CN101928468A - Bogus carved-bone artware and manufacturing process thereof - Google Patents
Bogus carved-bone artware and manufacturing process thereof Download PDFInfo
- Publication number
- CN101928468A CN101928468A CN2010102685594A CN201010268559A CN101928468A CN 101928468 A CN101928468 A CN 101928468A CN 2010102685594 A CN2010102685594 A CN 2010102685594A CN 201010268559 A CN201010268559 A CN 201010268559A CN 101928468 A CN101928468 A CN 101928468A
- Authority
- CN
- China
- Prior art keywords
- bone carving
- artwork
- carving artwork
- manufacturing process
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a bogus carved-bone artware which comprises the following components in parts by weight: 100 parts of resin, 4-6 parts of accelerating agent, 1-4 parts of curing agent, 10-35 parts of refractory clay and 15-20 parts of release agent. The preparation process thereof comprises the following steps: (1) preparing the release agent; (2) coating the release agent on the inner surface of a mold; (3) weighing and adding the resin, the curing agent, the refractory clay and the accelerating agent according to the weight parts, evenly mixing, and pouring the mixture into the mold coated with the release agent; and (4) forming by solidifying to obtain the bogus carved-bone artware. The artware manufactured by the invention has low cost, short production period, high yield, high artistry, large-scale production and good development prospect.
Description
Technical field
The present invention relates to a kind of artwork, especially a kind of imitative bone carving artwork and manufacturing process.
Background technology
Along with the continuous lifting of people's living standard, people more and more pay attention to the raising of quality of the life; Simultaneously, in home environment, people also are particular about the decoration of living environment day by day, arrange some artworks in the house, to promote the comfort level of living environment.In various artworks, bone carving has higher aesthetic value, the artwork kind that to be people like in decorating at home decorates; Yet traditional bone carving artwork is because the rare and hand-built difficulty of raw material resources makes that its production efficiency is low, and output is few, can not satisfy the market requirement that develops rapidly; Simultaneously, traditional bone carving is the wastage of material resource with the sclerotin, destroys the ecosystem, does not meet the demand of national industrial policies and Sustainable development, and its development will be subjected to increasing restriction.
Summary of the invention
In order to overcome above defective, the technical problem to be solved in the present invention provides a kind of imitative bone carving artwork and manufacturing process, and is with low cost by the artwork that this technology makes, with short production cycle, the output height, and rich artistry and energy scale production, very promising.
The technical solution adopted in the present invention is: a kind of imitative bone carving artwork is characterized in that each component of this artwork and mass fraction are:
100 parts of resins,
Promotor 4-6 part,
Solidifying agent 1-4 part,
Fireclay 10-35 part,
Releasing agent 15-20 part.
According to another preferred embodiment, a kind of imitative bone carving artwork comprises that further described promotor is cobalt naphthenate solution.
According to another preferred embodiment, a kind of imitative bone carving artwork comprises that further described solidifying agent is a cyclohexanone peroxide.
According to another preferred embodiment, a kind of imitative bone carving artwork further comprises talcum powder, and massfraction is 10-20 part.
According to another preferred embodiment, a kind of imitative bone carving artwork comprises that further the component of described releasing agent is polyvinyl alcohol 100-120 part, alcohol 350-380 part, acetone 6-8 part, water 1000-1200 part.
The invention also discloses a kind of manufacturing process of imitative bone carving artwork, it is characterized in that comprising following step of preparation process:
(1) preparation releasing agent;
(2) at the mould inner surface coating release agent;
(3) take by weighing resin, solidifying agent, fireclay, talcum powder, promotor adding uniform mixing by massfraction, cast to coat in the mould of releasing agent;
(4) curing molding must be imitated the bone carving artwork.
According to another preferred embodiment, a kind of manufacturing process of imitative bone carving artwork comprises that further the concrete steps of described preparation releasing agent are for to join polyvinyl alcohol in 1000-1200 part hot water, heat while stirring till dissolving fully, allow it cool to 60-70 ℃ then, under agitation slowly drip alcohol, alcohol cools to below 60 ℃ after adding again, under agitation slowly adds acetone again, dropwises the back and uses filtered through gauze stand-by.
According to another preferred embodiment, a kind of manufacturing process of imitative bone carving artwork comprises that further the mode of described curing molding is heating cure.
According to another preferred embodiment, a kind of manufacturing process of imitative bone carving artwork comprises that further the temperature of described curing molding is 30 ℃-35 ℃.
According to another preferred embodiment, a kind of manufacturing process of imitative bone carving artwork further comprise described curing molding time be 5-10 hour.
A kind of imitative bone carving artwork provided by the invention, by with resin, promotor, solidifying agent, talcum powder, the fire-resistant soil curing molding in mould of being stained with, get finished product in the demoulding, compare with existing bone carving artwork, imitative bone carving artwork of the present invention can scale production, satisfies the needs in market; Need be not raw material, economize on resources with the sclerotin.Preserve the ecological environment; Artwork is with low cost, and is with short production cycle, the output height, and rich artistry, very promising.
Embodiment
The present invention is further detailed explanation in conjunction with the preferred embodiments now.
