CN102010580A - PET multicolor bottle - Google Patents
PET multicolor bottle Download PDFInfo
- Publication number
- CN102010580A CN102010580A CN 201010544354 CN201010544354A CN102010580A CN 102010580 A CN102010580 A CN 102010580A CN 201010544354 CN201010544354 CN 201010544354 CN 201010544354 A CN201010544354 A CN 201010544354A CN 102010580 A CN102010580 A CN 102010580A
- Authority
- CN
- China
- Prior art keywords
- pet
- bottle
- multicolor
- short
- polycarbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a polyethylene terephthalate (PET) multicolor bottle, which comprises the following components in part by mass: 30 to 99.8 parts of polyethylene terephthalate (PET for short), 0.01 to 35 parts of polymethyl methacrylate (PMMA for short) and 0.01 to 35 parts of polycarbonate (PC for short). The PET multicolor bottle prepared from the polyethylene terephthalate (PET), the polymethyl methacrylate (PMMA) and the polycarbonate (PC) serving as raw materials has three-dimensional, hierarchical and multicolor effects, and a production process for preparing the PET multicolor bottle has high stability and continuity and is environmentally-friendly. The PET multicolor bottle has low cost of raw materials, and a simple process, can be widely applied to various plastic bottles, and has high market value and great market potential.
Description
Technical field
The present invention relates to technical field of polymer materials, referring in particular to poly terephthalic acid ethylene glycol (being called for short PET), polymethylmethacrylate (being called for short PMMA), polycarbonate (being called for short PC) is the PET illusion-colour bottle of feedstock production.
Background technology
In today of more and more paying attention to environmental consciousness, the PET bottle is because keeping quality is good, withstand voltage and heat-resisting, have characteristics such as low environment contaminative and energy consumption and begun progressively to replace the Traditional Packing material, in daily life, play a part very importantly, become the wrapping material of tool growth potentiality.
Traditional PET bottle adopts spraying method that body is modified, can present effects such as stereoscopic sensation, gradation sense and magical feeling with the expectation body, but existing product does not only present above-mentioned effect, and cost height, the production technique instability, also contaminate environment can not satisfy modern society to PET bottle product quality and the more and more higher requirement of production efficiency.
Summary of the invention
Weak point at prior art exists the objective of the invention is to design a kind of brand-new prescription, and the PET illusion-colour bottle that uses this prescription to produce has stereoscopic sensation and gradation sense, it is effective to dazzle beautiful illusion-colour, production cost is low, and stable processing technique and continuity are good, nonpollution environment.
For achieving the above object, the technical solution used in the present invention is: a kind of PET illusion-colour bottle, comprise poly terephthalic acid ethylene glycol (being called for short PET), polymethylmethacrylate (being called for short PMMA), polycarbonate (being called for short PC), the mass fraction of described each component is as follows respectively:
Poly terephthalic acid ethylene glycol (PET) 30-99.8;
Polymethylmethacrylate (PMMA) 0.01-35;
Polycarbonate (PC) 0.01-35.
The preparation method and the processing step of above-mentioned PET illusion-colour bottle are as follows:
1) polymethylmethacrylate and polycarbonate are put into stirrer with 1500 rev/mins of stirrings 5-10 minute, obtain solid-state compound;
2) compound being put into parallel dual-screw extruding machine extrudes and obtains concentrating master batch;
3) will concentrate master batch and poly terephthalic acid ethylene glycol is put into injection moulding machine, obtain the type embryo;
4) the type embryo is put into bottle blowing machine, can obtain PET illusion-colour bottle.
The PET illusion-colour bottle that the present invention obtains for feedstock production with poly terephthalic acid ethylene glycol (PET), polymethylmethacrylate (PMMA), polycarbonate (PC), not only have stereoscopic sensation, gradation sense and illusion-colour sense, and the stable processing technique and the continuity that prepare this PET illusion-colour bottle are better, and contaminate environment is few.Raw materials cost of the present invention is low, and technology is simple, but in the various plastic bottle producings of widespread use, has marketable value and huge market potential widely.
