CN102031168A - Anionic-nonionic complex gasified coal water slurry additive - Google Patents
Anionic-nonionic complex gasified coal water slurry additive Download PDFInfo
- Publication number
- CN102031168A CN102031168A CN2010106007716A CN201010600771A CN102031168A CN 102031168 A CN102031168 A CN 102031168A CN 2010106007716 A CN2010106007716 A CN 2010106007716A CN 201010600771 A CN201010600771 A CN 201010600771A CN 102031168 A CN102031168 A CN 102031168A
- Authority
- CN
- China
- Prior art keywords
- dispersing agent
- coal
- agent
- anionic dispersing
- anionic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an anionic-nonionic complex gasified coal water slurry additive. The additive is prepared by mixing the following components in part by mass uniformly: 21 to 41 parts of anionic dispersant lignosulfonate, 20.5 to 47.4 parts of anionic dispersant naphthalene sulfonate formaldehyde condensate, 5.3 to 10.3 parts of nonionic dispersant oxirane and poxypropane segmented copolymer, 21 to 25.6 parts of hole plugging agent, and 2.6 to 5.3 parts of acid-base regulator, wherein a composition of the anionic dispersant lignosulfonate, the naphthalene sulfonate formaldehyde condensate, and the nonionic dispersant oxirane and poxypropane segmented copolymer has unique synergistic property, so the synergistic effect of learn strong points to offset weakness can be played.
Description
Technical field
The present invention relates to the coal water slurry field, particularly a kind of negatively charged ion-nonionic Compositional type gasification slurries additive agent.
Background technology
Coal water slurry is one of clean coal technology that last century, the eighties was risen.It is coal, water and a small amount of formulated a kind of slurry of chemical additive that is distributed by certain particle size.It has the same flowability of oil, can pumping, atomizing and fire burns, can substitute oil as boiler fuel, also can be used as gasification raw material preparing synthetic gas, processing downstream Chemicals.
Water coal slurry replacing oil and coal water slurry gasification have obtained widespread use in China over past ten years, and especially coal water slurry is developing faster as the gasification raw material, and existing nearly ten coal water slurry gasifications are runed factory, nearly ten million ton of year slurrying amount.Present rise along with coal resources in China anxiety and coal price, many coal water slurry gasification raw materials adopt or have allocated into the difficult sludge forming performance coal of relative low price, but because interior water-content height, hole prosperity, that oxygen-containing functional group enriches metamorphic grade is low, the coal-water fluid concentration of operation is only about 60%.Many coal water slurry gasifications enterprise needs the coal-water fluid concentration that improves low rank coal badly.
Coal water slurry product requirement with industrial application value has characteristics such as high density, low-viscosity, good flowability and steady time is long.In the coal water slurry production process, slurries additive agent plays crucial effects to the coal water slurry performance.Slurries additive agent mainly contains dispersion agent, stablizer and other assistant medicaments, and wherein dispersion agent plays a key effect.At present, coal water slurry dispersing agent mainly contains Lignins, naphthalene system, humic acid and non-ionic type etc.But these products respectively have advantage, also each defectiveness, and application facet is restricted to some extent.Advantage as sulfonated lignin is an abundant raw material, low price, and stability is better, but shortcoming is that the slurrying viscosity is bigger, slurry is mobile bad; Naphthalene is that dispersion agent good dispersity, viscosity reduction effect are strong, the slurry good fluidity, but slurry stability is relatively poor, and bleed produces hard-caked sediment easily; The major advantage of non-ionic dispersing agent is that the amphipathic property of molecule and relative molecular mass are easy to regulate and control, is not subjected to the influence of solvend in water quality and the coal, need not add stablizer, but cost an arm and a leg.
Because slurries additive agent molecular structure and ature of coal exist matching, this matching affects sludge forming performance, rheological and the slurry stability of coal.The universality of slurries additive agent is limited, and several additives can not be pervasive in all coals.Studies show that at present anionic dispersing agent and non-ionic dispersing agent composite not only has more good effects on slurry making, that lacks when the total consumption of dispersion agent is than the corresponding dispersion agent of independent use simultaneously is many.This shows that the composite of dispersion agent not only can be improved water coal slurry concentration, reduce viscosity of coal slurry, can also reduce the consumption of total additive simultaneously, reach inexpensive, purpose efficiently.
