CN101890808B - Integrally forming method of heating closestool cushion - Google Patents
Integrally forming method of heating closestool cushion Download PDFInfo
- Publication number
- CN101890808B CN101890808B CN 201010220187 CN201010220187A CN101890808B CN 101890808 B CN101890808 B CN 101890808B CN 201010220187 CN201010220187 CN 201010220187 CN 201010220187 A CN201010220187 A CN 201010220187A CN 101890808 B CN101890808 B CN 101890808B
- Authority
- CN
- China
- Prior art keywords
- formation method
- heater wire
- integral formation
- molding compound
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides an integrally forming method of a heating closestool cushion, which comprises the following steps: providing a mold with a cavity; adding a molding material and a heating wire into the cavity in a mold opening state; heating and pressurizing the mold in a mold closing state, and enabling the heating wire to be contained in the molding material and closely combined with the molding material; and removing the mold after forming and curing to form an integrally formed closestool cushion in which the heating wire is embedded. The invention has the advantages that the heating wire is put into the molding material to be molded and integrally formed, so that the heating wire and the molding material are closely combined to improve the heat conductivity, thereby preventing excessive electric energy from being wasted.
Description
[technical field]
The present invention relates to heater, particularly a kind of integral formation method of heating closestool cushion.
[background technology]
Present employed toilet mainly is comprised of a closestool body and a water tank, because this closestool body is mainly ceramic, have ice-cold sensation, therefore, above closestool body, usually all can increase a plastic toilet seat pad, to overcome ice-cold problem.But when temperature reduced, plastic toilet seat pad was still suitable cold.Therefore, a kind of heating pipe's of utilization method is arranged, so that toilet seat pad reaches the temperature near human body, make people more comfortable when entering the lavatory.Fig. 1 is toilet seat pad cutaway view commonly used, the vinyl cover 10 and the plastic seat 11 that mainly comprise upper and lower symmetry, and form several low grooves 101 in the bottom surface of vinyl cover 10, the end face of plastic seat 11 forms several upper grooves 111, to hold several heating tubes 12 in the centre of each upper and lower groove (101,111), again vinyl cover 10 and plastic seat 11 fitted, and the water in each heating tube 12 is heated and when producing heat, see through vinyl cover 10 and upwards conduct heat, reach the effect of heating.Yet, when heating tube heats, because vinyl cover has suitable thickness, be not very good in heat conduction efficiency, will cause the excessive loss of electric power.
[summary of the invention]
In order to solve existing technical problem, the invention provides a kind of integral formation method of heating closestool cushion, it adopts buries the then one-body molded heating closestool cushion of making of heater wire underground.
The present invention solves existing technical problem, and a kind of integral formation method of heating closestool cushion is provided, and it comprises the steps: to provide a mould with die cavity; Under the die opening state, molding compound and heater wire are added in the die cavity; Under the mold closing state, mold heated and pressurization are placed in the molding compound and with molding compound heater wire and combine closely; The demoulding behind the forming and hardening forms the integrated toilet seat pad of burying heater wire underground.
The present invention further improves:
Molding compound and heater wire are added in the die cavity step, and described molding compound is plastics; First plastics are added in the die cavity, after heater wire is put into plastics.
Molding compound and heater wire are added in the die cavity step, and described molding compound is base plate and plastics; First the fluted base plate of tool is positioned in the die cavity, again heater wire is positioned in the groove, then add plastics.
Described groove is ring-type, and described plastics are arranged at the top of described base plate.
Described base plate is plastic plate or wood plank.
Molding compound and heater wire are added in the die cavity step, and described molding compound is prepreg; First prepreg is positioned in the die cavity, again heater wire is positioned on the prepreg, then then place prepreg.
The prepreg of putting into first is multilayer, after the prepreg put into be multilayer.
Described prepreg is that glass fibre mats contain resin pickup.
Described resin is thermosetting resin.
Described plastics include adhesive, filler and colorant.
Described adhesive is thermosetting resin or thermoplastic resin.
Described thermosetting resin is any in usefulness fluosite, urea resin, epoxy resin, silica resin, melamine resin, alkyd resins, polyurethane and the amino methanol ethyl ester.
