CN101942719A - Production method of blending yarn of Newdal, pearl fiber and viscose - Google Patents
Production method of blending yarn of Newdal, pearl fiber and viscose Download PDFInfo
- Publication number
- CN101942719A CN101942719A CN 201010239935 CN201010239935A CN101942719A CN 101942719 A CN101942719 A CN 101942719A CN 201010239935 CN201010239935 CN 201010239935 CN 201010239935 A CN201010239935 A CN 201010239935A CN 101942719 A CN101942719 A CN 101942719A
- Authority
- CN
- China
- Prior art keywords
- viscose
- fiber
- pearl fiber
- pearl
- newdal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a production method of blending yarn of Newdal, pearl fiber and viscose, which is characterized in that Newdal, pearl fiber and viscose are mixed and are prepared into the blending yarn successively by a blowing working procedure, a cotton carding working procedure, a drawing working procedure and a rotor-spun working procedure, wherein the blending yarn contains 30-50 wt% of Newdal, 20-40 wt% of pearl fiber and 20-40 wt% of viscose. The invention mixes and spins Newdal, pearl fiber and viscose at certain ratio to cause three types of fibers to complement advantages, and prepared underwear is breathable, is comfortable to wear, has the characteristics of beautifying and nourishing skin, has favourable heat retention and satisfies requirements on comfort, health care and heat retention for people. The rotor-spun working procedure adopts an air exhaust type rotor spinning frame to produce so as to improve spinning count.
Description
Technical field
The invention belongs to the rotor spinning technical field, be specifically related to a kind of Niu Daier fiber and pearl fiber, viscose blended yarn production method.
Background technology
Along with the continuous listing of multiple functional fiber, people have also had new lifting and requirement to the pursuit of functional textile in recent years, and the key of decision functions of textile fabrics and taking is the function of yarn.Common a kind of yarn is difficult to accomplish existing good functional, and good taking is arranged again, wherein just comprises Niu Daier, pearl fiber, viscose etc.
Niu Daier fiber (Newdal) is to be a kind of high-tenacity fiber of raw material production with reproducible high quality cotton/wood pulp, fiber is keeping on the viscose good characteristic basis, because brute force, wet modulus that it is suitable, superior elongation at break and unique high crimpiness make product have better weaving machinability.Fiber quality softness is smooth, and the silk quality sense is strong, has good hand feeling and the sense of dangling, and the fabric shape-retaining ability is good, easily arranges wash resistant, anti-fold; Moisture permeability is better than cotton, and is comfortable and easy to wear; The fiber price is suitable, is more suitable for popular consumption, is the desirable feedstock of making underwear, garment for children, sportswear, various top-grade fashions.
Pearl fiber have pearl beauty care, relieve inflammation or internal heat relieve internal heat, tender white muscle skin, uvioresistant and emission infrared function, and moisture absorption is ventilative, comfortable and easy to wear, but wet low especially by force, not water-fastly washes poor dimensional stability.Pearl fiber is to adopt high-tech means that nano-glass pearl powder is added in the fiber when the viscose spinning, makes in the corpus fibrosum and appearance is uniform-distribution with the nano-pearl particulate.Be specially the section of pearl protein function master batch and fibre resin and constitute, functional agglomerate comprises: pearl protein superfine powder additive 15%~40%, coupling agent 2.5%~9%, dispersant 15%~25%, vector resin 36%~67%.Its manufacture method is above-mentioned material to be carried out high speed mediate in heating process, extrudes through the twin-screw blend, makes functional agglomerate; With adding the fibre resin section after the functional agglomerate drying,,, promptly make function synthetic fibre again through post processing by the melt extruded spinning.Make in the corpus fibrosum and be uniform-distribution with the nano-pearl particulate with appearance, fiber is just as a string pearl necklace one by one, and light is smooth.
The viscose feel is smooth, and drapability is good, and moisture absorption and gas permeability are better, and be comfortable and easy to wear, and lovely luster is dazzled beautiful colorfully, be rich in the sensation of silk, and cost is low.But the elastic resilience of viscose is poor, it is low by force, not wear-resisting to wet, and poor dimensional stability when viscose and other fiber blend, can make up for each other's deficiencies and learn from each other, and improves the engineering properties of fabric.
It is a kind of spinning method that revolving cup spins, compare with traditional ring spinning have flow process short (6 procedures shorten to 4 roads), recruitment economize (with the output recruitment have only RING SPINNING 1/4), efficient height (6-8 that single ingot output is RING SPINNING doubly), and the rotor spinning line all is better than RING SPINNING at aspects such as yarn evenness, filoplume, surface smoothness, ABRASION RESISTANCE.
