CN101948666A - Method and equipment for continuously preparing hot melt glue - Google Patents
Method and equipment for continuously preparing hot melt glue Download PDFInfo
- Publication number
- CN101948666A CN101948666A CN 201010285864 CN201010285864A CN101948666A CN 101948666 A CN101948666 A CN 101948666A CN 201010285864 CN201010285864 CN 201010285864 CN 201010285864 A CN201010285864 A CN 201010285864A CN 101948666 A CN101948666 A CN 101948666A
- Authority
- CN
- China
- Prior art keywords
- hot melt
- melt adhesive
- metered charge
- resin
- metering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a method and equipment for continuously preparing hot melt glue, and belongs to the technical field of preparing the hot melt glue. The method for continuously preparing the hot melt glue comprises the following steps of: metering extrusion of base resin, melt metering charge of solid tackifiers, metering charge of liquid plasticizers, metering charge of other auxiliary agents and violent stirring and mixing, and is characterized in that: the base resin is solely subjected to metering extrusion by an extruder according to a factory formula of the hot melt glue, and simultaneously the solid tackifiers, liquid plasticizers and other auxiliary agents are heated to the processing temperature respectively, the additives are metered and then added into a mixed kettle together with the base resin, the materials are uniformly mixed by violent stirring and subjected to discharging to obtain the hot melt glue products. The method for continuously preparing the hot melt glue has the advantages of simple process, high production efficiency, easy operation and low requirements on equipment and operators.
Description
Technical field
The present invention relates to a kind of continuous preparation method and equipment of hot melt adhesive, belong to the hot melt adhesive preparing technical field.
Background technology
Thermosol (abbreviation hot melt adhesive) typically refers to and at room temperature is solid-state, and it is liquid that heating and melting becomes, and behind coating, the wetting adherend, through pressing, cooling, finished bonding sizing agent in the kind at several seconds.Have curing speed soon, advantage such as not moisture and other solvents, be widely used in industries such as packing, printing, clothes and electronics.
The preparation method of hot melt adhesive adopts the melting mixing method usually, generally is divided into two kinds of interrupter method and continuous processings, and the former mainly is that the still formula is produced, and the latter mainly is extrusion molding production.It is each component of a certain amount of sizing agent to be pulverized the back adding have in the mixing kettle of stirring that the still formula is produced, the heating and melting and the back discharging that stirs, and then make second batch, its production efficiency is not high, and thermooxidative degradation easily takes place the hot melt adhesive component.Extrusion-type production is that each component of sizing agent is sent in the airtight forcing machine that is heated to certain temperature after pulverizing and tentatively mixing continuously, and fusion also mixes, and is extruded by screw rod continuously then.But because the various feed composition density variations of preparation thermosol are bigger, each component blanking speed difference, inhomogenous problem can appear in the material that enters forcing machine.In addition, the low-melting component in the raw material is in blanking channel or have the screw front end of certain temperature promptly to melt, and causes the uneven even obstruction cutting agency of blanking.If at first with each component of sizing agent raw material through mixing roll or the mixing forcing machine that enters again of reactor, on the one hand, technology is loaded down with trivial details, on the other hand, through mixing semi-product material malleable chemical property in transfer way, more than these reasons all can cause the quality problems and the production efficiency of hot melt adhesive.
But, carried out the improvement of many technologies in order to prepare the second best in quality hot melt adhesive product of continuous production.Patent CN 101264659A and U.S.P.No 4337721 disclose a kind of forcing machine equipment of processing hot melt adhesive, all be to increase by a vertical feeding unit at forcing machine charging opening place, can make each component of hot melt adhesive raw material thorough mixing before entering forcing machine, charging is even.But this method all has problems when producing the product of tackifier or liquid starting material large usage quantity.The fusing point of general tackifier is all lower, and as tackifier large usage quantity in hot melt adhesive, when producing, the tackifier that enter in the forcing machine can be melted in the screw flight, cause buildup, make the product of extruding inhomogeneous, quality problems occur.Using continuous processing to produce this hot melt adhesive needs forcing machine should make each feed composition thorough mixing of hot melt adhesive even, and extruder screw also needs good automatically cleaning ability.Patent U.S.P.No 4300839 discloses a kind of self-cleaning type forcing machine, this forcing machine has the screw rod of special shape, can solve the automatically cleaning problem of screw rod, and can make each material thorough mixing, but this forcing machine is not applied to the production of hot melt adhesive, and the forcing machine that needs special construction, technology are complicated.
The above-mentioned the whole bag of tricks of mentioning all can not solve a present the second best in quality hot melt adhesive quantity-produced difficult problem.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, provide a kind of successive processing method to come the hot melt adhesive of processability excellence, is that existing hot melt adhesive production technology is improved, thereby improves the hot melt adhesive performance, reduces investment and improve throughput rate.