Described thermoplastic resin is polyethylene, polypropylene, polystyrene, polyvinyl chloride, acrylonitrile-butadiene-styrene copolymer, polymethyl methacrylate, polyamide, saturated polyester terephthaldehyde acid butyl ester, saturated polyester terephthaldehyde acetoacetic ester, polymethylpentene, Merlon, polyacetals, sex change polyoxygenated xylene resin, liquid crystal polyester, polyamidoimide, the poly terephthalic acid cyclohexanol, polyether-ketone, PEI, polyether sulfone, polyimides, poly-sulfuration dimethylbenzene, polysulfones; Rubber alloy is ABS/Nylon, ABS/PVC, ABS/PC, ABS/SMA, PPO/PS, PPE/PS, ABS/Polysulfone, PC/PBT, PC/PET, PC/PE, PC/ASA, PC/PU, PC/SMA, PBT/Elastomer, PET/Elastomer, PET/PMMA, PET/Polysulfone, PPO/PBT, Nylon/Ethylene, ylon/Elastomer, Nylon/PTFE, PPO/Nylon.
Described filler is wood powder, cellulose wood pulp, asbestos or mica; The kenel of described filler is powdery or long fibre shape.
Compared to prior art, the invention has the beneficial effects as follows: adopt in the molding compound and put into heater wire, mold pressing is one-body molded, and heater wire and mold pressing are combined closely, and with the raising thermal conductivity, thereby avoids the too much loss of electric energy.
[description of drawings]
Fig. 1 is the cross-sectional schematic of existing Water pipe heating toilet seat pad;
Fig. 2 has the structural representation that integral formation method of the present invention makes the toilet of toilet seat pad;
Fig. 3 is the perspective diagram of the positive surface state of described toilet seat pad;
Fig. 4 is the generalized section of A-A among Fig. 3;
Fig. 5 is the structural representation that comprises the heating component of heater wire;
Fig. 6 is the flow chart of integral formation method one embodiment of the present invention;
Fig. 7 a-7d is the mould molding figure of Fig. 6;
Fig. 8 is the flow chart of the another embodiment of integral formation method of the present invention;
Fig. 9 a-9d is the mould molding figure of Fig. 8;
Figure 10 is the again flow chart of an embodiment of integral formation method of the present invention;
Figure 11 a-11f is the mould molding figure of Figure 10.
[specific embodiment]
The present invention is further described below in conjunction with description of drawings and the specific embodiment.
Shown in Fig. 1 to 11, a kind of integral formation method of heating closestool cushion, it comprises the steps:
One mould with die cavity is provided; Under the die opening state, molding compound and heater wire are added in the die cavity; Under the mold closing state, mold heated and pressurization are placed in the molding compound and with molding compound heater wire and combine closely; The demoulding behind the forming and hardening forms the integrated toilet seat pad of burying heater wire underground.
This integral formation method can be finished with in compression forming (compressing), ejection formation, metaideophone moulding (transferring) or the cast molding (casting) any.
Embodiment one
See also Fig. 6 and 7, molding compound is plastics 25.This integral formation method step is as follows:
One mould with die cavity is provided; Under the die opening state, first plastics 25 are added in the die cavities, after heater wire 212 is put into plastics; Under the mold closing state, mold heated and pressurization are placed in the plastics and with molding compound heater wire 212 and combine closely; The demoulding behind the forming and hardening forms the integrated toilet seat pad of burying heater wire underground.
Embodiment two
See also Fig. 8 and 9 molding compounds comprise base plate and plastics, this base plate is plastic plate or wood plank.This integral formation method step is as follows:
One mould with die cavity is provided; Under the die opening state, the base plate 26 that will have first groove 261 is positioned in the die cavity, heater wire 212 is positioned in the groove 261 again, then adds plastics 25; Under the mold closing state, mold heated and pressurization are placed between base plate and the plastics and with molding compound heater wire and combine closely; The demoulding behind the forming and hardening forms the integrated toilet seat pad of burying heater wire underground.
In above-mentioned steps, groove is ring-type, and plastics are arranged at the top of base plate.
Embodiment three
Seeing also Figure 10 and 11 molding compounds is prepreg, and this prepreg is multilayer, is got by glass fibre mats impregnation resin.This integral formation method step is as follows:
One mould with die cavity is provided; Under the die opening state, first prepreg 271 is positioned in the die cavity, again heater wire 212 is positioned on the prepreg 271, then then place prepreg 272; Under the mold closing state, mold heated and pressurization are placed in the prepreg and with molding compound heater wire and combine closely; The demoulding behind the forming and hardening forms the integrated toilet seat pad of burying heater wire underground.
In above-mentioned steps, the prepreg of putting into first is multilayer, after the prepreg put into be multilayer 27.
