CN101987469B - Method for producing veneers and wood jointed board - Google Patents
Method for producing veneers and wood jointed board Download PDFInfo
- Publication number
- CN101987469B CN101987469B CN2010105478740A CN201010547874A CN101987469B CN 101987469 B CN101987469 B CN 101987469B CN 2010105478740 A CN2010105478740 A CN 2010105478740A CN 201010547874 A CN201010547874 A CN 201010547874A CN 101987469 B CN101987469 B CN 101987469B
- Authority
- CN
- China
- Prior art keywords
- generous
- bar
- little side
- gluing
- veneers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a method for producing veneers and wood jointed boards, comprising the following steps of: breaking up rubber wood used as raw material into big square rods for manufacturing the veneers, and breaking up remaining small materials into small square rods; antiseptic material boiling: boiling the big square rods with water and then keeping the constant temperature for 4.5-6 hours and then taking the big square rods out; boiling the small square rods with the water and then keeping the constant temperature for 1.5-2 hours; adding 20kg/m<3> of borax, 15kg/m<3> of boric acid and 2-6kg/m<3> of sodium pentachlorophenate to the water when the materials are boiled; then dispersing, drying, planing, shuttle tooth gluing, toothing, board arranging, gluing and board jointing, then gluing and stacking to certain thickness, and then slicing the veneers, and drying the veneers at the temperature of 80-160 DEG C to obtain veneer finished products and then casing. In the invention, the rubber wood veneers with high quality are produced by taking the rubber wood as the raw material by using a special production method. The production method overcomes the defects of the prior art and opens up the new application of the rubber wood. Moreover, the product has high quality, high yield and cost reduction and does not discolor or deform.
Description
Technical field
The present invention relates to wooden processing technique field, specifically a kind of production method of wooden skin.
Background technology
Natural wooden skin because its very thin thickness, to the having relatively high expectations of timber, needs the reasonable timber could the wooden preferably skin of the quality of production in the production.Rubber wood timber is difficult to produce the measured wooden skin finished product of matter because wooden unstability is easy to generate variable color and distortion with existing method.
Summary of the invention
The purpose of this invention is to provide a kind of method of producing wooden skin and wooden jigsaw with rubber wood timber.
The production method of wooden skin of the present invention is carried out according to the following steps:
1) raw material: with the rubber wood timber is raw material, and after the system of being broken down into generous of wooden skin, remaining small powder is separated into little side's bar;
2) the anticorrosion material that boils: constant temperature keeps playing pot in 4.5～6 hours behind generous the water boil, and constant temperature kept 1.5～2 hours behind little side's bar water boil, puts into borax 20kg/m in the water when boiling material
3, boric acid 15kg/m
3, penta sodium pentachlorophenate 2～6kg/m
3
3) generous takes the dish out of the pot with little side's bar and to scatter in back 10 minutes, avoids sealing for a long time in a pile variable color;
4) oven dry: get into kiln drying with generous with little side's bar, the greenhouse degree is 50～85 ℃ in the kiln, dries about 24 hours for generous, little side's bar oven dry about 7 days, kiln discharge when making kiln temperature drop to 45～50 ℃ then;
5) by each face of planing behind the specification fracture;
6) carry out shuttle tooth → gluing → toe joint → row's plate → gluing → jigsaw with generous with little side's bar, process satisfactory generous wood strip piece and little side's wood strip piece;
7) generous wood strip piece is planished back gluing, the folded high certain thickness that arrives on four sides (to 38～42cm); Carry out wooden skin slicing then, the oven dry of wooden skin, 80～160 ℃ of bake out temperatures are (according to wooden tape measure cun size, thickness; In this scope, select bake out temperature) oven dry after wooden skin finished product, the vanning.
The present invention is raw material with the rubber wood timber, produces high-quality rubber wood timber wood skin with special production method, and utilizes the residue small powder to produce wooden jigsaw, makes full use of natural timber.Production method of the present invention has overcome the deficiency of prior art, has opened up the new purposes of rubber wood timber, and good product quality, nondiscolouring, indeformable, and yield rate is high, and cost reduces.
