CN1019932C - Shaped products of colour cement and method for mfg. same - Google Patents
Shaped products of colour cement and method for mfg. same Download PDFInfo
- Publication number
- CN1019932C CN1019932C CN 88104194 CN88104194A CN1019932C CN 1019932 C CN1019932 C CN 1019932C CN 88104194 CN88104194 CN 88104194 CN 88104194 A CN88104194 A CN 88104194A CN 1019932 C CN1019932 C CN 1019932C
- Authority
- CN
- China
- Prior art keywords
- cement
- glue
- water
- plain
- weight ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a cement forming product and a field of a production method thereof, particularly to a color cement forming product and a production method thereof. The cement forming product of the present invention is composed of a substrate, stereo lines formed into a color picture, and color filling parts, wherein the substrate is coagulated by a cement mixture, the pictures which are firstly formed from the inner part and are formed from the stereo lines of the color picture and the color filling parts formed among the lines by color cement are arranged on the substrate, and the stereo lines are composed of cement color picture lines or metal plates. Products of the present invention comprise color picture waterstone, color picture stained stone waterstone and color picture artificial marble. The cement forming product of the present invention has the method that an initial edition is turned into a stencil edition which is turned into a blank edition, the color filling parts are manufactured among the lines of the blank edition, and the color cement forming product can be formed by grinding and surface layer processing. The product of the present invention has an artistic style of the Chinese painting and simultaneously has the practicability, for example, the product has the advantages of high degree of finish, no cracks, abrasion resistance and strong compressive resistance, and the product can be used for building finishing ornaments.
Description
The present invention relates to cement moulded products and production method thereof.
Cement is main construction material in modern architecture, and wherein also mostly as building and ornament materials is the sheet material of cement products such as terrazzo, artificial marble, cement tile etc., and their decorative pattern all belongs to the nature moulding.Though cement tile can be produced simple pattern,,, can not change figure by people's wish again so colour is dull, pattern contour is unclear owing to be the machine pressing moulding; Simultaneously since the color face of ornamental slab for paving the floor as thin as a wafer, can not the polishing of mano machine, so the fineness difference is not wear-resisting again, so practicality is also poor.On the other hand, some building and ornament materials adopts the high marble of price, aluminium alloy etc., and the effect of its decoration can only give people with magnificent sensation, and the glamour on the shortage art.Present situation is that the ornament materials kind is limited, and the decoration of many buildings is stereotyped, the effect on the shortage art.
Chinese patent application prospectus CN86103197A, denomination of invention are: described the construction and decoration gadget of being made up of surface layer, interlayer and osteoplaque in " colored carving marble construction and decoration gadget ", it is characterized in that this gadget has relief shape, surface layer adopts the macromolecular material that contains suitable ornament materials, then for adding the above-mentioned macromolecular material of required pigment, osteoplaque is to mix other aggregate stirring to form in above-mentioned macromolecular material to interlayer.Its preparation method is: " make the mud original text according to required decorative patterns; turn over external mold; on former, be coated with remover; be coated with the last layer macromolecular material again; coating is transferred and the coloured silk material of required pigment to be arranged as interlayer on this relief shape as surface layer; pour into thereon again be mixed with aggregate macromolecular material as osteoplaque, make the decorating building product after the demoulding ".This decoration adopts the macromolecular material of volume, costs an arm and a leg, and has only the interlayer of one deck surface layer and the wounded look of one deck on relief shape, can not polish by the mano machine; Therefore colored just one deck can not be used as floor and frayed position; In addition, the mud original text time has been grown easy deformation, and the ornament of being worked it out is owing to be added with ornament materials such as glittering material etc. in the surface layer, and color is no doubt bright magnificent, yet but lacks artistic effect.
The object of the invention is, mainly adopts cement to make decoration, and need not use macromolecular material to do raw material in a large number, and main simultaneously employing cement is made as plate-making material, thereby reduces the cost of ornament.
The object of the invention also is to create the road that a cement products and the fine arts combine, utilize the plasticity of cement before not solidifying, design according to people's design, reach perfect artistic effect, make cement products become the elegant art product, the grey image of cement is changed over coloured artistic image, thereby improve the artistic level of building decoration, make cement products both have practical value, also have artistic value and economic benefit.