The invention provides a kind of negatively charged ion-nonionic Compositional type gasification slurries additive agent, be by anionic dispersing agent sulfonated lignin, naphthalene sulfonic acidformaldehyde condensation product, non-ionic dispersing agent oxyethane and propylene oxide block copolymer, hole-blocking agent, acid-base modifier is composite by a certain percentage forms.It has the wide characteristics of suitable coal scope, and especially internally water-content height, hole prosperity, oxygen-containing functional group enrich the low coal water slurry gasification coal of metamorphic grade, have improved the sludge forming performance and the concentration of coal for gasification.
Summary of the invention
The object of the present invention is to provide the gasification slurries additive agent that a kind of preparation method is simple, applied widely, slurry performance is good.
The technical scheme of slurries additive agent of the present invention is as follows:
A kind of negatively charged ion-nonionic Compositional type gasification slurries additive agent, it is formed by following mass parts uniform mixing by anionic dispersing agent sulfonated lignin, anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product, non-ionic dispersing agent oxyethane and propylene oxide block copolymer, hole-blocking agent, acid-base modifier:
Anionic dispersing agent sulfonated lignin 21~41
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 20.5~47.4
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 5.3~10.3
Hole-blocking agent 21~25.6
Acid-base modifier 2.6~5.3.
Above-mentioned a kind of negatively charged ion-nonionic Compositional type gasification slurries additive agent, it is characterized in that: described sulfonated lignin are one or more in sodium salt, calcium salt, magnesium salts or the ammonium salt; The polymerization degree of described naphthalene sulfonic acidformaldehyde condensation product is 7~15; The molecular-weight average of described non-ionic dispersing agent oxyethane and propylene oxide block copolymer is controlled between 4000 to 6000; Described hole-blocking agent is that carbonate can be one or more in sodium salt, sylvite or the ammonium salt, is to comprise the chemical that carbonate maybe can generate carbonate; Described acid-base modifier is one or both in solid sodium hydroxide, the potassium hydroxide.
Above-mentioned a kind of negatively charged ion-nonionic Compositional type gasification slurries additive agent, it is characterized in that: each component forms by following mass parts uniform mixing:
Anionic dispersing agent sodium lignosulfonate 21
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 47.4
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 5.3
Yellow soda ash 21
Sodium hydroxide 5.3.
Above-mentioned a kind of negatively charged ion-nonionic Compositional type gasification slurries additive agent, it is characterized in that: each component forms by following mass parts uniform mixing:
Anionic dispersing agent sodium lignosulfonate 41
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 20.5
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 10.3
Salt of wormwood 25.6
Potassium hydroxide 2.6.
Above-mentioned a kind of negatively charged ion-nonionic Compositional type gasification slurries additive agent, it is characterized in that: each component forms by following mass parts uniform mixing:
Anionic dispersing agent calcium lignin sulphonate 30
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 40
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 6
Volatile salt 21
Sodium hydroxide 3.
Above-mentioned a kind of negatively charged ion-nonionic Compositional type gasification slurries additive agent, it is characterized in that: each component forms by following mass parts uniform mixing:
Anionic dispersing agent magnesium lignosulfonate 21
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 47.4
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 5.3
Yellow soda ash 21
Sodium hydroxide, 1: 1 mixture 5.3 of potassium hydroxide.
Above-mentioned a kind of negatively charged ion-nonionic Compositional type gasification slurries additive agent, it is characterized in that: each component forms by following mass parts uniform mixing:
Anionic dispersing agent ammonium lignosulphonate 41
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 20.5
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 10.3
Volatile salt 25.6
Sodium hydroxide 2.6.
Above-mentioned a kind of negatively charged ion-nonionic Compositional type gasification slurries additive agent, it is characterized in that: each component forms by following mass parts uniform mixing:
The mixture 30 of anionic dispersing agent calcium lignin sulphonate and sodium lignosulfonate
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 40
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 6
Yellow soda ash 21
Sodium hydroxide 3.
