CN102031430A - 一种铝合金复合管预钎焊层材料 - Google Patents
一种铝合金复合管预钎焊层材料 Download PDFInfo
- Publication number
- CN102031430A CN102031430A CN 201010533899 CN201010533899A CN102031430A CN 102031430 A CN102031430 A CN 102031430A CN 201010533899 CN201010533899 CN 201010533899 CN 201010533899 A CN201010533899 A CN 201010533899A CN 102031430 A CN102031430 A CN 102031430A
- Authority
- CN
- China
- Prior art keywords
- welding
- alloy
- zinc
- aluminum
- layer material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铝合金复合管预钎焊层材料，其特征为化学成分重量百分比为：硅8.6~11.5%，锌0.9~1.2%，铁0.1~0.7%，其余为铝；其组分按重量百分比还可以为：硅8.83～11.2%、锌0.95～1.17%、铁0.19～0.65%，铝为余量；其组分按重量百分比进一步可以为：硅10.2%、锌1.01%、铁0.41%，铝为余量。合金中大量的Si在合金中主要以α+Si共晶体形式存在，Si含量提高，其共晶体增加，合金流动性增加，起到提高焊接流动性的作用，少量的Zn能起到改善焊接热应力，减少焊接气泡，从而提高焊接性能，微量的Fe，形成的FeAl3能起到好的再结晶晶粒细化效果,改善焊接流动性。
Description
技术领域
本发明属于变形铝合金材料领域。
背景技术
目前铝合金复合管预钎焊层材料主要为4343或4045铝合金牌号，在焊接过程中，由于其流动性不够好，导致焊接后局部形成一定的缝隙，达不到预期的密封性能。
发明内容
本发明所要解决的技术问题是提供一种具有良好焊接性的新型铝合金复合管预钎焊材料。
本发明的技术方案是：
一种铝合金复合管预钎焊材料，其主要特征为化学成分重量百分比为：
硅 8.6～11.5％；
锌 0.9～1.2％；
铁 0.1～0.7％；
其余为铝。
其组分按重量百分比还可以为：硅8.83～11.2％、锌0.95～1.17％、铁0.19～0.65％，其余为铝。
其组分按重量百分比进一步可以为：硅10.2％、锌1.01％、铁0.41％，其余为铝。
有益效果：该合金中大量的Si在本合金中主要以α+Si共晶体形式存在，Si含量提高，其共晶体增加，合金流动性增加，起到提高焊接流动性的作用，过量的Si会形成偏析瘤，粗大晶粒，影响浇铸质量，所以Si不得超过11.5％。少量的Zn能起到改善焊接热应力，减少焊接气泡，从而提高焊接性能。微量的Fe，形成的FeAl3能起到好的再结晶晶粒细化效果，改善焊接流动性。
与已有的铝合金复合管预钎焊层材料相比，本发明的最大优点在于具有更好的焊接性能，本新合金比传统的预钎焊层材料4343和4045具有更优良的焊接流动性，能够有效地减少焊接泄露。
具体实施方式
铝合金复合管预钎焊层材料，其化学成分重量百分比为：
硅 8.6～11.5％；
锌 0.9～1.2％；
铁 0.1～0.7％；
其余为铝。
其组分按重量百分比还可以为：硅8.83～11.2％、锌0.95～1.17％、铁0.19～0.65％，其余为铝。
其组分按重量百分比进一步可以为：硅10.2％、锌1.01％、铁0.41％，其余为铝。
新合金中按所有成分上限制备一种规格复合铝管A，按成分下限制备同种产品B，成分中间值制备同规格产品C、D、E、F、G、H、I、J、K、L、M，取4343，4045合金成分也挤压同样规格产品，它们的化学成分重量百分比为：
| 硅 | 铁 | 锌 | 铝 | |
| A | 11.50 | 0.70 | 1.20 | 余量 |
| B | 8.60 | 0.10 | 0.90 | 余量 |
| C | 11.20 | 0.35 | 0.90 | 余量 |
| D | 9.55 | 0.59 | 0.95 | 余量 |
| E | 9.39 | 0.61 | 0.99 | 余量 |
| F | 10.53 | 0.20 | 1.02 | 余量 |
| G | 8.71 | 0.65 | 1.17 | 余量 |
| H | 10.20 | 0.41 | 1.01 | 余量 |
| I | 9.25 | 0.19 | 1.15 | 余量 |
| J | 11.43 | 0.53 | 0.94 | 余量 |
| K | 10.77 | 0.24 | 1.05 | 余量 |
| L | 8.83 | 0.46 | 1.09 | 余量 |
| M | 10.64 | 0.31 | 0.98 | 余量 |
| 4045 | 10.41 | 0.22 | 0.06 | 余量 |
| 4343 | 7.33 | 0.16 | 0.03 | 余量 |
将合金A-M与4343，4045的产品管与相同规格的配套焊接型材做焊接实验，统计焊接后的缝隙，所得结果见表1。
表1焊接结果
结论：由表1可以看出新合金的焊接性能要优于传统合金4343，4045。
合金中大量的Si在本合金中主要以α+Si共晶体形式存在，Si含量提高，其共晶体增加，合金流动性增加，起到提高焊接流动性的作用，过量的Si会形成偏析瘤，粗大晶粒，影响浇铸质量，所以Si不得超过11.5％。少量的Zn能起到改善焊接热应力，减少焊接气泡，从而提高焊接性能。微量的Fe，形成的FeAl3能起到好的再结晶晶粒细化效果，改善焊接流动性。
Claims (3)
1.一种铝合金复合管预钎焊层材料，其主要特征在于，组分按重量百分比为：
硅 8.6～11.5%；
锌 0.9～1.2%；
铁 0.1～0.7%；
其余为铝。
2.根据权利要求1所述的铝合金复合管预钎焊层材料，其特征在于，其组分按重量百分比为：硅 8.83～11.2%、锌0.95～1.17%、铁0.19～0.65%，其余为铝。
3.根据权利要求1所述的铝合金复合管预钎焊层材料，其特征在于，其组分按重量百分比进一步可以为：硅 10.2%、锌1.01%、铁0.41%，其余为铝。