Another purpose of the present invention is that colour does not exist only in product surface one deck, but thinks and acts in one and the same way, and construction makes chrominance section have suitable thickness internally, thereby makes goods wear-resisting and can protect the artistic image of color face forever.
Observe for many years through the inventor, research and practice, invented and had substrate, the cement moulded products of three-dimensional line and colored filling part, and adopt following technology: mainly with cement itself as plate-making material, translate into masterplate from parison plate, translate into the base version from masterplate again, form three-dimensional line internally, to fill between the lines of base version with certain thickness by the required coloured cement mixture of picture then, plasticity before utilizing cement not solidify, make coloured cement and three-dimensional line form graceful picture, both have the cement moulded products that practicality also has artistry thereby make, thereby the object of the invention has just reached fully.
Chinese painting is that lines are shaped, and its technique of painting is that the simple, straight-forward style of writing that draws lines is earlier gone up coloured silk then.Because playing up between the colour makes picture lively and graceful touching.The last color technology of cement products of the present invention is exactly to utilize the plasticity of cement before not solidifying, and carry out according to the program of drawing a picture of traditional Chinese Painting, so artistic effect is better.The picture of all lines moulding all can be constructed in cement products according to this technology.The lines method of forming can be translated into masterplate with the parison plate that is carved into lines, translates into the base version identical with the parison plate shape of band lines again with masterplate; Also can be according to the method for Chinese gold filigree, embed parison plate with sheet metal as three-dimensional line, translating at last with the sheet metal is the base version of lines, between the lines of above-mentioned two kinds of base versions, insert picture required do not solidify the coloured cement mixture, can obtain the cement products of colour painting.
Problem of materials about plate-making is very important, goes into operation in batch and reduces cost and quality problems because this is related to cement products, and CN86103197A turns over external mold with the mud original text, though this masterplate of doing with mud is cheaply, and easy deformation in use.Japanese Unexamined Patent Publication No is that clear-56-148515 does masterplate with the thermoplasticity material, this masterplate cost height, and plate-making speed is slow.And cement itself is cheap construction material, make a plate to turn over again with it and make cement products such as sheet material, member etc. and can construct easily by the picture of design, plate-making speed is fast, used tool and technology are all simple, remarkable in economical benefits, mainly using cement itself is one of feature of the present invention as the plate-making material of cement products of the present invention.
After selecting for use cement to make a plate to produce cement products, also must solve the relevant technologies problem, as method for platemaking problem, problems such as release problems and fineness according to the characteristics of cement construction.
About method for platemaking, the present invention adopts lines moulding graphic arts process, on the one hand goes up color rendering effect owing to will obtain traditional Chinese Painting after with a simple, straight-forward style of writing, is the needs owing to practicality on the other hand.For example concrete floor must be stood people's thousand and steps on ten thousand and step on and wear-resistant, therefore color face can not be only on the surface, must simultaneously, can not reduce requirement with color surface construction in inner and make colour painting reach necessarily required thickness because of forming colour painting to the compression strength and the fineness of cement products.The lines method of forming can satisfy these requirements, thereby lines moulding graphic arts process is one of feature of the inventive method.Make a plate with the lines method of forming, make the lines of picture in construction, become three-dimensional line, between the lines of band lines base version, fill out the required coloured cement mixture of picture, utilize three-dimensional line the coloured cement mixture to be controlled in certain zone of lines and make it in certain thickness, flow naturally, play up and permeate, thereby generate lively picture.Goods are after polishing, and from the plane, lines (black or other color) are the profiles of picture, and the coloured cement mixture between lines is through the complex colors of playing up, thereby are formed with the picture of traditional Chinese Painting style, and this cement products is both beautiful and practical.
About the demoulding or misplacing of stencil problem is the major issue of producing by batch in the masterplate; because cement itself is exactly gelling agent; cohesive force is very strong, can not make releasing agent with used oil when particularly making plate-making material with cement, because used oil can not stick together coloured cement and base version.In mask-making technology of the present invention, use remover such as waterproofing agent, shellac varnish, when the demoulding, obtain good result.
