CN102031922A - 一种防火门门扇 - Google Patents
一种防火门门扇 Download PDFInfo
- Publication number
- CN102031922A CN102031922A CN 201010567991 CN201010567991A CN102031922A CN 102031922 A CN102031922 A CN 102031922A CN 201010567991 CN201010567991 CN 201010567991 CN 201010567991 A CN201010567991 A CN 201010567991A CN 102031922 A CN102031922 A CN 102031922A
- Authority
- CN
- China
- Prior art keywords
- door leaf
- fireproof door
- intermediate layer
- grid
- chloride solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种防火门门扇,包括表底层、表面层、夹在表底层和表面层之间的中间层、设在中间层四周且位于表底层和表面层之间的封边框架,其特征是:所述中间层由网格子和填在网格中的防火材料构成;所述防火材料由重量为40%-75%的白泡石颗粒、13%-40%的氯化镁溶液、10%-40%的氧化镁、重量为1%-3%的改性剂混合而成,其中氯化镁溶液的重量百分比浓度为22%-30%。本发明的优点:结构简单,易于生产,耐火时间长,耐火温度高,生产成本低,抗压能力强,质量稳定,完全达到并超过了国家GB12955-2008防火门新标准的要求,耐火时间达到了3h。
Description
技术领域
本发明涉及建筑防火构件,具体涉及一种防火门门扇。
技术背景
目前,现有的防火门门扇基本上都在使用珍珠岩系列产品作为防火门门扇的填芯材料。膨胀珍珠岩是一种无毒、无味、不燃、不腐、耐酸碱、保温、隔音隔热,内部呈蜂窝状结构的产品,该产品主要用于建筑物屋面及墙体的保温、隔热;建筑材料的轻质骨料;各种工业设备、管道绝热层;各种深冷、冷库工程的内壁;农业及园艺的无土栽培、改良土壤,保水保肥等,被广泛应用于石油、化工、电力、建筑、冶金等行业。使用温度为-256-800℃,导热系数为0.055w/m,抗压强度:0.8-2.0MPA。但目前珍珠岩系列产品已大幅度涨价,中信膨胀珍珠岩价格4.2元/包,18包为一立方米,使防火门生产企业的利润空间受到严重的挤压,在激烈的市场竞争中,防火门生产企业的利润越来越微薄。加之新的国家GB12955-2008防火门标准对耐火温度和耐火时间的要求提高(甲级耐火时间:1.5h乙级耐火时间:1.0h),现有的防火门门扇低于新的国家标准,因此,需要另辟蹊径。
发明内容
本发明的目的是提供一种防火门门扇,它结构简单,耐火温度高,耐火时间长,抗压强度高,生产成本低,完全能达到并超过国家GB12955-2008防火门新标准的要求。
本发明的目的是这样来实现的:
本发明所述的一种防火门门扇,包括表底层、表面层、夹在表底层和表面层之间的中间层、设在中间层四周且位于表底层和表面层之间的封边框架,其特征是:所述中间层由网格子和填在网格中的防火材料构成;所述防火材料由重量为40%-75%的白泡石颗粒、13%-40%的氯化镁溶液、10%-40%的氧化镁、重量为1%-3%的改性剂混合而成,其中氯化镁溶液的重量百分比浓度为22%-30%。
所述的一种防火门门扇,其所述白泡石颗粒的粒度为20目-500目。
所述的一种防火门门扇,其所述网格子的网格形状为多边形,网格子的厚度与封边框架的厚度相等。
所述的一种防火门门扇,其所述底面层和表面层为经过防火液浸泡后的木板或钢板。
所述的一种防火门门扇,其所述封边框架为冷扎钢板或经过防火液浸泡后的木板。
本发明采用的防火材料中的白泡石是天然硅矿,主要矿物组成为石英和高岭石,耐火温度为1650℃-1730℃,抗压强度为96-116 MPA,热膨胀率在1000℃为0.4-1.2,整块的白泡石用于制作耐火砖。白泡石颗粒价格目前为160-580元/吨,均优于膨胀珍珠岩。