Above-mentioned a kind of negatively charged ion-nonionic Compositional type gasification slurries additive agent, the processing step when using its preparation coal water slurry is as follows:
(1), the preparation coal dust: with feed coal be crushed to certain particle size (≤3mm), use the omnipotent crusher dry ground of high speed then.The broken time of control, directly fragmentation makes the suitable coal dust of size-grade distribution, according to the requirement of coal for gasification slurry, should control coal powder size and satisfy the 40-60% that the following coal dust of 200 orders accounts for the coal dust total amount.
(2), preparation coal water slurry: according to the addition of predefined water coal slurry concentration and additive according to formula:
Wherein, m
WaterBe the water yield of adding, m
CoalBe the coal amount of needs, m
AdditiveBe additive amount, C is a coal-water fluid concentration, M
AdBe moisture in coal.
Calculate the needed coal amount of pressed powder additive, the water yield that need add and pulping, coal dust, additive and the water added are mixed, homogenate is 5~10 minutes under 500~1500 rev/mins stirring velocity, and this moment, the coal slurry pH value was between 6 to 10.
Complex additive of the present invention is made up of anionic dispersing agent sulfonated lignin, naphthalene sulfonic acidformaldehyde condensation product, non-ionic dispersing agent oxyethane and propylene oxide block copolymer, hole-blocking agent, acid-base modifier.Wherein, anionic dispersing agent sulfonated lignin, naphthalene sulfonic acidformaldehyde condensation product, non-ionic dispersing agent oxyethane and propylene oxide block copolymer three are composite as a kind of additive, and its characteristic that has not only had general dispersion agent promptly improves the wetting ability on coal surface; Electrostatic repulsion between enhanced granule, thus help improving the flowability of coal water slurry; Produce stronger space steric effect, thereby realize slurry rheology stability, it has also had distinctive synergy characteristic, thereby has played the effect of the synergy of learning from other's strong points to offset one's weaknesses.Hole-blocking agent carbonate and coal mineral form carbonate depositions such as lime carbonate in pulping process, because what form is the colloidal precipitation of calcium carbonate, its adhesive ability is strong, can be adsorbed in the coal hole, improve the deposition efficiency and the stability of coal water slurry, the precipitation of calcium carbonate of Sheng Chenging is helpful to the ash fusion point that reduces coal simultaneously, and this is very useful for slag tap.
Embodiment
Below in conjunction with embodiment invention being further described in detail, below only is preferred embodiment of the present invention, can not limit scope of the present invention with this.
Embodiment 1:
Coal sample source: Shenmu County, Shaanxi coal
Coal analysis is as follows:
(1) preparation pressed powder additive: take by weighing anionic dispersing agent sodium lignosulfonate, anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product, non-ionic dispersing agent oxyethane and propylene oxide block copolymer, yellow soda ash, sodium hydroxide in quality than ratio (21.0: 47.4: 5.3: 21.0: 5.3), mix;
(2) preparation coal dust: with Shenmu County's coal be crushed to certain particle size (≤3mm), use the omnipotent crusher dry ground of high speed then.The broken time of control, directly fragmentation makes the suitable coal dust of size-grade distribution, the size-grade distribution of coal dust:
〉=40 orders 2.8%
40 orders~80 orders 15.6%
80 orders~120 orders 24.8%
120 orders~200 orders 12.6%
200 orders~325 orders 22.2%
≤ 325 orders 22.0%
(3) preparation coal water slurry: according to the addition (0.1% of predefined water coal slurry concentration (62%) and additive, 0.15%, 0.2%, 0.25% or 0.30%), calculate the needed coal amount of pressed powder additive, the water yield that need add and pulping, coal dust, additive and the water added are mixed, and homogenate is 5 minutes under 1000 rev/mins stirring velocity.