Below according to accompanying drawing invention is explained in detail as embodiment:
Accompanying drawing 1 is the production method block diagram of coloured cement goods.
Accompanying drawing 2 is the front views as the square decorative panel of cement moulded products of the present invention; Accompanying drawing 3 is that accompanying drawing 2 is with the A-A sectional view of coloured cement mixture as the square decorative panel of three-dimensional line; Accompanying drawing 4 is that accompanying drawing 2 is with the A-A sectional view of sheet metal as the square decorative panel of three-dimensional line; Accompanying drawing 5 and accompanying drawing 6 are parison plates, and accompanying drawing 7 and accompanying drawing 8 are masterplates, and accompanying drawing 9 and accompanying drawing 10 are base versions, and accompanying drawing 11 and accompanying drawing 12 are moulded products of the present invention of band mould.
Coloured cement goods of the present invention are by substrate, and three-dimensional line and colored filling part are formed, and see accompanying drawing 2 and accompanying drawing 3, and accompanying drawing 2 is the front views as the square decorative panel of cement moulded products of the present invention.Accompanying drawing 3 is that accompanying drawing 2 is with the square decorative panel A-A sectional view of coloured cement mixture as three-dimensional line, the 1st, substrate, the 2nd, colored filling part, the 3rd, three-dimensional line.Substrate (1) is to be made of cement admixture, it comprises 1: 2～and 2.5 conventional cement mortar, fiber reinforced cement mortar, cement colored stone slurry, concrete etc., when the length of made sheet forming surpasses 40 centimetres, palpus reinforcement substrate (1) in.Coloured cement goods of the present invention can divide colour painting terrazzo, colored stone shape colour painting terrazzo and colour painting artificial marble.The three-dimensional line of goods (3) is solidified by the plain cement colorful slurry of black or colored 107 glue (or epoxy resin) and forms or be made of sheet metal, as make the colour painting terrazzo, its three-dimensional line (3) is by black cement or coloured cement: 107 glue (polyvinyl formal) (or epoxy resin): the weight ratio of water is that 1: 0.2: 0.4 plain cement colorful slurry solidifies and forms; As make colored stone shape colour painting terrazzo, as long as change black cement or the coloured cement in the above-mentioned plain cement colorful slurry into black or 1: 2.5 colored cement eight-centimetre stone powder; As make the colour painting artificial marble, its three-dimensional line (3) is by the cement silica flour of black or colored 1: 1～1.5: 107 glue (or epoxy resin): the weight ratio of water is that the quartzy powder enamel slurry of 1: 0.2: 0.4 plain cement solidifies and forms.Another kind of with the product of plastic metal sheet as three-dimensional line, this plastic metal sheet is copper sheet or aluminium flake.About colored filling part (2), as make the colour painting terrazzo, then by coloured cement: 107 glue (or epoxy resin): the weight ratio of water is that 1: 0.2: 0.4 plain cement colorful slurry solidifies and forms, as make colored stone shape colour painting terrazzo, then by colored 1: 2.5 cement eight-centimetre stone: 107 glue (or epoxy resin): the weight ratio of water is that the color slurry of 1: 0.2: 0.4 plain cement eight-centimetre stone solidifies and forms; As make the colour painting artificial marble, then by 1: 1～1.5 cement silica flour of colour: 107 glue (or epoxy resin): the weight ratio of water is that 1: 0.2: 0.4 plain cement silica flour slurry solidifies and forms.About the plastic metal sheet, its width is about 1 centimetre, and the one side is cut into indenting shape, by this clip sheet metal is embedded among the substrate (1) securely, its not a side of clip form picture as the three-dimensional line and the colored filling part of colour painting.Accompanying drawing 4 also is the A-A profile, but its three-dimensional line (3) is made of the plastic metal sheet.
The production method of coloured cement moulded products of the present invention such as accompanying drawing 1.
About mould:
With angle iron or timber mfg. moulding die optimum, mould must guarantee glacing flatness and accurate dimension accurately except that various specification and size must be arranged for cement products sheet material.Generally when making cement sheet material, use the angle iron mould that fixes, for guaranteeing that profiled sheeting is indeformable and connect together with mould securely in mould, the weldering muscle to be arranged; Generally do flexible mould, when making member, also use the respective activity mould with timber.
