CN101974815A - Acrylic fiber and wool blended yarn - Google Patents
Acrylic fiber and wool blended yarn Download PDFInfo
- Publication number
- CN101974815A CN101974815A CN201010566931XA CN201010566931A CN101974815A CN 101974815 A CN101974815 A CN 101974815A CN 201010566931X A CN201010566931X A CN 201010566931XA CN 201010566931 A CN201010566931 A CN 201010566931A CN 101974815 A CN101974815 A CN 101974815A
- Authority
- CN
- China
- Prior art keywords
- yarn
- acrylic fiber
- blended yarn
- wool
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an acrylic fiber and wool blended yarn which comprises the following components in percent by weight: 80-90 percent of acrylic fiber and 10-20 percent of wool fiber, wherein the fineness of the acrylic fiber is 1.5D and the length of the acrylic fiber is 38mm. The acrylic fiber and wool blended yarn has the advantages that: 1, the process is simple, and characteristics of the acrylic fiber and the wool fiber can be better compensated; 2, better yarn properties are obtained; and 3, the fabric made of the blended yarn has better taking function and meets the requirement on comfortable clothes for people.
Description
Technical field
The present invention relates to a kind of blended yarn, specifically, relate to a kind of acrylic fibers wool blended yarn, belong to the spinning engineering field.
Background technology
At present, the development trend of international clothes is " Machine Washable, wash and wear, easily maintenances, lightening ", and traditional pure spinning as single varieties such as cotton textiles, pure wools all more or less exists such-and-such deficiency, brought the defective in the design.
Blended yarn is the yarn that is spun into by two or more fiber, as fiber crops/cotton, hair/cotton, hair/fiber crops/thin,tough silk, wash/cotton, wash/hair or the like, broken the boundary between original cotton, fiber crops, hair, silk, the chemical fibre, can remedy the deficiency of single certain textile material, embody the superiority of each component fibre, to improve the einnehmen function of fabric, enlarge the scope of application.
Acrylic fiber has the laudatory title of " artificial wool ", the similar natural wool of its elasticity and bulking intensity, the fabric that it is made has preferably warmth retention property, stability, heat resistance, acidproof, antioxidant, organic solvent-resistant and light resistance, portability is better, but its hygroscopicity is relatively poor, stain easily, dress has a sulks sense, and alkali resistance, ABRASION RESISTANCE are relatively poor.
Wool fibre is the important source material of textile industry, and the fabric that it is made has good springiness, hygroscopicity is strong, warmth retention property good, good chemical stability.But on the one hand because the higher cost that causes of cost of material is higher, fabric color is single and based on cream-coloured on the other hand.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art part, a kind of new acrylic fibers wool blended yarn is provided.
Acrylic fibers wool blended yarn of the present invention comprises following ingredients according to percentage by weight: acrylic fiber be 80～90% and wool fibre be 10～20%, wherein the fineness of said acrylic fiber is 1.5D, length is 38mm.
Preferably,
Acrylic fibers wool blended yarn of the present invention comprises following ingredients according to percentage by weight: acrylic fiber be 85% and wool fibre be 15%.
Acrylic fibers wool blended yarn of the present invention has following technique effect:
1) technology is simple, can complementary better acrylic fiber and the characteristic of wool fibre;
2) has better yarn property;
3) lining that uses blended yarn of the present invention to make has better einnehmen function, satisfies people to wearing comfortable requirement clothes.
The specific embodiment
" the spinning experiment study course " that test method in the present embodiment is all edited with reference to the Yang Suoting that in July, 2007, China Textiles Press published.
Embodiment 1
In the present embodiment, the raw material of acrylic fibers wool blended yarn is composed as follows: 85% acrylic fiber, and 15% wool fibre, wherein the fineness of acrylic fiber is 1.2D, length is 38mm.Manually carrying out raw material mixes.
The production method step is as follows:
(1) blowing: the raw materials mixed dimension is made volume by scutcher;
(2) comb and parallel cotton fibers prior to spinning: will roll into the carded sliver by carding machine;
(3) drafting: the carded sliver is merged ripe bar by drawing frame;
(4) rove: stretching oneself and yawn to attenuate for ripe that will merge by Speed frames becomes the rove bar;
(5) spun yarn: rove is stretched oneself and yawn yarn into certain number by fine spining machine;
(6) winder: by bobbin winder with spinning volume cheese coning;
(7) the packing finished product blended yarn of weighing.