The technical scheme that the present invention is adopted for achieving the above object is as follows:
A kind of continuous preparation method of hot melt adhesive, comprise that matrix resin metering is extruded, solid tackifier fusion metered charge, liquid plasticizer metered charge, other auxiliary agent metered charge, brute force mix step, it is characterized in that, according to the hot melt adhesive production formula matrix resin is extruded by the forcing machine metering separately, solid tackifier, liquid plasticizer and other auxiliary agents are heated to processing temperature respectively simultaneously, add in the mixing kettle simultaneously by metering and matrix resin, mix through brute force, discharging obtains the hot melt adhesive product.
Described matrix resin is selected from the mixture of ethylene-vinyl acetate resin, polyacrylate resin, polyethylene and ethylene copolymer resin, acrylic resin, vinylbenzene and block copolymer resin thereof or above-mentioned resin.
Described solid tackifier are selected from the mixture of petroleum resin, terpine resin, rosin and derivative thereof, resol, coumarone indene resin or above-mentioned resin.
Described liquid plasticizer is selected from aliphatics mineral oil, dioctyl phthalate (DOP), dibutyl phthalate, whiteruss.
Described other auxiliary agents are oxidation inhibitor, wax, functional agent, oxidation inhibitor is selected from N-phenyl-β naphthylamines, 2,6-ditertbutylparacresol, 4,4 ' thiobis (3-methyl-6-tert butyl) phenol, wax is selected from paraffin, Microcrystalline Wax, polyethylene wax, and functional agent is selected from medicine, conductive auxiliary agent or heat conduction auxiliary agent.
The specific equipment of the continuous preparation method of above-mentioned hot melt adhesive comprises screw extrusion press, solid tackifier metered charge jar, liquid plasticizer metered charge jar, other auxiliary agent metered charge jars, mixing kettle, powerful stirring arm.Screw extrusion press, solid tackifier metered charge jar, liquid plasticizer metered charge jar, other auxiliary agent metered charge jars link to each other with the mixing kettle that powerful stirring arm is housed by web member respectively.
Described screw extrusion press has metering system, and described solid tackifier metered charge jar, liquid plasticizer metered charge jar and other auxiliary agent metered charge jars all have heating and metering system.
Described powerful stirring arm has at least 10 paddles.
The processing temperature of described screw extrusion press is 60-200 ℃, the reinforced temperature of described solid tackifier fusion is 60-200 ℃, the reinforced temperature of described liquid tackifiers is 60-200 ℃, and the reinforced temperature of described other auxiliary agents is 60-200 ℃, and the Heating temperature of mixing kettle is 60-200 ℃.
This equipment work process is as follows:
At first mixing kettle is heated to preset temperature, the solid tackifier join in the solid tackifier metered charge jar that transfers to preset temperature and carry out fusion, liquid plasticizer, other auxiliary agents add liquid plasticizer metered charge jar, other auxiliary agent metered charge jars respectively, then matrix resin being added screw extrusion press measures and extrudes, solid tackifier, liquid plasticizer and other auxiliary agents are pressed the production formula metered charge simultaneously, be fed in the mixing kettle that has powerful stirring arm, be mixed to while stirring evenly.
The present invention has following advantage compared to existing technology:
1, facility investment is little, production efficiency is high.The present invention need not the forcing machine of special tectonic, matrix resin, solid tackifier, liquid plasticizer and other auxiliary agents is stirred by brute force in melt temperature mix, and device structure is simple, invests little; In addition, whole process of production is carried out continuously, and production efficiency improves greatly.
2, technology is simple, easy to operate.The continuous preparation technology of hot melt adhesive is simple, simple to operate among the present invention, less demanding for equipment and operator.
Description of drawings
Fig. 1 prepares the structural representation of equipment for the continuity of hot melt adhesive;
Wherein: 1, screw extrusion press, 2, solid tackifier metered charge jar, 3, liquid plasticizer metered charge jar, 4, other auxiliary agent metered charge jars, 5, mixing kettle, 6, powerful stirring arm.
Embodiment
In conjunction with the accompanying drawings the present invention is described in detail below by embodiment.It is important to point out that embodiment only is used for the present invention is further specified; can not be interpreted as limiting the scope of the invention, the person skilled in the art in this field can make some nonessential improvement and adjustment to the present invention according to the invention described above content.
A kind of continuous preparation method of hot melt adhesive, mixing kettle is heated to 140 ℃, the powerful stirring transfers to 100 rev/mins, with 10 parts of 40 parts of rosin, Microcrystalline Wax, 2, the 6-ditertbutylparacresol adds in the solid tackifier metered charge jar for 0.5 part, is heated to 120 ℃ and carries out fusion, and 40 parts of ethylene-vinyl acetate resins (vinyl acetate content is 28%) are extruded through screw extrusion press, be dosed to simultaneously in the mixing kettle with the raw material that fusion is good in the solid tackifier metered charge jar, mix the back discharging.This hot melt adhesive can be used for books unsewn binding glue.
A kind of continuous preparation method of hot melt adhesive, mixing kettle is heated to 150 ℃, the powerful stirring transfers to 110 rev/mins, with 30 parts of staybelites, 4,4 ' thiobis (3-methyl-6-tert butyl) phenol adds in the solid tackifier metered charge jar for 0.5 part, be heated to 125 ℃ and carry out fusion, 150 parts of polyethylene (relative molecular mass 12000), 10 parts of ethylene-propylene copolymers (propylene content 47%), 20 parts of isotactic polyprophlenes are extruded through screw extrusion press, be dosed to simultaneously in the mixing kettle with the raw material that fusion is good in the solid tackifier metered charge jar, mix the back discharging.