The technology of system parison plate is as follows:
For guaranteeing the glacing flatness of the space of a whole page, fixed mould is placed on the glass plate, the mixture that with the weight ratio of water and 107 glue (polyvinyl formal) is 4: 1 then is even in container for stirring, again 1: 1 cement and gypsum are poured in this container, the limit bevelling stirs, inject the said fixing mould when waiting to become starchiness, bevelling shake in limit is smash.After solidifying, version is turned over, duplicate designed picture on this light face, cut blocks for printing with cutter then, be about to the lines part and do not carve, stay on the space of a whole page, and remainder is dug up by desired thickness, this degree of depth is exactly the thickness of color face in future.Like this, lines are convex and appear on the space of a whole page, and for the purpose of misplacing of stencil was convenient, convex should have suitable tapering, are about to the three-dimensional line that these lines are carved into tapering.Brush shellac varnish so that parison plate is promptly made in reprint, see accompanying drawing 5, accompanying drawing 5 is the parison plates with taper gypsum cement three-dimensional line that have mould (5), the 4th, and cement gypsum.
The technology of making masterplate is as follows: will be up with parison plate (4) pattern of mould (5), and the mould with a same specification is placed on the mould of parison plate (4) again, and alignment is also fixed.(cement: 107 glue: the weight ratio of water is 1: 0.2: 0.4 a mixture with 107 glairin cement mortars, do not contain sand) inject 4～7 millimeters on mould, shake simultaneously and smash, fill and lead up mould with cement admixture subsequently, the demoulding after maintenance, brush waterproofing agent as releasing agent, stamp floor wax, with waterproof and air tight, making masterplate (7) (seeing accompanying drawing 7), was that the convex line bar on the parison plate becomes the concave bar originally on masterplate, can produce a large amount of masterplates with the continuous reprint of parison plate, wherein 7 is 107 glairin cement, the 8th, and cement admixture.
The technology of making the base version is as follows:
With up with the picture of the masterplate of mould, then flexible mould is fixed on the mould (5) of dress masterplate (7), with black cement or coloured cement: 107 glue (or epoxy resin): the weight ratio of water is the matrix lines that 1: 0.2: 0.4 107 glairin cement colorful slurry (or the plain cement colorful slurry of epoxy resin) is filled and led up masterplate, shake simultaneously and smash, as produce colored stone shape colour painting terrazzo and can replace above-mentioned black cement or coloured cement to make black or colored 107 glairin cement colored stone slurries or black or colour epoxy resene cement colored stone slurry with black or 1: 2.5 colored cement eight-centimetre stone powder, can be with 1: 1～1.5 coloured cement silica flour if produce artificial marble products: 107 glue (or epoxy resin): the weight ratio of water be that quartzy powder enamel slurry of 1: 0.2: 0.4 107 glairin cement or the quartzy powder enamel of the plain cement of epoxy resin are starched the matrix lines of filling and leading up masterplate (7), fills and leads up mould with cement admixture then.Cement admixture comprises 1: 2～2.5 conventional cement mortar, and fiber adds strength mortar, concrete or cement colored stone slurry, and the sheet material more than 40 centimetres must reinforcement in this way.Solidify back misplacing of stencil maintenance, make the base version, on the space of a whole page of base version, form black or colored convex bargraphs, its shape is fully identical with parison plate, and different is that original lines are replaced by black or color solid lines, sees accompanying drawing 9, wherein 8 is cement admixtures, the 9th, and various cement colorful slurries.
The technology of making colored filling part (2) is as follows:
Close out the plain cement colorful slurry of versicolor 107 glairin cement colorful slurry or epoxy resin at first respectively, can close out earlier 107 glue or the color slurry of the plain cement eight-centimetre stone of epoxy resin as producing colored stone shape colour painting terrazzo; As produce artificial marble, can close out earlier quartzy powder enamel slurry of 107 glairin cement or the quartzy powder enamel slurry of the plain cement of epoxy resin, need allocate composite coloured cement mortar or coloured cement silica flour slurry etc. by picture then, starch with painting mode with this coloured silk, by picture they are inserted respectively between the lines (3) of base version, again by the cement construction method colored filling part (2) roll receive water till.After colored filling part (2) solidifies, carry out the maintenance misplacing of stencil, the mano machine polishes flat, polishing, and brush oxalic acid is so that colored bright-coloured, brush waterproofing agent and waxing are so that the anti-be full of cracks of goods, through maintenance, promptly can be made into coloured cement plate again, i.e. colour painting terrazzo plate or colored stone shape colour painting terrazzo plate or colour painting artificial marble plate with coloured cement lines, see accompanying drawing 1,1st, the substrate that cement admixture constitutes.The method of manufacturing member similarly.