Employed resin is thermosetting resin in the integral formation method of the present invention, and employed plastics comprise adhesive, filler (filler) and colorant (pigment).Described adhesive can be selected thermosetting (thermosetting) resin or thermoplasticity (thermoplastic) resin.Described thermosetting (thermosetting) resin can adopt fluosite (PE), urea resin (UF), epoxy resin, silica resin (Silicone), melamine resin (melamine), alkyd resins, polyurethane (UP), poly-amino methanol ethyl ester (PU); Wherein thermoplastic resin can adopt general with plastics, engineering plastics or rubber alloy, for example general is polyethylene (PE) with plastics, polypropylene (PP), polystyrene (PS), polyvinyl chloride (PVC), acrylonitrile-butadiene-styrene copolymer (ABS), polymethyl methacrylate (PMMA); Engineering plastics are polyamide (PA, nylon Nylon), saturated polyester terephthaldehyde acid butyl ester (PBT), saturated polyester terephthaldehyde acetoacetic ester (PET), polymethylpentene (PMP), Merlon (PC), polyacetals (POM), sex change polyoxygenated xylene resin (MPPO), liquid crystal polyester (LCP), polyamidoimide (PAI), poly terephthalic acid cyclohexanol (PCT), polyether-ketone (PEEK), PEI (PEI), polyether sulfone (PES), polyimides (PI), poly-sulfuration dimethylbenzene (PPS), polysulfones (PFS); Rubber alloy is ABS/Nylon, ABS/PVC, ABS/PC, ABS/SMA, PPO/PS, PPE/PS, ABS/Polysulfone, PC/PBT, PC/PET, PC/PE, PC/ASA, PC/PU, PC/SMA, PBT/Elastomer, PET/Elastomer, PET/PMMA, PET/Polysulfone, PPO/PBT, Nylon/Ethylene, Nylon/Elastomer, Nylon/PTFE, PPO/Nylon.Again in above-mentioned forming method, wherein said filler is organic or inorganic thing material, mineral such as wood powder (wood flours), cellulose wood pulp (cellulose pulp), asbestos, mica, its kenel can be powdery or long fibre etc., purpose is as spreading agent, sometimes also reach the effect of reinforcement, and strengthen mechanical strength of resin.The making of above-mentioned plastics can change according to different proportion prescription, and for example phenol resin adopts 45% resin, 50% filler, and 5% is colorant, the releasing agent that other demouldings when adding flexibilizer and making forming operation are easy etc.Because resin is a kind of solid at normal temperatures, it rubbing must be added colorant, the demoulding and flexibilizer, add at last filler, thoroughly milling makes by rotating heating drum again.The adhesive melted by heating soaks filler mixed, has gone out behind the cylinder in the form of sheets, after the cooling it is made granule, and this last product is shaping powder (molding powder).
The present invention adopts and puts into heater wire in the molding compound, and mold pressing is one-body molded, and heater wire and mold pressing are combined closely, and with the raising thermal conductivity, thereby avoids the too much loss of electric energy.
The heating closestool cushion that is made by integral formation method of the present invention, it comprises body 20, toilet seat pad 21, toilet lid 22 and water tank 23, at toilet seat pad 21 heating component 211 is set, heating component 211 includes heater wire 212, wire terminal 213 and power-supply controller of electric 214, heater wire 212 two ends are connected with wire terminal 213, wire terminal 213 has first joint 215, power-supply controller of electric 214 1 ends connect power supply, the other end has one second joint 216, the first joint 215 and the second joint 216 are done the waterproof embedding, and the second joint 216 can insert the first joint 215 interior turn-on powers.Wire terminal 213 and the first joint 215 can be fixed on toilet seat pad 21 tail edges or extend to outside the toilet seat pad 21.
Mainly utilize plastics or glass fibre mats reinforced plastics with the heater wire embedding wherein, form the toilet seat pad of one-body molded embedding heater wire.
Above content is in conjunction with concrete preferred embodiment further description made for the present invention, can not assert that implementation of the present invention is confined to these explanations.For the general technical staff of the technical field of the invention, without departing from the inventive concept of the premise, can also make some simple deduction or replace, all should be considered as belonging to protection scope of the present invention.
Claims (18)
1. the integral formation method of a heating closestool cushion, it comprises the steps: to provide a mould with die cavity; Under the die opening state, molding compound and heater wire are added in the die cavity; Under the mold closing state, mold heated and pressurization are placed in the molding compound and with molding compound heater wire and combine closely; The demoulding behind the forming and hardening forms the integrated toilet seat pad of burying heater wire underground; It is characterized in that: molding compound and heater wire are added in the die cavity step, and described molding compound is prepreg; First prepreg is positioned in the die cavity, again heater wire is positioned on the prepreg, then then place prepreg.
2. the integral formation method of heating closestool cushion according to claim 1, it is characterized in that: the prepreg of putting into first is multilayer, after the prepreg put into be multilayer.