Embodiment 2
In the present embodiment, the raw material of acrylic fibers wool blended yarn is composed as follows: 80% acrylic fiber, and 20% wool fibre, wherein the fineness of acrylic fiber is 1.2D, length is 38mm.
The production method step is identical with embodiment 1.
Embodiment 3
In the present embodiment, the raw material of acrylic fibers wool blended yarn is composed as follows: 90% acrylic fiber, and 10% wool fibre, wherein the fineness of acrylic fiber is 1.2D, length is 38mm.
The production method step is identical with embodiment 1.
Reference examples 1
In this reference examples, the raw material of acrylic fibers wool blended yarn is composed as follows: 70% acrylic fiber, 30% wool fibre.
The production method step is identical with embodiment 1.
Reference examples 2
In this reference examples, the raw material of acrylic fibers wool blended yarn is composed as follows: 50% acrylic fiber, 50% wool fibre.
The production method step is identical with embodiment 1.
Embodiment 4
The yarn property of 1～2 acrylic fibers wool blended yarn of comparing embodiment 1～3 and reference examples.
1, yarn linear density test
The line density of yarn is one of yarn most important characteristic index, and it directly has influence on fabric property and appearance style, as stiffness, gloss, lines, ABRASION RESISTANCE etc.
1～2 acrylic fibers wool blended yarn that obtains to embodiment 1～3 and reference examples carries out the yarn linear density test.Its test result such as following table:
Table 1 yarn linear density experimental control table
| Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Reference examples 1 | Reference examples 2 |
| Yarn linear density (tex) | 28.1 | 28.1 | 28.1 | 28.1 | 28.1 |
2, yarn strength test
The end breakage rate of operation was closely related under yarn strength and this operation reached, and was the important references index that product waited and evaluated the spun yarn quality surely.
1～2 acrylic fibers wool blended yarn that obtains to embodiment 1～3 and reference examples carries out the yarn strength test.Its test result such as following table:
| Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Reference examples 1 | Reference examples 2 |
| Yarn strength (CN) | 300 | 280 | 260 | 250 | 220 |
Table 2 yarn strength experimental control table
3, yarn twist test
Yarn twist is to weigh an important parameter of yarn qualities, and what of yarn twist directly influence outward appearance and many physical properties of performance such as the brute force, ABRASION RESISTANCE, weight, elasticity, filoplume, shrinkage of yarn and product.
1～2 acrylic fibers wool blended yarn that obtains to embodiment 1～3 and reference examples carries out the yarn twist test.Its test result such as following table:
Table 3 yarn twist experimental control table
| Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Reference examples 1 | Reference examples 2 |
| Yarn twist 10CM/ | 49 | 49 | 49 | 49 | 49 |
4, irregularity test
Bar evenness is the important indicator of evaluation yarn qualities, whether the thickness of bar evenness reflection yarn is consistent, this numerical value is big more, yarn is inhomogeneous more with regard to thickness so, directly influence outward appearance uniformity, durability of fabric etc., and the superfine place of the yarn twist concentrates intensity decreases, brings many difficulties for the processing of later process, as winder, weave in broken end and stop platform and increase.
1～2 acrylic fibers wool blended yarn that obtains to embodiment 1～3 and reference examples carries out the yarn evenness test.Its test result such as following table:
The table 4 yarn Ubbelohde irregularity test table of comparisons
 |
Embodiment 1 | Embodiment 2 | Embodiment 3 | Reference examples 1 | Reference examples 2 |
| Strip (CV%) | 5.2 | 5.5 | 5.6 | 5.9 | 6.5 |
| Rove (CV%) | 4.5 | 4.6 | 4.7 | 4.6 | 4.8 |
| Spun yarn (CV%) | 18.5 | 18.9 | 19.2 | 19.2 | 19.5 |
From table 1 to table 4 as can be seen, acrylic fiber blended yarn of the present invention is with respect to existing
The acrylic fiber blended yarn has better yarn property.
Claims (2)
1. the acrylic fibers wool blended yarn is characterized in that, comprises following ingredients according to percentage by weight: acrylic fiber be 80～90% and wool fibre be 10～20%, wherein the fineness of said acrylic fiber is 1.5D, length is 38mm.
2. acrylic fibers wool blended yarn according to claim 1 is characterized in that, comprises following ingredients according to percentage by weight: acrylic fiber be 85% and wool fibre be 15%.