The method of coloured cement moulded products that manufacturing has the sheet metal lines is as follows:
Flexible mould is lain against on the glass plate, to pour water and 107 glue weight ratios in container into be 1: 3 mixture and stir, land plaster is poured into, the limit bevelling stirs, make the mixture in the container become the congee shape, this congee shape mixture is poured in the flexible mould, and making the thickness after this 107 glue calcium plaster solidifies is 4～7 millimeters, solidifies back brush shellac varnish or waterproofing agent.Then picture is copied on the plane of this 107 glue plasterboard, with sharp knife by the picture lines matrix lines ditch that vertically draws.The sheet metal of getting about 10 mm wides is copper sheet or aluminium flake for example, with scissors the one side is cut into staggered dogtooth, and purpose is to increase sheet metal fixing fastness in substrate.Not clip one side of cutting mouth metal plate is inserted in the chase of lines figure bend, firmly sheet metal is pressed vertically downward then, vertical compression arrives with till glass plate as backing plate contacts.Inject interior 4～7 millimeters of mould with 107 glairin cement mortars then, fill up mould with cement admixture again, solidify back misplacing of stencil maintenance, at last version is turned over, with cutter the gypsum on the version is partly carved, sheet metal is exposed on the substrate (1) becomes the three-dimensional line figure, makes parison plate, sees accompanying drawing 6, wherein 5 is moulds, 4 is 107 glairin cement, the 8th, and cement admixture, the 6th, sheet metal.
The method of masterplate of coloured cement moulding product that manufacturing has the sheet metal lines is as follows:
With the parison plate figure of band sheet metal up, other gets a mould and makes and align with the mould of parison plate and fixing, and 107 glairin cement mortars are injected in the mould 4～7 millimeters, shake simultaneously and smash, fill and lead up mould with cement admixture again, climb over mould before the due-in water, parison plate is taken off, handling through maintenance and surface layer, obtain masterplate, is the cancave groove figure that certain depth is arranged on its surface, see accompanying drawing 8, wherein, 7 is 107 glairin cement, the 8th, and cement admixture.
The base version technology of making the band sheet metal is as follows:
On above-mentioned masterplate according to the construction thickness of color face and the chase degree of depth of above-mentioned masterplate, the sheet metal that one side clip is become indenting shape is along in the vertical cancave groove that inserts above-mentioned masterplate of clip one side not, the delivery tool makes on its mould that is fixed on masterplate subsequently, cement admixture is poured into, up to mould is filled and led up, the maintenance misplacing of stencil, originally the sheet metal that was inserted in the cancave groove is securely fixed on the substrate by its clip, constitute and have the base version of sheet metal three-dimensional line figure, see accompanying drawing 10, wherein, the 8th, cement admixture, the 6th, sheet metal, the 5th, mould.
The making of other colored filling part, polishing, polishing surface layer handle have colour painting terrazzo, the colored stone shape colour painting terrazzo of coloured cement lines with above-mentioned making respectively or have the technology of colour painting artificial marble of coloured cement lines identical.
Embodiment 1:
Water intaking: 107 glue weight ratios are that 4: 1 mixture and 1: 1 cement and the starchiness mixture of gypsum inject mould, after solidifying, duplicate picture and cut blocks for printing on its light face, and the brush shellac varnish is made parison plate.Inject 5 millimeters of 107 glairin cement mortars having on the parison plate of mould, use 1: 2 conventional cement mortar to fill and lead up mould subsequently, make masterplate.Having on the masterplate of mould, starching the matrix lines of filling and leading up masterplate, using 1: 2.5 conventional cement mortar to fill and lead up mould again, making blanket with 107 glairin cement black color.Between the lines of this base version, insert by the required 107 glairin cement colorful slurry of all kinds of picture, make colored filling part, black lines on the base version and colored filling part constitute picture, behind the maintenance misplacing of stencil, the colour painting terrazzo plate with black cement lines is made in polishing, polishing, brush oxalic acid and waterproofing agent, waxing.