Embodiment 1
100 parts of resins, 4 parts of cobalt naphthenate solutions, 1 part of cyclohexanone peroxide, 10 parts of fireclays, 15 parts of releasing agents.
Its preparation technology comprises following step of preparation process:
(1) preparation releasing agent: polyvinyl alcohol is joined in 1000-1200 part hot water, heat while stirring till dissolving fully, allow it cool to 60-70 ℃ then, under agitation slowly drip alcohol, alcohol cools to below 60 ℃ after adding again, under agitation slowly add acetone again, dropwise the back and use filtered through gauze stand-by.
(2) at the mould inner surface coating release agent;
(3) take by weighing resin, solidifying agent, fireclay, talcum powder, promotor adding uniform mixing by mass fraction, cast to coat in the mould of releasing agent;
(4) heating cure, the temperature of curing molding are 30 ℃-35 ℃.Time is 10 hours, and curing molding must be imitated the bone carving artwork.
Embodiment 2
100 parts of resins, 6 parts of cobalt naphthenate solutions, 2 parts of cyclohexanone peroxides, 20 parts of fireclays, 18 parts of releasing agents.
Its preparation technology comprises following step of preparation process:
(1) preparation releasing agent: polyvinyl alcohol is joined in 1000-1200 part hot water, heat while stirring till dissolving fully, allow it cool to 60-70 ℃ then, under agitation slowly drip alcohol, alcohol cools to below 60 ℃ after adding again, under agitation slowly add acetone again, dropwise the back and use filtered through gauze stand-by.
(2) at the mould inner surface coating release agent;
(3) take by weighing resin, solidifying agent, fireclay, talcum powder, promotor adding uniform mixing by mass fraction, cast to coat in the mould of releasing agent;
(4) heating cure, the temperature of curing molding are 30 ℃-35 ℃.Time is 8 hours, and curing molding must be imitated the bone carving artwork.
Embodiment 3
100 parts of resins, 6 parts of cobalt naphthenate solutions, 4 parts of cyclohexanone peroxides, 35 parts of fireclays, 20 parts of releasing agents.
Its preparation technology comprises following step of preparation process:
(1) preparation releasing agent: polyvinyl alcohol is joined in 1000-1200 part hot water, heat while stirring till dissolving fully, allow it cool to 60-70 ℃ then, under agitation slowly drip alcohol, alcohol cools to below 60 ℃ after adding again, under agitation slowly add acetone again, dropwise the back and use filtered through gauze stand-by.
(2) at the mould inner surface coating release agent;
(3) take by weighing resin, solidifying agent, fireclay, talcum powder, promotor adding uniform mixing by mass fraction, cast to coat in the mould of releasing agent;
(4) heating cure, the temperature of curing molding are 30 ℃-35 ℃.Time is 5 hours, and curing molding must be imitated the bone carving artwork.
With above-mentioned foundation desirable embodiment of the present invention is enlightenment, and by above-mentioned description, the related work personnel can carry out various change and modification fully in the scope that does not depart from this invention technological thought.The technical scope of this invention is not limited to the content on the specification sheets, must determine its technical scope according to the claim scope.
Claims (10)
1. imitative bone carving artwork is characterized in that each component of this artwork and mass fraction are:
100 parts of resins,
Promotor 4-6 part,
Solidifying agent 1-4 part,
Fireclay 10-35 part,
Releasing agent 15-20 part.
2. according to right 1 described a kind of imitative bone carving artwork, it is characterized in that described promotor is cobalt naphthenate solution.
3. according to right 1 described a kind of imitative bone carving artwork, it is characterized in that described solidifying agent is a cyclohexanone peroxide.
4. according to right 1 described a kind of imitative bone carving artwork, it is characterized in that also comprising talcum powder, massfraction is 10-20 part.
5. according to right 1 described a kind of imitative bone carving artwork, the component that it is characterized in that described releasing agent is polyvinyl alcohol 100-120 part, alcohol 350-380 part, acetone 6-8 part, water 1000-1200 part.
6. the manufacturing process of an imitative bone carving artwork is characterized in that comprising following step of preparation process:
(1) preparation releasing agent;
(2) at the mould inner surface coating release agent;
(3) take by weighing resin, solidifying agent, fireclay, talcum powder, promotor adding uniform mixing by massfraction, cast to coat in the mould of releasing agent;
(4) curing molding must be imitated the bone carving artwork.
7. the manufacturing process of a kind of imitative bone carving artwork according to claim 6, the concrete steps that it is characterized in that described preparation releasing agent are for to join polyvinyl alcohol in 1000-1200 part hot water, heat while stirring till dissolving fully, allow then its cool to below 70 ℃, more than 60 ℃, under agitation slowly drip alcohol, alcohol cools to below 60 ℃ after adding again, under agitation slowly adds acetone again, dropwises the back and uses filtered through gauze stand-by.
8. the manufacturing process of a kind of imitative bone carving artwork according to claim 6, the mode that it is characterized in that described curing molding is heating cure.
9. the manufacturing process of a kind of imitative bone carving artwork according to claim 7, the temperature that it is characterized in that described curing molding are 30 ℃-35 ℃.
10. the manufacturing process of a kind of imitative bone carving artwork according to claim 6, it is characterized in that described curing molding time be 5-10 hour.