本发明的优点:结构简单,易于生产,耐火时间长,耐火温度高,生产成本低,抗压能力强,质量稳定,完全达到并超过了国家GB12955-2008防火门新标准的要求,耐火时间达到了3 h。
附图说明
图1:为本发明的结构示意图。
图2:为图1的A-A剖示图。
具体实施方式
下面结合附图和实施例对本发明作进一步的说明。
实施例一:参见图1和图2所示的一种防火门门扇,包括表底层1、表面层2、夹在表底层和表面层之间的中间层3、设在中间层四周且位于表底层和表面层之间的封边框架6;所述中间层3由网格子5和填在网格中的防火材料4构成;
防火材料4由重量为65%的白泡石颗粒、20%的氯化镁溶液、13%的氧化镁、重量为2%的改性剂混合而成,其中白泡石颗粒的粒度为20目-500目、氯化镁溶液的重量百分比浓度为25%。
网格子5的网格形状为三角形,网格子5的厚度与封边框架6的厚度相等,底面层1和表面层2为钢板,封边框架6为冷扎钢板或经过防火液浸泡后的木板。
防火材料的制作和填充方法如下:
先在搅拌机中加入白泡石颗粒65%,氯化镁溶液20%,改性剂2%后,搅拌均匀后,再加入氧化镁13%充分搅拌至粘稠壮。将此材料填入网格内,经热压后,可以使防火材料因膨胀后,将腔内填满,无遗漏。
实施例二:参见图1和图2所示的一种防火门门扇,包括表底层1、表面层2、夹在表底层和表面层之间的中间层3、设在中间层四周且位于表底层和表面层之间的封边框架6;所述中间层3由网格子5和填在网格中的防火材料4构成;
防火材料4由重量为75%的白泡石颗粒、14%的氯化镁溶液、10%的氧化镁、重量为1%的改性剂混合而成,其中白泡石颗粒的粒度为20目-500目、氯化镁溶液的重量百分比浓度为22%。
网格子5的网格形状为菱形和三角形,网格子5的厚度与封边框架6的厚度相等,底面层1和表面层2为经过防火液浸泡后的木板,封边框架6为经过防火液浸泡后的木板。
防火材料的制作和填充方法如下:
先在搅拌机中加入白泡石颗粒75%,氯化镁溶液14%,改性剂1%后,搅拌均匀后,再加入氧化镁10%充分搅拌至粘稠壮。将此材料填入网格内,经热压后,可以使防火材料因膨胀后,将腔内填满,无遗漏。
实施例三:参见图1和图2所示的一种防火门门扇,包括表底层1、表面层2、夹在表底层和表面层之间的中间层3、设在中间层四周且位于表底层和表面层之间的封边框架6;所述中间层3由网格子5和填在网格中的防火材料4构成;
防火材料4由重量为40%的白泡石颗粒、35%的氯化镁溶液、22%的氧化镁、重量为3%的改性剂混合而成,其中白泡石颗粒的粒度为20目-500目、氯化镁溶液的重量百分比浓度为30%。
网格子5的网格形状为四边形,网格子5的厚度与封边框架6的厚度相等,底面层1和表面层2为防火玻璃板,封边框架6为冷扎钢板。
防火材料的制作和填充方法如下:
先在搅拌机中加入白泡石颗粒40%,氯化镁溶液35%,改性剂3%后,搅拌均匀后,再加入氧化镁22%充分搅拌至粘稠壮。将此材料填入网格内,经热压后,可以使防火材料因膨胀后,将腔内填满,无遗漏。
Claims (5)
1.一种防火门门扇,包括表底层(1)、表面层(2)、夹在表底层和表面层之间的中间层(3)、设在中间层四周且位于表底层和表面层之间的封边框架(6),其特征是:所述中间层(3)由网格子(5)和填在网格中的防火材料(4)构成;所述防火材料由重量为40%-75%的白泡石颗粒、13%-40%的氯化镁溶液、10%-40%的氧化镁、重量为1%-3%的改性剂混合而成,其中氯化镁溶液的重量百分比浓度为22%-30%。
2.根据权利要求1所述的一种防火门门扇,其特征是:所述白泡石颗粒的粒度为20目-500目。
3.根据权利要求1或2所述的一种防火门门扇,其特征是:所述网格子(5)的网格形状为多边形,网格子(5)的厚度与封边框架(6)的厚度相等。
4.根据权利要求1或2所述的一种防火门门扇,其特征是:所述底面层(1)和表面层(2)为经过防火液浸泡后的木板或钢板。
5.根据权利要求1或2所述的一种防火门门扇,其特征是:所述封边框架(6)为冷扎钢板或经过防火液浸泡后的木板。