CN102010953B - 一种钢紫铜半固态复合板的均匀后处理方法 - Google Patents
一种钢紫铜半固态复合板的均匀后处理方法 Download PDFInfo
- Publication number
- CN102010953B CN102010953B CN201010613871A CN201010613871A CN102010953B CN 102010953 B CN102010953 B CN 102010953B CN 201010613871 A CN201010613871 A CN 201010613871A CN 201010613871 A CN201010613871 A CN 201010613871A CN 102010953 B CN102010953 B CN 102010953B
- Authority
- CN
- China
- Prior art keywords
- red copper
- steel
- semisolid
- clad plate
- composite plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种钢紫铜半固态复合板的均匀后处理方法,属于钢紫铜半固态复合板界面剪切强度室温轧制后处理研究领域,本发明对由1.2mm厚的08Al钢板和1.5mm厚的紫铜覆层构成的钢紫铜半固态复合板,在室温下,在精密轧机上,进行总压下率为1.8%的、第一道次与第二道次的道次压下率比例为1∶3.5~1∶1的二道次轧制处理,可将复合板横向界面剪切强度差值降低到2.2MPa以内。
Description
技术领域
本发明涉及一种钢紫铜半固态复合板的界面剪切强度室温轧制后处理方法。
背景技术
公开号:CN101117696A,发明名称:“一种钢背铝基半固态复合板的后处理方法”上,阐述了钢背铝基半固态复合板的室温轧制后处理方法,即,在室温下,在精密轧机上,对钢背铝基半固态复合板,进行轧制后处理,利用轧制处理产生的铝基覆层与钢背变形量的差异来弥补复合凝固冷却过程中铝基覆层与钢背收缩量的差异,进而减小复合板界面附加应力,使复合板界面剪切强度得以提高。该方法工艺简单、复合板界面剪切强度值提高较大,但是,由于该方法在进行单道次轧制处理时存在铝基覆层变形量不均匀现象,因此通常导致复合板界面剪切强度的不均匀分布,在复合板横向上的界面剪切强度差值可高达2.6~3.2MPa。
钢紫铜半固态复合板是采用固态钢板与紫铜半固态浆料复合而成的、由1.2mm厚的08Al钢板和1.5mm厚的紫铜覆层构成的半固态复合板,当采用CN101117696A专利方法进行轧制后处理时,在较为理想的压下率为1.8%条件下,由于紫铜覆层在复合板横向上的变形量分布不均匀,导致复合板横向上的界面剪切强度之间的差值可高达4.1MPa。
对于钢紫铜半固态复合板,横向界面剪切强度的差值越小,使用可靠性越高,应用范围越广,因此钢紫铜半固态复合板横向界面剪切强度的差值越小越好。
发明内容
本发明所要解决的技术问题是,克服现有钢紫铜半固态复合板室温轧制后处理方法“横向界面剪切强度差值大”的不足,提供一种能够提高钢紫铜半固态复合板横向界面剪切强度分布均匀性的后处理方法,进一步缩小复合板横向界面剪切强度的差值。
本发明解决其技术问题所采用的技术方案是:对钢紫铜半固态复合板,在室温下,在精密轧机上,进行总压下率为1.8%的、第一道次与第二道次的道次压下率比例为1∶3.5~1∶1的二道次轧制处理。
本发明的有益效果是:对于复合板室温轧制处理,由于辊跳、基体不均等因素的存在,在复合板横向上不可避免地产生不均匀变形,导致复合板横向界面剪切强度的差异,而且压下率越大,横向上的变形越不均匀,复合板横向界面剪切强度的差异越大。如果将单道次大压下率轧制产生的横向上的不均匀变形,分解到多道次小压下率变形当中,则可将单道次轧制处理产生的横向变形量的大差异,分解为多道次的横向变形量的小差异,而且通过各道次压下率的优化组合,还可以进一步协调横向变形量的差异。本发明就是利用第一道次与第二道次的道次压下率的优化组合进一步减小和协调了室温轧制处理的横向变形量的差异,从而达到了降低复合板横向界面剪切强度差值的目的。利用本发明,对钢紫铜半固态复合板进行室温轧制处理,可将复合板横向界面剪切强度差值降低到2.2MPa以内,比采用CN101117696A专利方法进行室温轧制处理得到的4.1MPa至少降低了46%。
具体实施方式
一种钢紫铜半固态复合板的均匀后处理方法,在室温下,在精密轧机上,对由1.2mm厚的08Al钢板和1.5mm厚的紫铜覆层构成的钢紫铜半固态复合板,进行二道次、总压下率为1.8%的轧制后处理,将单道次大压下率轧制后处理产生的紫铜覆层横向变形量的大差异,分解并协调为二道次小压下率轧制后处理产生的紫铜覆层横向变形量的小差异,从而进一步降低了复合板横向界面剪切强度差值,提高了钢紫铜半固态复合板界面剪切强度的分布均匀性。
实施方式一,对钢紫铜半固态复合板,进行第一道次与第二道次的道次压下率比例为1∶3.5的二道次室温轧制后处理,在复合板横向上的界面剪切强度差值为2.2MPa。
实施方式二,对钢紫铜半固态复合板,进行第一道次与第二道次的道次压下率比例为1∶3的二道次室温轧制后处理,在复合板横向上的界面剪切强度差值为2.0MPa。
实施方式三,对钢紫铜半固态复合板,进行第一道次与第二道次的道次压下率比例为1∶2.5的二道次室温轧制后处理,在复合板横向上的界面剪切强度差值为1.9MPa。
实施方式四,对钢紫铜半固态复合板,进行第一道次与第二道次的道次压下率比例为1∶2的二道次室温轧制后处理,在复合板横向上的界面剪切强度差值为2.0MPa。
实施方式五,对钢紫铜半固态复合板,进行第一道次与第二道次的道次压下率比例为1∶1的二道次室温轧制后处理,在复合板横向上的界面剪切强度差值为2.1MPa。
可见,对由1.2mm厚的08Al钢板和1.5mm厚的紫铜覆层构成的钢紫铜半固态复合板,进行总压下率为1.8%、第一道次与第二道次的道次压下率比例为1∶3.5~1∶1的二道次室温轧制后处理,可使复合板横向上的界面剪切强度差值降低到2.2MPa以内。
Claims (1)
1.一种钢紫铜半固态复合板的均匀后处理方法,在室温下,在精密轧机上,对由1.2mm厚的08Al钢板和1.5mm厚的紫铜覆层构成的钢紫铜半固态复合板进行轧制后处理,其特征在于,对钢紫铜半固态复合板,进行总压下率为1.8%的、第一道次与第二道次的道次压下率比例为1:3.5~1:1的二道次轧制处理,将复合板横向上的界面剪切强度差值降低到2.2MPa以内。