CN101974261B - 一种中性耐水腻子膏及其制备方法 - Google Patents

一种中性耐水腻子膏及其制备方法 Download PDF

Info

Publication number
CN101974261B
CN101974261B CN201010545220A CN201010545220A CN101974261B CN 101974261 B CN101974261 B CN 101974261B CN 201010545220 A CN201010545220 A CN 201010545220A CN 201010545220 A CN201010545220 A CN 201010545220A CN 101974261 B CN101974261 B CN 101974261B
Authority
CN
China
Prior art keywords
neutral water
water proof
proof putty
parts
putty cream
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201010545220A
Other languages
English (en)
Other versions
CN101974261A (zh
Inventor
吴军
杨永强
卢雅楠
孙志瑞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin 303 Chemical Building Material Co., Ltd.
Original Assignee
TIANJIN 303 CHEMICAL BUILDING MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN 303 CHEMICAL BUILDING MATERIAL CO Ltd filed Critical TIANJIN 303 CHEMICAL BUILDING MATERIAL CO Ltd
Priority to CN201010545220A priority Critical patent/CN101974261B/zh
Publication of CN101974261A publication Critical patent/CN101974261A/zh
Application granted granted Critical
Publication of CN101974261B publication Critical patent/CN101974261B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种中性耐水腻子膏及其制备方法，所述腻子膏是由包括下述原料及按照下述重量份数比例制成的混合物：水为18-25份，杀菌剂为0.1-0.3份，消泡剂为0.1-0.3份，成膜助剂为0.5-1.5份，羟丙基甲基纤维素为0.2-0.5份，丙烯酸乳液为7-20份，钠质膨润土为1-5份，重质碳酸钙为60-80份。本发明还提供了上述腻子膏的制备方法，这种腻子膏在性能上能够完全达到建筑行业标准JC/T 3049-1998建筑室内用腻子(N型)要求的指标。