Spin the exploitation yarn with revolving cup and can have complementary advantages three kinds of fibers are mixed, the clothes of making can increase the functional of product when improving the product wearability, improve product specification, satisfy high-end consumer market demand.
Still the three not being carried out at present the technology of blending attempts.
Summary of the invention
It is a kind of with mixed according to a certain percentage spinning of Niu Daier fiber, pearl fiber, viscose and production method thereof that technical problem to be solved by this invention is to provide, three kinds of fibers are had complementary advantages, the underwear of making not only moisture absorption is ventilative, comfortable and easy to wear, and have characteristics such as beauty care, warmth retention property be good, satisfy that people are comfortable to wearing clothes, health care, warming demand.
A kind of Niu Daier fiber and pearl fiber, viscose blended yarn production method is characterized in that: the Niu Daier fiber is mixed with pearl fiber, viscose, spin the operation blending through cotton cleaning process, carding step, mixing in doubling step, revolving cup successively and form; Niu Daier fiber quality content is 30~50%, and the pearl fiber mass content is 20~40%, and the viscose mass content is 20~40%.
Preferably, described cotton cleaning process relative humidity is controlled at 58%, and carding step relative humidity is controlled at 60%, and mixing in doubling step relative humidity is controlled at 62%, and revolving cup spins operation relative humidity and is controlled at 68%.
Preferably, the mass ratio of described Niu Daier fiber, pearl fiber, viscose is 667: 500: 500.
Preferably, revolving cup spins and adopts the bleeder rotor spinning machine to produce.
The present invention is with the mixed according to a certain percentage spinning of Niu Daier fiber, pearl fiber, viscose, three kinds of fibers are had complementary advantages, the underwear of making not only moisture absorption is ventilative, comfortable and easy to wear, and have characteristics such as beauty care, warmth retention property be good, satisfy that people are comfortable to wearing clothes, health care, warming demand.Revolving cup spins and adopts the bleeder rotor spinning machine to produce, and can improve spinning count.
The specific embodiment
Below by embodiment the present invention is specifically described.It is important to point out that present embodiment only is used for invention is further specified, but can not be interpreted as restriction the invention protection domain.The person skilled in art can make some nonessential improvement and adjustment to the present invention according to the above-mentioned technology contents that provides.
Unless stated otherwise, each raw material and equipment all can obtain by commercial sources in the embodiment.
667kg Niu Daier fiber, 500kg viscose, the blending of 500kg pearl fiber, in the blending process, earlier Niu Daier fiber, pearl fiber, viscose are mixed, spin the operation blending and get finished product through cotton cleaning process, carding step, mixing in doubling step, revolving cup successively again.Workshop moisture temperature control: cotton cleaning process relative humidity is controlled at 58%, and carding step relative humidity is controlled at 60%, and mixing in doubling step relative humidity is controlled at 62%, and revolving cup spins operation relative humidity and is controlled at 68%.
The equipment that adopts in the blending process is successively: FA002 griping cotton machine, SFA035 mixing and blowing machine, FA025 multi-mixer, FA106A card wire opener, FA161 vibration hopper feeder, A076F lapper, A186H carding machine, FA306A first drawing frame, FA306A intermediate drawing frame, RSB D401 three road drawing frames, R923 rotor spinning machine, Cheng Bao.
1, cotton cleaning process
1.1 667kg Niu Daier fiber+500kg viscose+500kg pearl fiber mixes and enters in the FA002A bale plucker disk.
1.2 FA002A griping cotton machine: hired roughneck's speed 740r/min, the each slippage 3mm of hired roughneck, carriage walking speed 2.16r/min, blade stretches out rib apart from 2mm.
1.3 the automatic mixing and blowing machine of SFA035: cotton-pressing curtain speed 1.25m/min, brad curtain speed 100m/min, the first brad hired roughneck speed 673r/min, the second brad hired roughneck speed 799r/min, evener roller speed 313r/min, brad curtain and cotton-pressing curtain spacing 60mm, brad curtain and the equal cotton hired roughneck 40mm that spaces, dirt interrod spacing 5mm.
1.4 FA025 multi-mixer: evener roller rotating speed 726r/min, stripping roller rotating speed 543r/min, exhaust duct negative pressure 80Pa.