Embodiment
Now the present invention is described in further detail in conjunction with example:
Embodiment 1:
A kind of PET illusion-colour of the present invention bottle comprises poly terephthalic acid ethylene glycol (PET), polymethylmethacrylate (PMMA), polycarbonate (PC), and the quality that takes by weighing each component respectively is as follows:
Poly terephthalic acid ethylene glycol (PET) 790 grams;
Polymethylmethacrylate (PMMA) 10 grams;
Polycarbonate (being called for short PC) 200 grams.
The preparation method and the processing step of above-mentioned PET illusion-colour bottle are as follows:
1) 10 gram polymethylmethacrylates and 200 gram polycarbonate are put into stirrer with 1500 rev/mins of stirrings 5 minutes, obtain solid-state compound;
2) compound being put into parallel dual-screw extruding machine extrudes and obtains concentrating master batch;
3) will concentrate master batch and 790 gram poly terephthalic acid ethylene glycol are put into injection moulding machine, obtain the type embryo;
4) the type embryo is put into bottle blowing machine, can obtain PET illusion-colour bottle.
Embodiment 2:
A kind of PET illusion-colour of the present invention bottle comprises poly terephthalic acid ethylene glycol (PET), polymethylmethacrylate (PMMA), polycarbonate (PC), and the quality that takes by weighing each component respectively is as follows:
Poly terephthalic acid ethylene glycol (PET) 998 grams;
Polymethylmethacrylate (PMMA) 1 gram;
Polycarbonate (being called for short PC) 1 gram.
The preparation method and the processing step of above-mentioned PET illusion-colour bottle are as follows:
1) 1 gram polymethylmethacrylate and 1 gram polycarbonate are put into stirrer with 1500 rev/mins of stirrings 10 minutes, obtain solid-state compound;
2) compound being put into parallel dual-screw extruding machine extrudes and obtains concentrating master batch;
3) will concentrate master batch and 998 gram poly terephthalic acid ethylene glycol are put into injection moulding machine, obtain the type embryo;
4) the type embryo is put into bottle blowing machine, can obtain PET illusion-colour bottle.
Embodiment 3:
A kind of PET illusion-colour of the present invention bottle comprises poly terephthalic acid ethylene glycol (PET), polymethylmethacrylate (PMMA), polycarbonate (PC), and the quality that takes by weighing each component respectively is as follows:
Poly terephthalic acid ethylene glycol (PET) 600 grams;
Polymethylmethacrylate (PMMA) 300 grams;
Polycarbonate (being called for short PC) 100 grams.
The preparation method and the processing step of above-mentioned PET illusion-colour bottle are as follows:
1) 300 gram polymethylmethacrylates and 100 gram polycarbonate are put into stirrer with 1500 rev/mins of stirrings 8 minutes, obtain solid-state compound;
2) compound being put into parallel dual-screw extruding machine extrudes and obtains concentrating master batch;
3) will concentrate master batch and 600 gram poly terephthalic acid ethylene glycol are put into injection moulding machine, obtain the type embryo;
4) the type embryo is put into bottle blowing machine, can obtain PET illusion-colour bottle.
As prescription or the method for above-mentioned embodiment, employing and the same or similar prescription of this embodiment or other PET illusion-colour bottles that method obtained are all within protection domain of the present invention.
Claims (1)
1. a PET illusion-colour bottle comprises poly terephthalic acid ethylene glycol (being called for short PET), polymethylmethacrylate (being called for short PMMA), polycarbonate (being called for short PC), and it is characterized in that: the mass fraction of described each component is as follows respectively:
Poly terephthalic acid ethylene glycol (PET) 30-99.8;
Polymethylmethacrylate (PMMA) 0.01-35;
Polycarbonate (PC) 0.01-35.