Embodiment 2:
Picture is copied on the plane of 107 glue plasterboards, go out matrix lines ditch with graduating with cutter, not clip one side of the copper sheet of clip is inserted in this matrix lines ditch, 107 glairin cement mortars inject interior 6 millimeters of mould, use 1: 2.5 conventional cement mortar to fill and lead up mould again, carve and go gypsum partly to make parison plate.Inject 6 millimeters of 107 glairin cement mortars having on the parison plate of mould, use 1: 2.5 conventional cement mortar to fill and lead up mould again, make masterplate.The aluminium flake that to cut then mouthful vertically inserts in the cancave groove of masterplate along clip one side not, 1: 2 conventional cement mortar is injected and fills and leads up mould, makes the base version.Between the sheet metal lines of this base version, starch by the required plain cement silica flour of epoxy resin of all kinds of inserting of picture, then color face is rolled and receive till the water, solidify back maintenance misplacing of stencil and make colour painting artificial marble plate with copper sheet three-dimensional line through polishing, polishing and surface layer processing.
The used lines method of forming of coloured cement moulded products of the present invention also comprises the goods of those wide lines, and these wide lines can be flatbed, arc top type, the matrix that tapering is arranged or lower arcuate surface type etc., make polychrome sculpture face with so wide lines.Thereby can be made into the polychrome sculpture goods, simultaneously above indication " protruding " and " recessed " all is to illustrate of the present inventionly as embodiment, and " protruding " and " recessed " can intercourse sometimes.
The raw material that the inventive method is used for making parison plate, masterplate and base version is various plain cement admixtures slurries, the substrate cement admixture.
So the inventive method is starched with various plain cement admixture slurries or coloured cement mixture and is made parison plate, masterplate and base version, exactly because cement is inexpensive raw material, thereby low cost of manufacture of the present invention, but also can use the more expensive material of price in the present invention, make masterplate such as thermoplastic plastic, rubber, metal mold etc., produce the base version with such masterplate then.Equally, the gelling agent of Shi Yonging has 107 glue, epoxy resin in the present invention, and in addition, the present invention also can use similar gelling agent such as various unsaturated polyester resin.
Coloured cement goods of the present invention have floor, wallboard, balcony slab, staircase boards, ceiling, windowsill version, all kinds of fine arts decorative panel and various decoration element, mural painting, board, handicraft, small-sized furniture and the sculpture spare etc. of colour painting terrazzo, colored stone shape colour painting terrazzo and colour painting artificial marble.
The production method that the inventive method will be produced the gold filigree handicraft of the lines composition method of cement products technology and picture or China combines, the coloured cement goods of being produced are bright in luster, picture is clear, be similar to the picture effect and have Chinese folk art style, for the cement building material goods develop new road of developing to the handicraft direction.Because color face thickness is no less than 4 millimeters, it is highly polished to handle the back through maintenance, polishing, polishing and surface layer, do not chap, wear-resisting, compressive resistance is strong, therefore both having had artistry also has very high practicability.Cement products of the present invention is the cheap flawless finish product that are suitable for indoor and outdoor building finishing.Do such cement products factory and do not need big machinery, only can produce by batch with small instruments and tools, plate-making speed is fast, cheap, construction method is easy to grasp.