The comparison of embodiment 1 product sludge forming performance and stability:
Embodiment 2:
Coal sample source: place, north, Yan ore deposit coal
Coal analysis is as follows:
(1) preparation pressed powder additive: take by weighing anionic dispersing agent sodium lignosulfonate, anionic naphthalene sulfonic acidformaldehyde condensation product, non-ionic dispersing agent oxyethane and propylene oxide block copolymer, salt of wormwood, potassium hydroxide in quality than ratio (41.0: 20.5: 10.3: 25.6: 2.6), mix;
(2) preparation coal dust: with northern place coal be crushed to certain particle size (≤3mm), use the omnipotent crusher dry ground of high speed then.The broken time of control, directly fragmentation makes the suitable coal dust of size-grade distribution, the size-grade distribution of coal dust:
〉=40 orders 2.1%
40 orders~80 orders 12.9%
80 orders~120 orders 17.2%
120 orders~200 orders 9.7%
200 orders~325 orders 20.3%
≤ 325 orders 37.8%
(3) preparation coal water slurry: according to the addition (0.1% of predefined water coal slurry concentration (64%) and additive, 0.15%, 0.2%, 0.25% or 0.30%) according to formula, calculate the needed coal amount of pressed powder additive, the water yield that need add and pulping, coal dust, additive and the water added are mixed, and homogenate is 5 minutes under 1000 rev/mins stirring velocity.
The comparison of embodiment 2 product sludge forming performance and stability:
Embodiment 3:
Coal sample source: Kaiyang, Guizhou coal
Coal analysis is as follows:
(1) preparation pressed powder additive: take by weighing anionic dispersing agent calcium lignin sulphonate, anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product, non-ionic dispersing agent oxyethane and propylene oxide block copolymer, volatile salt, sodium hydroxide in quality than ratio (30: 40: 6: 21: 3), mix;
(2) preparation coal dust: with the Kaiyang coal be crushed to certain particle size (≤3mm), use the omnipotent crusher dry ground of high speed then.The broken time of control, directly fragmentation makes the suitable coal dust of size-grade distribution, the size-grade distribution of coal dust:
〉=40 orders 3.9%
40 orders~80 orders 12.4%
80 orders~120 orders 10.0%
120 orders~200 orders 16.9%
200 orders~325 orders 37.6%
≤ 325 orders 19.2%
(3) preparation coal water slurry: according to the addition (0.1% of predefined water coal slurry concentration (62%) and additive, 0.15%, 0.2%, 0.25% or 0.30%) according to formula, calculate the needed coal amount of pressed powder additive, the water yield that need add and pulping, coal dust, additive and the water added are mixed, and homogenate is 5 minutes under 1000 rev/mins stirring velocity.
The comparison of embodiment 3 product sludge forming performance and stability:
Embodiment 4:
Coal sample source: Shenmu County, Shaanxi coal
Coal analysis is as follows:
(1) preparation pressed powder additive: take by weighing anionic dispersing agent magnesium lignosulfonate, naphthalene sulfonic acidformaldehyde condensation product, non-ionic dispersing agent oxyethane and propylene oxide block copolymer, yellow soda ash, sodium hydroxide and 1: 1 mixture of potassium hydroxide in quality than ratio (21.0: 47.4: 5.3: 21.0: 5.3), mix;
(2) preparation coal dust: with Shenmu County's coal be crushed to certain particle size (≤3mm), use the omnipotent crusher dry ground of high speed then.The broken time of control, directly fragmentation makes the suitable coal dust of size-grade distribution, the size-grade distribution of coal dust:
20 orders~40 orders 2.76%
40 orders~80 orders 15.1%
80 orders~120 orders 14.8%
120 orders~200 orders 13.1%
200 orders~325 orders 22.2%
≤ 325 orders 32.0%
(3) preparation coal water slurry: according to predefined water coal slurry concentration (59%, 60%, 61%, 62%, 63%) and the addition of additive (0.15%),, calculates the needed coal amount of pressed powder additive, the water yield that need add and pulping according to formula, coal dust, additive and the water added are mixed, and homogenate is 5 minutes under 1000 rev/mins stirring velocity.