3. the integral formation method of a heating closestool cushion, it comprises the steps: to provide a mould with die cavity; Under the die opening state, molding compound and heater wire are added in the die cavity; Under the mold closing state, mold heated and pressurization are placed in the molding compound and with molding compound heater wire and combine closely; The demoulding behind the forming and hardening forms the integrated toilet seat pad of burying heater wire underground; It is characterized in that: molding compound and heater wire are added in the die cavity step, and described molding compound is plastics; First plastics are added in the die cavity, after heater wire is put into plastics.
4. the integral formation method of heating closestool cushion according to claim 3, it is characterized in that: described plastics include adhesive, filler and colorant.
5. the integral formation method of heating closestool cushion according to claim 4, it is characterized in that: described adhesive is thermosetting resin or thermoplastic resin.
6. the integral formation method of heating closestool cushion according to claim 5, it is characterized in that: described thermosetting resin is any in urea resin, epoxy resin, silica resin, melamine resin, alkyd resins and the unsaturated polyester (UP).
7. the integral formation method of heating closestool cushion according to claim 5, it is characterized in that: described thermoplastic resin is polyethylene, polypropylene, polystyrene, polyvinyl chloride, polyamide, saturated polyester terephthaldehyde acid butyl ester, saturated polyester terephthaldehyde acetoacetic ester, polymethylpentene, Merlon, polyacetals, sex change polyoxygenated xylene resin, liquid crystal polyester, polyamidoimide, polyether-ketone, PEI, polyether sulfone, polyimides, poly-sulfuration dimethylbenzene, polysulfones, ABS/PVC, ABS/PC, ABS/SMA, PPO/PS, the ABS/ polysulfones, PC/PE, PC/PU, PC/SMA, the PBT/ elastomer, the PET/ elastomer, PET/PMMA, nylon/elastomer.
8. the integral formation method of heating closestool cushion according to claim 5, it is characterized in that: described thermoplastic resin is polymethyl methacrylate, PC/PBT, PPO/PBT, PC/PET, PET/PMMA, PET/ polysulfones, ABS/ nylon, nylon/PTFE, PPO/ nylon.
9. the integral formation method of heating closestool cushion according to claim 4, it is characterized in that: described filler is wood powder, cellulose wood pulp or mica; The kenel of described filler is powdery or long fibre shape.
10. the integral formation method of a heating closestool cushion, it comprises the steps: to provide a mould with die cavity; Under the die opening state, molding compound and heater wire are added in the die cavity; Under the mold closing state, mold heated and pressurization are placed in the molding compound and with molding compound heater wire and combine closely; The demoulding behind the forming and hardening forms the integrated toilet seat pad of burying heater wire underground; It is characterized in that: molding compound and heater wire are added in the die cavity step, and described molding compound is base plate and plastics; First the fluted base plate of tool is positioned in the die cavity, again heater wire is positioned in the groove, then add plastics.
11. the integral formation method of heating closestool cushion according to claim 10 is characterized in that: described groove is ring-type, and described plastics are arranged at the top of described base plate.
12. the integral formation method of heating closestool cushion according to claim 10 is characterized in that: described base plate is plastic plate or wood plank.
13. the integral formation method of heating closestool cushion according to claim 10 is characterized in that: described plastics include adhesive, filler and colorant.
14. the integral formation method of heating closestool cushion according to claim 13 is characterized in that: described adhesive is thermosetting resin or thermoplastic resin.
15. the integral formation method of heating closestool cushion according to claim 14 is characterized in that: described thermosetting resin is any in urea resin, epoxy resin, silica resin, melamine resin, alkyd resins and the unsaturated polyester (UP).
16. the integral formation method of heating closestool cushion according to claim 14, it is characterized in that: described thermoplastic resin is polyethylene, polypropylene, polystyrene, polyvinyl chloride, polyamide, saturated polyester terephthaldehyde acid butyl ester, saturated polyester terephthaldehyde acetoacetic ester, polymethylpentene, Merlon, polyacetals, sex change polyoxygenated xylene resin, liquid crystal polyester, polyamidoimide, polyether-ketone, PEI, polyether sulfone, polyimides, poly-sulfuration dimethylbenzene, polysulfones, ABS/PVC, ABS/PC, ABS/SMA, PPO/PS, the ABS/ polysulfones, PC/PE, PC/PU, PC/SMA, the PBT/ elastomer, the PET/ elastomer, PET/PMMA, nylon/elastomer.
17. the integral formation method of heating closestool cushion according to claim 14 is characterized in that: described thermoplastic resin is polymethyl methacrylate, PC/PBT, PPO/PBT, PC/PET, PET/PMMA, PET/ polysulfones, ABS/ nylon, nylon/PTFE, PPO/ nylon.
18. the integral formation method of heating closestool cushion according to claim 13 is characterized in that: described filler is wood powder, cellulose wood pulp or mica; The kenel of described filler is powdery or long fibre shape.