A kind of continuous preparation method of hot melt adhesive, mixing kettle is heated to 180 ℃, the powerful stirring transfers to 120 rev/mins, with 50 parts of terpine resins, 4,4 ' thiobis (3-methyl-6-tert butyl) phenol adds in the solid tackifier metered charge jar for 1 part, be heated to 130 ℃ and carry out fusion, 20 parts of naphthenic oils add in the liquid plasticizer metered charge jar, be heated to 100 ℃, 30 parts of styrene-isoprene-phenylethene resins naphthenic oil in 10 parts soaked 8 hours after screw extrusion press is extruded, be dosed to simultaneously in the mixing kettle with the raw material that fusion is good in the solid tackifier metered charge jar, mix the back discharging.
A kind of continuous preparation method of hot melt adhesive, mixing kettle is heated to 200 ℃, the powerful stirring transfers to 180 rev/mins, with 50 parts of terpine resins, 4,4 ' thiobis (3-methyl-6-tert butyl) phenol adds in the solid tackifier metered charge jar for 1 part, be heated to 130 ℃ and carry out fusion, 20 parts of naphthenic oils add in the liquid plasticizer metered charge jar, 10 parts of Chinese medical concretes add in other auxiliary agent metered charge jars, be heated to 60 ℃, 30 parts of styrene-isoprene-phenylethene resins naphthenic oil in 10 parts soaks 8 hours after screw extrusion press is extruded, and is dosed to simultaneously in the mixing kettle with the raw material that fusion is good in the solid tackifier metered charge jar, mixes the back discharging.
Claims (9)
1. the continuous preparation method of a hot melt adhesive, comprise that matrix resin metering is extruded, solid tackifier fusion metered charge, liquid plasticizer metered charge, other auxiliary agent metered charge, brute force mix step, it is characterized in that, according to the hot melt adhesive production formula matrix resin is extruded by the forcing machine metering separately, solid tackifier, liquid plasticizer and other auxiliary agents are heated to processing temperature respectively simultaneously, add in the mixing kettle simultaneously by metering and matrix resin, mix through brute force, discharging obtains the hot melt adhesive product.
2. the continuous preparation method of hot melt adhesive as claimed in claim 1, it is characterized in that described matrix resin is selected from the mixture of ethylene-vinyl acetate resin, polyacrylate resin, polyethylene and ethylene copolymer resin, acrylic resin, vinylbenzene and block copolymer resin thereof or above-mentioned resin.
3. the continuous preparation method of hot melt adhesive as claimed in claim 1 is characterized in that, described solid tackifier are selected from the mixture of petroleum resin, terpine resin, rosin and derivative thereof, resol, coumarone indene resin or above-mentioned resin.
4. the continuous preparation method of hot melt adhesive as claimed in claim 1 is characterized in that, described liquid plasticizer is selected from aliphatics mineral oil, dioctyl phthalate (DOP), dibutyl phthalate or whiteruss.
5. the continuous preparation method of hot melt adhesive as claimed in claim 1, it is characterized in that, described other auxiliary agents are oxidation inhibitor, wax, functional agent, oxidation inhibitor is selected from N-phenyl-β naphthylamines, 2,6-ditertbutylparacresol or 4,4 ' thiobis (3-methyl-6-tert butyl) phenol, wax is selected from paraffin, Microcrystalline Wax or polyethylene wax, and functional agent is selected from medicine, conductive auxiliary agent or heat conduction auxiliary agent.
6. the continuity of the described hot melt adhesive of claim 1 prepares specific equipment, comprises screw extrusion press, solid tackifier metered charge jar, liquid plasticizer metered charge jar, other auxiliary agent metered charge jars, mixing kettle, powerful stirring arm.Screw extrusion press, solid tackifier metered charge jar, liquid plasticizer metered charge jar, other auxiliary agent metered charge jars link to each other with the mixing kettle that powerful stirring arm is housed by web member respectively.
7. the continuity of hot melt adhesive as claimed in claim 6 prepares specific equipment, it is characterized in that, screw extrusion press has metering system, and described solid tackifier metered charge jar, liquid plasticizer metered charge jar and other auxiliary agent metered charge jars all have heating and metering system.
8. the continuity of hot melt adhesive as claimed in claim 6 prepares specific equipment, it is characterized in that described powerful stirring arm has at least 10 paddles.
9. the continuity of hot melt adhesive as claimed in claim 6 prepares specific equipment, it is characterized in that, the processing temperature of described screw extrusion press is 60-200 ℃, the reinforced temperature of described solid tackifier fusion is 60-200 ℃, the reinforced temperature of described liquid tackifiers is 60-200 ℃, the reinforced temperature of described other auxiliary agents is 60-200 ℃, and the Heating temperature of mixing kettle is 60-200 ℃.