The comparison of embodiment 4 product sludge forming performance and stability:
Embodiment 5:
Coal sample source: place, north, Yan ore deposit coal
Coal analysis is as follows:
(1) preparation pressed powder additive: take by weighing anionic dispersing agent ammonium lignosulphonate, anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product, non-ionic dispersing agent oxyethane and propylene oxide block copolymer, volatile salt, sodium hydroxide in quality than ratio (41.0: 20.5: 10.3: 25.6: 2.6), mix;
(2) preparation coal dust: with northern place coal be crushed to certain particle size (≤3mm), use the omnipotent crusher dry ground of high speed then.The broken time of control, directly fragmentation makes the suitable coal dust of size-grade distribution, the size-grade distribution of coal dust:
〉=40 orders 2.10%
40 orders~80 orders 12.88%
80 orders~120 orders 17.33%
120 orders~200 orders 9.62%
200 orders~325 orders 19.26%
≤ 325 orders 38.81%
(3) preparation coal water slurry: according to predefined water coal slurry concentration (61%, 62%, 63%, 64%, 65%) and the addition of additive (0.15%),, calculates the needed coal amount of pressed powder additive, the water yield that need add and pulping according to formula, coal dust, additive and the water added are mixed, and homogenate is 5 minutes under 1000 rev/mins stirring velocity.
The comparison of embodiment 5 product sludge forming performance and stability:
Embodiment 6:
Coal sample source: Kaiyang, Guizhou coal
Coal analysis is as follows:
(1) preparation pressed powder additive: take by weighing mixture, anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product, non-ionic dispersing agent oxyethane and propylene oxide block copolymer, yellow soda ash, the sodium hydroxide of anionic dispersing agent calcium lignin sulphonate and sodium lignosulfonate in quality than ratio (30: 40: 6: 21: 3), mix;
(2) preparation coal dust: with the Kaiyang coal be crushed to certain particle size (≤3mm), use the omnipotent crusher dry ground of high speed then.The broken time of control, directly fragmentation makes the suitable coal dust of size-grade distribution, the size-grade distribution of coal dust:
〉=40 orders 2.9%
40 orders~80 orders 12.5%
80 orders~120 orders 10.0%
120 orders~200 orders 15.9%
200 orders~325 orders 38.2%
≤ 325 orders 19.6%
(3) preparation coal water slurry: according to predefined water coal slurry concentration (60%, 61%, 62%, 63%, 64%) and the addition of additive (0.15%),, calculates the needed coal amount of pressed powder additive, the water yield that need add and pulping according to formula, coal dust, additive and the water added are mixed, and homogenate is 5 minutes under 1000 rev/mins stirring velocity.
The comparison of embodiment 6 product sludge forming performance and stability:
Embodiment 7:
Coal sample source: Yulin coal
Coal analysis is as follows:
Additive types: negatively charged ion-nonionic Compositional type additive
Additive amount: the quality of complex additive (folding is solid) is 0.15% of coal (butt) quality
Coal-water fluid concentration: 59%, 60%, 61%, 62%, 63%
(1) preparation pressed powder additive: take by weighing anionic dispersing agent sodium lignosulfonate, naphthalene sulfonic acidformaldehyde condensation product, non-ionic dispersing agent oxyethane and propylene oxide block copolymer, yellow soda ash, sodium hydroxide in quality than ratio (21.0: 47.4: 5.3: 21.0: 5.3), mix;
(2) preparation coal dust: with Yulin coal be crushed to certain particle size (≤3mm), use the omnipotent crusher dry ground of high speed then.The broken time of control, directly fragmentation makes the suitable coal dust of size-grade distribution, the size-grade distribution of coal dust:
〉=40 orders 7.79%
40 orders~80 orders 27.26%
80 orders~120 orders 8.44%
120 orders~200 orders 0.45%
200 orders~325 orders 31.14%
≤ 325 orders 24.90%
(3) preparation coal water slurry: according to predefined water coal slurry concentration (59%, 60%, 61%, 62%, 63%) and the addition of additive (0.15%),, calculates the needed coal amount of pressed powder additive, the water yield that need add and pulping according to formula, coal dust, additive and the water added are mixed, and homogenate is 5 minutes under 1000 rev/mins stirring velocity.