1.5 FA106A opener: hired roughneck's speed 480r/min, the hired roughneck with to the cotton roller 11mm that spaces, hired roughneck and the dirt rod import 14mm that spaces, outlet 18mm, dirt rod spacer import 11mm exports 6mm.
1.6 FA161 vibrates hopper feeder: 150 times/min of vibration plate vibrates frequency, brad curtain speed 40m/min, flat curtain speed 10m/min, evener roller 230r/min, stripping roller rotating speed 354r/min.
1.7 A076F lapper: kirschner beater speed 800r/min, fan speed 1200r/min, the hired roughneck and the 11mm that spaces to cotton roller, hired roughneck and the dirt rod import 8mm that spaces, outlet 18mm, dirt interrod spacing 5mm, lap is done quantitative 360g/m, lap roller rotating speed 12r/min.
2 carding steps
2.1 A186H carding machine: cylinder speed 323r/min, licker-in speed 754r/min, cover plate speed 81mm, doffer speed 15r/min, the carded sliver is done quantitative 21g/5m, feed plate and the licker-in 0.381mm that spaces, licker-in and the mote knife 0.508mm that spaces, licker-in and the cylinder 0.177mm that spaces, licker-in and the pre-combing plate 0.558mm that spaces, cylinder and the securing cover plate 0.406mm that spaces, 0.355mm, cylinder and the removable cover 0.254mm that spaces, 0.228mm, 0.203mm, 0.203mm, 0.228mm, cylinder and the preceding securing cover plate 0.254mm0.228mm0.203mm that spaces, cylinder and the doffer 0.127mm that spaces.
3 mixing in doubling step
3.1 FA306A first drawing frame: spin and do quantitative 18.0g/5m; And close 6 of radicals; Sliver exporting speed 300m/min, 1.77 times of back area drafts; 7 times of total draft multiples; Roller grips apart from 47mm * 53mm.
3.2 FA306A intermediate drawing frame: spin and do quantitative 18.0g/5m; And close 8 of radicals; Sliver exporting speed 300m/min, 1.30 times of back area drafts; 8.21 times of total draft multiples; Roller grips apart from 47mm * 53mm.
3.3 RSB D401 three road drawing frames: spin and do quantitative 20.2g/5m; And close 8 of radicals; Sliver exporting speed 600m/min, 1.30 times of back area drafts; 8.21 times of total draft multiples; Roller grips apart from 47mm * 53mm.
4 revolving cups spin operation
4.1 R923 rotor spinning machine: spin dry weight 1.743g/10m, the twist 820 sth. made by twisting/m, rotor speed 100000r/min, negative pressure 6.8Kpa.
Technical target of the product:
1. strip dry uniformity variant coefficient CV% is not more than 16.5
2. hundred meters qualitative variability coefficient CV% are not more than 2.0
3. single thread ultimate strength coefficient of variation CV% is not more than 13.5
4. single thread fracture strength (cN/tex) is not less than 10.2
5. ten myriametre yarn defects are no more than 10
Hundred meters mass deviations (%) be not more than ± 2.5
7. amino acid content is not less than 0.05%
8. micro-kind is not less than 13 kinds
At last, it is also to be noted that what more than enumerate only is specific embodiments of the invention, obviously, the invention is not restricted to above examples of implementation, many distortion can also be arranged.All distortion that those of ordinary skill in the art can directly derive or associate from content disclosed by the invention all should be thought protection scope of the present invention.
Claims (4)
1. Yi Zhong Niu Daier fiber and pearl fiber, viscose blended yarn production method is characterized in that: the Niu Daier fiber is mixed with pearl fiber, viscose, spin the operation blending through cotton cleaning process, carding step, mixing in doubling step, revolving cup successively and form; Niu Daier fiber quality content is 30~50%, and the pearl fiber mass content is 20~40%, and the viscose mass content is 20~40%.
2. Niu Daier fiber according to claim 1 and pearl fiber, viscose blended yarn production method, it is characterized in that: described cotton cleaning process relative humidity is controlled at 58%, carding step relative humidity is controlled at 60%, mixing in doubling step relative humidity is controlled at 62%, and revolving cup spins operation relative humidity and is controlled at 68%.
3. Niu Daier fiber according to claim 1 and pearl fiber, viscose blended yarn production method is characterized in that: the mass ratio of described Niu Daier fiber, pearl fiber, viscose is 667: 500: 500.
4. Niu Daier fiber according to claim 1 and pearl fiber, viscose blended yarn production method is characterized in that: revolving cup spins and adopts the bleeder rotor spinning machine to produce.