Claims (13)
1, the production method of coloured cement moulded products is characterized in that: with cement as main making sheet material and with black cement or coloured cement as the picture three-dimensional line, make colour painting water by following operation and waste stone:
(1) makes parison plate: be 1: 1 mixture and water to the weight ratio of 107 glue with cement to the weight ratio of gypsum be that 4: 1 mixture mixes the back and injects fixed mould in container, solidify the back and on its light face, duplicate picture, the picture lines have been carved into the tapering three-dimensional line, make parison plate, brush shellac varnish;
(2) make masterplate: with cement: 107 glue: the weight ratio of water is that 1: 0.2: 0.4 plain-water slurry injects 4-7 millimeter on the parison plate that places mould, fills and leads up mould with cement admixture again, and through the maintenance demoulding, the brush waterproofing agent is stamped floor wax, makes masterplate;
(3) make the base version: with black cement or coloured cement: 107 glue or epoxy resin: the weight ratio of water is that 1: 0.2: 0.4 plain cement colorful slurry injects the masterplate that places mould, fill and lead up the lines of masterplate, shake simultaneously and smash, fill and lead up mould with cement admixture again, through the maintenance demoulding, make the base version;
(4) make colored filling part:
Elder generation's water is that 1: 3 mixture is brushed on the base version with the weight ratio of 107 glue or epoxy resin, again with coloured cement: 107 glue or epoxy resin: the weight ratio of water is that the plain cement colorful slurry of each color of 1: 0.2: 0.4 need be inserted between each lines of the base version that places mould with painting mode by drawing, after color face filling part solidifies, through maintenance, the mano polishing, the colour painting terrazzo product is made in brush oxalic acid, brush waterproofing agent and waxing.
2, according to the said method of claim 1, it is characterized in that making in the base version operation cement eight-centimetre stone powder with black or colored 1: 2.5 in said (3): 107 glue or epoxy resin: the weight ratio of water is that 1: 0.2: 0.4 plain cement eight-centimetre stone powder enamel slurry replaces said plain cement colorful slurry, make in the colored filling part operation 1: 2.5 cement eight-centimetre stone with colour in said (4): 107 glue or epoxy resin: the weight ratio of water is that the color slurry of 1: 0.2: 0.4 plain cement eight-centimetre stone replaces said plain cement colorful slurry, makes colored stone shape colour painting terrazzo product.
3, according to the said method of claim 1, it is characterized in that making in the base version operation black or coloured cement silica flour with 1: 1～1.5 in said (3): 107 glue or epoxy resin: water weight ratio is that the quartzy powder enamel slurry of 1: 0.2: 0.4 plain cement replaces said plain cement colorful slurry, make in the colored filling part operation with coloured cement silica flour in said (4): 107 glue or epoxy resin: water weight ratio is that the quartzy powder enamel slurry of 1: 0.2: 0.4 plain cement replaces said plain cement colorful slurry, makes artificial marble products.
4, the production method of coloured cement moulded products is characterized in that: with cement as main plate-making material and with the plastic metal sheet as the colour painting lines, make the colorful terrazzo goods by following operation:
(1) make parison plate: land plaster is added entry: 107 glue or weight ratio are to make congee shape thing in 1: 3 the mixture, this congee shape thing is injected mould, thickness after it is solidified is the 4-7 millimeter, after solidifying, picture is replicated on the light face of this plasterboard, with cutter the picture lines vertically are carved into cancave groove, the plastic metal sheet of 10 mm wides that one side is cut into indenting shape along clip one side straight cutting not in above-mentioned matrix lines ditch, hand over cement: 107 glue: the weight ratio of water is that 1: 0.2: 0.4 plain-water slurry injects 4～7 millimeters on mould, fill up mould with cement admixture again, solidify back hectograph maintenance, version is turned over, with cutter gypsum on the version is partly carved, exposed sheet metal, make parison plate;
(2) make template: with cement: the weight ratio of 107 glue is that 1: 0.2: 0.4 plain-water slurry injects 4-7 millimeter on the parison plate that places mould, fills and leads up mould with cement admixture again, and through the maintenance misplacing of stencil, the brush waterproofing agent is stamped floor wax, makes masterplate;
(3) make the base version: the sheet metal of a side clip is vertically inserted in the chase of masterplate along clip one side not, inject on the masterplate that places mould until filling and leading up mould with cement admixture again, solidify back maintenance misplacing of stencil, make the base version;
(4) make colored filling part: first water is brushed on the base version with the mixture that with 107 glue or weight epoxy ratio is 1: 3, again with coloured cement: 107 glue or epoxy resin: the weight ratio of water is 1: 0.2: 0.4 a plain cement colorful slurry, need insert by picture with painting mode between each sheet metal lines of the base version that places mould, after color face solidifies, polish, brush oxalic acid, brush waterproofing agent and wax, make colored filling part through maintenance, mano, it and sheet metal lines form colour painting, make the colour painting terrazzo product.