The comparison of embodiment 7 product sludge forming performance and stability:
Water-content height, hole prosperity, oxygen-containing functional group enriched the low difficult pulping coal of metamorphic grade in wherein Shenmu County's coal and Yulin coal belonged to, and all can obtain concentration height, coal water slurry that flow effect is good after having used the prepared slurries additive agent of the present invention.The prepared slurries additive agent of the present invention has used cheap sulfonated lignin and has fallen glutinous effective naphthalene sulfonic acidformaldehyde condensation product, non-ionic dispersing agent oxyethane and propylene oxide block copolymer, not only guarantee the effect of additive but also reduced the cost of additive, reached inexpensive, purpose efficiently.
Claims (8)
1. negatively charged ion-nonionic Compositional type gasification slurries additive agent, it is formed by following mass parts uniform mixing by anionic dispersing agent sulfonated lignin, anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product, non-ionic dispersing agent oxyethane and propylene oxide block copolymer, hole-blocking agent, acid-base modifier:
Anionic dispersing agent sulfonated lignin 21~41
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 20.5~47.4
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 5.3~10.3
Hole-blocking agent 21~25.6
Acid-base modifier 2.6~5.3.
2. a kind of negatively charged ion according to claim 1-nonionic Compositional type gasification slurries additive agent, it is characterized in that: described sulfonated lignin are one or more in sodium salt, calcium salt, magnesium salts or the ammonium salt; The polymerization degree of described naphthalene sulfonic acidformaldehyde condensation product is 7~15; The molecular-weight average of described non-ionic dispersing agent oxyethane and propylene oxide block copolymer is controlled between 4000 to 6000; Described hole-blocking agent is that carbonate can be one or more in sodium salt, sylvite or the ammonium salt, is to comprise the chemical that carbonate maybe can generate carbonate; Described acid-base modifier is one or both in solid sodium hydroxide, the potassium hydroxide.
3. a kind of negatively charged ion according to claim 2-nonionic Compositional type gasification slurries additive agent, it is characterized in that: each component forms by following mass parts uniform mixing:
Anionic dispersing agent sodium lignosulfonate 21
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 47.4
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 5.3
Yellow soda ash 21
Sodium hydroxide 5.3.
4. a kind of negatively charged ion according to claim 2-nonionic Compositional type gasification slurries additive agent, it is characterized in that: each component forms by following mass parts uniform mixing:
Anionic dispersing agent sodium lignosulfonate 41
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 20.5
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 10.3
Salt of wormwood 25.6
Potassium hydroxide 2.6.
5. a kind of negatively charged ion according to claim 2-nonionic Compositional type gasification slurries additive agent, it is characterized in that: each component forms by following mass parts uniform mixing:
Anionic dispersing agent calcium lignin sulphonate 30
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 40
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 6
Volatile salt 21
Sodium hydroxide 3.
6. a kind of negatively charged ion according to claim 2-nonionic Compositional type gasification slurries additive agent, it is characterized in that: each component forms by following mass parts uniform mixing:
Anionic dispersing agent magnesium lignosulfonate 21
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 47.4
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 5.3
Yellow soda ash 21
Sodium hydroxide, 1: 1 mixture 5.3 of potassium hydroxide.
7. a kind of negatively charged ion according to claim 2-nonionic Compositional type gasification slurries additive agent, it is characterized in that: each component forms by following mass parts uniform mixing:
Anionic dispersing agent ammonium lignosulphonate 41
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 20.5
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 10.3
Volatile salt 25.6
Sodium hydroxide 2.6.
8. a kind of negatively charged ion according to claim 2-nonionic Compositional type gasification slurries additive agent, it is characterized in that: each component forms by following mass parts uniform mixing:
The mixture 30 of anionic dispersing agent calcium lignin sulphonate and sodium lignosulfonate
Anionic dispersing agent naphthalene sulfonic acidformaldehyde condensation product 40
Non-ionic dispersing agent oxyethane and propylene oxide block copolymer 6
Yellow soda ash 21
Sodium hydroxide 3.