Description

一种中性耐水腻子膏及其制备方法
技术领域
本发明涉及墙体装饰的技术领域、具体的说是一种用于内墙装饰的中性耐水腻子膏及其制备方法。
背景技术
传统的耐水腻子主要使用无机胶凝材料白水泥或灰钙与有机胶凝材料复合作用达到耐水效果，刮涂后无机胶凝材料白水泥遇水后，水化反应开始，氢氧化钙溶液达到饱和并析出晶体，同时形成钙矾石晶体及水化硅酸钙胶体，灰钙粉则是通过氢氧化钙和空气中二氧化碳作用形成晶体碳酸钙，两者在胶凝过程中都会有大量的氢氧化钙存在，从而造成了施工后基层表面表现出高碱性(PH值＞12)；另外，胶凝后形成的是一种刚性的无机高分子。这种高碱性和刚性使其出现了一些不可避免的缺点：一、这种高碱性需要长时间的养护才能够减弱，但不能完全消除，碱性过大容易造成面层乳胶漆的色浆分解，导致颜色不均，二、打磨时产生的碱性粉末会对施工者的皮肤及呼吸***造成危害；三、刚性基层的强度较大，使得打磨比较困难。
发明内容
本发明为了解决传统耐水腻子高碱性和刚性引起的缺点，如传统耐水腻子碱性大，养护周期长，不易打磨和打磨时碱性粉末对人体有伤害，以及涂刷乳胶漆时易造成发花等问题，提供了一种粘结强度高，易打磨，耐水性好的中性腻子膏(腻子PH值约为9，施工后腻子层的PH值接近中性)及其制备方法。
本发明是通过以下的技术方案实现的：
一种中性耐水腻子膏，所述腻子膏是由包括下述原料及按照下述重量份数比例制成的混合物：
水                                                 18-25份
杀菌剂                                             0.1-0.3份
消泡剂                                             0.1-0.3份
成膜助剂                                           0.5-1.5份
羟丙基甲基纤维素                                   0.2-0.5份
丙烯酸乳液                                         7-20份
钠质膨润土                                         1-5份
重质碳酸钙                                    60-80份。
本发明使用的杀菌剂主要是为了防止腻子膏的在储存过程中受到霉菌的侵害，所述的杀菌剂优选为异噻唑啉酮类杀菌剂；
本发明使用的消泡剂主要是用于抑制生产过程中产生的气泡，所述的消泡剂优选为矿物油型消泡剂；
本发明使用的成膜助剂是为了辅助丙烯酸乳液成膜，所述的成膜助剂优选为醇酯-12。
本发明使用的羟丙基甲基纤维素为有机增稠剂，主要起保水增稠作用，延长腻子层干燥时间，有助于成膜，保持腻子水份延长施工时间从而提高施工性，所述的羟丙基甲基纤维素优选为粘度为5～10万的羟丙基甲基纤维素。
所述丙烯酸乳液最主要的作用在于作为成膜物质，包裹在无机物粉体表面，依靠其成膜后自身的耐水性实现腻子层的耐水性能。所述丙烯酸乳液优选为固含量大于45％，玻璃化温度为20～30℃之间的苯乙烯和丙烯酸酯类共聚乳液，较高的玻璃化温度是其具有优异耐水性的保证。
本发明使用的钠质膨润土具有极强的保水性，防止腻子膏储存过程中发生离析，由于自身具有膨胀性，致使腻子膏具有很好的触变性，静止状态不易流动，但是刮涂时却十分流畅，有助于提高施工性能，所述钠质膨润土优选为目数为250～400目之间的钠质膨润土。
本发明使用重质碳酸钙则是主要的填料，所述重质碳酸钙优选为白度大于90，细度大于325目的重质碳酸钙。
本发明还提供了上述腻子膏的制备方法：
在水中加入杀菌剂、消泡剂、成膜助剂、丙烯酸乳液后，在搅拌条件下加入钠质膨润土和重质碳酸钙，最后加入羟丙基甲基纤维素的水溶液进行增稠，混合均匀后即可出料。
本发明所具有的有益效果为：
本发明提供了一种中性的耐水腻子膏。这种腻子膏在性能上能够完全达到建筑行业标准JC/T 3049-1998建筑室内用腻子(N型)要求的指标。且由于没有使用无机胶凝材料来实现耐水性，从而施工后的腻子层表现为中性，与传统的耐水腻子相比，具有养护周期短，易打磨，并且和乳胶漆的兼容性好等特点。膏状腻子可以直接批刮，施工简便。
具体实施方式
下面结合具体实施例对本发明作进一步说明。
实施例1
本发明是由下述重量的原料配制而成：水18份、杀菌剂0.2份、消泡剂0.2份、成膜助剂1份、羟丙基甲基纤维素0.3份、丙烯酸乳液15份、钠质膨润土4.3份、重质碳酸钙61份。
实施例2
本发明是由下述重量的原料配制而成：水25份、杀菌剂0.2份、消泡剂0.2份、成膜助剂0.5份、羟丙基甲基纤维素0.4份、丙烯酸乳液7份、钠质膨润土1.7份、重质碳酸钙65份。
实施例3
本发明是由下述重量的原料配制而成：水22份、杀菌剂0.2份、消泡剂0.2份、成膜助剂0.8份、羟丙基甲基纤维素0.3份、丙烯酸乳液10份、钠质膨润土3.5份、重质碳酸钙63份。
以上所述，仅是本发明的较佳实施例而已，并非对本发明的技术方案作任何形式上的限制。凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明的技术方案的范围内。

Claims (8)

1.一种中性耐水腻子膏，其特征在于：所述腻子膏是由下述原料及按照下述重量份数比例制成的混合物：
Figure FDA0000131162430000011
所述丙烯酸乳液为固含量大于45％，玻璃化温度在20～30℃之间的苯乙烯和丙烯酸酯类共聚乳液。
2.根据权利要求1所述的一种中性耐水腻子膏，其特征在于：所述的杀菌剂为异噻唑啉酮类杀菌剂。
3.根据权利要求1所述的一种中性耐水腻子膏，其特征在于：所述的消泡剂为矿物油型消泡剂。
4.根据权利要求1所述的一种中性耐水腻子膏，其特征在于：所述的成膜助剂为醇酯-12。
5.根据权利要求1所述的一种中性耐水腻子膏，其特征在于：所述的羟丙基甲基纤维素为粘度为5～10万的羟丙基甲基纤维素。
6.根据权利要求1所述的一种中性耐水腻子膏，其特征在于：所述钠质膨润土为目数为250～400目之间的钠质膨润土。
7.根据权利要求1所述的一种中性耐水腻子膏，其特征在于：所述重质碳酸钙为白度大于90，细度大于325目的重质碳酸钙。
8.权利要求1所述的一种中性耐水腻子膏的制备方法，其特征在于：
在水中加入杀菌剂、消泡剂、成膜助剂、丙烯酸乳液后，在搅拌条件下加入钠质膨润土和重质碳酸钙，最后加入羟丙基甲基纤维素的水溶液进行增稠，混合均匀后即可出料。
CN201010545220A 2010-11-16 2010-11-16 一种中性耐水腻子膏及其制备方法 Expired - Fee Related CN101974261B (zh)