The specific embodiment
Embodiment 1
1) raw material: with the rubber wood timber is raw material, and after the system of being broken down into generous of wooden skin, remaining small powder is separated into little side's bar;
2) the anticorrosion material that boils: constant temperature keeps playing pot in 4.5 hours behind generous the water boil, and constant temperature keeps playing pot in 1.5 hours behind little side's bar water boil, puts into borax 20kg/m in the water when boiling material
3, boric acid 15kg/m
3, the addition of penta sodium pentachlorophenate is: do day: square bar was 2kg/m at 7 days with interior processing
3, that processed in 10～14 days is 3kg/m
3, that processing is 4kg/m more than 15 days
3, water boiling back control fire can not be too big, in order to avoid liquid medicine runs off;
3) generous takes the dish out of the pot with little side's bar and to scatter in back 10 minutes, avoids sealing for a long time in a pile variable color;
4) oven dry: get into kiln drying with generous with little side's bar, the greenhouse degree is 65 ℃ in the kiln, dries about 24 hours for generous, little side's bar oven dry about 7 days, kiln discharge when making kiln temperature drop to 45～50 ℃ then;
5) by each face of planing behind the specification fracture;
6) carry out shuttle tooth → gluing → toe joint → row's plate → gluing → jigsaw with generous with little side's bar, process satisfactory generous wood strip piece and little side's wood strip piece (shuttle tine length: 0.9cm, toe joint side's bar length keeps the plus tolerance of 2～3cm),
7) generous wood strip piece is planished back gluing, folded height on four sides to certain thickness to 38～42cm; Carry out wooden skin slicing then, the oven dry of wooden skin, 100～160 ℃ of bake out temperatures are (according to wooden tape measure cun size, thickness; In this scope, select bake out temperature; Like the thick temperature of 0.4mm is about 140 ℃, about 110 ℃ of the thick temperature of 0.3mm) after the oven dry wooden skin finished product, vanning.
It is by the splicing of specification requirement size that assembly is pulled, two ends equating then, and white glue with vinyl is all coated on both sides, prevents to split.
Embodiment 2:
Different with embodiment 1 is following steps:
2) the anticorrosion material that boils: constant temperature keeps playing pot in 6 hours behind generous the water boil, and constant temperature keeps playing pot in 2 hours behind little side's bar water boil, puts into borax 20kg/m in the water when boiling material
3, boric acid 15kg/m
3, the addition of penta sodium pentachlorophenate is: rainy season the sky: square bar was 4kg/m at 7 days with interior processing
3, that processing is 6kg/m more than 7 days
3Water boiling back control fire can not be too big, in order to avoid liquid medicine runs off;
4) oven dry: get into kiln drying with generous with little side's bar, the greenhouse degree is 85 ℃ in the kiln, dries about 20 hours for generous, little side's bar oven dry about 6 days, kiln discharge when making kiln temperature drop to 45～50 ℃ then.
Claims (1)
1. the production method of a wooden skin is characterized in that carrying out according to the following steps:
1) raw material: with the rubber wood timber is raw material, and after the system of being broken down into generous of wooden skin, remaining small powder is separated into little side's bar;
2) the anticorrosion material that boils: constant temperature keeps playing pot in 4.5～6 hours behind generous the water boil, and constant temperature kept 1.5～2 hours behind little side's bar water boil, puts into borax 20kg/m in the water when boiling material
3, boric acid 15kg/m
3, penta sodium pentachlorophenate 2～6kg/m
3
3) generous takes the dish out of the pot with little side's bar and to scatter in back 10 minutes;
4) oven dry: get into kiln drying with generous with little side's bar, the greenhouse degree is 50～85 ℃ in the kiln, dries about 24 hours for generous, little side's bar oven dry about 7 days, kiln discharge when making kiln temperature drop to 45～50 ℃ then;
5) by each face of planing behind the specification fracture;
6) carry out shuttle tooth → gluing → toe joint → row's plate → gluing → jigsaw with generous with little side's bar, process satisfactory generous wood strip piece and little side's wood strip piece;
7) gluing, the folded high certain thickness that arrives carried out wooden skin slicing then after generous wood strip piece was planished on four sides, wooden skin oven dry, and 80～160 ℃ of bake out temperatures get wooden skin finished product, vanning after the oven dry.