：
高抗冲高透明环保阻燃聚氯乙烯粒料配方：(Kg)
  PVC   100
  MBS   30
  CPE   15
  透明性增强剂TMZQ210   5
  稳定剂(市售有机锡稳定剂)   3
  加工改性剂(市售ACR401)   2
  增塑剂(聚邻苯二甲酸二辛酯)   2
  润滑剂   1
  环保阻燃剂   10
将PVC、MBS、透明性增强剂、环保透明阻燃剂、稳定剂、增塑剂放入高混机中混合搅拌，温度达到90℃时开始抽湿，抽湿的同时将润滑剂放入高混机中并继续混合，当温度升至135℃时，将高混机中的混合料放进冷混机中进行冷却，冷却到80℃以下时加入加工改性剂，继续冷却到50℃后出料备用，然后经双螺杆挤出机挤出造粒制得高抗冲高透明环保阻燃PVC/CPE/MBS三相合金粒料。
其挤出成型工艺(温度℃)参数：
  1段   2段   3段   4段   5段   6段   模头
  温度，℃   160   160   170   170   180   190   200
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。

Claims (4)

1.一种高抗冲高透明环保阻燃聚氯乙烯粒料，包括聚氯乙烯、即PVC，聚甲基丙烯酸甲酯-聚丁二烯-聚苯乙烯共聚物、即MBS，氯化聚乙烯、即CPE，稳定剂，加工改性剂，增塑剂，硬脂酸，润滑剂。其特征在于，还包括环保透明阻燃剂，以及透明性增强剂。
2.根据权利要求1所述的高抗冲高透明环保阻燃聚氯乙烯粒料，其特征在于，所述PVC的重量份数为100；CPE的重量份数为6至15；MBS的重量份数为8至30；环保透明阻燃剂的重量份数为1至10；透明性增强剂1至5份。
3.根据权利要求1所述的高抗冲高透明环保阻燃聚氯乙烯粒料，其特征在于，所述环保透明阻燃剂为FR7080(有效成分为全氟碳的钾盐)。
4.根据权利要求1所述的高抗冲高透明环保阻燃聚氯乙烯粒料，其特征在于，所述透明性增强剂为TMZQ210(有效成分为PMMA)。
CN2009100707473A 2009-10-09 2009-10-09 高抗冲高透明环保阻燃聚氯乙烯粒料 Pending CN102040783A (zh)