5, according to the said method of claim 4, it is characterized in that making in the colored filling part operation in said (4), cement eight-centimetre stone with colored 1: 2.5: 107 glue or epoxy resin: the weight ratio of water is that the color slurry of 1: 0.2: 0.4 plain cement eight-centimetre stone replaces said plain cement colorful slurry, and making with the plastic metal sheet is the colored stone shape colour painting terrazzo product of lines.
6, according to the said method of claim 4, it is characterized in that making in the colored filling part operation of colored 1 in said (4): the cement silica flour of 1-1.5: 107 glue or epoxy resin: the weight ratio of water is that 1: 0.2: 0.4 plain cement silica flour slurry replaces said plain cement colorful to starch, and making with the plastic metal sheet is the artificial marble products of lines.
7, coloured cement moulded products, has the cement admixture substrate, it is characterized in that: form by three-dimensional line that constitutes colour painting and colored filling part on the substrate, at the picture of forming by the certain thickness colored filling part that between lines, forms by three-dimensional line that forms colour painting internally and coloured cement mixture on the substrate.
8, according to the said coloured cement moulded products of claim 7, it is characterized in that said colour painting three-dimensional line is by black cement: 107 glue or epoxy resin: the weight ratio of water is that 1: 0.2: 0.4 plain cement colorful slurry solidifies and forms, colored filling part is by coloured cement: the weight ratio of 107 glue (or epoxy resin) water is that 1: 0.2: 0.4 plain cement colorful slurry solidifies and forms, and goods are colour painting terrazzos.
9, according to the said coloured cement moulded products of claim 7, it is characterized in that said colour painting three-dimensional line is cut into the plastic metal sheet of indenting shape by a side non-clip one side constitutes, colored filling part is by coloured cement: 107 glue or epoxy resin: water weight ratio is that 1: 0.2: 0.4 plain cement colorful slurry solidifies and forms, and goods are colour painting terrazzos.
10, according to the said coloured cement moulded products of claim 7, it is characterized in that: said colour painting three-dimensional line is by the cement eight-centimetre stone powder of black or colored 1: 2.5: 107 glue or epoxy resin: the weight ratio of water is that 1: 0.2: 0.4 plain cement eight-centimetre stone powder enamel slurry solidifies and forms colored filling part by colored 1: 2.5 cement eight-centimetre stone powder: 107 glue or epoxy resin: the weight of water, solidify than the color slurry of the plain cement eight-centimetre stone that is 1: 0.2: 0.4 and to form, goods are colored stone shape colour painting terrazzos.
11, according to the said coloured cement moulded products of claim 7, it is characterized in that said colour painting three-dimensional line is cut into the plastic metal sheet of indenting shape by a side non-clip one side constitutes, colored filling part was by eight lis of powder of cement of colored 1: 2.5: 107 glue or epoxy resin: the weight ratio of water is that the color slurry of 1: 0.2: 0.4 plain cement eight-centimetre stone solidifies and forms, and goods are colored stone shape colour painting terrazzos.
12, according to the said coloured cement moulded products of claim 7, it is characterized in that the cement silica flour of said colour painting lines by black or colored 1: 1～1.5: 107 glue or epoxy resin: the weight ratio of water is that the quartzy powder enamel slurry of 1: 0.2: 0.4 plain cement solidifies and forms, colored filling part is by the cement silica flour of 1 of colour: 1-1.5: 107 glue or epoxy resin: the weight ratio of water is that the quartzy powder enamel slurry of 1: 0.2: 0.4 plain water Buddhist nun solidifies and forms, and goods are colour painting artificial marbles.
13, according to the said coloured cement moulded products of claim 7, it is characterized in that said colour painting lines are cut into the plastic metal sheet of indenting shape by a side non-clip one side constitutes, colored filling part is by the cement silica flour of 1 of colour: 1-1.5: 107 glue or epoxy resin: the weight ratio of water is that the quartzy powder enamel slurry of 1: 0.2: 0.4 plain cement solidifies and forms, and goods are colour painting artificial marbles.